CN105860706A - Lacquer for building outer wall marble-imitated decoration - Google Patents
Lacquer for building outer wall marble-imitated decoration Download PDFInfo
- Publication number
- CN105860706A CN105860706A CN201610285027.9A CN201610285027A CN105860706A CN 105860706 A CN105860706 A CN 105860706A CN 201610285027 A CN201610285027 A CN 201610285027A CN 105860706 A CN105860706 A CN 105860706A
- Authority
- CN
- China
- Prior art keywords
- parts
- lacquer
- add
- sufficiently mixed
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses lacquer for building outer wall marble-imitated decoration and relates to the technical field of building coating. The lacquer is prepared from, by weight, 30-40 parts of acrylic acid resin, 20-30 parts of methylated amino resin, 12-17 parts of natural colorful sand, 10-15 parts of fly ash, 8-12 parts of petroleum coke, 6-10 parts of chlorosulfonated polyethylene, 5-8 parts of Carbomer resin, 5-8 parts of soybean albumin glue, 4-6 parts of flexibilizer, 4-6 parts of nano titanium dioxide, 3-5 parts of nano aluminum oxide, 3-5 parts of castor oil, 2-3 parts of polyoxyethylene lauryl ether, 2-3 parts of sodium hexametaphosphate and 100-150 parts of water. The lacquer can be firmly attached to a building outer wall, is free of toxin and smell, and does not release harmful matter, appearance of a formed lacquer film is similar to that of marble, and the lacquer has natural and real gloss, has excellent fire prevention performance, water prevention performance, acid and alkali resistance and stain resistance, can effectively relieve erosion of the outside environment to the building outer wall and prolongs the service life of a building.
Description
Technical field:
The present invention relates to building coating technical field, be specifically related to a kind of external wall parian decoration and use
True mineral varnish.
Background technology:
True mineral varnish is the coating that a kind of decorative effect exactly likes marble, granite.Mainly use shades of colour
Natural stone-powder formulated, be applied to the imitative stone effect of external wall, therefore also known as liquid stone.Very
Building after mineral varnish finishing, has natural real natural colour, gives elegance, harmony, serious
Aesthetic feeling, be suitable for the indoor and outdoor decoration of all kinds of building.Particularly decorate on curved-surface building thing, raw
Dynamic true to nature, there is the effect of a kind of back to nature.But the resistance to water of presently commercially available true mineral varnish and resistance to soiling are poor,
Have a strong impact on the true mineral varnish decorative effect as exterior coating.
Summary of the invention:
The technical problem to be solved is to provide one to have excellent fire prevention, waterproof, acid and alkali-resistance
Decorate with the external wall parian of resistance to soiling and good decorating effect and use true mineral varnish.
The technical problem to be solved uses following technical scheme to realize:
True mineral varnish used by a kind of external wall parian decoration, is made up of the raw material of following parts by weight:
Acrylic resin 30-40 part, methyl-etherified amino resins 20-30 part, natural color stone sand 12-17 part,
Flyash 10-15 part, petroleum coke 8-12 part, chlorosulfonated polyethylene 6-10 part, carbomer 5-8 part,
Soybean protein glue 5-8 part, toughener 4-6 part, nanometer titanium dioxide 4-6 part, nano aluminium oxide 3-5 part,
Castor oil 3-5 part, ethoxylated dodecyl alcohol 2-3 part, calgon 2-3 part, water 100-150 part.
Its preparation method comprises the steps:
(1) acrylic resin, methyl-etherified amino resins and nano aluminium oxide are sufficiently mixed, grinding at room temperature 15
Min, microwave treatment 10min under microwave frequency 2450MHz, power 700W, it is subsequently adding oil
Jiao, chlorosulfonated polyethylene and soybean protein glue, continue microwave treatment 5min, obtain material I;
(2) in water, add flyash and nanometer titanium dioxide, be sufficiently mixed the gentle and quiet 30min that puts of rear chamber, then add
Enter castor oil and ethoxylated dodecyl alcohol, at 0-5 DEG C, stand 1h after mixing, obtain material II;
(3) in material I, material II, natural color stone sand, carbomer, toughener and calgon are added,
Add in ball mill after being sufficiently mixed, be milled to fineness less than 50 μm.
Described toughener is made up of the raw material of following parts by weight: low density polyethylene (LDPE) 15-20 part, ardealite
Powder 10-15 part, microwax 8-11 part, glutinous rice flour 6-9 part, microcrystalline cellulose 4-7 part, PEG400
4-7 part, polyvinylpyrrolidone 3-6 part, nano-calcium carbonate 3-6 part, urea 2-4 part, spaonin powder 2-4
Part, bone black 1-2 part, melamine 1-2 part, coal tar 10-15 part, rosin 20-25 part, its system
Preparation Method is: first add in rosin by low density polyethylene (LDPE) and microwax, in supersonic frequency 40kHz,
Ultrasonically treated 15min under power 50W, under microwave frequency 2450MHz, power 700W at microwave
Reason 10min, is subsequently adding PEG400, nano-calcium carbonate and bone black, continues microwave treatment 5min,
After naturally cool to adding phosphogypsum powder, urea, melamine and coal tar when 60-70 DEG C, insulation mixing
10min, adds glutinous rice flour, microcrystalline cellulose, polyvinylpyrrolidone after continuing to naturally cool to room temperature
And spaonin powder, it is sufficiently mixed uniformly.
The addition of this toughener can not only improve paint vehicle mobility and paint film flexibility, moreover it is possible to improves paint film
Insulating properties, wearability and heat-resisting quantity.
The invention has the beneficial effects as follows: the present invention true mineral varnish energy strong bond on external wall, nontoxic nothing
Taste, will not discharge harmful substance, and the paint film appearance formed is similar to marble, have natural truly
Natural gloss, and have excellence fire prevention, waterproof, acid and alkali-resistance and resistance to soiling, outside effectively slowing down
The erosion to external wall of boundary's environment, extends the life-span of building.
Detailed description of the invention:
For the technological means making the present invention realize, creation characteristic, reach purpose and effect and be readily apparent from
Solve, below in conjunction with specific embodiment, the present invention is expanded on further.
Embodiment 1
(1) 30 parts of acrylic resins, 30 parts of methyl-etherified amino resins and 3 parts of nano aluminium oxides are sufficiently mixed,
Grinding at room temperature 15min, microwave treatment 10min under microwave frequency 2450MHz, power 700W, so
8 parts of petroleum cokes of rear addition, 8 parts of chlorosulfonated polyethylenes and 5 parts of soybean protein glue, continue microwave treatment 5min,
Obtain material I;
(2) in 150 parts of water, add 10 parts of flyash and 6 parts of nanometer titanium dioxides, be sufficiently mixed that rear chamber is gentle and quiet puts
30min, adds 3 parts of castor oil and 2 parts of ethoxylated dodecyl alcohols, quiet at 0-5 DEG C after mixing
Put 1h, obtain material II;
(3) in material I add material II, 12 parts of natural color stone sands, 6 parts of carbomers, 4 parts of toughener and
2 parts of calgons, add in ball mill after being sufficiently mixed, and are milled to fineness less than 50 μm.
The preparation of toughener: first 20 parts of low density polyethylene (LDPE)s and 10 parts of microwaxes are added in 25 parts of rosin,
Ultrasonically treated 15min under supersonic frequency 40kHz, power 50W, then at microwave frequency 2450MHz,
Microwave treatment 10min under power 700W, is subsequently adding 4 parts of PEG400s, 5 parts of nano-calcium carbonates and 1
Part bone black, continues microwave treatment 5min, after naturally cool to add when 60-70 DEG C 10 parts of phosphogypsum powders, 2
Part urea, 1 part of melamine and 15 parts of coal tar, insulation mixing 10min, continues to naturally cool to room temperature
After add 8 parts of glutinous rice flours, 4 parts of microcrystalline celluloses, 4 parts of polyvinylpyrrolidones and 2 parts of spaonin powders, fill
Divide and mix.
Embodiment 2
(1) 40 parts of acrylic resins, 25 parts of methyl-etherified amino resins and 4 parts of nano aluminium oxides are sufficiently mixed,
Grinding at room temperature 15min, microwave treatment 10min under microwave frequency 2450MHz, power 700W, so
8 parts of petroleum cokes of rear addition, 6 parts of chlorosulfonated polyethylenes and 5 parts of soybean protein glue, continue microwave treatment 5min,
Obtain material I;
(2) in 150 parts of water, add 15 parts of flyash and 4 parts of nanometer titanium dioxides, be sufficiently mixed that rear chamber is gentle and quiet puts
30min, adds 4 parts of castor oil and 2 parts of ethoxylated dodecyl alcohols, quiet at 0-5 DEG C after mixing
Put 1h, obtain material II;
(3) in material I add material II, 15 parts of natural color stone sands, 5 parts of carbomers, 5 parts of toughener and
2 parts of calgons, add in ball mill after being sufficiently mixed, and are milled to fineness less than 50 μm.
The preparation of toughener: first 15 parts of low density polyethylene (LDPE)s and 8 parts of microwaxes are added in 20 parts of rosin,
Ultrasonically treated 15min under supersonic frequency 40kHz, power 50W, then at microwave frequency 2450MHz,
Microwave treatment 10min under power 700W, is subsequently adding 6 parts of PEG400s, 3 parts of nano-calcium carbonates and 1
Part bone black, continues microwave treatment 5min, after naturally cool to add when 60-70 DEG C 15 parts of phosphogypsum powders, 2
Part urea, 2 parts of melamines and 10 parts of coal tar, insulation mixing 10min, continues to naturally cool to room temperature
After add 6 parts of glutinous rice flours, 5 parts of microcrystalline celluloses, 3 parts of polyvinylpyrrolidones and 2 parts of spaonin powders, fill
Divide and mix.
The general principle of the present invention and principal character and advantages of the present invention have more than been shown and described.One's own profession
Skilled person will appreciate that of industry, the present invention is not restricted to the described embodiments, above-described embodiment and explanation
The principle that the present invention is simply described described in book, without departing from the spirit and scope of the present invention,
The present invention also has various changes and modifications, and these changes and improvements both fall within claimed invention model
In enclosing.Claimed scope is defined by appending claims and equivalent thereof.
Claims (3)
1. true mineral varnish used by an external wall parian decoration, it is characterised in that by following parts by weight
Raw material make:
Acrylic resin 30-40 part, methyl-etherified amino resins 20-30 part, natural color stone sand 12-17 part,
Flyash 10-15 part, petroleum coke 8-12 part, chlorosulfonated polyethylene 6-10 part, carbomer 5-8 part,
Soybean protein glue 5-8 part, toughener 4-6 part, nanometer titanium dioxide 4-6 part, nano aluminium oxide 3-5 part,
Castor oil 3-5 part, ethoxylated dodecyl alcohol 2-3 part, calgon 2-3 part, water 100-150 part.
True mineral varnish used by external wall parian the most according to claim 1 decoration, it is characterised in that
Described toughener is made up of the raw material of following parts by weight: low density polyethylene (LDPE) 15-20 part, phosphogypsum powder
10-15 part, microwax 8-11 part, glutinous rice flour 6-9 part, microcrystalline cellulose 4-7 part, PEG400 4-7
Part, polyvinylpyrrolidone 3-6 part, nano-calcium carbonate 3-6 part, urea 2-4 part, spaonin powder 2-4 part,
Bone black 1-2 part, melamine 1-2 part, coal tar 10-15 part, rosin 20-25 part, its preparation side
Method is: first add in rosin by low density polyethylene (LDPE) and microwax, in supersonic frequency 40kHz, power
Ultrasonically treated 15min under 50W, microwave treatment 10 under microwave frequency 2450MHz, power 700W
Min, is subsequently adding PEG400, nano-calcium carbonate and bone black, continues microwave treatment 5min, treats certainly
So being cooled to when 60-70 DEG C add phosphogypsum powder, urea, melamine and coal tar, insulation mixes 10min,
Glutinous rice flour, microcrystalline cellulose, polyvinylpyrrolidone and Chinese honey locust is added after continuing to naturally cool to room temperature
Powder, is sufficiently mixed uniformly.
True mineral varnish used by external wall parian the most according to claim 1 decoration, it is characterised in that
Its preparation method comprises the steps:
(1) acrylic resin, methyl-etherified amino resins and nano aluminium oxide are sufficiently mixed, grinding at room temperature 15
Min, microwave treatment 10min under microwave frequency 2450MHz, power 700W, it is subsequently adding oil
Jiao, chlorosulfonated polyethylene and soybean protein glue, continue microwave treatment 5min, obtain material I;
(2) in water, add flyash and nanometer titanium dioxide, be sufficiently mixed the gentle and quiet 30min that puts of rear chamber, then add
Enter castor oil and ethoxylated dodecyl alcohol, at 0-5 DEG C, stand 1h after mixing, obtain material II;
(3) in material I, material II, natural color stone sand, carbomer, toughener and calgon are added,
Add in ball mill after being sufficiently mixed, be milled to fineness less than 50 μm.