CN105837166A - Medical stone ware preparing method and ware prepared by method - Google Patents
Medical stone ware preparing method and ware prepared by method Download PDFInfo
- Publication number
- CN105837166A CN105837166A CN201610163593.2A CN201610163593A CN105837166A CN 105837166 A CN105837166 A CN 105837166A CN 201610163593 A CN201610163593 A CN 201610163593A CN 105837166 A CN105837166 A CN 105837166A
- Authority
- CN
- China
- Prior art keywords
- raw material
- medical stone
- ware
- vessel
- pureed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a medical stone ware preparing method. In the method, original medical stone is ground, and then is mixed with other mineral materials and the like to prepare a blank, and the blank is sintered to obtain a medical stone ware, so as to solve the problem in the prior art of waste of raw material original medical stone; at the same time, by grinding, minerals and other beneficial components in the medical stone can be fully released, so that the problem in the prior art that mineral elements in medical stone cannot be fully utilized is solved. Furthermore, by adding other minerals, the content of the minerals in the prepared ware is more abundant. At the same time, the invention also provides the medical stone ware prepared by the method provided by the invention; the medical stone ware has the advantages of short ware preparation period, high forming rate and easy mass production, the ware has good mineral absorption performance and can effectively purify water quality, and substances in the ware have the advantages of being rich in content, easy to seep, good in health care performance and the like.
Description
Technical field
The present invention relates to vessel preparation field, in particular to a kind of medical stone container
Preparation method and the vessel prepared by the method.
Background technology
Maifanitum has load in Compendium of Material Medica: " shape such as holds a poly-wheat meal, has grain such as
Bean such as rice, its yellow skin is white." therefore thus gain the name.Maifanitum quality in historical records especially with
Area, high Lip river is preferred, and powder enters Chinese medicine, and the water soaked can be drunk, it is possible to for taking a shower, have strong
Body and the drug effect of life lengthening.Detecting through authoritative institution, Maifanitum adsorptivity is activated carbon
20000 times, can not only purify water and increase the trace element useful to human body, moreover it is possible to remove tea
The two of water poison greatly: one is to remove pesticide residues, and two is effectively to reduce and eliminate heavy metal to surpass
The effects such as mark.
People the most naturally contemplate and utilize Maifanitum rich in beneficial element and to have suction
The performance of attached harmful substance, and prepare can medical stone container used in everyday, thus pass through
These vessel are used to realize the purpose of health care.
Such as, prior art (CN1073343A, publication date on June 23rd, 1993) is just
Disclosing a kind of maifanshi health-care vessel, it is raw material by Maifanitum, and to grind
The technique of cutting prepares corresponding medical stone container.
Meanwhile, prior art (CN102190109A, publication date: on JIUYUE 21st, 2011)
Also disclosing that the Maifan stone container that a kind of cloisonné is decorated, its agent structure is Maifanitum carving
Form.
But, existing medical stone container method, is all logical on the basis of natural medical stone
The methods such as engraving, polishing of crossing make, and therefore there is serious waste in manufacturing process
The phenomenon of raw ore building stones.Meanwhile, environment and water source can be made by existing manufacture method aborning
Becoming to pollute, and existing methodical fabrication cycle is longer, ratio of briquetting is relatively low, and type controls difficulty
Degree is relatively big, and production and factory calibration are also difficult to formulate, and mass production difficulty also compares
Greatly.Further, the product efficacy of the medical stone container that existing method makes is poor, slightly
The production process put makes that some Maifanitums are original is of value to the mineral element of health not
Can obtain Appropriate application, mineral characteristic could not obtain good performance.
In view of this, the special proposition present invention.
Summary of the invention
The first object of the present invention is to provide the preparation method of a kind of medical stone container.This
In bright method, by by former for Maifanitum stone grinder powder, and after mixing with other mineral raw materials etc.
Base is fired and is obtained medical stone container, to solve stone former to raw material Maifanitum wave in prior art
The problem taken；Meanwhile, in the present invention, by grinding the mineral etc. also made in Maifanitum
Beneficiating ingredient can fully be discharged, thus solves Maifanitum chats in prior art
Matter-element element fails the problem being fully utilized.Further, in the present invention, by adding it
His mineral, also makes the vessel mineral content obtained by the inventive method richer
Rich.It is high that the inventive method has Maifanitum raw material utilization efficiency, and vessel fabrication cycle is short, one-tenth
The advantages such as type rate is high, health properties is good.
The second object of the present invention is to provide a kind of by medical stone container, and it is by institute of the present invention
The method of stating prepares, and has that vessel fabrication cycle is short, ratio of briquetting is high, is prone to batch production,
Vessel ore deposit absorption property well and can effectively purify water, and in vessel, content of material is abundant and easily oozes
Go out and the advantage such as health properties is good.
In order to realize the above-mentioned purpose of the present invention, spy by the following technical solutions:
The preparation method of a kind of medical stone container, described method comprises the steps: according to weight
Amount percent weighs Maifanitum raw ore 50-85%, Kaolin 10-20%, anion powder respectively
3%-10% and mixed mineral raw material 2-20%, as raw material, and by after raw material mixed grinding,
Raw material add after mixed grinding water and is in harmonious proportion, obtaining pureed compound, and pureed is mixed
Close material to shape after base, fire, obtain medical stone container；
Wherein, described mixed mineral raw material is magnesium, copper, zinc, rare earth, potassium, nickel compound
Mixed mineral raw material.
In the present invention, by by former for Maifanitum stone with after the raw material mixing pulverizing such as other mineral
Base is fired and is obtained medical stone container, so that raw material Maifanitum can be by fully profit
With, and improve obtained vessel mineral content；Meanwhile, wheat meal is also made by grinding
The beneficiating ingredients such as the mineral in stone can fully be discharged.The inventive method has wheat
Meal stone raw material utilization efficiency is high, and vessel fabrication cycle is short, ratio of briquetting is high, health properties is good
Advantage.
Optionally, in the present invention, according to percent by weight, described raw material is respectively wheat meal
Stone raw ore 60-70%, Kaolin 15-18%, anion powder 5%-10% and mixed mineral are former
Material 10-12%.
Optionally, in the present invention, described Maifanitum raw ore is deep layer Maifanitum ore deposit, In The Songshan Region
Stone.Further, after the deep layer Maifanitum ore extraction of described In The Songshan Region, and it is positioned over certainly
So environment is after lower more than 2 years, is re-used as raw material Maifanitum raw ore of the present invention and uses.
Optionally, heretofore described magnesium, copper, zinc, rare earth, potassium, nickel compound be magnesium,
Copper, zinc, rare earth, potassium, the inorganic salt compound of nickel.
Optionally, in the present invention, still further comprise after raw material is cleaned, sieves, then enter
Row weighs, mixes and the step of pulverizing.
Optionally, in the present invention, in described grinding steps, may further include ground
By attraction in journey, drying and sieving carries out the step of remove impurity.
In the present invention, by remove impurity in process of lapping, such that it is able to unnecessary by raw material
Mineral remove, improve precision and the purity of effective raw material.
Optionally, in the present invention, described attraction remove impurity is during raw mill,
Use the removal step that ferrum element absorption unnecessary for raw material is removed by the mode of attraction.
Optionally, in the present invention, described blowing remove impurity is during raw mill, uses
The dust produced in process of lapping and unnecessary impurity are removed by small blast fan by blowing
Removal step.
Optionally, in the present invention, described in remove impurity of sieving for after process of lapping, use dusting cover
Powder stock is sieved, to remove the bigger impurity of volume and the removal step of raw material.
Optionally, in the present invention, described raw material add after mixed grinding water and is in harmonious proportion
In step, the raw material after described mixed grinding is (5-8) with the mass ratio of water: (2-5)；Excellent
Choosing, the raw material after described mixed grinding is (6-7) with the mass ratio of water: (3-4).
In the present invention, by the selection of raw material and water ratio and adjustment, so that enter one
Step and rear gained pug have preferable viscosity.
Optionally, in the present invention, still further comprise and the obtained pureed that tempers is mixed
Close after material vacuum seals and deposit, then pureed is mixed raw material and takes out, then by mud after taking-up
Shape mixing raw material carries out cutting, and the sealing of pureed raw material piecemeal vacuum room temperature after cutting is deposited
Put, after then again depositing the taking-up of rear gained clod, then carry out the step of base.
In the present invention, by pureed mixing material vacuum is encapsulated and deposits, so that mud
In shape raw material, each component can fully merge fermentation；Meanwhile, Vacuum Package is it is also possible that former
Material Mineral Elements in Jadeite Shellfish fully separates out, and then improves the health-care effect of obtained vessel.
Optionally, in the present invention, described in temper after obtained pureed mixing raw material true
The temperature deposited after empty sealing is 10-20 DEG C, and the time deposited is 30-60d.
Optionally, in the present invention, described is will by after taking-up, pureed mixing raw material carries out cutting
After taking-up sized by pureed mixing raw material cutting uniformly and be suitable to the pureed raw material of carrying.
Optionally, in the present invention, after described cutting, pureed raw material piecemeal vacuum seals and deposits
Temperature be 10-20 DEG C, the time deposited is 60-90d.Optionally, in the present invention, described
Base is that the cutting pureed raw material after taking out from sealing device breaks on surface platform
The uniform slice of thin and thick；Slice is cut into required width again；Then moderate by width then,
Slice be combined into the corresponding form of required vessel；It follows that dip in water with brush pen, by slice
In conjunction with part carry out organic adhesive, i.e. obtain base type.Further, if tea to be produced
Kettle class vessel, then need to reserve corresponding pore in base type.
Optionally, in the present invention, described in be fixed to first be positioned over dry by gained base type after base
In dry shady and cool environment, dry in the sun sizing the most in the sun.
Optionally, gained base type after base is first positioned over dry by heretofore described being fixed to
In shady and cool environment after 24h, then place it in dry in the sun 48h under sunlight, burn the most again
System.
Optionally, in the present invention, described in the temperature fired be 1000-1500 DEG C, fire time
Between be 12-24h.
In the present invention, by the selection of the firing condition such as firing temperature and firing time and excellent
Change, thus further increase and fire the intensity of gained medical stone container and vessel are kept
Original high mineral content, thus improve practicality and the health of vessel；Meanwhile,
By the regulation to firing temperature, it is also possible to further the color firing vessel is adjusted
Whole.
Optionally, heretofore described firing temperature is 1100-1300 DEG C；Preferably, this
In bright, described firing temperature is 1200-1300 DEG C.
Optionally, in the present invention, described in fire be to fire for 2 times, rear base type will be dried and burn
Make 2 times.
Optionally, in the present invention, it is also possible to include quartz sand is positioned over teapot, teacup etc.
After at the device mouth of shape base type, then it is fired, thus avoids vessel in sintering procedure
The step of bonding is there is with the device body part of vessel at device mouth.
Optionally, in the present invention, also include to fire the step that rear gained vessel are polished further
Suddenly.
Optionally, in the present invention, described polishing for will fire rear gained vessel polished silicon wafer and
Sand paper is polished respectively.
Optionally, heretofore described polished silicon wafer is the polished silicon wafer made by coconut husk.
Optionally, in the present invention, described sand paper is 320-600 code sand paper；Preferably, originally
In invention, described sand paper is 360 yards of sand paper.
Optionally, the present invention still further comprises the step of vessel wiping after polishing.Enter
One step, described wiping is the wiping carried out with high absorption affinity sea, and after wiping, uses
Boiling water carries out 3 times and cleans vessel.
Optionally, in the present invention, it is also possible to include class vessel with cover such as the teapots after polishing
Carry out the step of whole mouth process.Described whole mouth is processed as entering Hu Kou with lid corundum
The grinding that row is careful, non-loosening, seamless, antiseep so that the two is combined closely.
The present invention additionally provides a kind of medical stone container simultaneously, and described vessel are by of the present invention
Method prepares.
In the present invention, prepare medical stone container by using with the method for the invention, thus
Having that vessel fabrication cycle is short, ratio of briquetting is high, vessel content of mineral substances enriches, health properties
The advantage such as good.
Optionally, the one during heretofore described vessel are kettle, cup, bucket, bowl, bottle.
Compared with prior art, the invention have the benefit that
(1) in the present invention, by by former for Maifanitum stone grinder powder and former with other mineral
After the mixing such as material, base is fired and is obtained medical stone container, so that raw material Maifanitum is former
Material can be fully utilized, and improves obtained vessel mineral content；Meanwhile, pass through
Grind the beneficiating ingredients such as the mineral also made in Maifanitum can fully be discharged.This
It is high that inventive method has Maifanitum raw material utilization efficiency, vessel fabrication cycle is short, ratio of briquetting is high,
It is prone to batch production and the advantage such as health properties is good；
(2), in the present invention, medical stone container is prepared by using with the method for the invention,
Thus have that vessel fabrication cycle is short, ratio of briquetting is high, it is easy to batch production and vessel adsorptivity
Can effectively purify water well, vessel content of mineral substances is abundant and be prone to ooze out, health
Advantage can be waited well.
Detailed description of the invention
Below in conjunction with embodiment, embodiment of the present invention are described in detail, but this
Skilled person is it will be appreciated that the following example is merely to illustrate the present invention, and should not regard
For limiting the scope of the present invention.Unreceipted actual conditions person in embodiment, according to normal condition
Or the condition of manufacturer's suggestion is carried out.Agents useful for same or instrument unreceipted production firm person, all
For the conventional products that can be obtained by commercially available purchase.
Embodiment 1
(1) ore dressing: choose In The Songshan Region deep layer Maifanitum Ore, and be placed on blowing
Lower more than 2 years of Exposure to Sunlight natural environment so that it is effectively decompose released mineral matter, then, by ore deposit
After stone use water rinses, sieve, remove little granule foreign, be raw material Maifanitum raw ore.So
After, sieving after being cleaned by Maifanitum raw ore, it is standby to dry.
(2) proportioning mixing: according to mass percent 70% Maifanitum raw ore, the kaolinite of 15%
Soil, 5% anion powder and 10% magnesium, copper, zinc, rare earth, potassium, the inorganic salt chemical combination of nickel
Thing mixture, weighs appropriate raw material respectively, then, in enclosed environment, is mixed by each raw material
Close, and by each raw mill powdering in grinder.In process of lapping, in grinder
It is provided above one block of Magnet, is processed into during powder unnecessary iron tramp to remove；Meanwhile,
One small blast fan is set by grinder, and persistently dries in process of lapping, to remove
Remove the dust in raw material and impurity.Then, after grinding, gained powder raw material is respectively at aperture
It is that the sieve of 1 μm sieves, obtains mixing powder raw material.
(3) mud refining: according to mass percent, mixes powder raw material 70%, distilled water 30%
Weigh each raw material respectively, then the two mixed and be in harmonious proportion and be processed into pureed, then by institute
Obtain pureed compound and use thin film environmental sealing under vacuum, and by pureed mixing after sealing
Material is positioned at the dry cool place that ambient temperature is 10 DEG C and deposits 45 days.To seal after 45 days
Raw material takes out from thin film, and cutting also obtains as shape that uniformly and to be suitable to the pureed of carrying former
Material, and pureed raw material after cutting is carried out the most under vacuum thin film environmental sealing, and
60d is deposited at the dry cool place that ambient temperature is 10 DEG C.
(4) base:
1. after sealing, pureed raw material takes out from thin film, and breaks into thin and thick on surface platform
Uniform slice；
2. with rule car, slice is cut into the width made required for teapot bottle body and pot lid,
And slice moderate for width is combined into the form of teapot and pot lid；Then, water is dipped in brush pen
The position that slice combines is carried out organic bonding, and reserved in the appropriate location of pot lid gives vent to anger
Hole, obtains teapot base type.
(5) sizing:
Teapot base type is left at the dry cool place that ambient temperature is 10 DEG C, and place
24 hours；Then, base type is transferred under sunlight, and dry in the sun 48 hours.
(6) fire:
Appropriate amount of quartz sand is uniformly placed at the device mouth of teapot base type after dry in the sun, and by teapot base
Type is fired 15 hours under the conditions of 1200 DEG C, after firing after the cooling of base type, is drawn off.
Repeat the most under the same conditions to fire 2 times, i.e. obtain forming by a firing teapot.
(7) finished product:
The polished silicon wafer forming by a firing the making of teapot coconut husk is once polished；The most again
Secondary careful polishing in all directions is carried out with the sand paper of 360 yards；It follows that again with 200 yards
Corundum teapot Hu Kou and lid corundum are carried out careful grinding, make the two tight
Close combination non-loosening, seamless, antiseep.After polishing at three times, with sponge to teapot table
Face carries out wiping, and cleans teapot three times with 100 DEG C of boiling water, i.e. obtains embodiment 1
Finished product teapot.
After pouring tea in obtained finished product teapot in embodiment 1, kettle body also finds no
Tea seepage.Pour out after tea is placed 1h, and respectively to not pouring in teapot and at tea
Tea water sample Pesticide Residues and content of mineral substances after placing in kettle detect and unite
Meter, result is such as table 1 below, shown in 2:
Table 1 do not pour in kettle and in embodiment 1 teapot place after tea persticide residue
Table 2 do not pour in kettle and in embodiment 1 teapot place after tea content of mineral substances
Embodiment 2
Clean according to method ore dressing described in embodiment 1 and sieve, and according to mass percent 50%
Maifanitum raw ore, the Kaolin of 20%, 10% anion powder and 20% magnesium, copper, zinc,
Rare earth, potassium, the inorganic salt compound mixture of nickel, weigh appropriate each raw material.Then, press
According to method described in embodiment 1 carry out proportioning mixing pulverizing, mud refining, and just seal after pureed
Raw material takes out from thin film, and breaks into the uniform slice of thin and thick on surface platform；Then,
Slice is cut into width needed for making tubbiness vessel, and slice moderate for width is combined into
The form of bucket, then dips in, with brush pen, the position that slice combines by water and carries out organic bonding, and press
Shape according to method described in embodiment 1 and fire, and to firing rear tubbiness vessel coconut husk
Polish with 320 yards of sand paper, then with sponge, vessel surface is carried out wiping, and use
Vessel are cleaned three times by 100 DEG C of boiling water, i.e. obtain the finished product tubbiness vessel of embodiment 2.
Embodiment 3
Clean according to method ore dressing described in embodiment 1 and sieve, and according to mass percent 85%
Maifanitum raw ore, the Kaolin of 10% is 3% anion powder and 2% magnesium, copper, zinc, dilute
Soil, potassium, the inorganic salt compound mixture of nickel, weigh appropriate each raw material.Then, according to
Method described in embodiment 1 carry out proportioning mixing pulverizing, mud refining, and just seal after pureed former
Material takes out from thin film, and breaks into the uniform slice of thin and thick on surface platform；Then, will
Slice is cut into width needed for ampuliform vessel processed, and slice moderate for width is combined into bottle
Form, then dip in, with brush pen, the position that slice combines by water and carry out organic bonding, and according to
Method described in embodiment 1 is shaped and fires, and to fire rear ampuliform vessel coconut husk and
320 yards of sand paper are polished, and then with sponge, vessel surface carry out wiping, and with 100 DEG C
Vessel are cleaned three times by boiling water, i.e. obtain the finished product ampuliform vessel of embodiment 3.
Experimental example 1-5
According to method described in embodiment 1 carry out ore dressing clean sieve, proportioning mixing, mud refining,
Base, fire and through polishing, wiping and cleaning, to obtain the teapot of experimental example 1-5；
Wherein, in experimental example 1-5, the number of described base is 100, and the temperature fired is respectively
It is 900 DEG C, 1100 DEG C, 1300 DEG C, 1500 DEG C and 1700 DEG C.
Meanwhile, ore dressing, proportioning mixing, mud refining, system are carried out according to method described in embodiment 1
Base, fire and through polishing, wiping and cleaning, to obtain the teapot of embodiment 1, wherein,
The number of base is 100.
Then, carry out embodiment 1 and experimental example 1-5 are fired the teapot obtained respectively
Finished product number and finished product seepage rate are added up, and result is as shown in table 1 below:
Table 1 embodiment 1 and experimental example 1-5 teapot finished product number and finished product seepage rate are added up
| Scheme | Base number | Finished product number | Finished product seepage rate (%) |
| Embodiment 1 | 100 | 99 | 0 |
| Experimental example 1 | 100 | 65 | 32 |
| Experimental example 2 | 100 | 89 | 15 |
| Experimental example 3 | 100 | 86 | 7 |
| Experimental example 4 | 100 | 73 | 11 |
| Experimental example 5 | 100 | 53 | 13 |
Then, respectively finished product teapot in embodiment 1 and experimental example 1-5 is carried out outward appearance inspection
Survey, it was found that the color of teapot is normal in embodiment 1 and experimental example 2,3, experiment
In example 1, teapot color is the most shallow, and in experimental example 4, teapot color is the most black, and tea in experimental example 5
Kettle is the most black.
Further, enter embodiment 1 and experimental example 1-5 fire unsuccessfully teapot respectively
Row detection, found that.Embodiment 1 is fired unsuccessfully teapot bottle body overall structure preferable,
Simply spout structure separates with bottle body, thus it is speculated that when should be base caused by misoperation；Experimental example
1-2 fires unsuccessfully teapot and mostly is bottle body or pot lid is chipping；Experimental example 3-5 fires mistake
Lose teapot mostly to be overall structure and rupture caused.
The inventive method can effectively utilize Maifanitum raw material, and vessel ratio of briquetting is high, it is simple to
Carrying out mass production, commercial value is high.Meanwhile, obtained vessel can be with active adsorption
Pesticide residues in Folium Camelliae sinensis, and reduce and eliminate heavy metals exceeding standard.Meanwhile, tea set made of China medical stone
The beneficially trace element such as the ferrum of health, magnesium, zinc can be oozed out, there is good health care
Effect
Although illustrate and describing the present invention with specific embodiment, but it will be appreciated that
May be made that other changes many without departing from the spirit and scope of the present invention
And amendment.It is, therefore, intended that include in the following claims belonging in the scope of the invention
All such changes and modifications.
Claims (10)
1. a medical stone container preparation method, it is characterised in that described method includes
Following steps:
Weigh respectively according to percetage by weight Maifanitum raw ore 50-85%, Kaolin 10-20%,
Anion powder 3%-10% and mixed mineral raw material 2-20%, as raw material, and mixes raw material
Close after grinding, raw material add after mixed grinding water and is in harmonious proportion, obtaining pureed compound,
And pureed compound is shaped after base, fired, obtain medical stone container；
Wherein, described mixed mineral raw material is magnesium, copper, zinc, rare earth, potassium, nickel compound
Mixed mineral raw material.
Method the most according to claim 1, it is characterised in that in described method,
May further include in process of lapping the remove impurity step passed through attraction, dry and sieve
Suddenly.
Method the most according to claim 1, it is characterised in that described grind to mixing
Raw material adds in water the step that is in harmonious proportion after mill, the quality of the raw material after mixed grinding and water
Than being (5-8): (2-5).
Method the most according to claim 1, it is characterised in that described method is also entered
One step includes that the pureed compound vacuum obtained by adding water and be in harmonious proportion is deposited, so after sealing
After by pureed compound take out after cutting, and by after cutting pureed raw material piecemeal vacuum seal also
Deposit, after then again depositing the taking-up of rear gained clod, then carry out the step of base.
Method the most according to claim 4, it is characterised in that described addition water is also
The temperature that pureed compound vacuum obtained by after mediation is deposited after sealing is 10-20 DEG C, deposits
Time be 30-60d.
Method the most according to claim 4, it is characterised in that mud after described cutting
The temperature that shape raw material piecemeal vacuum seals and deposits is 10-20 DEG C, and the time deposited is
60-90d。
Method the most according to claim 1, it is characterised in that described in be fixed to by
After base, gained base type is first positioned over and is dried in shady and cool environment, then dry in the sun sizing in the sun.
Method the most according to claim 1, it is characterised in that described in the temperature fired
Degree is for 1000-1500 DEG C, and the time fired is 12-24h.
9. a medical stone container, it is characterised in that described vessel are by claim 1-8
According to any one of method prepare.
Vessel the most according to claim 9, it is characterised in that described vessel be kettle,
One in cup, bucket, bowl, bottle.