CN105820477A - Composite anti-corrosive and anti-static plastic - Google Patents
Composite anti-corrosive and anti-static plastic Download PDFInfo
- Publication number
- CN105820477A CN105820477A CN201610345325.2A CN201610345325A CN105820477A CN 105820477 A CN105820477 A CN 105820477A CN 201610345325 A CN201610345325 A CN 201610345325A CN 105820477 A CN105820477 A CN 105820477A
- Authority
- CN
- China
- Prior art keywords
- accounts
- parts
- agent
- corrosive
- antistatic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses composite anti-corrosive and anti-static plastic which comprises an anti-corrosive layer as a surface layer and an anti-static layer as an inner layer .The anti-corrosive layer is made from polyvinyl chloride, an antioxidant, an anti-corrosive agent, a filling agent and a toughening agent .The anti-static layer is made from polyethylene, an antistatic agent, a plasticizer, a dispersing agent and a reinforcing agent .The antioxidant is 2-hydroxy-4-n-octyloxybenzophenone .The anti-corrosive agent is sorbitan monooleate .The filling agent is kaolin .The toughening agent is polyvinyl butyral .The antistatic agent is alkyl sodium sulfonate .The plasticizer is triethyl citrate .The dispersing agent is triethylhexyl phosphoric acid .The reinforcing agent is talcum powder .By arranging a double-layer composite structure, the anti-corrosive and anti-aging effects can be effectively achieved, the internal structure is safe and resistant to static electricity, wrapping is complete, and the use effect is good.
Description
Technical field
The present invention relates to a kind of plastic applications, be specifically related to a kind of composite anti-corrosive antistatic plastic.
Background technology
Cable cover(ing) is the outermost layer of cable, if VV is polyvinyl chloride insulation, and pvc sheath.Outside wear to cry protection manage.The sheath used in prior art is mostly single layer structure, uses function the most single, it is impossible to fully effective plays protected effect.
Summary of the invention
It is an object of the invention to provide and a kind of arrange by two-layer composite, not only can effectively play the age inhibiting effect of anticorrosion, and the safe antistatic of internal structure, cladding is complete, the composite anti-corrosive antistatic plastic that using effect is good.
nullThe technical scheme is that,A kind of composite anti-corrosive antistatic plastic,Corrosion-resistant coating and the antistatic backing of internal layer including top layer,Described corrosion-resistant coating is by polrvinyl chloride、Antioxidant、Corrosion-resistant agent、Filler and toughener composition,Described antioxidant is Octabenzone,Described corrosion-resistant agent is sorbitan monooleate,Described filler is Kaolin,Described toughener is polyvinyl butyral resin,Parts by weight shared by each composition of described corrosion-resistant coating are respectively as follows: described polrvinyl chloride and account for 57-63 part,Described Octabenzone accounts for 10-15 part,Described sorbitan monooleate accounts for 14-18 part,Described Kaolin accounts for 42-46 part,Described polyvinyl butyral resin accounts for 23-27 part,Described antistatic backing is by polyethylene、Antistatic additive、Plasticiser、Dispersant and reinforcing agent composition,Described antistatic additive is sodium alkyl sulfonate,Described plasticiser is triethyl citrate,Described dispersant is triethyl group hexyl phosphoric acid,Described reinforcing agent is Pulvis Talci,Parts by weight shared by each composition of described antistatic backing are respectively as follows: described polyethylene and account for 48-52 part,Described sodium alkyl sulfonate accounts for 9-14 part,Described triethyl citrate accounts for 5-10 part,Described triethyl group hexyl phosphoric acid accounts for 7-11 part,Described Pulvis Talci accounts for 31-36 part.
In a preferred embodiment of the present invention, parts by weight shared by each composition of described corrosion-resistant coating are particularly as follows: described polrvinyl chloride accounts for 58 parts, described Octabenzone accounts for 11 parts, and described sorbitan monooleate accounts for 15 parts, and described Kaolin accounts for 43 parts;Described polyvinyl butyral resin accounts for 24 parts.
In a preferred embodiment of the present invention, parts by weight shared by each composition of described antistatic backing are particularly as follows: described polyethylene accounts for 49 parts, and described sodium alkyl sulfonate accounts for 10 parts, and described triethyl citrate accounts for 6 parts, described triethyl group hexyl phosphoric acid accounts for 8 parts, and described Pulvis Talci accounts for 32 parts.
Of the present invention is a kind of composite anti-corrosive antistatic plastic, is arranged by two-layer composite, not only can effectively play the age inhibiting effect of anticorrosion, and the safe antistatic of internal structure, completely, using effect is good for cladding.
Detailed description of the invention
Below presently preferred embodiments of the present invention is described in detail, so that advantages and features of the invention can be easier to be readily appreciated by one skilled in the art, thus protection scope of the present invention is made apparent clear and definite defining.
nullOf the present invention is a kind of composite anti-corrosive antistatic plastic,Corrosion-resistant coating and the antistatic backing of internal layer including top layer,Described corrosion-resistant coating is by polrvinyl chloride、Antioxidant、Corrosion-resistant agent、Filler and toughener composition,Described antioxidant is Octabenzone,Described corrosion-resistant agent is sorbitan monooleate,Described filler is Kaolin,Described toughener is polyvinyl butyral resin,Parts by weight shared by each composition of described corrosion-resistant coating are respectively as follows: described polrvinyl chloride and account for 57-63 part,Described Octabenzone accounts for 10-15 part,Described sorbitan monooleate accounts for 14-18 part,Described Kaolin accounts for 42-46 part,Described polyvinyl butyral resin accounts for 23-27 part,Described antistatic backing is by polyethylene、Antistatic additive、Plasticiser、Dispersant and reinforcing agent composition,Described antistatic additive is sodium alkyl sulfonate,Described plasticiser is triethyl citrate,Described dispersant is triethyl group hexyl phosphoric acid,Described reinforcing agent is Pulvis Talci,Parts by weight shared by each composition of described antistatic backing are respectively as follows: described polyethylene and account for 48-52 part,Described sodium alkyl sulfonate accounts for 9-14 part,Described triethyl citrate accounts for 5-10 part,Described triethyl group hexyl phosphoric acid accounts for 7-11 part,Described Pulvis Talci accounts for 31-36 part.
Further, parts by weight shared by each composition of described corrosion-resistant coating are particularly as follows: described polrvinyl chloride accounts for 58 parts, and described Octabenzone accounts for 11 parts, and described sorbitan monooleate accounts for 15 parts, and described Kaolin accounts for 43 parts;Described polyvinyl butyral resin accounts for 24 parts.
Further, parts by weight shared by each composition of described antistatic backing are particularly as follows: described polyethylene accounts for 49 parts, and described sodium alkyl sulfonate accounts for 10 parts, and described triethyl citrate accounts for 6 parts, and described triethyl group hexyl phosphoric acid accounts for 8 parts, and described Pulvis Talci accounts for 32 parts.
Further, parts by weight shared by each composition of described corrosion-resistant coating are respectively as follows: described polrvinyl chloride and account for 62 parts, and described Octabenzone accounts for 14 parts, and described sorbitan monooleate accounts for 17 parts, and described Kaolin accounts for 45 parts;Described polyvinyl butyral resin accounts for 26 parts.
Further, parts by weight shared by each composition of described antistatic backing are respectively as follows: described polyethylene and account for 48-52 part, and described sodium alkyl sulfonate accounts for 13 parts, and described triethyl citrate accounts for 9 parts, and described triethyl group hexyl phosphoric acid accounts for 10 parts, and described Pulvis Talci accounts for 35 parts.
It addition, can be by regulating the Different Weight number of each composition of product so that the properties of product height obtained differs.
Of the present invention is a kind of composite anti-corrosive antistatic plastic, is arranged by two-layer composite, not only can effectively play the age inhibiting effect of anticorrosion, and the safe antistatic of internal structure, completely, using effect is good for cladding.
The foregoing is only the detailed description of the invention of the present invention; but protection scope of the present invention is not limited thereto; any those of ordinary skill in the art are in the technical scope that disclosed herein; the change can expected without creative work or replacement, all should contain within protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claims are limited.
Claims (3)
- null1. a composite anti-corrosive antistatic plastic,Corrosion-resistant coating and the antistatic backing of internal layer including top layer,It is characterized in that: described corrosion-resistant coating is by polrvinyl chloride、Antioxidant、Corrosion-resistant agent、Filler and toughener composition,Described antioxidant is Octabenzone,Described corrosion-resistant agent is sorbitan monooleate,Described filler is Kaolin,Described toughener is polyvinyl butyral resin,Parts by weight shared by each composition of described corrosion-resistant coating are respectively as follows: described polrvinyl chloride and account for 57-63 part,Described Octabenzone accounts for 10-15 part,Described sorbitan monooleate accounts for 14-18 part,Described Kaolin accounts for 42-46 part,Described polyvinyl butyral resin accounts for 23-27 part,Described antistatic backing is by polyethylene、Antistatic additive、Plasticiser、Dispersant and reinforcing agent composition,Described antistatic additive is sodium alkyl sulfonate,Described plasticiser is triethyl citrate,Described dispersant is triethyl group hexyl phosphoric acid,Described reinforcing agent is Pulvis Talci,Parts by weight shared by each composition of described antistatic backing are respectively as follows: described polyethylene and account for 48-52 part,Described sodium alkyl sulfonate accounts for 9-14 part,Described triethyl citrate accounts for 5-10 part,Described triethyl group hexyl phosphoric acid accounts for 7-11 part,Described Pulvis Talci accounts for 31-36 part.
- Composite anti-corrosive antistatic plastic the most according to claim 1, it is characterized in that: parts by weight shared by each composition of described corrosion-resistant coating are particularly as follows: described polrvinyl chloride accounts for 58 parts, described Octabenzone accounts for 11 parts, described sorbitan monooleate accounts for 15 parts, and described Kaolin accounts for 43 parts;Described polyvinyl butyral resin accounts for 24 parts.
- Composite anti-corrosive antistatic plastic the most according to claim 1, it is characterized in that: parts by weight shared by each composition of described antistatic backing are particularly as follows: described polyethylene accounts for 49 parts, described sodium alkyl sulfonate accounts for 10 parts, described triethyl citrate accounts for 6 parts, described triethyl group hexyl phosphoric acid accounts for 8 parts, and described Pulvis Talci accounts for 32 parts.