CN105777001A - Plastered fireproof stone composite reinforcing insulation board for building and preparation method of insulation board - Google Patents
Plastered fireproof stone composite reinforcing insulation board for building and preparation method of insulation board Download PDFInfo
- Publication number
- CN105777001A CN105777001A CN201610127832.9A CN201610127832A CN105777001A CN 105777001 A CN105777001 A CN 105777001A CN 201610127832 A CN201610127832 A CN 201610127832A CN 105777001 A CN105777001 A CN 105777001A
- Authority
- CN
- China
- Prior art keywords
- stone material
- preparation
- building
- plastering
- fire prevention
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a plastered fireproof stone composite reinforcing insulation board for a building and a preparation method of the insulation board.A plastering mortar layer is composited on the base surface of a foamed phenolic resin material and prepared from, by weight, 250-500 kg of quartz sand, 150-250 kg of Portland cement, 100-150 kg of fly ash, 50-100 kg of wollastonite, 5-25 kg of inorganic pigments and 20-50 kg of an additive.According to the insulation board and the preparation method thereof, the plastering mortar is composited on the phenolic resin material, therefore, the strength is improved while the thermal insulation property of the building is improved, and the insulation board is not prone to damage and crack; stone is composited with the insulation board, therefore, the decorative effect of the building is greatly improved, the advantages of being not prone to fall off, easy to construct and the like are achieved, and the cost input is low; the preparation technology is simple and environmentally friendly, industrialized production is easy to achieve, and the good social and economic benefits are achieved.
Description
Technical field
The present invention relates to building heat preservation and decoration technique field, particularly related to a kind of building and smeared
Ash fire prevention composite reinforced warming plate of stone material and preparation method thereof.
Background technology
Gradually being taken seriously along with energy-saving building technology and promote, exterior-wall heat insulation is building joint
One of energy technology, is a kind of power-saving technology reducing building energy loss.Exterior-wall heat insulation is logical
After plinth course outside (including cast or building block exterior wall) one or more layers thermal insulating material of surface recombination
Material.Wherein, if insulation material has decoration function in building, then there is bigger application empty
Between, it is possible not only to improve environment, has preferable economic benefit simultaneously.Therefore building is being ensured
While insulation, in order to play building decoration effect, the method for prior art is usually is protecting
Ceramic tile or coating decorative coating is laid, owing to ceramic tile and heat preservation plate material heat are swollen outside temperature sheet material
Swollen performance difference is relatively big, i.e. ftractures in being used in architectural very short time, and quality can not be guaranteed.
At present, people, when construction, use and are affixed directly to outside building by TERRAZZO
Method on wall reaches the effect of decorative architecture, but can easily come off after Long-Time Service,
Service life is short, and complexity of constructing, the time of the straight line duration accounting for pressure construction is longer,
Cost of labor is high.
Therefore, in order to solve the problem of above-mentioned existence, spy of the present invention provides a kind of new skill
Art scheme.
Summary of the invention
It is an object of the invention to provide the fire prevention composite reinforced insulation of stone material of a kind of building plastering
Plate and preparation method thereof, it is possible to prior art warming plate dicoration is poor, intensity is relatively low in solution,
The problems such as construction cost is high, fully meet the demand of building heat preservation decoration.
The present invention is directed to above-mentioned technological deficiency be the technical scheme is that
A kind of building plastering fire prevention composite reinforced warming plate of stone material and preparation method thereof, is sending out
The basal plane of bubble phenolic resin material is compounded with plastering sand pulp layer, and described plastering sand pulp layer includes following
The raw material composition of weight:
Further, the thickness of described plastering sand pulp layer is 1-3mm.
Further, described inorganic pigment is carbon black, titanium white, barba hispanica, iron oxide series face
One or more combination in material.
Further, the preparation side of a kind of building plastering fire prevention composite reinforced warming plate of stone material
Method, comprises the steps:
A: carry out stone material picking, polish, the pretreatment such as cleaning, then by surfacing
Stone material is inserted baking box and is carried out once baking process；
B: the surface coated with adhesive of the stone material after toasting through step a；
C: step b is coated with the stone material of binding agent and inserts baking box and carry out secondary baking process；
D: the stone material that step c was processed and the foamed phenolic resin being compounded with plastering sand pulp layer
Material carries out bonding compound, fire prevention stone composite insulation board of must plastering.
Further, the baking temperature that the once baking described in step a processes is 80-100 DEG C,
Baking time 1.5-2h.
Further, the binding agent described in step b is epoxy adhesive.
Further, the baking temperature that the secondary baking described in step c processes is 45--60 DEG C,
Baking time 3.5-4h.
The invention has the beneficial effects as follows: the present invention is compounded with motar on phenolic resin material,
While improving building heat preservation performance, increase intensity, be hardly damaged cracking；And by stone material with
Warming plate is combined, and is greatly improved the effect of building decoration, has difficult drop-off, construction
The advantage such as simple, cost puts into low；And preparation technology of the present invention is simple and environmentally-friendly, it is easy to work
Industry metaplasia is produced, and has good Social and economic benef@.
Detailed description of the invention
Below in conjunction with detailed description of the invention, technical scheme is further limited,
But claimed scope is not only limited to description.
Embodiment 1
A kind of building plastering fire prevention composite reinforced warming plate of stone material and preparation method thereof, is sending out
The basal plane of bubble phenolic resin material is compounded with plastering sand pulp layer, and plastering sand pulp layer includes following weight
Raw material composition:
Wherein, the thickness of plastering sand pulp layer is 1mm, and inorganic pigment is carbon black, titanium white, iron
One or more combination in indigo plant, iron oxide serial pigment.
It addition, the preparation method of a kind of building plastering fire prevention composite reinforced warming plate of stone material,
Comprise the steps:
A: carry out stone material picking, polish, the pretreatment such as cleaning, then by surfacing
Stone material is inserted baking box and is carried out once baking process, and baking temperature is 80 DEG C, baking time
1.5h；
The surface coating epoxy adhesive of b: the stone material after toasting through step a；
C: step b is coated with the stone material of binding agent and inserts baking box and carry out secondary baking process,
Baking temperature is 45 DEG C, baking time 3.5h；
D: the stone material that step c was processed and the foamed phenolic resin being compounded with plastering sand pulp layer
Material carries out bonding compound, fire prevention stone composite insulation board of must plastering.
Embodiment 2
A kind of building plastering fire prevention composite reinforced warming plate of stone material and preparation method thereof, is sending out
The basal plane of bubble phenolic resin material is compounded with plastering sand pulp layer, and plastering sand pulp layer includes following weight
Raw material composition:
Wherein, the thickness of plastering sand pulp layer is 2mm, and inorganic pigment is carbon black, titanium white, iron
One or more combination in indigo plant, iron oxide serial pigment.
It addition, the preparation method of a kind of building plastering fire prevention composite reinforced warming plate of stone material,
Comprise the steps:
A: carry out stone material picking, polish, the pretreatment such as cleaning, then by surfacing
Stone material is inserted baking box and is carried out once baking process, and baking temperature is 90 DEG C, baking time
1.8h；
The surface coating epoxy adhesive of b: the stone material after toasting through step a；
C: step b is coated with the stone material of binding agent and inserts baking box and carry out secondary baking process,
Baking temperature is 55 DEG C, baking time 3.8h；
D: the stone material that step c was processed and the foamed phenolic resin being compounded with plastering sand pulp layer
Material carries out bonding compound, fire prevention stone composite insulation board of must plastering.
Embodiment 3
A kind of building plastering fire prevention composite reinforced warming plate of stone material and preparation method thereof, is sending out
The basal plane of bubble phenolic resin material is compounded with plastering sand pulp layer, and plastering sand pulp layer includes following weight
Raw material composition:
Wherein, the thickness of plastering sand pulp layer is 3mm, and inorganic pigment is carbon black, titanium white, iron
One or more combination in indigo plant, iron oxide serial pigment.
It addition, the preparation method of a kind of building plastering fire prevention composite reinforced warming plate of stone material,
Comprise the steps:
A: carry out stone material picking, polish, the pretreatment such as cleaning, then by surfacing
Stone material is inserted baking box and is carried out once baking process, and baking temperature is 100 DEG C, baking time
2h；
The surface coating epoxy adhesive of b: the stone material after toasting through step a；
C: step b is coated with the stone material of binding agent and inserts baking box and carry out secondary baking process,
Baking temperature is 60 DEG C, baking time 4h；
D: the stone material that step c was processed and the foamed phenolic resin being compounded with plastering sand pulp layer
Material carries out bonding compound, fire prevention stone composite insulation board of must plastering.
The invention has the beneficial effects as follows: the present invention is compounded with motar on phenolic resin material,
While improving building heat preservation performance, increase intensity, be hardly damaged cracking；And by stone material with
Warming plate is combined, and is greatly improved the effect of building decoration, has difficult drop-off, construction
The advantage such as simple, cost puts into low；And preparation technology of the present invention is simple and environmentally-friendly, it is easy to work
Industry metaplasia is produced, and has good Social and economic benef@.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention,
For a person skilled in the art, the present invention can have various modifications and variations.All
Within the spirit and principles in the present invention, any modification, equivalent substitution and improvement etc. made,
Should be included within the scope of the present invention.
Claims (7)
1. building plastering fire prevention composite reinforced warming plate of stone material and preparation method thereof, its feature
It is: the basal plane at foamed phenolic resin material is compounded with plastering sand pulp layer, described motar
Layer includes that the raw material of following weight forms:
A kind of building plastering fire prevention composite reinforced warming plate of stone material the most according to claim 1
And preparation method thereof, it is characterised in that: the thickness of described plastering sand pulp layer is 1-3mm.
A kind of building plastering fire prevention composite reinforced warming plate of stone material the most according to claim 1
And preparation method thereof, it is characterised in that: described inorganic pigment be carbon black, titanium white, barba hispanica,
One or more combination in iron oxide serial pigment.
A kind of building plastering fire prevention composite reinforced warming plate of stone material the most according to claim 1
And preparation method thereof, it is characterised in that: comprise the steps:
A: carry out stone material picking, polish, the pretreatment such as cleaning, then by surfacing
Stone material is inserted baking box and is carried out once baking process；
B: the surface coated with adhesive of the stone material after toasting through step a；
C: step b is coated with the stone material of binding agent and inserts baking box and carry out secondary baking process；
D: the stone material that step c was processed and the foamed phenolic resin being compounded with plastering sand pulp layer
Material carries out bonding compound, fire prevention stone composite insulation board of must plastering.
A kind of building plastering fire prevention composite reinforced warming plate of stone material the most according to claim 4
And preparation method thereof, it is characterised in that: the baking temperature that the once baking described in step a processes
Degree is 80-100 DEG C, baking time 1.5-2h.
A kind of building plastering fire prevention composite reinforced warming plate of stone material the most according to claim 4
And preparation method thereof, it is characterised in that: the binding agent described in step b is epoxy bond
Agent.
A kind of building plastering fire prevention composite reinforced warming plate of stone material the most according to claim 4
And preparation method thereof, it is characterised in that: the baking temperature that the secondary baking described in step c processes
Degree is 45--60 DEG C, baking time 3.5-4h.