CN111377725A - Muyu stone ceramic product and preparation method and application thereof - Google Patents
Muyu stone ceramic product and preparation method and application thereof Download PDFInfo
- Publication number
- CN111377725A CN111377725A CN202010244546.7A CN202010244546A CN111377725A CN 111377725 A CN111377725 A CN 111377725A CN 202010244546 A CN202010244546 A CN 202010244546A CN 111377725 A CN111377725 A CN 111377725A
- Authority
- CN
- China
- Prior art keywords
- yellow river
- parts
- muyu stone
- muyu
- stone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a muyu stone ceramic product and a preparation method and application thereof, and belongs to the technical field of ceramic products. The wooden fish stone ceramic product comprises the following components in parts by weight: 5-15 parts of yellow river mud, 10-30 parts of yellow river sand and 55-85 parts of muyu stone. The muyu stone ceramic product prepared by selecting muyu stone and yellow river silt as raw materials has the effects of changing acidic water into weak alkaline water and delaying the decay and deterioration of tea water, can also separate out various mineral substances and trace elements beneficial to a human body, has a good health-care effect, and can be used as tea set artware such as teapots, tea cups and the like.
Description
Technical Field
The invention relates to the technical field of ceramic products, in particular to a muyu stone ceramic product and a preparation method and application thereof.
Background
The mineral component of the muyu stone is limonite, the content of ferric oxide in the limonite is different from 20 percent to 78 percent, other impurities are phosphate, a small amount of metasilicate and trace elements such as strontium, molybdenum, lithium, zinc, selenium and the like.
The ceramic product is prepared by using clay as a raw material and performing the working procedures of molding, drying, firing and the like, and can be used for artware such as bowls, plates, cups and the like. Along with the improvement of the living standard of people, the requirements of people on artware are gradually improved, and compared with the traditional artware, the artware with the health-care function is more favored.
However, the existing artware such as ceramic products have the problems of poor health care effect and the like, so further research on the ceramic products is needed.
Disclosure of Invention
An embodiment of the present invention is directed to providing a muyu stone ceramic product to solve the problems in the background art.
In order to achieve the above purpose, the embodiments of the present invention provide the following technical solutions:
a muyu stone ceramic product comprises the following components in parts by weight: 5-15 parts of yellow river mud, 10-30 parts of yellow river sand and 55-85 parts of muyu stone.
As a preferable scheme of the embodiment of the invention, the muyu stone ceramic comprises the following components in parts by weight: 8-12 parts of yellow river mud, 15-25 parts of yellow river sand and 63-77 parts of Muyu stone.
As another preferable scheme of the embodiment of the invention, the mass content of the ferric oxide in the wooden fish stone is 50-70%.
As another preferable scheme of the embodiment of the invention, the severe degree of the yellow river mud is 2500-2700 kg/m3。
Another object of an embodiment of the present invention is to provide a method for preparing the above muyu stone pottery, which comprises the following steps:
weighing yellow river mud, yellow river sand and Muyu stone according to the weight parts for later use;
grinding and mixing the yellow river mud, the yellow river sand and the wooden fish stone to obtain powder;
adding water into the powder, stirring, forming, and then drying to obtain a blank;
and firing the blank to obtain the muyu stone ceramic product.
In another preferable embodiment of the present invention, in the step, the firing temperature is 900 to 1050 ℃.
Another object of the embodiments of the present invention is to provide a muyu stone ceramic product prepared by the above preparation method.
Another object of an embodiment of the present invention is to provide an application of the muyu stone pottery product as a tea set.
Compared with the prior art, the embodiment of the invention has the beneficial effects that:
the muyu stone ceramic product prepared by selecting muyu stone and yellow river silt as raw materials has the effects of changing acidic water into weak alkaline water and delaying the decay and deterioration of tea water, can also separate out various mineral substances and trace elements beneficial to a human body, has a good health-care effect, and can be used as tea set artware such as teapots, tea cups and the like.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
Example 1
This embodiment provides a muyu stone ceramic, the preparation method of which comprises the steps of:
(1) weighing 5 parts of yellow river mud, 10 parts of yellow river sand and 85 parts of Muyu stone for later use; wherein the mass content of ferric oxide in the muyu stone is 50%; the weight of the yellow river mud is 2500kg/m3(ii) a The yellow river mud and the yellow river sand are obtained by filtering, washing and screening the mud and sand obtained from the yellow river.
(2) And grinding and mixing the yellow river mud, the yellow river sand and the wooden fish stone to obtain powder.
(3) Adding water into the powder, stirring, molding according to a certain model (such as teapot or teacup), manually kneading, and air drying to obtain blank.
(4) And (3) placing the blank in a furnace at 900 ℃ for firing for 17h to obtain the muyu stone ceramic product.
Example 2
This embodiment provides a muyu stone ceramic, the preparation method of which comprises the steps of:
(1) weighing 15 parts of yellow river mud, 30 parts of yellow river sand and 55 parts of Muyu stone for later use; wherein the mass content of ferric oxide in the muyu stone is 70%; the gravity of the yellow river mud is 2700kg/m3(ii) a The yellow river mud and the yellow river sand are obtained by filtering, washing and screening the mud and sand obtained from the yellow river.
(2) And grinding and mixing the yellow river mud, the yellow river sand and the wooden fish stone to obtain powder.
(3) Adding water into the powder, stirring, molding according to a certain model (such as teapot or teacup), manually kneading, and air drying to obtain blank.
(4) And (3) placing the blank in a furnace at 1050 ℃ for firing for 15h to obtain the muyu stone ceramic product.
Example 3
This embodiment provides a muyu stone ceramic, the preparation method of which comprises the steps of:
(1) weighing 8 parts of yellow river mud, 15 parts of yellow river sand and 77 parts of Muyu stone for later use; wherein the mass content of ferric oxide in the muyu stone is 60 percent; the gravity of the yellow river mud is 2650kg/m3(ii) a The yellow river mud and the yellow river sand are obtained by filtering, washing and screening the mud and sand obtained from the yellow river.
(2) And grinding and mixing the yellow river mud, the yellow river sand and the wooden fish stone to obtain powder.
(3) Adding water into the powder, stirring, molding according to a certain model (such as teapot or teacup), manually kneading, and air drying to obtain blank.
(4) And (3) placing the blank in a furnace at 1000 ℃ for firing for 16h to obtain the muyu stone ceramic product.
Example 4
This embodiment provides a muyu stone ceramic, the preparation method of which comprises the steps of:
(1) weighing 12 parts of yellow river mud, 25 parts of yellow river sand and 63 parts of Muyu stone for later use; wherein the mass content of ferric oxide in the muyu stone is 60 percent; the gravity of the yellow river mud is 2650kg/m3(ii) a The yellow river mud and the yellow river sand are obtained by filtering, washing and screening the mud and sand obtained from the yellow river.
(2) And grinding and mixing the yellow river mud, the yellow river sand and the wooden fish stone to obtain powder.
(3) Adding water into the powder, stirring, molding according to a certain model (such as teapot or teacup), manually kneading, and air drying to obtain blank.
(4) And (3) placing the blank in a furnace at 1000 ℃ for firing for 16h to obtain the muyu stone ceramic product.
Example 5
This embodiment provides a muyu stone ceramic, the preparation method of which comprises the steps of:
(1) weighing 9 parts of yellow river mud, 20 parts of yellow river sand and 71 parts of Muyu stone for later use; wherein the mass content of ferric oxide in the muyu stone is 70%; the gravity of the yellow river mud is 2650kg/m3(ii) a The yellow river mud and the yellow river sand are obtained by filtering, washing and screening the mud and sand obtained from the yellow river.
(2) And grinding and mixing the yellow river mud, the yellow river sand and the wooden fish stone to obtain powder.
(3) Adding water into the powder, stirring, molding according to a certain model (such as teapot or teacup), manually kneading, and air drying to obtain blank.
(4) And (3) placing the blank in a furnace at 1000 ℃ for firing for 16h to obtain the muyu stone ceramic product.
Example 6
This embodiment provides a muyu stone ceramic, the preparation method of which comprises the steps of:
(1) weighing 11 parts of yellow river mud, 24 parts of yellow river sand and 65 parts of Muyu stone for later use; wherein the mass content of ferric oxide in the muyu stone is 65 percent; the gravity of the yellow river mud is 2650kg/m3(ii) a The yellow river mud and the yellow river sand are obtained by filtering, washing and screening the mud and sand obtained from the yellow river.
(2) And grinding and mixing the yellow river mud, the yellow river sand and the wooden fish stone to obtain powder.
(3) Adding water into the powder, stirring, molding according to a certain model (such as teapot or teacup), manually kneading, and air drying to obtain blank.
(4) And (3) placing the blank in a furnace at 950 ℃ for firing for 17 hours to obtain the muyu stone ceramic product.
Example 7
This embodiment provides a muyu stone ceramic, the preparation method of which comprises the steps of:
(1) weighing 10 parts of yellow river mud, 20 parts of yellow river sand and 70 parts of Muyu stone for later use; wherein the mass content of ferric oxide in the muyu stone is 60 percent; the gravity of the yellow river mud is 2650kg/m3(ii) a The yellow river mud and the yellow river sand are obtained by filtering, washing and screening the mud and sand obtained from the yellow river.
(2) And grinding and mixing the yellow river mud, the yellow river sand and the wooden fish stone to obtain powder.
(3) Adding water into the powder, stirring, molding according to a certain model (such as teapot or teacup), manually kneading, and air drying to obtain blank.
(4) And (3) placing the blank in a furnace at 1000 ℃ for firing for 17 hours to obtain the muyu stone ceramic product.
Soaking the muyu stone ceramic product obtained in the example 7 in water for 1 day to obtain a sample soaking solution as an experimental group; taking water without soaking the Muyu stone pottery products as a blank group; the safety test was performed on each of the experimental group and the blank group, and the test results are shown in table 1 below.
TABLE 1
As can be seen from the above table 1, the muyu stone ceramic product prepared by the embodiment of the invention does not affect the water quality of water, and can ensure that the content of harmful elements in the water does not exceed the standard.
In addition, after the muyu stone pottery products obtained in examples 1 to 7 were respectively soaked in tea water for 4 days, the tea water was observed, and no turbidity, no odor and no deterioration occurred. In addition, the detection results of the trace elements of the soaked tea water are as follows: the content of magnesium is 0.5-1.5 mg/L; the content of selenium is 0.2-0.8 mug/L; the content of iron is 0.01-0.05 mg/L; the content of manganese is 0.02-0.04 mg/L; the content of lithium is 0.2-0.8 mu g/L; the strontium content is 20-80 μ g/L. It can be known that the muyu stone ceramic product obtained by the embodiment of the invention can separate out a plurality of trace elements beneficial to human bodies when being soaked in tea water.
In light of the foregoing description of the preferred embodiment of the present invention, many modifications and variations will be apparent to those skilled in the art without departing from the spirit and scope of the invention. The technical scope of the present invention is not limited to the content of the specification, and must be determined according to the scope of the claims.
Claims (8)
1. The wooden fish stone ceramic product is characterized by comprising the following components in parts by weight: 5-15 parts of yellow river mud, 10-30 parts of yellow river sand and 55-85 parts of muyu stone.
2. The muyu stone ceramic as claimed in claim 1, wherein the muyu stone ceramic comprises the following components in parts by weight: 8-12 parts of yellow river mud, 15-25 parts of yellow river sand and 63-77 parts of Muyu stone.
3. The muyu stone ceramic product according to claim 1 or 2, wherein the muyu stone contains ferric oxide 50-70% by mass.
4. The muyu stone ceramic product as claimed in claim 1 or 2, wherein the weight of the yellow river mud is 2500 to 2700kg/m3。
5. A method for preparing the muyu stone pottery according to any one of claims 1 to 4, comprising the steps of:
weighing yellow river mud, yellow river sand and Muyu stone according to the weight parts for later use;
grinding and mixing the yellow river mud, the yellow river sand and the wooden fish stone to obtain powder;
adding water into the powder, stirring, forming, and then drying to obtain a blank;
and firing the blank to obtain the muyu stone ceramic product.
6. The method for preparing Muyu stone pottery according to claim 5, wherein the firing temperature in the step is 900-1050 ℃.
7. A muyu stone pottery prepared by the method of claim 5 or 6.
8. Use of the muyu stone pottery according to any one of claims 1 to 4 and 7 as a tea set.