CN105837165A - 一种带有葡萄酸甜气味的环保装饰砖块 - Google Patents
一种带有葡萄酸甜气味的环保装饰砖块 Download PDFInfo
- Publication number
- CN105837165A CN105837165A CN201610160463.3A CN201610160463A CN105837165A CN 105837165 A CN105837165 A CN 105837165A CN 201610160463 A CN201610160463 A CN 201610160463A CN 105837165 A CN105837165 A CN 105837165A
- Authority
- CN
- China
- Prior art keywords
- parts
- brick
- vitis viniferae
- sour
- soak
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种带有葡萄酸甜气味的环保装饰砖块，涉及建筑材料领域，所述砖块由以下重量份的配方配比制成：凹凸棒粘土30‑45份、草木灰20‑25份、松香油5‑10份、煤矸石25‑30份、河沙10‑15份、石灰粉10‑15份、浸泡液60‑80份。与传统砖块相比，该砖块在原料成分上，不含化学添加剂成分，在制造工艺上大大改进，不仅自身带有淡淡的葡萄酸甜气味，具有安脑提神的功效，而且不会释放出有害气体，更加绿色环保，解决了传统装饰砖块体自身带有较大的刺鼻气味，长时间使用，容易释放出有害气体，不仅污染环境，而且对人体健康带来损伤的问题。
Description
技术领域：
本发明涉及建筑材料领域，具体涉及一种带有葡萄酸甜气味的环保装饰砖块。
背景技术：
随着社会进步和发展，砖块不再仅仅局限用于房屋地基、墙体支撑等，越来越多的砖块应用于美化环境和装饰环境，例如用于铺设草坪的植草砖，用于店内装修的装饰砖块，以及仅仅用作欣赏的欣赏用砖块，不管是在工艺还是在造型上，都有很大的突破，以满足人类和市场的需求，传统的装饰砖块由于原料配方以及制造工艺的差别，仅仅在造型上较为吸引人，却忽略砖体自身改进，导致很多种装饰砖块体自身带有较大的刺鼻气味，长时间使用，容易释放出有害气体，不仅污染环境，而且对人体健康带来损伤。
发明内容：
本发明为解决上述问题，提供一种带有葡萄酸甜气味的环保装饰砖块，该砖块在原料配方以及制造工艺方面与传统砖块相比都有很大的改进，不含化学添加剂成分，不仅自身带有淡淡的葡萄酸甜气味，具有安脑提神的功效，而且不会释放出有害气体，更加绿色环保。
本发明所要解决的技术问题采用以下的技术方案来实现：
一种带有葡萄酸甜气味的环保装饰砖块，其特征在于，所述砖块由以下重量份的配方配比制成：
凹凸棒粘土30-45份、草木灰20-25份、松香油5-10份、煤矸石25-30份、河沙10-15份、石灰粉10-15份、浸泡液60-80份。
优选的，所述砖块由以下重量份的配方配比制成：凹凸棒粘土30份、草木灰20份、松香油5份、煤矸石25份、河沙10份、石灰粉10份、浸泡液60份。
所述凹凸棒粘土由以下重量份的配方配比制成：凹凸棒土100份、菜籽油饼35份、蒸馏水100份。
所述浸泡液由以下重量份的配方配比及制作工艺制成：葡萄汁100份、植物油8份、白醋5份、酒精5份、水80份。
本发明还包括一种带有葡萄酸甜气味的环保装饰砖块的制造方法，根据上述所述的重量份的原料，其特征在于以下步骤：
1)、制作凹凸棒粘土：将凹凸棒土和菜籽油饼放入粉碎搅拌机进行粉碎搅拌后混合均匀，过200目筛网过滤后，加蒸馏水再次搅拌混合后，置入高压蒸锅蒸8-10小时，加热温度为180-230℃，冷却取出，制得凹凸棒粘土备用，凹凸棒粘土的含水率为45-50％，凹凸棒土与菜籽油饼搅拌混合后，滤除杂质，得到凹凸棒精土和粉碎菜籽油饼颗粒，经过蒸馏水二次搅拌混合得到凹凸棒浆料，通过高压蒸锅加热熏蒸，使得凹凸棒精土与菜籽油饼中的菜籽油充分融合，制得的凹凸棒粘土，颗粒均匀、粘度大、吸附性强，增加了原料的粘度和强度，对后期制作的砖块也能起到提高硬度和致密性的效果，使制得的砖块结实耐用；
2)、制作浸泡液：将葡萄汁、植物油、白醋、酒精和水搅拌混合后，置于120℃的蒸锅加热蒸煮1-2小时，冷却，制得浸泡液备用，将葡萄汁与植物油、白醋、酒精加水加热，植物油增加葡萄汁的粘度，同时加热后利于葡萄汁的溶解，白醋和酒精与葡萄汁加热后产生反应，增强葡萄自身的气味，通过加水后加热，使葡萄汁充分与水溶解，葡萄的特有的酸甜溶于水并通过植物油锁住，避免挥发浪费，使得后期制造砖块时，充分与砖块融合，增加砖块的酸甜气味；
3)、将煤矸石粉碎后过200目筛网滤除杂质，得到煤矸石细料，将煤矸石细料与草木灰、河沙、石灰粉、凹凸棒粘土，通过密封搅拌机搅拌混合均匀，制得混合料备用，通过密封搅拌，使得上述各原料充分均匀混合，保证后期制砖时砖块的砖体纹理细腻，提高强度；
4)、将上述混合料加入浸泡液和松香油，密封加热搅拌，加热温度为60-80℃，搅拌时间为6-8小时，搅拌结束后，冷却静置至浸泡液彻底被混合料吸收，制得浸泡混合料备用，密封加热搅拌，使得浸泡液和松香油更加易于与混合料融合，浸泡液加热后与混合料快速融合，避免香味挥发和逃逸，松香油增加混合料内部的粘性，利于锁住浸泡液的香味，使得后期制成的砖块，不仅结实耐用、纹理细腻，而且香味更加持久；
5)、将上述浸泡混合料倒入模具，通过蒸汽加压、切块、抽真空除去水分、快速风干后，即制得带有葡萄酸甜气味的环保装饰砖块，通过上述步骤，避免通过烧结方式，造成砖体内部的葡萄酸甜在高温烧结下流失，同时通过蒸汽加压、切块、抽真空除去水分、快速风干的方式，利于锁住砖体内部的葡萄酸甜，保证砖体纹理的细腻，以及砖体内部材质的致密性，以增强砖体的强度和耐久度。
本发明的有益效果为：提供一种带有葡萄酸甜气味的环保装饰砖块，与传统砖块相比，该砖块在原料成分上，不含化学添加剂成分，在制造工艺上大大改进，不仅自身带有淡淡的葡萄酸甜气味，具有安脑提神的功效，而且不会释放出有害气体，更加绿色环保。
具体实施方式：
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合实施例，进一步阐述本发明。
实施例一
一种带有葡萄酸甜气味的环保装饰砖块，由以下重量份的配方配比制成：
凹凸棒粘土30份、草木灰20份、松香油5份、煤矸石25份、河沙10份、石灰粉10份、浸泡液60份。
所述凹凸棒粘土由以下重量份的配方配比制成：凹凸棒土100份、菜籽油饼35份、蒸馏水100份。
所述浸泡液由以下重量份的配方配比及制作工艺制成：葡萄汁100份、植物油8份、白醋5份、酒精5份、水80份。
一种带有葡萄酸甜气味的环保装饰砖块的制造方法，根据上述所述的重量份的原料，其特征在于以下步骤：
1)、制作凹凸棒粘土：将凹凸棒土和菜籽油饼放入粉碎搅拌机进行粉碎搅拌后混合均匀，过200目筛网过滤后，加蒸馏水再次搅拌混合后，置入高压蒸锅蒸8-10小时，加热温度为180-230℃，冷却取出，制得凹凸棒粘土备用；
2)、制作浸泡液：将葡萄汁、植物油、白醋、酒精和水搅拌混合后，置于120℃的蒸锅加热蒸煮1-2小时，冷却，制得浸泡液备用；
3)、将煤矸石粉碎后过200目筛网滤除杂质，得到煤矸石细料，将煤矸石细料与草木灰、河沙、石灰粉、凹凸棒粘土，通过密封搅拌机搅拌混合均匀，制得混合料备用；
4)、将上述混合料加入浸泡液和松香油，密封加热搅拌，加热温度为60-80℃，搅拌时间为6-8小时，搅拌结束后，冷却静置至浸泡液彻底被混合料吸收，制得浸泡混合料备用；
5)、将上述浸泡混合料倒入模具，通过蒸汽加压、切块、抽真空除去水分、快速风干后，即制得带有葡萄酸甜气味的环保装饰砖块。
实施例二
一种带有葡萄酸甜气味的环保装饰砖块，由以下重量份的配方配比制成：
凹凸棒粘土40份、草木灰23份、松香油8份、煤矸石258份、河沙12份、石灰粉12份、浸泡液70份。
所述凹凸棒粘土由以下重量份的配方配比制成：凹凸棒土100份、菜籽油饼35份、蒸馏水100份。
所述浸泡液由以下重量份的配方配比及制作工艺制成：葡萄汁100份、植物油8份、白醋5份、酒精5份、水80份。
一种带有葡萄酸甜气味的环保装饰砖块的制造方法，根据上述所述的重量份的原料，其特征在于以下步骤：
1)、制作凹凸棒粘土：将凹凸棒土和菜籽油饼放入粉碎搅拌机进行粉碎搅拌后混合均匀，过200目筛网过滤后，加蒸馏水再次搅拌混合后，置入高压蒸锅蒸8-10小时，加热温度为180-230℃，冷却取出，制得凹凸棒粘土备用；
2)、制作浸泡液：将葡萄汁、植物油、白醋、酒精和水搅拌混合后，置于120℃的蒸锅加热蒸煮1-2小时，冷却，制得浸泡液备用；
3)、将煤矸石粉碎后过200目筛网滤除杂质，得到煤矸石细料，将煤矸石细料与草木灰、河沙、石灰粉、凹凸棒粘土，通过密封搅拌机搅拌混合均匀，制得混合料备用；
4)、将上述混合料加入浸泡液和松香油，密封加热搅拌，加热温度为60-80℃，搅拌时间为6-8小时，搅拌结束后，冷却静置至浸泡液彻底被混合料吸收，制得浸泡混合料备用；
5)、将上述浸泡混合料倒入模具，通过蒸汽加压、切块、抽真空除去水分、快速风干后，即制得带有葡萄酸甜气味的环保装饰砖块。
实施例三
一种带有葡萄酸甜气味的环保装饰砖块，由以下重量份的配方配比制成：
凹凸棒粘土45份、草木灰25份、松香油10份、煤矸石30份、河沙15份、石灰粉15份、浸泡液80份。
所述凹凸棒粘土由以下重量份的配方配比制成：凹凸棒土100份、菜籽油饼35份、蒸馏水100份。
所述浸泡液由以下重量份的配方配比及制作工艺制成：葡萄汁100份、植物油8份、白醋5份、酒精5份、水80份。
一种带有葡萄酸甜气味的环保装饰砖块的制造方法，根据上述所述的重量份的原料，其特征在于以下步骤：
1)、制作凹凸棒粘土：将凹凸棒土和菜籽油饼放入粉碎搅拌机进行粉碎搅拌后混合均匀，过200目筛网过滤后，加蒸馏水再次搅拌混合后，置入高压蒸锅蒸8-10小时，加热温度为180-230℃，冷却取出，制得凹凸棒粘土备用；
2)、制作浸泡液：将葡萄汁、植物油、白醋、酒精和水搅拌混合后，置于120℃的蒸锅加热蒸煮1-2小时，冷却，制得浸泡液备用；
3)、将煤矸石粉碎后过200目筛网滤除杂质，得到煤矸石细料，将煤矸石细料与草木灰、河沙、石灰粉、凹凸棒粘土，通过密封搅拌机搅拌混合均匀，制得混合料备用；
4)、将上述混合料加入浸泡液和松香油，密封加热搅拌，加热温度为60-80℃，搅拌时间为6-8小时，搅拌结束后，冷却静置至浸泡液彻底被混合料吸收，制得浸泡混合料备用；
5)、将上述浸泡混合料倒入模具，通过蒸汽加压、切块、抽真空除去水分、快速风干后，即制得带有葡萄酸甜气味的环保装饰砖块。
Claims (5)
1.一种带有葡萄酸甜气味的环保装饰砖块，其特征在于，所述砖块由以下重量份的配方配比制成：
凹凸棒粘土30-45份、草木灰20-25份、松香油5-10份、煤矸石25-30份、河沙10-15份、石灰粉10-15份、浸泡液60-80份。
2.根据权利要求1所述的一种带有葡萄酸甜气味的环保装饰砖块，其特征在于，优选的，所述砖块由以下重量份的配方配比制成：凹凸棒粘土30份、草木灰20份、松香油5份、煤矸石25份、河沙10份、石灰粉10份、浸泡液60份。
3.根据权利要求1所述的一种带有葡萄酸甜气味的环保装饰砖块，其特征在于，所述凹凸棒粘土由以下重量份的配方配比制成：凹凸棒土100份、菜籽油饼35份、蒸馏水100份。
4.根据权利要求1所述的一种带有葡萄酸甜气味的环保装饰砖块，其特征在于，所述浸泡液由以下重量份的配方配比及制作工艺制成：葡萄汁100份、植物油8份、白醋5份、酒精5份、水80份。
5.一种带有葡萄酸甜气味的环保装饰砖块的制造方法，根据上述所述的重量份的原料，其特征在于以下步骤：
1)、制作凹凸棒粘土：将凹凸棒土和菜籽油饼放入粉碎搅拌机进行粉碎搅拌后混合均匀，过200目筛网过滤后，加蒸馏水再次搅拌混合后，置入高压蒸锅蒸8-10小时，加热温度为180-230℃，冷却取出，制得凹凸棒粘土备用，凹凸棒粘土的含水率为45-50％；
2)、制作浸泡液：将葡萄汁、植物油、白醋、酒精和水搅拌混合后，置于120℃的蒸锅加热蒸煮1-2小时，冷却，制得浸泡液备用；
3)、将煤矸石粉碎后过200目筛网滤除杂质，得到煤矸石细料，将煤矸石细料与草木灰、河沙、石灰粉、凹凸棒粘土，通过密封搅拌机搅拌混合均匀，制得混合料备用；
4)、将上述混合料加入浸泡液和松香油，密封加热搅拌，加热温度为60-80℃，搅拌时间为6-8小时，搅拌结束后，冷却静置至浸泡液彻底被混合料吸收，制得浸泡混合料备用；
5)、将上述浸泡混合料倒入模具，通过蒸汽加压、切块、抽真空除去水分、快速风干后，即制得带有葡萄酸甜气味的环保装饰砖块。