CN105758885A - 一种粉煤灰竖向膨胀率检测方法 - Google Patents

一种粉煤灰竖向膨胀率检测方法 Download PDF

Info

Publication number
CN105758885A
CN105758885A CN201610141495.9A CN201610141495A CN105758885A CN 105758885 A CN105758885 A CN 105758885A CN 201610141495 A CN201610141495 A CN 201610141495A CN 105758885 A CN105758885 A CN 105758885A
Authority
CN
China
Prior art keywords
flyash
hours
expansion ratio
vertical expansion
die trial
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610141495.9A
Other languages
English (en)
Inventor
樊钧
施钟毅
林茂松
韩建军
杨利香
朱盛胜
樊俊江
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Building Science Research Institute Co Ltd
Original Assignee
Shanghai Building Science Research Institute Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Building Science Research Institute Co Ltd filed Critical Shanghai Building Science Research Institute Co Ltd
Priority to CN201610141495.9A priority Critical patent/CN105758885A/zh
Publication of CN105758885A publication Critical patent/CN105758885A/zh
Pending legal-status Critical Current

Abstract

一种粉煤灰竖向膨胀率检测方法通过确定浆体配比、试模规格、检测工具精度等，实现了粉煤灰竖向膨胀率的定量检测，解决了现有标准安定性检测方法的不适用的难题题。

Description

一种粉煤灰竖向膨胀率检测方法
技术领域
本发明属于物质参数检测技术领域，具体讲就是涉及一种粉煤灰竖向膨胀率检测方法。
背景技术
粉煤灰是燃煤电厂的副产物，广泛用于混凝土、砂浆和墙体材料等建材的生产。近年来在粉煤灰的应用中陆续发现了若干异常现象，具体表现为粉煤灰具有严重氨味，制备的混凝土、砂浆体积膨胀，力学性能和耐久性能严重劣化。但参照现行粉煤灰标准检测该类粉煤灰的安定性是合格的，目前尚无相关方法标准对粉煤灰的竖向膨胀率指标进行检测控制，粉煤灰仍按传统资源化利用方式处置，具有极大的安全隐患。
发明内容
本发明的目的就是针对现有的粉煤灰竖向膨胀率指标无法检测的技术缺陷，提供一种粉煤灰竖向膨胀率检测方法，可用于粉煤灰竖向膨胀率的定量检测。
技术方案
为了实现上述技术目的，本发明设计的一种粉煤灰竖向膨胀率检测方法，其特征在于，它包括以下几个步骤：
第一步，采用基准水泥，粉煤灰掺量取30％，固定水胶比0.5，制备粉煤灰水泥净浆；
第二步，将重为50g±2g的玻璃板置于100mm×100mm×100mm试模上方中间位置，浆料一次性从一侧注满试模，至另一侧溢出并高于试模边缘约2mm，成型过程应在搅拌结束3分钟内完成；
第三步，用湿棉布覆盖玻璃两侧的浆料；
第四步，把千分表测量头垂直放在玻璃板中央，并安装牢固,在30s内读取初始读数h0；
第五步，自加水搅拌起分别于1小时、2小时、3小时、4小时、5小时、6小时....i小时分别读取千分表读数h1，h2，h3，h4，h5，h6，.....hi；
第六步，整个测试过程应保持棉布湿润、装置不得受震动、成型养护温度均为20℃±2℃。
第七步，粉煤灰单位时间的竖向膨胀率ci按下述公式进行计算：
c i = ( h i - h 0 ) 100 × 100 %
有益效果
本发明供一种粉煤灰竖向膨胀率检测方法通过确定浆体配比、试模规格、检测工具精度等，实现了粉煤灰竖向膨胀率的定量检测，解决了现有标准安定性检测方法的不适用性问题。
附图说明
附图1是本发明实施例中测试装置结构示意图。
具体实施方式
下面结合附图和实施例，对本发明做进一步说明。
实施例
利用如附图1所示的测试装置进行粉煤灰竖向膨胀率的检测，
①选取上海市燃煤电厂和施工现场取样粉煤灰5种，记为F1、F2、F3、F4、F5，其中F1-F3为电厂取样粉煤灰，各项性能正常；F4、F5为施工现场取样粉煤灰，配制的混凝土体积膨胀。采用基准水泥，粉煤灰掺量取30％，固定水胶比0.5，制备各组粉煤灰水泥净浆C1-C5；
②将重为50g±2g的玻璃板置于100mm×100mm×100mm试模上方中间位置，将浆料C1一次性从一侧注满试模，至另一侧溢出并高于试模边缘2mm，成型过程应在搅拌结束3min内完成。
③用湿棉布覆盖玻璃两侧的浆料。
④把千分表测量头垂直放在玻璃板中央，井安装牢固。在30s内读取初始读数h0。
⑤自加水搅拌起分别于1h、2h、3h、4h、5h、6h读取千分表读数h1，h2，h3，h4，h5，h6。
⑥整个测试过程应保持棉布湿润、装置不得受震动、成型养护温度均为20℃±2℃。
⑦粉煤灰单位时间的竖向膨胀率ci按下式进行计算：
c i = ( h i - h 0 ) 100 × 100
所得结果精确至0.01，单位为％。
⑧重复C2-C5粉煤灰的单位时间竖向膨胀率ci测量试验。
试验结果见表1。由表可知，F1-F3粉煤灰性能正常，竖向膨胀率为0；而F4、F5粉煤灰配制混凝土体积膨胀，6小时的粉煤灰竖向膨胀率分别为5.62％、2.12％，该方法可实现粉煤灰竖向膨胀率的定量表征，填补标准方法的空白，为粉煤灰的质量控制与安全利用提供技术支撑。
表1粉煤灰竖向膨胀率

Claims (1)

1.一种粉煤灰竖向膨胀率检测方法，其特征在于，它包括以下几个步骤：
(1)采用基准水泥，粉煤灰掺量取30％，固定水胶比0.5，制备粉煤灰水泥净浆；
(2)将重为50g±2g的玻璃板置于100mm×100mm×100mm试模上方中间位置，浆料一次性从一侧注满试模，至另一侧溢出并高于试模边缘2mm±0.5mm，成型过程应在搅拌结束3分钟内完成；
(3)用湿棉布覆盖玻璃两侧的浆料；
(4)把千分表测量头垂直放在玻璃板中央，并安装牢固,在30s内读取初始读数h0；
(5)自加水搅拌起分别于1小时、2小时、3小时、4小时、5小时、6小时....i小时分别读取千分表读数h1，h2，h3，h4，h5，h5，.....hi；
(6)整个测试过程应保持棉布湿润、装置不得受震动、成型养护温度均为20℃±2℃。
(7)粉煤灰单位时间的竖向膨胀率ci按下述公式进行计算：
c i = ( h i - h 0 ) 100 × 100 %
CN201610141495.9A 2016-03-11 2016-03-11 一种粉煤灰竖向膨胀率检测方法 Pending CN105758885A (zh)