CN105860818A - 一种抗氧化水性聚氨酯涂料及其制备方法 - Google Patents

一种抗氧化水性聚氨酯涂料及其制备方法 Download PDF

Info

Publication number
CN105860818A
CN105860818A CN201610279949.9A CN201610279949A CN105860818A CN 105860818 A CN105860818 A CN 105860818A CN 201610279949 A CN201610279949 A CN 201610279949A CN 105860818 A CN105860818 A CN 105860818A
Authority
CN
China
Prior art keywords
parts
mentioned
minute
weight
aqueous polyurethane
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201610279949.9A
Other languages
English (en)
Inventor
李强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610279949.9A priority Critical patent/CN105860818A/zh
Publication of CN105860818A publication Critical patent/CN105860818A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种抗氧化水性聚氨酯涂料，它是由下述重量份的原料组成的：抗氧剂1681‑3、N‑月桂酰肌氨酸钠1‑2、双酚a二缩水甘油醚0.7‑1、尼龙酸甲酯3‑5、聚天冬氨酸0.2‑0.7、铝酸钙2‑3、四氯化钛10‑14、六水三氯化铁0.3‑0.7、28‑30%的过氧化氢溶液30‑40、聚ε‑己内酯二醇600‑700、异佛尔酮二异氰酸酯470‑500、丙酮20‑30、二羟甲基丙酸13‑20、二甘醇4‑6、辛酸亚锡0.1‑0.16、三乙胺5‑7、吡啶硫酮锌0.6‑2、棕榈蜡3‑4、sp800.1‑0.6。本发明的涂膜具有很好的紫外光吸收能力、自清洁性能及拉伸强度。

Description

一种抗氧化水性聚氨酯涂料及其制备方法
技术领域
本发明涉及水性聚氨酯涂料技术领域，尤其涉及一种抗氧化水性聚氨酯涂料及其制备方法。
背景技术
水性聚氨酯以水作为分散介质，与传统溶剂型聚氨酯相比，具有环保、不易燃烧、无毒等优点，广泛应用于涂料、粘合剂、皮革涂饰剂、纺织工业等领域。但是，水性聚氨酯膜的抗紫外老化能力弱，且易被污染，影响了其使用效果。研究表明，通过无机纳米粒子改性的纳米复合材料不仅具有聚合物诸如延展性、弹性等性质，而且也能表现出所添加无机材料的性质。纳米二氧化钛（TiO2）是一种重要的无机半导体材料，具有良好的光催化性、高稳定性、无毒及强紫外线吸收等优异性能。因此，通过纳米TiO2 改性，可以赋予水性聚氨酯复合膜抗菌性、自洁性和紫外吸收能力等，是提高水性聚氨酯膜性能的一种有效途径。
发明内容
本发明目的就是为了弥补已有技术的缺陷，提供一种抗氧化水性聚氨酯涂料及其制备方法。
本发明是通过以下技术方案实现的：
一种抗氧化水性聚氨酯涂料，它是由下述重量份的原料组成的：
抗氧剂1681-3、N-月桂酰肌氨酸钠1-2、双酚a二缩水甘油醚0.7-1、尼龙酸甲酯3-5、聚天冬氨酸0.2-0.7、铝酸钙2-3、四氯化钛10-14、六水三氯化铁0.3-0.7、28-30%的过氧化氢溶液30-40、聚ε-己内酯二醇600-700、异佛尔酮二异氰酸酯470-500、丙酮20-30、二羟甲基丙酸13-20、二甘醇4-6、辛酸亚锡0.1-0.16、三乙胺5-7、吡啶硫酮锌0.6-2、棕榈蜡3-4、sp800.1-0.6。
一种所述的抗氧化水性聚氨酯涂料的制备方法，包括以下步骤：
（1）将上述棕榈蜡加入到其重量3-5倍的无水乙醇中，在80-90℃下保温搅拌6-10分钟，加入抗氧剂168，搅拌至常温，得抗氧化醇液；
（2）将上述sp80、吡啶硫酮锌混合，加入到混合料重量50-60倍的去离子水中，搅拌均匀，得乳化液；
（3）将上述四氯化钛加入到其重量40-50倍的去离子水中，在3-5℃下搅拌混合20-30分钟，加入六水三氯化铁、乳化液，搅拌条件下滴加浓度为5-6%的氨水溶液，调节pH为8.1-8.6，静置30-40分钟，加入上述抗氧化醇液，1000-1200转/分搅拌3-4分钟，抽滤，将滤饼水洗3-4次，常温干燥，得掺杂沉淀；
（4）将上述铝酸钙、N-月桂酰肌氨酸钠混合，加入到混合料重量20-30倍的去离子水中，搅拌均匀，得分散液；
（5）将上述掺杂沉淀加入到其重量80-100倍的去离子水中，超声分散3-5分钟，加入上述28-30%的过氧化氢溶液，磁力搅拌30-40分钟，送入到沸水浴中，恒温加热3-5小时，与上述分散液混合，搅拌至常温，得掺杂钛溶胶；
（6）将上述聚ε-己内酯二醇在100-110℃下真空脱水10-15分钟，冷却至30-40℃，通入氮气，加入上述异佛尔酮二异氰酸酯、尼龙酸甲酯，升高温度为80-90℃，恒温搅拌1.6-2小时，加入上述丙酮重量的20-30%，降低温度为30-40℃，加入上述掺杂钛溶胶、二羟甲基丙酸，升高温度为76-80℃，保温反应40-50分钟，降低温度为40-50℃，依次加入剩余的丙酮、二甘醇、辛酸亚锡，缓慢升高温度为70-75℃，保温反应5-6小时，冷却至常温，倒入乳化桶中，加入剩余各原料，搅拌均匀，加入体系重量30-40%的去离子水，1200-1700转/分搅拌16-20分钟，得抗氧化水性聚氨酯涂料。
所述的一种抗氧化水性聚氨酯涂料及其制备方法，本发明涂料的使用方法为：
将需要涂覆的基材加入到本发明的钛掺杂水洗聚氨酯涂料中，浸润10-20分钟，取出后置于常温下通风4-5天，再在46-50℃下干燥6-10小时，即可。
本发明的优点是：本发明的涂膜具有很好的拉伸强度：
高力学稳定性的粒子成为固定位点，限制了基体分子链的运动，从而提高拉伸强度，纳米粒子在基体中分散均匀，材料受到外力拉伸时形成受力中心，能够引发更多的银纹，消耗大量的能量，起到了补强的作用，因此将纳米二氧化钛加入到有机聚合物中可以提高有机基底的力学性能，提高涂膜的拉伸强度；
本发明的涂膜具有很好的紫外光吸收能力及自清洁性能：
Fe3+掺杂纳米二氧化钛溶胶在可见光下具有最强的光催化性能，能够明显提高涂膜的抗紫外光性能；同时可以利用其光催化降解能力将表面附着的污染物降解去除，因此也具有很好的自清洁性能。
本发明的涂料具有很好的抗氧化性能，使用寿命长，稳定性好。
具体实施方式
一种抗氧化水性聚氨酯涂料，它是由下述重量份的原料组成的：
抗氧剂1681、N月桂酰肌氨酸钠1、双酚a二缩水甘油醚0.7、尼龙酸甲酯3、聚天冬氨酸0.2、铝酸钙2、四氯化钛10、六水三氯化铁0.3、28%的过氧化氢溶液30、聚ε己内酯二醇600、异佛尔酮二异氰酸酯470、丙酮20、二羟甲基丙酸13、二甘醇4、辛酸亚锡0.1、三乙胺5、吡啶硫酮锌0.6、棕榈蜡3、sp800.1。
一种所述的抗氧化水性聚氨酯涂料的制备方法，包括以下步骤：
（1）将上述棕榈蜡加入到其重量3倍的无水乙醇中，在80℃下保温搅拌6分钟，加入抗氧剂168，搅拌至常温，得抗氧化醇液；
（2）将上述sp80、吡啶硫酮锌混合，加入到混合料重量50倍的去离子水中，搅拌均匀，得乳化液；
（3）将上述四氯化钛加入到其重量40倍的去离子水中，在3℃下搅拌混合20分钟，加入六水三氯化铁、乳化液，搅拌条件下滴加浓度为5%的氨水溶液，调节pH为8.1，静置30分钟，加入上述抗氧化醇液，1000转/分搅拌3分钟，抽滤，将滤饼水洗3次，常温干燥，得掺杂沉淀；
（4）将上述铝酸钙、N月桂酰肌氨酸钠混合，加入到混合料重量20倍的去离子水中，搅拌均匀，得分散液；
（5）将上述掺杂沉淀加入到其重量80倍的去离子水中，超声分散3分钟，加入上述28%的过氧化氢溶液，磁力搅拌30分钟，送入到沸水浴中，恒温加热3小时，与上述分散液混合，搅拌至常温，得掺杂钛溶胶；
（6）将上述聚ε己内酯二醇在100℃下真空脱水10分钟，冷却至30℃，通入氮气，加入上述异佛尔酮二异氰酸酯、尼龙酸甲酯，升高温度为80℃，恒温搅拌1.6小时，加入上述丙酮重量的20%，降低温度为30℃，加入上述掺杂钛溶胶、二羟甲基丙酸，升高温度为76℃，保温反应40分钟，降低温度为40℃，依次加入剩余的丙酮、二甘醇、辛酸亚锡，缓慢升高温度为70℃，保温反应5小时，冷却至常温，倒入乳化桶中，加入剩余各原料，搅拌均匀，加入体系重量30%的去离子水，1200转/分搅拌16分钟，得抗氧化水性聚氨酯涂料。
一种抗氧化水性聚氨酯涂料及其制备方法，本发明涂料的使用方法为：
将需要涂覆的基材加入到本发明的钛掺杂水洗聚氨酯涂料中，浸润10分钟，取出后置于常温下通风4天，再在46℃下干燥6小时，即可。
性能测试 ：
吸水率 0.0147%，吸水前粘结力为 12.70 MPa，在吸水浸泡实验浸泡 3200 h 后保持10.39MPa 的高粘结力。

Claims (3)

1.一种抗氧化水性聚氨酯涂料，其特征在于，它是由下述重量份的原料组成的：
抗氧剂1681-3、N-月桂酰肌氨酸钠1-2、双酚a二缩水甘油醚0.7-1、尼龙酸甲酯3-5、聚天冬氨酸0.2-0.7、铝酸钙2-3、四氯化钛10-14、六水三氯化铁0.3-0.7、28-30%的过氧化氢溶液30-40、聚ε-己内酯二醇600-700、异佛尔酮二异氰酸酯470-500、丙酮20-30、二羟甲基丙酸13-20、二甘醇4-6、辛酸亚锡0.1-0.16、三乙胺5-7、吡啶硫酮锌0.6-2、棕榈蜡3-4、sp800.1-0.6。
2.一种如权利要求1所述的抗氧化水性聚氨酯涂料的制备方法，其特征在于，包括以下步骤：
（1）将上述棕榈蜡加入到其重量3-5倍的无水乙醇中，在80-90℃下保温搅拌6-10分钟，加入抗氧剂168，搅拌至常温，得抗氧化醇液；
（2）将上述sp80、吡啶硫酮锌混合，加入到混合料重量50-60倍的去离子水中，搅拌均匀，得乳化液；
（3）将上述四氯化钛加入到其重量40-50倍的去离子水中，在3-5℃下搅拌混合20-30分钟，加入六水三氯化铁、乳化液，搅拌条件下滴加浓度为5-6%的氨水溶液，调节pH为8.1-8.6，静置30-40分钟，加入上述抗氧化醇液，1000-1200转/分搅拌3-4分钟，抽滤，将滤饼水洗3-4次，常温干燥，得掺杂沉淀；
（4）将上述铝酸钙、N-月桂酰肌氨酸钠混合，加入到混合料重量20-30倍的去离子水中，搅拌均匀，得分散液；
（5）将上述掺杂沉淀加入到其重量80-100倍的去离子水中，超声分散3-5分钟，加入上述28-30%的过氧化氢溶液，磁力搅拌30-40分钟，送入到沸水浴中，恒温加热3-5小时，与上述分散液混合，搅拌至常温，得掺杂钛溶胶；
（6）将上述聚ε-己内酯二醇在100-110℃下真空脱水10-15分钟，冷却至30-40℃，通入氮气，加入上述异佛尔酮二异氰酸酯、尼龙酸甲酯，升高温度为80-90℃，恒温搅拌1.6-2小时，加入上述丙酮重量的20-30%，降低温度为30-40℃，加入上述掺杂钛溶胶、二羟甲基丙酸，升高温度为76-80℃，保温反应40-50分钟，降低温度为40-50℃，依次加入剩余的丙酮、二甘醇、辛酸亚锡，缓慢升高温度为70-75℃，保温反应5-6小时，冷却至常温，倒入乳化桶中，加入剩余各原料，搅拌均匀，加入体系重量30-40%的去离子水，1200-1700转/分搅拌16-20分钟，得抗氧化水性聚氨酯涂料。
3.根据权利要求1、2所述的一种抗氧化水性聚氨酯涂料及其制备方法，本发明涂料的使用方法为：
将需要涂覆的基材加入到本发明的钛掺杂水洗聚氨酯涂料中，浸润10-20分钟，取出后置于常温下通风4-5天，再在46-50℃下干燥6-10小时，即可。
CN201610279949.9A 2016-04-29 2016-04-29 一种抗氧化水性聚氨酯涂料及其制备方法 Withdrawn CN105860818A (zh)