CN105820672A - Household appliance anticorrosive coating and preparation method thereof - Google Patents
Household appliance anticorrosive coating and preparation method thereof Download PDFInfo
- Publication number
- CN105820672A CN105820672A CN201610304295.0A CN201610304295A CN105820672A CN 105820672 A CN105820672 A CN 105820672A CN 201610304295 A CN201610304295 A CN 201610304295A CN 105820672 A CN105820672 A CN 105820672A
- Authority
- CN
- China
- Prior art keywords
- water
- agent
- parts
- taeniam
- caulis bambusae
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses household appliance anticorrosive coating and a preparation method thereof. The household appliance anticorrosive coating is mainly prepared from modified epoxy resin, a TGIC curing agent, epoxy chloropropane, organic soil, an ammonium polyphosphate temperature resistant auxiliary, phosphite antioxidant, a sand grain agent, carbon black, precipitated barium sulphate, asbestos powder, nanosilicon dioxide, chlorinated rubber, titanium dioxide, talcum powder, barium sulfate, an anti-settling agent, an antifoaming agent, pigment, leucoxene powder, bamboo fungi, water, smoked plums, radix paeoniae alba, poria cocos, the bulb of fritillary, fructus aurantii, ginger, PVA, starch, ammonia water, AA, an AAm mixture, ammonium persulfate, ammonium hydrogen sulfite, polyvinyl alcohol, a cross-linking agent, liquid low molecular weight polyamides, casein, sodium hydroxide, hydroquinone, urea and a silane coupling agent. The coating prepared through the method has no foreign smell, the formaldehyde content is far lower than the national standard, particular fragrance is released, the coating is suitable for being used in household appliances and furniture and is high in high temperature resistance and cold resistance, and defects of existing coating are effectively overcome.
Description
Technical field:
The present invention designs a kind of chemistry painting industry and preparation method thereof, is specifically related to a kind of for household electrical appliances anticorrosive paint and preparation method thereof.
Background technology:
On market, dragons and fishes jumbled together for existing coating, protects the coating time of occurrence length especially of household electrical appliances long afterwards, it is impossible to reach antiseptic property, cold-proof on household electrical appliances furniture, in order to meet the market demand, is badly in need of a kind of preferably coating of research and development.
Summary of the invention:
The technical problem to be solved is to overcome the defect of prior art, it is provided that a kind of field soybean plantation herbicide and preparation method thereof in early days.
The technical problem to be solved realizes by the following technical solutions.
It is a kind of for household electrical appliances anticorrosive paint, it is characterised in that: mainly it is composed of the following components in parts by weight:
nullModified epoxy: 10-15 part，TGIC firming agent: 2-3 part，Epoxychloropropane: 1-2 part，Organoclay: 3-5 part，APP heatproof auxiliary agent: 1-2 part，Phosphite antioxidant: 5-6 part，Sand streak agent: 7-9 part，Carbon black: 1-2 part，Blanc fixe: 3-5 part，Flake asbestos: 3-5 part，Nano silicon: 10-12 part，Chlorinated rubber: 16-18 part，Titanium dioxide: 2-5 part，Pulvis Talci: 6-9 part，Barium sulfate: 3-6 part，Anti-settling agent: 1-2 part，Defoamer: 1-2 part，Pigment: 10-12 part，Titanium stone white lead: 30-35 part，Caulis Bambusae In Taeniam: 60-70 part，Water: 1000-1100 part，Fructus Mume: 10-15 part，The Radix Paeoniae Alba: 10-15 part，Poria: 10-15 part，Bulbus Fritillariae Uninbracteatae: 10-15 part，Fructus Aurantii: 10-15 part，Rhizoma Zingiberis Recens: 10-15 part，PVA:50-60 part，Starch: 12-15 part，Ammonia: 5-15 part，AA、AAm mixture: 0.3-0.4 part，Ammonium persulfate.: 0.2-0.3 part，Ammonium bisulfite: 0.2-0.3 part，Polyvinyl alcohol: 10-15 part，Cross-linking agent: 0.1-0.2 part，Liquid low-molecular polyamide 0.5-1 part，Casein: 2-5 part，Sodium hydroxide: 0.1-0.2 part，Hydroquinone: 0.2-0.5 part，Carbamide: 1-2 part，Silane coupler: 0.1-0.2 part.
Mainly comprise the steps that
1) cut into slices after Caulis Bambusae In Taeniam being cleaned, be immersed in evaporated milk, treat that evaporated milk is absorbed totally by Caulis Bambusae In Taeniam, take Semen arachidis hypogaeae, grinds, be sprinkled upon on Caulis Bambusae In Taeniam；
2) being ground by nano silicon, milling time is 60min, and grinding rate is 600 turns/min, puts in reactor；
3) taking chlorinated rubber, titanium dioxide, Pulvis Talci, barium sulfate, anti-settling agent, defoamer, pigment, titanium stone white lead, Caulis Bambusae In Taeniam, mixing adds in reactor；
4) take in Fructus Mume, the Radix Paeoniae Alba, Poria, Bulbus Fritillariae Uninbracteatae, Fructus Aurantii, Rhizoma Zingiberis Recens grinds addition alembic, add the water of 50%, distillation, collect distilled water；
5) distilled water is added in reactor, filter with the detailed catalogue filter screen of 300 mesh, filter out thicker granule, pulverize；
6) PVA and 13% water are mixed in addition reactor, within 4 hours, make PVA be completely dissolved with 90 DEG C of stirrings, be cooled to 75 DEG C, Ammonium persulfate., ammonium bisulfite and 2% water are mixed, dropping AA, AAm mixture and Ammonium persulfate., ammonium bisulfite and water mixed solution, within about 1-2 hour, drip off, insulation reaction 1 hour, be subsequently adding starch, continue heated and stirred 1 hour, add silane coupler stirring, drop to less than 50 DEG C to temperature, with discharging after ammonia regulation pH value；
7) water taking polyvinyl alcohol, liquid low-molecular polyamide and 10% carries out mix and blend, temperature controls at 90-92 DEG C, treat that polyvinyl alcohol, liquid low-molecular polyamide are dissolved completely in water, it is cooled to 65-70 DEG C, the water insulation reaction of addition casein, carbamide, hydroquinone and 5% 2 hours, is subsequently adding the water of cross-linking agent and 5%, continues insulation reaction 1 hour, dropping sodium hydroxide and the water mixed liquid of 5%, stir 5-10 minute；
8) by step 6) and step 7) gained mixture is in step 5) granular powder mixing；
9) taking modified epoxy, TGIC firming agent, epoxychloropropane, organoclay, APP heatproof auxiliary agent, phosphite antioxidant, sand streak agent, carbon black, blanc fixe, flake asbestos simultaneously, grind, the water adding 10% adds hot mixing；
10) finally by step 9) gained mixture addition step 8) in, stirring obtains coating.
The invention has the beneficial effects as follows: coating prepared by this law, free from extraneous odour, content of formaldehyde is far below national standard, discharges a kind of exclusive fragrance simultaneously, it is adaptable to use on family's household electrical appliances and furniture, high temperature resistant, and cold tolerance is high, effectively solves the deficiency of existing coating.
Detailed description of the invention:
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below in conjunction with specific embodiment, the present invention is expanded on further.
Specific embodiment 1: a kind of for household electrical appliances anticorrosive paint, is mainly composed of the following components in parts by weight:
nullModified epoxy: 10 parts，TGIC firming agent: 2 parts，Epoxychloropropane: 1 part，Organoclay: 3 parts，APP heatproof auxiliary agent: 1 part，Phosphite antioxidant: 5 parts，Sand streak agent: 7 parts，Carbon black: 1 part，Blanc fixe: 3 parts，Flake asbestos: 3 parts，Nano silicon: 10 parts，Chlorinated rubber: 16 parts，Titanium dioxide: 2 parts，Pulvis Talci: 6 parts，Barium sulfate: 3 parts，Anti-settling agent: 1 part，Defoamer: 1 part，Pigment: 10 parts，Titanium stone white lead: 30 parts，Caulis Bambusae In Taeniam: 60 parts，Water: 1000 parts，Fructus Mume: 10 parts，The Radix Paeoniae Alba: 10 parts，Poria: 10 parts，Bulbus Fritillariae Uninbracteatae: 10 parts，Fructus Aurantii: 10 parts，Rhizoma Zingiberis Recens: 10 parts，PVA:50 part，Starch: 12 parts，Ammonia: 5 parts，AA、AAm mixture: 0.3 part，Ammonium persulfate.: 0.2 part，Ammonium bisulfite: 0.2 part，，Polyvinyl alcohol: 10 parts，Cross-linking agent: 0.1 part，Liquid low-molecular polyamide 0.5 part，Casein: 2 parts，Sodium hydroxide: 0.1 part，Hydroquinone: 0.2 part，Carbamide: 1 part，Silane coupler: 0.1 part.
Specific embodiment 2: a kind of for household electrical appliances anticorrosive paint, is mainly composed of the following components in parts by weight:
nullModified epoxy: 15 parts，TGIC firming agent: 3 parts，Epoxychloropropane: 2 parts，Organoclay: 5 parts，APP heatproof auxiliary agent: 2 parts，Phosphite antioxidant: 6 parts，Sand streak agent: 9 parts，Carbon black: 2 parts，Blanc fixe: 5 parts，Flake asbestos: 5 parts，Nano silicon: 12 parts，Chlorinated rubber: 18 parts，Titanium dioxide: 5 parts，Pulvis Talci: 9 parts，Barium sulfate: 6 parts，Anti-settling agent: 2 parts，Defoamer: 2 parts，Pigment: 12 parts，Titanium stone white lead: 35 parts，Caulis Bambusae In Taeniam: 70 parts，Water: 1100 parts，Fructus Mume: 15 parts，The Radix Paeoniae Alba: 15 parts，Poria: 15 parts，Bulbus Fritillariae Uninbracteatae: 15 parts，Fructus Aurantii: 15 parts，Rhizoma Zingiberis Recens: 15 parts，PVA:60 part，Starch: 15 parts，Ammonia: 15 parts，AA、AAm mixture: 0.4 part，Ammonium persulfate.: 0.3 part，Ammonium bisulfite: 0.3 part，Polyvinyl alcohol: 15 parts，Cross-linking agent: 0.2 part，Liquid low-molecular polyamide 1 part，Casein: 5 parts，Sodium hydroxide: 0.2 part，Hydroquinone: 0.5 part，Carbamide: 2 parts，Silane coupler: 0.2 part.
Mainly comprise the steps that
1) cut into slices after Caulis Bambusae In Taeniam being cleaned, be immersed in evaporated milk, treat that evaporated milk is absorbed totally by Caulis Bambusae In Taeniam, take Semen arachidis hypogaeae, grinds, be sprinkled upon on Caulis Bambusae In Taeniam；
2) being ground by nano silicon, milling time is 60min, and grinding rate is 600 turns/min, puts in reactor；
3) taking chlorinated rubber, titanium dioxide, Pulvis Talci, barium sulfate, anti-settling agent, defoamer, pigment, titanium stone white lead, Caulis Bambusae In Taeniam, mixing adds in reactor；
4) take in Fructus Mume, the Radix Paeoniae Alba, Poria, Bulbus Fritillariae Uninbracteatae, Fructus Aurantii, Rhizoma Zingiberis Recens grinds addition alembic, add the water of 50%, distillation, collect distilled water；
5) distilled water is added in reactor, filter with the detailed catalogue filter screen of 300 mesh, filter out thicker granule, pulverize；
6) PVA and 13% water are mixed in addition reactor, within 4 hours, make PVA be completely dissolved with 90 DEG C of stirrings, be cooled to 75 DEG C, Ammonium persulfate., ammonium bisulfite and 2% water are mixed, dropping AA, AAm mixture and Ammonium persulfate., ammonium bisulfite and water mixed solution, within about 1-2 hour, drip off, insulation reaction 1 hour, be subsequently adding starch, continue heated and stirred 1 hour, add silane coupler stirring, drop to less than 50 DEG C to temperature, with discharging after ammonia regulation pH value；
7) water taking polyvinyl alcohol, liquid low-molecular polyamide and 10% carries out mix and blend, temperature controls at 90-92 DEG C, treat that polyvinyl alcohol, liquid low-molecular polyamide are dissolved completely in water, it is cooled to 65-70 DEG C, the water insulation reaction of addition casein, carbamide, hydroquinone and 5% 2 hours, is subsequently adding the water of cross-linking agent and 5%, continues insulation reaction 1 hour, dropping sodium hydroxide and the water mixed liquid of 5%, stir 5-10 minute；
8) by step 6) and step 7) gained mixture is in step 5) granular powder mixing；
9) taking modified epoxy, TGIC firming agent, epoxychloropropane, organoclay, APP heatproof auxiliary agent, phosphite antioxidant, sand streak agent, carbon black, blanc fixe, flake asbestos simultaneously, grind, the water adding 10% adds hot mixing；
10) finally by step 9) gained mixture addition step 8) in, stirring obtains coating.
The ultimate principle of the present invention, principal character and advantages of the present invention have more than been shown and described.Skilled person will appreciate that of the industry; the present invention is not restricted to the described embodiments; the principle that the present invention is simply described described in above-described embodiment and description; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements both fall within scope of the claimed invention.Claimed scope is defined by appending claims and equivalent thereof.
Claims (2)
1. one kind is used for household electrical appliances anticorrosive paint, it is characterised in that: mainly it is composed of the following components in parts by weight:
nullModified epoxy: 10-15 part，TGIC firming agent: 2-3 part，Epoxychloropropane: 1-2 part，Organoclay: 3-5 part，APP heatproof auxiliary agent: 1-2 part，Phosphite antioxidant: 5-6 part，Sand streak agent: 7-9 part，Carbon black: 1-2 part，Blanc fixe: 3-5 part，Flake asbestos: 3-5 part，Nano silicon: 10-12 part，Chlorinated rubber: 16-18 part，Titanium dioxide: 2-5 part，Pulvis Talci: 6-9 part，Barium sulfate: 3-6 part，Anti-settling agent: 1-2 part，Defoamer: 1-2 part，Pigment: 10-12 part，Titanium stone white lead: 30-35 part，Caulis Bambusae In Taeniam: 60-70 part，Water: 1000-1100 part，Fructus Mume: 10-15 part，The Radix Paeoniae Alba: 10-15 part，Poria: 10-15 part，Bulbus Fritillariae Uninbracteatae: 10-15 part，Fructus Aurantii: 10-15 part，Rhizoma Zingiberis Recens: 10-15 part，PVA:50-60 part，Starch: 12-15 part，Ammonia: 5-15 part，AA、AAm mixture: 0.3-0.4 part，Ammonium persulfate.: 0.2-0.3 part，Ammonium bisulfite: 0.2-0.3 part，Polyvinyl alcohol: 10-15 part，Cross-linking agent: 0.1-0.2 part，Liquid low-molecular polyamide 0.5-1 part，Casein: 2-5 part，Sodium hydroxide: 0.1-0.2 part，Hydroquinone: 0.2-0.5 part，Carbamide: 1-2 part，Silane coupler: 0.1-0.2 part.
2. according to the one described in claim 1 for household electrical appliances anticorrosive paint, it is characterised in that: mainly comprise the steps that
1) cut into slices after Caulis Bambusae In Taeniam being cleaned, be immersed in evaporated milk, treat that evaporated milk is absorbed totally by Caulis Bambusae In Taeniam, take Semen arachidis hypogaeae, grinds, be sprinkled upon on Caulis Bambusae In Taeniam；
2) being ground by nano silicon, milling time is 60min, and grinding rate is 600 turns/min, puts in reactor；
3) taking chlorinated rubber, titanium dioxide, Pulvis Talci, barium sulfate, anti-settling agent, defoamer, pigment, titanium stone white lead, Caulis Bambusae In Taeniam, mixing adds in reactor；
4) take in Fructus Mume, the Radix Paeoniae Alba, Poria, Bulbus Fritillariae Uninbracteatae, Fructus Aurantii, Rhizoma Zingiberis Recens grinds addition alembic, add the water of 50%, distillation, collect distilled water；
5) distilled water is added in reactor, filter with the detailed catalogue filter screen of 300 mesh, filter out thicker granule, pulverize；
6) PVA and 13% water are mixed in addition reactor, within 4 hours, make PVA be completely dissolved with 90 DEG C of stirrings, be cooled to 75 DEG C, Ammonium persulfate., ammonium bisulfite and 2% water are mixed, dropping AA, AAm mixture and Ammonium persulfate., ammonium bisulfite and water mixed solution, within about 1-2 hour, drip off, insulation reaction 1 hour, be subsequently adding starch, continue heated and stirred 1 hour, add silane coupler stirring, drop to less than 50 DEG C to temperature, with discharging after ammonia regulation pH value；
7) water taking polyvinyl alcohol, liquid low-molecular polyamide and 10% carries out mix and blend, temperature controls at 90-92 DEG C, treat that polyvinyl alcohol, liquid low-molecular polyamide are dissolved completely in water, it is cooled to 65-70 DEG C, the water insulation reaction of addition casein, carbamide, hydroquinone and 5% 2 hours, is subsequently adding the water of cross-linking agent and 5%, continues insulation reaction 1 hour, dropping sodium hydroxide and the water mixed liquid of 5%, stir 5-10 minute；
8) by step 6) and step 7) gained mixture is in step 5) granular powder mixing；
9) taking modified epoxy, TGIC firming agent, epoxychloropropane, organoclay, APP heatproof auxiliary agent, phosphite antioxidant, sand streak agent, carbon black, blanc fixe, flake asbestos simultaneously, grind, the water adding 10% adds hot mixing；
10) finally by step 9) gained mixture addition step 8) in, stirring obtains coating.