CN105881900A - 一种新型3d打印耗材 - Google Patents

一种新型3d打印耗材 Download PDF

Info

Publication number
CN105881900A
CN105881900A CN201610215387.1A CN201610215387A CN105881900A CN 105881900 A CN105881900 A CN 105881900A CN 201610215387 A CN201610215387 A CN 201610215387A CN 105881900 A CN105881900 A CN 105881900A
Authority
CN
China
Prior art keywords
consumptive material
main body
novel
material main
printable layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610215387.1A
Other languages
English (en)
Other versions
CN105881900B (zh
Inventor
李宗桦
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610215387.1A priority Critical patent/CN105881900B/zh
Publication of CN105881900A publication Critical patent/CN105881900A/zh
Application granted granted Critical
Publication of CN105881900B publication Critical patent/CN105881900B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种新型3D打印耗材，包括耗材主体，还在耗材主体内设置一中空的通孔，并且，通孔内填充有用于在3D打印时，将新打印层和被打印层充分粘合并固化的填充剂。本发明通过在耗材主体中设置一中空的通孔，并在通孔内设置将新打印层和被打印层充分粘合并固化的填充剂，如此，在打印时，通过填充剂使新打印层和旧的被打印层之间粘合牢固，受力不容易发生剥离甚至断裂，3D打印效果好。

Description

一种新型3D打印耗材
技术领域
本发明涉及3D打印材料领域，尤其涉及的是一种新型3D打印耗材。
背景技术
随着近年来3D打印行业的高速发展，廉价的FDM（熔融沉积成型法）的3D打印机已经迅速普及。
但是，由于受材料的限制（目前常用材料有PLA及ABS），其生成的模型实用性不大，特别是PLA容易分解，实用性并不大。其它材料如ABS、PA、PC、PETG等工程塑料，由于热塑性差，用作3D打印耗材打印出来的模型，因为3D打印机的热熔打印头根据设计图上需要喷胶的位置用耗材每喷（涂）一层（很薄）耗材后，喷头需要根据图纸移动到更高一层喷涂，而这个过程每层之间因为耗材的温度差，新喷（涂）的耗材是刚刚被热力溶化的耗材，而之前一层则是已经冷却的耗材，导致两层之间有很大的温差，导致层与层之间粘合度很差，令产品受力时容易发生剥离甚至断裂。
因此，现有技术存在缺陷，需要改进。
发明内容
本发明所要解决的技术问题是：提供一种在3D打印时，使新打印层和旧的被打印层之间粘合度好，打印产品受力不容易发生剥离和断裂的新型3D打印耗材。
本发明的技术方案如下：一种新型3D打印耗材，包括耗材主体，还在耗材主体内设置一中空的通孔，并且，通孔内填充有用于在3D打印时，将新打印层和被打印层充分粘合并固化的填充剂。
应用于上述技术方案，所述的新型3D打印耗材中，填充剂为与耗材主体热熔温度接近的塑化剂、或固态热敏粘合剂。
应用于各个上述技术方案，所述的新型3D打印耗材中，填充剂的热熔温度与耗材主体热熔温度的接近范围为正负20度。
应用于各个上述技术方案，所述的新型3D打印耗材中，填充剂的热熔温度与耗材主体热熔温度的接近范围为正负10度。
应用于各个上述技术方案，所述的新型3D打印耗材中，填充剂为在接近耗材主体热熔温度时，与耗材主体溶解反应并使新打印层和被打印层充分粘合并固化的溶剂。
应用于各个上述技术方案，所述的新型3D打印耗材中，填充剂为包裹有溶剂，并在耗材主体打印时，通过挤压释放溶剂使新打印层和被打印层充分粘合并固化的胶囊溶剂。
应用于各个上述技术方案，所述的新型3D打印耗材中，耗材主体为1.75mm的卷线的线状耗材。
采用上述方案，本发明通过在耗材主体中设置一中空的通孔，并在通孔内设置将新打印层和被打印层充分粘合并固化的填充剂，如此，在打印时，通过填充剂使新打印层和旧的被打印层之间粘合牢固，受力不容易发生剥离甚至断裂，3D打印效果好。
附图说明
图1为现有技术的线状耗材结构图；
图2为本发明的线状耗材结构图。
具体实施方式
以下结合附图和具体实施例，对本发明进行详细说明。
本实施例提供了一种新型3D打印耗材，如图2所示，新型3D打印耗材包括耗材主体201，其中，耗材主体201可以采用现在最流行的，直径为1.75mm的卷线的线状耗材，耗材主体201内设置一中空的通孔202，通孔202内填充有填充剂，其中，填充剂用于在3D打印时，将新打印层和被打印层充分粘合并固化，如此，在打印成型时，新打印层和被打印层粘合度好，使打印产品受力不容易发生剥离和断裂。
其中，填充剂可以设置为塑化剂、或固态热敏粘合剂、或溶剂，其中，塑化剂和固态热敏粘合剂的热熔温度与耗材主体的热熔温度接近，如此，在通过3D打印机的热熔打印头进行打印时，通过加热耗材主体的新打印层喷涂在旧的被打印层时，塑化剂和固态热敏粘合剂也同样被加热，加热的塑化剂或固态热敏粘合剂被加热融化，通过塑化剂或固态热敏粘合剂使新打印层和被打印层相互粘合，从而使新打印层和被打印层粘合度好，使打印产品受力不容易发生剥离和断裂。
其中，塑化剂和固态热敏粘合剂的热熔温度与耗材主体的热熔温度的接近范围为正负20度，优选的，其接近范围为正负10度，例如，打印耗材为ASB打印耗材，其热熔温度为230-240度，则塑化剂和固态热敏粘合剂的热熔温度选择为210度-260度，优选的热熔温度选择为220度-250度。
或者，填充剂也选择为在接近耗材主体热熔温度时，与耗材主体溶解反应并使新打印层和被打印层充分粘合并固化的溶剂，如此，在进行3D打印时，最新喷涂的耗材，即新打印层，虽然在温度上和之前喷涂的一层，即被打印层存在温差，但是因为这层新喷涂的热耗材中含有溶剂，这些溶剂在把之前一层的耗材稍溶化一些，把新旧层的结合处溶合在一起，形成充分粘合并固化。
或者，还可以将填充剂选择为包裹有溶剂，并在耗材主体打印时，通过挤压释放溶剂使新打印层和被打印层充分粘合并固化的胶囊溶剂，如此，通过该结构，可以实现冷打印，即在打印时，无需加热，胶囊溶剂在打印时，通过挤压的方式释放出来，并通过溶剂把被打印层的耗材溶化一些，如此，把新旧层的结合处溶合在一起，形成充分粘合并固化，使用效果更佳。
其中，溶剂的选择可以根据实际需要选取，只要达到以上打印效果即可，此处不做任何限制。
以上仅为本发明的较佳实施例而已，并不用于限制本发明，凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明的保护范围之内。

Claims (7)

1.一种新型3D打印耗材，包括耗材主体，其特征在于，
还在耗材主体内设置一中空的通孔，并且，通孔内填充有用于在3D打印时，将新打印层和被打印层充分粘合并固化的填充剂。
2.根据权利要求1所述的新型3D打印耗材，其特征在于：填充剂为与耗材主体热熔温度接近的塑化剂、或固态热敏粘合剂。
3.根据权利要求2所述的新型3D打印耗材，其特征在于：填充剂的热熔温度与耗材主体热熔温度的接近范围为正负20度。
4.根据权利要求3所述的新型3D打印耗材，其特征在于：填充剂的热熔温度与耗材主体热熔温度的接近范围为正负10度。
5.根据权利要求1所述的新型3D打印耗材，其特征在于：填充剂为在接近耗材主体热熔温度时，与耗材主体溶解反应并使新打印层和被打印层充分粘合并固化的溶剂。
6.根据权利要求1所述的新型3D打印耗材，其特征在于：填充剂为包裹有溶剂，并在耗材主体打印时，通过挤压释放溶剂使新打印层和被打印层充分粘合并固化的胶囊溶剂。
7.根据权利要求1-6任一所述的新型3D打印耗材，其特征在于：耗材主体为1.75mm的卷线的线状耗材。
CN201610215387.1A 2016-04-08 2016-04-08 一种新型3d打印耗材 Active CN105881900B (zh)