CN105884270B - A kind of improved binding agent for pasting stone material enhancing glass fiber net - Google Patents
A kind of improved binding agent for pasting stone material enhancing glass fiber net Download PDFInfo
- Publication number
- CN105884270B CN105884270B CN201410741721.8A CN201410741721A CN105884270B CN 105884270 B CN105884270 B CN 105884270B CN 201410741721 A CN201410741721 A CN 201410741721A CN 105884270 B CN105884270 B CN 105884270B
- Authority
- CN
- China
- Prior art keywords
- powder
- liquid component
- component
- binding agent
- major ingredient
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to building materials technology field, specifically a kind of improved binding agent for pasting stone material enhancing glass fiber net.Binding agent of the present invention is mixed by liquid component and powder component;Wherein liquid component includes mixed emulsion, water and defoamer;Powder component includes cement, quartz sand, cellulose ether, water reducer and retarder;Liquid component and the part by weight of powder component are 1: 3~1: 5, and the finished product viscosity matched somebody with somebody is 20000~60000 centipoises.Binding agent system of the present invention, wherein addition water reducer and retarder can make drying time shorten 40~50%, controls the viscosity B coefficent of slurry in less scope with simply, and the production efficiency and quality uniformity for pasting stone material enhancing glass fiber net is substantially improved.Component liquid powder ratio is improved in configuration, then use cost is greatly lowered 30~40%.The binding agent has setting time suitable, and drying time is short, and spread of viscosity is small, and production efficiency is high, and cost is relatively low, the advantages of beneficial to popularization and application.
Description
Technical field
The present invention relates to building materials technology field, and in particular to a kind of improved binding agent for pasting stone material enhancing glass fiber net.
Background technology
Stone material is a kind of good ornament materials, is widely used to construction and decoration, has preferable decorative effect.But
The anti-folding of TERRAZZO, the insufficient strength of bending resistance are high, need to use in actual use and paste fiberglass gridding cloth in back face of stone
Strengthened, conventional binding material is epoxy resin, unsaturated-resin, water-proof back adhesive for stone etc..Water-proof back adhesive for stone, its energy
Meet back face of stone adhesive property and decorative effect, waterproof gum be applied to back face of stone, one layer of good waterproof layer can be formed,
And the waterproof layer has preferable compatibility and durability with cement based adhesive.
But existing water-proof back adhesive for stone, such as trade mark AD2009 water-proof back adhesive for stone, spontaneously dry speed compared with
Slowly, drying time is grown, and production efficiency when influenceing to use, viscosity B coefficent is big, unfavorable uniform quality during operation, and cost is higher,
It has impact on its further genralrlization application.
The content of the invention
It is an object of the invention to provide a kind of improved binding agent for pasting stone material enhancing glass fiber net, its setting time closes
Suitable, drying time is short, and spread of viscosity is small, and production efficiency is high, and cost is relatively low, beneficial to popularization and application.
The purpose of the present invention is achieved through the following technical solutions, and a kind of improved stone material of pasting strengthens the viscous of glass fiber net
Tie agent, including liquid component and powder component, it is characterised in that:
A kind of improved binding agent for pasting stone material enhancing glass fiber net, is made up of liquid component and powder component two parts,
It is characterized in that:
Described liquid component includes major ingredient and auxiliary material;
The major ingredient of liquid component is the mixed liquor of mixed emulsion and water, wherein, the percentage by weight of mixed emulsion and water is:
Mixed emulsion:40~80%,
Water:20~60%,
The auxiliary material of liquid component is defoamer, and its addition is the 0.01~1% of liquid component major ingredient gross weight;
Described powder component includes major ingredient and auxiliary material;
The major ingredient of powder component is the mixture of cement and quartz sand, wherein, the percentage by weight of cement and quartz sand is:
Cement:35~65%,
Quartz sand:35~65%,
The auxiliary material of powder component is cellulose ether, water reducer and retarder, and the addition of three is respectively powder component master
Expect gross weight:
Cellulose ether:0.1~0.8%,
Water reducer:1~5%,
Retarder:0~0.5%;
Described liquid component and the part by weight of powder component are 1: 3~1: 5, and the finished product viscosity matched somebody with somebody is 20000
~60000 centipoises.
On the basis of above-mentioned technical proposal, described mixed emulsion is any two or three in following three emulsion
Obtained after mixing:
Three kinds of emulsions are respectively pure-acrylic emulsion, styrene-acrylic emulsion, styrene-butadiene emulsion, and in mixed emulsion, every kind of emulsion accounts for liquid group
The percentage by weight of point major ingredient is:10~70%.
On the basis of above-mentioned technical proposal, described defoamer be following material in any one, or two kinds and with
The mixture of upper any proportioning:
Natural oil, polyethers defoamer, higher alcohols, silicon class, polyether-modified silicon, self-emulsifying defoamer, polysiloxane defoaming agent.
On the basis of above-mentioned technical proposal, described water reducer be any one or two in following material and with
The mixture of upper any proportioning:High-efficiency water-reducing agent of poly-carboxylic acid, naphthalene water reducer, aliphatic water reducing agent, sulfamate water reducer;
Described retarder is the mixture of any one or two and any of the above proportioning in following material:Paste
Essence, starch, sodium phosphate, sucrose, tartaric acid.
On the basis of above-mentioned technical proposal, the ratio of described liquid component and powder component is optimal for 1: 4, matches somebody with somebody
Finished product viscosity for 20000~30000 centipoises it is optimal.
The present invention has advantages below;
The present invention is improved the binding agent of existing stickup stone material enhancing glass fiber net, is particularly added in powder component
Appropriate water reducer and retarder, under conditions of physical and mechanical property does not reduce, makes the drying time of binding agent reduce
40~50%, the viscosity B coefficent of slurry is controlled in a less scope, and user is greatly improved and pastes stone material enhancing glass
The production efficiency and quality uniformity of fibre web, solves the problems, such as stone material manufacturing enterprise low production efficiency;Simultaneously as liquid group
Point and the ratio of powder component bring up to 1: 3~5 so that unit area paste the binding agent materials of stone material enhancing glass fiber net into
Originally 30~40% are have dropped, time related cost is greatly lowered 30~40%., be advantageous to the popularization and application of the present invention.
In cement-based material, the ratio of cement and liquid is to have certain requirements, in the prior art the use of liquid component
Measure larger, use cost is higher.In order to be required in the physical and mechanical property requirement and the use operating characteristics of material that ensure material
On the premise of, cost is reduced, improves production efficiency.Present invention employs the method for adding certain additive to realize above-mentioned mesh
, such as to reduce the ratio of liquid component or increasing the ratio of powder, do not make product excessively sticky, add certain diminishing
Agent.Due to the liquid in the present invention be high content high molecular polymer, in low liquid fraction setting time can accelerate, can not
Operating characteristics requires when meeting to use, it is necessary to is adjusted, so the present invention adds retarder simultaneously.For ease of operation and matter
Amount it is uniform, stablizing for phosphoric acid is extremely important, when given formula balanced proper extension operating time and shortening is dried
Between contradiction, successfully solve high content polymer high efficiency diminishing, long-time slow setting, suitable viscosity, these technological difficulties.
The performance test results of product of the present invention such as table 1 below.
The performance test table of 1 product of the present invention of table
In table 1, preceding four groups of data correspond respectively to the product of embodiment one, two, three, four, last column liquid powder ratio
Example 1: 2 is the test data of trade mark AD2009 existing product, it is seen that the performance of product of the present invention is superior to prior art products
Performance.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in further detail.
A kind of improved binding agent for pasting stone material enhancing glass fiber net that the present invention provides, by liquid component and powder component
Two parts form.
Described liquid component includes:Major ingredient and auxiliary material.
Mixed liquor made of mixed emulsion and water is the major ingredient of liquid component;Defoamer is the auxiliary material of liquid component.
In mixed liquor, by weight percentage, mixed emulsion accounts for 40~80%, water:20~60% are accounted for, defoamer adds
Dosage is the 0.01~1% of mixed liquor gross weight.
In the proportioning 40~80% of described mixed emulsion, 40%, 50%, 60%, 70%, 80% can all select
Proportioning;In the proportioning 20~60% of described water, 20%, 30%, 40%, 50%, 60% is all the proportioning that can be selected.Mixing
The mixed liquor of emulsion and water composition, it is the major ingredient of liquid component.
The mixed emulsion is any two or three of mixture in following material:Pure-acrylic emulsion, styrene-acrylic emulsion, fourth
Benzene emulsion (i.e. SBR emulsion).
When configuring mixed emulsion from three kinds of emulsions, following proportioning can be used:Pure-acrylic emulsion 10~70%, phenylpropyl alcohol
Emulsion 10~70%, styrene-butadiene emulsion 10~70%, wherein 10,20,30,40,50,60,70% is all the proportioning that can be selected, three
The kind mixed mixed emulsion total amount of emulsion accounts for the 40%~80% of liquid component major ingredient.
When from any two kinds of emulsions configuration mixed emulsion, the percentage by weight that every kind of emulsion accounts for liquid component major ingredient is
10~70%, wherein 10,20,30,40,50,60,70% is all the proportioning that can be selected, the mixed mixing of two kinds of emulsions is newborn
Liquid total amount accounts for the 40%~80% of liquid component major ingredient, and the amount of one of which emulsion is at least 10%.
Such as:Pure-acrylic emulsion 10% mixes with styrene-acrylic emulsion 30%, pure-acrylic emulsion 10% mixes with styrene-acrylic emulsion 70%, fourth
Benzene emulsion 20% mixes with pure-acrylic emulsion 20%, styrene-butadiene emulsion 40% mixes with pure-acrylic emulsion 40%, styrene-acrylic emulsion 70% and fourth
Benzene emulsion 10% mixes, styrene-acrylic emulsion 30% mixes with styrene-butadiene emulsion 20%, and percentage described above is that emulsion accounts for liquid
The percentage by weight of component major ingredient.
The purpose being used cooperatively from two kinds or three kinds of emulsions is to improve the performance of emulsion.
Defoamer is the auxiliary material of liquid component;The addition of defoamer is the 0.01~1% of liquid component major ingredient weight, its
In 0.01,0.03,0.05,0.07,0.1,0.3,0.6,0.8,1.0% be all the numerical value that can be selected.
Defoamer, also known as anti-foaming agent, it is to eliminate caused unwanted bubbles in production process that it, which is acted on,.The present invention can select
With known defoamer, such as:Natural oil (such as soya-bean oil, corn oil), polyethers defoamer, higher alcohols, silicon class, polyethers
Any one in modified silicon, self-emulsifying defoamer, polysiloxane defoaming agent, or the mixture of two kinds and any of the above proportioning;
The liquid component of the present invention is formed after above each component is well mixed.
Powder component described in the present invention includes:Major ingredient and auxiliary material.
The major ingredient includes:Cement, quartz sand.
In major ingredient, by weight percentage, cement accounts for 35~65%, and quartz sand accounts for 35~65%;Wherein cement proportion
35th, 40,50,55,60,65% is all the numerical value that can be selected, and quartz sand proportioning 35,40,50,55,60,65% is all to select
Numerical value.
Cement can select 32.5 and above label, and quartz sand particle also should not be too thick, such as can select 40~140 mesh
Quartz sand, preferably 40~70 mesh quartz sand, quartz sand mainly plays skeletal support.
The auxiliary material includes:Cellulose ether, water reducer and retarder.
The addition of cellulose ether be major ingredient gross weight 0.1~0.8%, wherein 0.1,0.2,0.5,0.6,0.7,
0.8% is all the numerical value that can be selected;Cellulose ether is the product that the hydrogen of hydroxyl in cellulosic polymer is substituted by alkyl.It is fine
Dimension element is a kind of polyhydroxy high-molecular compound for both not dissolved or not melted, and water, diluted alkaline can be then dissolved in after cellulose is etherified
Solution and organic solvent, and there is thermoplasticity.The cellulose ether that the present invention uses can select molecular weight (viscosity) suitably, example
The relatively low centipoise of cellulose ether 300~10000 of viscosity can be such as used, it acts on the water-retaining property for mainly adjusting slurry;
The addition of water reducer is the 1~5% of major ingredient gross weight, wherein 1,1.5,2,3,4,4.5,5% is all to select
Numerical value;The present invention is to disperse cement granules using the purpose of water reducer, increases its mobility, improves workability, is reduced
Water consumption, rate of drying is improved, improve the compactness and hardness of cement-based material;Described water reducer can select conventional gather
Carboxylic acid high efficiency water reducing agent, naphthalene water reducer, aliphatic water reducing agent, one kind of sulfamate water reducer, or two kinds and to take up an official post
The mixture for proportioning of anticipating;
The addition of retarder be major ingredient gross weight 0~0.5%, wherein 0,0.05,0.1,0.2,0.3,0.4,0.45,
0.5% is all the numerical value that can be selected;The present invention add retarder purpose be in order to extend the presetting period of cement, can
Plasticity is kept in a long time, so as to adjust its setting time, is operated in favor of the brushing of binding agent;It can use what is commonly used
Retarder, such as one kind in dextrin, starch, sodium phosphate, sucrose, tartaric acid, or the mixture of two kinds and any of the above proportioning;
The well mixed powder component that can form the present invention of each component.
Foregoing liquid component and the ratio of powder component can be 1: 3~5, such as 1: 3,1: 3.5,1: 4,1:
4.5th, 1: 5, the finished product viscosity matched somebody with somebody is controlled between 20000~60000 centipoises;Wherein, liquid component and powder component
Ratio 1: 4 is optimal, and the centipoise of finished product viscosity 20000~30000 matched somebody with somebody is optimal.The present invention can be by changing water reducer
Proportioning control the viscosity of product between 20000~60000 centipoises, to adapt to the demand of different user.
In the range of said ratio, the present invention is listed below embodiment:
Embodiment one
Liquid component:
Pure-acrylic emulsion 10%,
Styrene-acrylic emulsion 50%,
Defoamer:Soya-bean oil, addition are the 0.02% of liquid component major ingredient,
Water:40%;
Powder component:
Cement:35%,
Quartz sand:65%,
Cellulose ether:Addition is the 0.1% of powder major ingredient,
High-efficiency water-reducing agent of poly-carboxylic acid:Addition is the 4% of powder major ingredient;
The ratio of liquid component and powder component is 1: 4.5;
The centipoise of finished product viscosity 40000~60000 matched somebody with somebody.
The present embodiment Product checking result:Table 2
Embodiment two
Liquid component:
Pure-acrylic emulsion:30%,
Styrene-butadiene emulsion:40%,
Defoamer:Polyethers defoamer mixes with corn oil, and addition is liquid component major ingredient
0.04%,
Water:30%;
Powder component:
Cement:40%,
Quartz sand:60%,
Cellulose ether:Addition is the 0.3% of powder major ingredient,
Naphthalene water reducer:Addition is the 2% of powder major ingredient,
High-efficiency water-reducing agent of poly-carboxylic acid:Addition is the 2% of powder major ingredient,
Retarder sodium phosphate:Addition is the 0.1% of powder major ingredient;
The ratio of liquid component and powder component is 1: 4;
The centipoise of finished product viscosity 30000~50000 matched somebody with somebody.
The present embodiment Product checking result:Table 3
Embodiment three
Liquid component:
Styrene-acrylic emulsion:35%,
Styrene-butadiene emulsion:25%,
Defoamer:Self-emulsifying defoamer, addition are the 0.1% of liquid component major ingredient,
Water:40%;
Powder component:
Cement:45%,
Quartz sand:55%,
Cellulose ether:Addition is the 0.4% of powder major ingredient,
Aliphatic water reducing agent:Addition is the 1% of powder major ingredient,
Naphthalene water reducer:Addition is the 1% of powder major ingredient,
Retarder sucrose:Addition is the 0.2% of powder major ingredient;
The ratio of liquid component and powder component is 1: 3;
The centipoise of finished product viscosity 30000~50000 matched somebody with somebody.
The present embodiment Product checking result:Table 4
Example IV
Liquid component:
Pure-acrylic emulsion 70%,
Styrene-acrylic emulsion 10%,
Defoamer:The mixture of higher alcohols and silicon class defoamer, addition are liquid component major ingredient
0.3%,
Water:20%;
Powder component:
Cement:50%,
Quartz sand:50%,
Cellulose ether:Addition is the 0.5% of powder major ingredient,
Aliphatic water reducing agent:Addition is the 2% of powder major ingredient,
Naphthalene water reducer:Addition is the 3% of powder major ingredient,
Retarder tartaric acid:Addition is the 0.3% of powder major ingredient;
The ratio of liquid component and powder component is 1: 5;
The centipoise of finished product viscosity 40000~60000 matched somebody with somebody.
The present embodiment Product checking result:Table 5
Embodiment five
Liquid component:
Pure-acrylic emulsion:60%,
Styrene-butadiene emulsion:20%,
Defoamer:Polyether-modified silicon, addition are the 0.9% of liquid component major ingredient,
Water:20%;
Powder component:
Cement:65%,
Quartz sand:35%,
Cellulose ether:Addition is the 0.7% of powder major ingredient,
Naphthalene water reducer:Addition is the 3.5% of powder major ingredient;
Retarder dextrin:Addition is the 0.4% of powder major ingredient;
The ratio of liquid component and powder component is 1: 4;
The centipoise of finished product viscosity 30000~50000 matched somebody with somebody.
Embodiment six
Liquid component:
Styrene-acrylic emulsion:70%,
Styrene-butadiene emulsion:10%,
Defoamer:Polysiloxane defoaming agent, addition are the 1% of liquid component major ingredient,
Water:20%;
Powder component:
Cement:50%,
Quartz sand:50%,
Cellulose ether:Addition is the 0.8% of powder major ingredient,
Aliphatic water reducing agent:Addition is the 2% of powder major ingredient,
Retarder starch:Addition is the 0.5% of powder major ingredient;
The ratio of liquid component and powder component is 1: 3.5;
The centipoise of finished product viscosity 20000~40000 matched somebody with somebody.
Embodiment seven
Liquid component:
Styrene-butadiene emulsion:50%,
Styrene-acrylic emulsion 10%,
Defoamer:Silicon class, polyether-modified silicon, the mixture of higher alcohols and self-emulsifying defoamer, addition is liquid component
The 0.06% of major ingredient,
Water:40%;
Powder component:
Cement:55%,
Quartz sand:45%,
Cellulose ether:Addition is the 0.2% of powder major ingredient,
High-efficiency water-reducing agent of poly-carboxylic acid:Addition is the 1.5% of powder major ingredient,
The ratio of liquid component and powder component is 1: 3;
The centipoise of finished product viscosity 20000~40000 matched somebody with somebody.
Embodiment eight
Liquid component:
Pure-acrylic emulsion:30%,
Styrene-butadiene emulsion:10%,
Defoamer:Corn oil mixes with polysiloxane defoaming agent, and addition is the 0.08% of liquid component major ingredient,
Water:60%;
Powder component:
Cement:60%,
Quartz sand:40%,
Cellulose ether:Addition is the 0.4% of powder major ingredient,
Naphthalene water reducer:Addition is the 2% of powder major ingredient,
Retarder sodium phosphate:Addition is the 0.15% of powder major ingredient;
The ratio of liquid component and powder component is 1: 3;
The centipoise of finished product viscosity 20000~40000 matched somebody with somebody.
Embodiment nine
Liquid component:
Styrene-acrylic emulsion:45%,
Styrene-butadiene emulsion:25%,
Defoamer:Silicon class defoamer, addition are the 0.15% of liquid component major ingredient,
Water:30%;
Powder component:
Cement:45%,
Quartz sand:55%,
Cellulose ether:Addition is the 0.5% of powder major ingredient,
Aliphatic water reducing agent:Addition is the 3.5% of powder major ingredient,
Retarder sucrose:Addition is the 0.3% of powder major ingredient;
The ratio of liquid component and powder component is 1: 4.5;
The centipoise of finished product viscosity 30000~50000 matched somebody with somebody.
Embodiment ten
Liquid component:
Pure-acrylic emulsion:35%,
Styrene-butadiene emulsion:20%,
Defoamer:Polyethers defoamer and polysiloxane defoaming agent mixture, addition are liquid component major ingredient
0.6%,
Water:45%;
Powder component:
Cement:45%,
Quartz sand:55%,
Cellulose ether:Addition is the 0.6% of powder major ingredient,
High-efficiency water-reducing agent of poly-carboxylic acid:Addition is the 3% of powder major ingredient,
Retarder tartaric acid:Addition is the 0.35% of powder major ingredient;
The ratio of liquid component and powder component is 1: 4;
The centipoise of finished product viscosity 20000~40000 matched somebody with somebody.
Embodiment 11
Liquid component:
Styrene-acrylic emulsion:10%,
Styrene-butadiene emulsion:70%,
Defoamer:Corn oil mixes with silicon class defoamer, and addition is the 0.8% of liquid component major ingredient,
Water:20%;
Powder component:
Cement:40%,
Quartz sand:60%,
Cellulose ether:Addition is the 0.8% of powder major ingredient,
Aliphatic water reducing agent:Addition is the 1% of powder major ingredient,
Naphthalene water reducer:Addition is the 4% of powder major ingredient;
Retarder dextrin:Addition is the 0.45% of powder major ingredient;
The ratio of liquid component and powder component is 1: 4;
The centipoise of finished product viscosity 20000~30000 matched somebody with somebody.
Embodiment 12
Liquid component:
Styrene-acrylic emulsion:40%,
Styrene-butadiene emulsion:20%,
Defoamer:The mixing of soya-bean oil and higher alcohols defoamer, addition are the 0.9% of liquid component major ingredient,
Water:40%;
Powder component:
Cement:50%,
Quartz sand:50%,
Cellulose ether:Addition is the 0.7% of powder major ingredient,
Aliphatic water reducing agent:Addition is the 2% of powder major ingredient,
Retarder starch:Addition is the 0.4% of powder major ingredient;
The ratio of liquid component and powder component is 1: 3;
The centipoise of finished product viscosity 20000~50000 matched somebody with somebody.
Embodiment 13
Liquid component:
Pure-acrylic emulsion:10%,
Styrene-acrylic emulsion:20%,
Styrene-butadiene emulsion:30%,
Defoamer:The mixing of soya-bean oil and higher alcohols defoamer, addition are the 0.09% of liquid component major ingredient,
Water:40%;
Powder component:
Cement:55%,
Quartz sand:45%,
Cellulose ether:Addition is the 0.8% of powder major ingredient,
Aliphatic water reducing agent:Addition is the 3% of powder major ingredient,
Retarder:Sucrose mixes with dextrin, and addition is the 0.4% of powder major ingredient;
The ratio of liquid component and powder component is 1: 3;
The centipoise of finished product viscosity 20000~40000 matched somebody with somebody.
Embodiment 14
Liquid component:
Pure-acrylic emulsion:20%,
Styrene-acrylic emulsion:10%,
Styrene-butadiene emulsion:10%,
Defoamer:Soya-bean oil, addition are the 0.05% of liquid component major ingredient,
Water:60%;
Powder component:
Cement:60%,
Quartz sand:40%,
Cellulose ether:Addition is the 0.3% of powder major ingredient,
Aliphatic water reducing agent:Addition is the 2% of powder major ingredient,
Retarder dextrin:Addition is the 0.35% of powder major ingredient;
The ratio of liquid component and powder component is 1: 3;
The centipoise of finished product viscosity 20000~60000 matched somebody with somebody.
The main distinction of the invention with original binding agent is:
1. the proportioning of original binding agent (stone material gum) is liquid: powder=1: 1.5~3, the quasi- example of former base (product) proportioning
For 1: 2, it is desirable in addition to final performance (physical and mechanical property) is met, also to meet the needs of operating characteristics, match somebody with somebody for 1: 2
Than prior art is easier to accomplish;For higher powder ratio, such as liquid: powder=1: 3~5, benchmark example (product) is 1:
4, prior art meets there is larger difficulty in terms of physical and mechanical property and operating characteristics at the same time.The formula success that the present invention provides
To solve these difficult.
2nd, product drying speed ratio of the invention is very fast, and fast more than 30% is wanted compared with original product, and this is for improving user
Production efficiency highly significant.
3rd, product cost of the invention reduces by more than 30%, and it is highly beneficial to reduce cost to client.
4th, product viscosity of the invention is in 20000~60000 centipoises, most preferably 20000~30000 centipoises;And viscosity becomes
Change small, stable operation when being user-friendly, be advantageous to the steady quality of consumer products, be more beneficial for user and use mechanization certainly
Dynamicization operates.
For the ease of comparing, inventor is detected to existing stone material binding agent (trade mark AD2009), as a result referring to table
6。
Table 6
From the contrast of 2~table of table 5 and table 6, product of the invention, in liquid: powder=1: 3,4,4.5,5 when items refer to
Mark is superior to existing gum in liquid: powder=1: indices when 2.
Claims (9)
1. a kind of improved binding agent for pasting stone material enhancing glass fiber net, is made up of liquid component and powder component two parts, its
It is characterised by:
Described liquid component includes major ingredient and auxiliary material;
The major ingredient of liquid component is the mixed liquor of mixed emulsion and water, wherein, the percentage by weight of mixed emulsion and water is:
Mixed emulsion:40~80%,
Water:20~60%,
The auxiliary material of liquid component is defoamer, and its addition is the 0.01~1% of liquid component major ingredient gross weight;
Described powder component includes major ingredient and auxiliary material;
The major ingredient of powder component is the mixture of cement and quartz sand, wherein, the percentage by weight of cement and quartz sand is:
Cement:35~65%,
Quartz sand:35~65%,
The auxiliary material of powder component is cellulose ether, water reducer and retarder, and the addition of three is respectively that powder component major ingredient is total
Weight:
Cellulose ether:0.1~0.8%,
Water reducer:1~5%,
Retarder:0~0.5%;
Described liquid component and the part by weight of powder component are 1: 3~1: 5, the finished product viscosity matched somebody with somebody for 20000~
60000 centipoises.
2. binding agent as claimed in claim 1, it is characterised in that described mixed emulsion is any in following three emulsion
Obtained after two or three of mixing:
Three kinds of emulsions are respectively pure-acrylic emulsion, styrene-acrylic emulsion, styrene-butadiene emulsion, and in mixed emulsion, every kind of emulsion accounts for liquid component master
The percentage by weight of material is:10~70%.
3. binding agent as claimed in claim 1 or 2, it is characterised in that:
Described defoamer be following material in any one, or two kinds and any of the above proportioning mixture:
Natural oil, polyethers defoamer, higher alcohols, silicon class;
The silicon class is:Polysiloxane defoaming agent or polyether-modified silicon.
4. binding agent as claimed in claim 1 or 2, it is characterised in that:
Described water reducer is the mixture of any one or two and any of the above proportioning in following material:Polycarboxylic acids is high
Imitate water reducer, naphthalene water reducer, aliphatic water reducing agent, sulfamate water reducer;
Described retarder is the mixture of any one or two and any of the above proportioning in following material:Dextrin, shallow lake
Powder, sodium phosphate, sucrose, tartaric acid.
5. binding agent as claimed in claim 3, it is characterised in that:
Described water reducer is any one kind in following material, or the mixture of two kinds and any of the above proportioning:Polycarboxylic acids
High efficiency water reducing agent, naphthalene water reducer, aliphatic water reducing agent, sulfamate water reducer;
Described retarder is any one kind in following material, or the mixture of two kinds and any of the above proportioning:Dextrin, shallow lake
Powder, sodium phosphate, sucrose, tartaric acid.
6. binding agent as claimed in claim 1 or 2, it is characterised in that described liquid component and the ratio of powder component are 1:
4 is optimal, and the finished product viscosity matched somebody with somebody is that 20000~30000 centipoises are optimal.
7. binding agent as claimed in claim 3, it is characterised in that described liquid component and the ratio of powder component are 1: 4 most
Good, the finished product viscosity matched somebody with somebody is that 20000~30000 centipoises are optimal.
8. binding agent as claimed in claim 4, it is characterised in that described liquid component and the ratio of powder component are 1: 4 most
Good, the finished product viscosity matched somebody with somebody is that 20000~30000 centipoises are optimal.
9. binding agent as claimed in claim 5, it is characterised in that described liquid component and the ratio of powder component are 1: 4 most
Good, the finished product viscosity matched somebody with somebody is that 20000~30000 centipoises are optimal.