CN103992674B - A kind of environmental protection acrylic paints containing stalky tea powder and preparation thereof - Google Patents
A kind of environmental protection acrylic paints containing stalky tea powder and preparation thereof Download PDFInfo
- Publication number
- CN103992674B CN103992674B CN201410163667.3A CN201410163667A CN103992674B CN 103992674 B CN103992674 B CN 103992674B CN 201410163667 A CN201410163667 A CN 201410163667A CN 103992674 B CN103992674 B CN 103992674B
- Authority
- CN
- China
- Prior art keywords
- agent
- parts
- stalky tea
- tea powder
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of environmental protection acrylic paints containing stalky tea powder, be divided into A agent, B agent；A agent is thickening agent, Radix Acaciae senegalis, water, stalky tea powder, polyacrylate emulsion, dispersant, pigment powder, wetting agent, preservative；B agent: acrylic resin, thickening agent, distilled water, dispersant, defoamer, preservative, filler, wetting agent.After using A agent 3 ~ 5d, in A agent surface spraying B agent, can effectively protect the color of pigment itself so that it is not fugitive color, weather-proof, stain resistant, and the original color of pigment will not be changed, improve the plumpness of its color and luster.Tea polyphenols in stalky tea can react with the harmful gas such as formaldehyde, dimethylbenzene, forms nonvolatile harmless macromolecular chain material, effectively removes the harmful gas in air；But the utilization rate of stalky tea is low at present, causes the biggest wasting of resources.Stalky tea powder is added in pigment by the present invention, improves the utilization rate of stalky tea so that the pigment environmental protection of preparation, pollution-free.
Description
Technical field
The invention belongs to fine arts pigment art, be specifically related to a kind of environmental protection acrylic paints containing stalky tea powder and preparation thereof.
Background technology
Stalky tea, refers to the leaf stalk of Folium Camelliae sinensis.All the time, people drink tea and the most do not drink the custom of stalky tea.Substantial amounts of stalky tea is directly thrown away, and utilization rate is the lowest.Stalky tea contains a considerable amount of aroma substance in fact, has a lot of purposes.As stalky tea contains aromatic substance energy hypnotic, improve sleep quality, calm the nerves and clear away heart-fire, eliminate brain fag, keeping tensions down pressure；Containing tannin, phenol and organic acid, there is the effect of bactericidal antiphlogistic.Therefore stalky tea is filled in pillow core by increasing people, makes tea stalk pillow.And the tea polyphenols in stalky tea can react with the harmful gas such as formaldehyde, dimethylbenzene, form nonvolatile harmless macromolecular chain material, remove abnormal flavour and other harmful gas.Therefore stalky tea is placed on the container of abnormal flavour by a lot of people, in newly-decorated house, eliminates the unusual smell in order to going in refrigerator.But these application all can only consume a small amount of stalky tea, and the stalky tea of the overwhelming majority is again without being utilized.
Fine arts Acrylic paint, owing to itself being slightly solubility or insoluble, when allotment makes, granules of pigments particle diameter is relatively large and cause painting that color shade is dull, saturation is poor, and physical stability is poor.And pigment generally individually contains poisonous organic volatile, life-time service has serious harm to the healthy of people.
Summary of the invention
Present invention aims to the shortcomings such as stalky tea utilization rate is low, the physical stability of pigment difference, it is provided that a kind of environmental protection acrylic paints containing stalky tea powder and preparation thereof.The environmental protection acrylic paints containing stalky tea powder that the present invention provides, in A agent surface spraying B agent, can protect the color of pigment itself so that it is not fugitive color effectively, weather-proof, stain resistant, and will not change the original color of pigment, improves the plumpness of its color and luster；And the addition of stalky tea powder can remove the harmful gass such as the formaldehyde in air, dimethylbenzene to a certain extent, remove abnormal flavour.
For achieving the above object, the present invention adopts the following technical scheme that
A kind of environmental protection acrylic paints containing stalky tea powder, including A agent and B agent；It is according to the mass fraction,
A agent: thickening agent 8 ~ 11 parts, Radix Acaciae senegalis 5 ~ 10 parts, 10 ~ 15 parts of water, 10 ~ 15 parts of stalky tea powder, polyacrylate emulsion 50 ~ 55 parts, dispersant 2 ~ 3 parts, 5 ~ 8 parts of pigment powder, wetting agent 4 ~ 10 parts, preservative 3 ~ 5 parts；
B agent: acrylic resin 40 ~ 55 parts, thickening agent 2 ~ 5 parts, distilled water 10 ~ 15 parts, dispersant 2 ~ 4 parts, defoamer 3 ~ 8 parts, preservative 2 ~ 4 parts, filler 2 ~ 5 parts, wetting agent 2 ~ 5 parts.
Described stalky tea powder is that stalky tea is pulverized through ball mill, crosses 1000 ~ 1200 mesh sieves and makes.
Described thickening agent is the one in hydroxypropyl methyl cellulose, sodium carboxymethyl cellulose or hydroxyethyl cellulose.
Described filler is precipitated calcium carbonate.
Described pigment powder is the one in titanium dioxide, ferrum oxide, calcium carbonate.
A kind of method preparing the environmental protection acrylic paints containing stalky tea powder as above, particularly as follows:
(1) preparation of A agent: first by after thickening agent, Radix Acaciae senegalis mix homogeneously, add water, after swelling 4 ~ 6 hours；Being heated to temperature is 60 ~ 70 DEG C, and heat time heating time is 10 ~ 20min, prepares binding agent glue；Then, after wetting agent being mixed 5 ~ 10min with stalky tea powder, add in binding agent glue, stir 10 ~ 15min；Add polyacrylate emulsion, after stirring 10 ~ 20min；Adding preservative, dispersant, pigment powder, stirring 5 ~ 10min prepares coarse particles；The ground machine of coarse particles is ground to fineness below 20 μm；In injection material storage barrel, seal, prepare A agent；
(2) preparation of B agent: by acrylic resin, thickening agent, distilled water, dispersant, defoamer, preservative, filler, wetting agent mixing, stirring at normal temperature 10 ~ 15min, inject in material storage barrel, seal and prepare B agent.
The using method of a kind of environmental protection acrylic paints containing stalky tea powder as above, after using A agent 3 ~ 5d, in A agent surface spraying B agent.
The beneficial effects of the present invention is:
1) pigment of the present invention is divided into A agent and B agent, after using A agent 3 ~ 5d, then in A agent surface spraying B agent; can effectively protect the color of pigment itself so that it is not fugitive color, weather-proof, stain resistant; and the original color of pigment will not be changed, improve the plumpness of its color and luster.
2) having substantial amounts of stalky tea to remain during Tea Processing, utilization rate is low；The present invention is added in pigment, turns waste into wealth, and improves its value；And because stalky tea contains substantial amounts of aroma substance, light tea smell can be distributed, solve the shortcoming that pigment has abnormal flavour；And the addition of stalky tea powder can remove poisonous organic gas to a certain extent, environmental protection, pollution-free.
3) preparation method of the present invention is simple, and production cost is low, has significant economic benefit.
Detailed description of the invention
Present invention the following example further illustrates the present invention, but protection scope of the present invention is not limited to the following example.
Embodiment
1
A kind of environmental protection acrylic paints containing stalky tea powder, including A agent and B agent；It is according to the mass fraction,
A agent: hydroxypropyl methyl cellulose 8 parts, Radix Acaciae senegalis 10 parts, 10 parts of water, 15 parts of stalky tea powder, polyacrylate emulsion 55 parts, dispersant 2 parts, 5 parts of pigment powder, JSA-206 aqueous wetting agent 6 parts, sodium benzoate 3 parts；
B agent: acrylic resin 40 parts, hydroxypropyl methyl cellulose 5 parts, distilled water 10 parts, dispersant 2 parts, defoamer 3 parts, sodium benzoate 2 parts, filler 2 parts, wetting agent 2 parts.
Stalky tea powder is that stalky tea is pulverized through ball mill, crosses 1000 ~ 1200 mesh sieves and makes.
The preparation method of the environmental protection acrylic paints containing stalky tea powder, particularly as follows:
(1) preparation of A agent: first by after hydroxypropyl methyl cellulose, Radix Acaciae senegalis mix homogeneously, add water, after swelling 6 hours；Being heated to temperature is 60 DEG C, and heat time heating time is 20min, prepares binding agent glue；Then by wetting agent with after stalky tea powder mixing 5min, add in binding agent glue, stir 10min；Add polyacrylate emulsion, after stirring 15min；Adding preservative, dispersant, pigment powder, stirring 5min prepares coarse particles；The ground machine of coarse particles is ground to fineness below 20 μm；In injection material storage barrel, seal, prepare A agent；
(2) preparation of B agent: by acrylic resin, thickening agent, distilled water, dispersant, defoamer, preservative, filler, wetting agent mixing, stirring at normal temperature 10min, inject in material storage barrel, seal and prepare B agent.
The using method of a kind of environmental protection acrylic paints containing stalky tea powder as above, after using A agent 3 ~ 5d, in A agent surface spraying B agent.
Embodiment
2
A kind of environmental protection acrylic paints containing stalky tea powder, including A agent and B agent；It is according to the mass fraction,
A agent: thickening agent 10 parts, Radix Acaciae senegalis 7 parts, 12 parts of water, 12 parts of stalky tea powder, polyacrylate emulsion 52 parts, dispersant 2 parts, 7 parts of pigment powder, propylene glycol 10 parts, 5 parts of benzoic acid；
B agent: acrylic resin 50 parts, sodium carboxymethyl cellulose 2 parts, distilled water 12 parts, dispersant 3 parts, defoamer 5 parts, 3 parts of benzoic acid, filler 5 parts, wetting agent 4 parts.
A kind of method preparing the environmental protection acrylic paints containing stalky tea powder as above, particularly as follows:
(1) preparation of A agent: first by after thickening agent, Radix Acaciae senegalis mix homogeneously, add water, after swelling 5 hours；Being heated to temperature is 70 DEG C, and heat time heating time is 10min, prepares binding agent glue；Then by wetting agent with after stalky tea powder mixing 7min, add in binding agent glue, stir 12min；Add polyacrylate emulsion, after stirring 10min；Adding preservative, dispersant, pigment powder, stirring 7min prepares coarse particles；The ground machine of coarse particles is ground to fineness below 20 μm；In injection material storage barrel, seal, prepare A agent；
(2) preparation of B agent: by acrylic resin, thickening agent, distilled water, dispersant, defoamer, preservative, filler, wetting agent mixing, stirring at normal temperature 15min, inject in material storage barrel, seal and prepare B agent.
The using method of a kind of environmental protection acrylic paints containing stalky tea powder as above, after using A agent 3 ~ 5d, in A agent surface spraying B agent.
Embodiment
3
A kind of environmental protection acrylic paints containing stalky tea powder, including A agent and B agent；It is according to the mass fraction,
A agent: thickening agent 11 parts, Radix Acaciae senegalis 5 parts, 15 parts of water, 10 parts of stalky tea powder, polyacrylate emulsion 50 parts, dispersant 2 parts, 8 parts of pigment powder, glycerol 4 parts, sodium benzoate 4 parts；
B agent: acrylic resin 55 parts, hydroxyethyl cellulose 5 parts, distilled water 15 parts, dispersant 4 parts, defoamer 8 parts, sodium benzoate 3 parts, filler 3 parts, wetting agent 5 parts.
A kind of method preparing the environmental protection acrylic paints containing stalky tea powder as above, particularly as follows:
(1) preparation of A agent: first by after thickening agent, Radix Acaciae senegalis mix homogeneously, add water, after swelling 4 hours；Being heated to temperature is 65 DEG C, and heat time heating time is 15min, prepares binding agent glue；Then by wetting agent with after stalky tea powder mixing 10min, add in binding agent glue, stir 15min；Add polyacrylate emulsion, after stirring 20min；Adding preservative, dispersant, pigment powder, stirring 10min prepares coarse particles；The ground machine of coarse particles is ground to fineness below 20 μm；In injection material storage barrel, seal, prepare A agent；
(2) preparation of B agent: by acrylic resin, thickening agent, distilled water, dispersant, defoamer, preservative, filler, wetting agent mixing, stirring at normal temperature 10min, inject in material storage barrel, seal and prepare B agent.
The using method of a kind of environmental protection acrylic paints containing stalky tea powder as above, after using A agent 3 ~ 5d, in A agent surface spraying B agent.
The implementation result of embodiment 1-3 is: the color of the sprayed protection pigment of B agent itself so that it is not fugitive color, weather-proof, stain resistant；The original color of pigment will not be changed, but also improve the plumpness of its color and luster；And because there being the addition of stalky tea powder in A agent, A agent does not has the bad smell of general pigment, has light tea smell；And after using this pigment, indoor content of formaldehyde, significantly lower than content of formaldehyde during other raw materials of use, illustrates that the addition of stalky tea powder is adsorbed with effect to indoor formaldehyde.
The foregoing is only presently preferred embodiments of the present invention, all impartial changes done according to scope of the present invention patent and modification, all should belong to the covering scope of the present invention.
Claims (5)
1. the preparation method of the environmental protection acrylic paints containing stalky tea powder, it is characterised in that: include A agent and B agent；It is according to the mass fraction,
A agent: thickening agent 8 ~ 11 parts, Radix Acaciae senegalis 5 ~ 10 parts, 10 ~ 15 parts of water, 10 ~ 15 parts of stalky tea powder, polyacrylate emulsion 50 ~ 55 parts, dispersant 2 ~ 3 parts, 5 ~ 8 parts of pigment powder, wetting agent 4 ~ 10 parts, preservative 3 ~ 5 parts；
B agent: acrylic resin 40 ~ 55 parts, thickening agent 2 ~ 5 parts, distilled water 10 ~ 15 parts, dispersant 2 ~ 4 parts, defoamer 3 ~ 8 parts, preservative 2 ~ 4 parts, filler 2 ~ 5 parts, wetting agent 2 ~ 5 parts；
Concrete preparation process is:
(1) preparation of A agent: first by after thickening agent, Radix Acaciae senegalis mix homogeneously, add water, after swelling 4 ~ 6 hours；Being heated to temperature is 60 ~ 70 DEG C, and heat time heating time is 10 ~ 20min, prepares binding agent glue；Then, after wetting agent being mixed 5 ~ 10min with stalky tea powder, add in binding agent glue, stir 10 ~ 15min；Add polyacrylate emulsion, after stirring 10 ~ 20min；Adding preservative, dispersant, pigment powder, stirring 5 ~ 10min prepares coarse particles；The ground machine of coarse particles is ground to fineness below 20 μm；In injection material storage barrel, seal, prepare A agent；Described stalky tea powder is that stalky tea is pulverized through ball mill, crosses 1000 ~ 1200 mesh sieves and makes；
(2) preparation of B agent: by acrylic resin, thickening agent, distilled water, dispersant, defoamer, preservative, filler, wetting agent mixing, stirring at normal temperature 10 ~ 15min, inject in material storage barrel, seal and prepare B agent.
The preparation method of the environmental protection acrylic paints containing stalky tea powder the most according to claim 1, it is characterised in that: described filler is precipitated calcium carbonate.
The preparation method of the environmental protection acrylic paints containing stalky tea powder the most according to claim 1, it is characterised in that: described thickening agent is the one in hydroxypropyl methyl cellulose, sodium carboxymethyl cellulose or hydroxyethyl cellulose.
The preparation method of the environmental protection acrylic paints containing stalky tea powder the most according to claim 1, it is characterised in that: described pigment powder is the one in titanium dioxide, ferrum oxide, calcium carbonate.
5. the using method of the environmental protection acrylic paints containing stalky tea powder that a preparation method as claimed in claim 1 prepares, it is characterised in that: after using A agent 3 ~ 5d, in A agent surface spraying B agent.