CN105753463B - One kind mixing feldspar material - Google Patents
One kind mixing feldspar material Download PDFInfo
- Publication number
- CN105753463B CN105753463B CN201410780095.3A CN201410780095A CN105753463B CN 105753463 B CN105753463 B CN 105753463B CN 201410780095 A CN201410780095 A CN 201410780095A CN 105753463 B CN105753463 B CN 105753463B
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- low
- powders
- calcite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses one kind to mix feldspar material, is formed by the polished firing of the component of following number：100 150 parts of mullite powders, 50 60 parts of quartz powders, 80 85 parts of calcite in powder, 30 45 parts of olive mountain flours, 50 55 parts of Giallo Cecilia stone material powder, 58 parts of diatom oozes, 35 parts of dimethyl silicone polymers, 8 10 parts of sodium carboxymethylcelluloses, 68 parts of hydroxyethyl celluloses, 58 parts of rosin, 68 parts of glycerine, 10 12 parts of lime stones.The mixing feldspar material has high heat conductance, and high radiation coefficient, low cost, the features such as can manufacture, solves the shortcomings that high cost of existing aluminium oxide ceramics, low yield energy, the lower thermal conductivity of steatite ceramic, radiation coefficient is low.Raw material passes through working process, pass through hot pressing or dry pressuring forming process again, high heat conductance, height heat dissipation, inexpensive special ceramic material are prepared into after high-temperature firing, suitable for high power and the LED lamp of low-power, including lamp cap, LED support, substrate or COB substrates, it is widely used in the fields such as commercial lighting, room lighting.
Description
Technical field
The present invention relates to one kind to mix feldspar material, more particularly to a kind of mixing feldspar material with high heat conductance
Material.
Background technology
Ceramic material is as a kind of heat sink material that LED lamp radiating shells are rises in this 2 years, currently on the market conduct
The ceramics of LED lamp outer casings are mainly aluminium oxide ceramics and steatite ceramic, and ceramic material can effectively solve the heat dissipation problem of LED
And Insulation Problems.
Alumina ceramic material density is high, expensive starting materials, and firing temperature is more than 1600 degree, firing period length, it is impossible to batch
Amount production, although thermal conductivity is high, manufacture cost is too high, and product is too heavy.
Steatite ceramic thermal conductivity is low, although low manufacture cost, can manufacture, and thermal conductivity is too low, and heat dissipation is not good enough, can only
Make the LED lamps and lanterns of low-power.
The content of the invention
For the defects of present invention is intended to overcome the prior art, and it is an object of the present invention to provide a kind of mixing feldspar material, this is mixed
Closing feldspar material has high heat conductance, and high radiation coefficient, low cost, the features such as can manufacture, solves existing aluminium oxide
The shortcomings that high cost of ceramics, low yield energy, the lower thermal conductivity of steatite ceramic, radiation coefficient is low.Raw material passes through working process, then passes through
Hot pressing or dry pressuring forming process, are prepared into high heat conductance, height heat dissipation, inexpensive special ceramic material, is fitted after high-temperature firing
For high power and the LED lamps and lanterns of low-power, including lamp cap, LED stents, substrate or COB substrates are widely used in business
The fields such as illumination, room lighting.
The technical solution adopted by the present invention to solve the technical problems is：One kind mixing feldspar material, by following number
Component it is polished firing form：100-150 parts of mullite powders, 50-60 parts of quartz powders, 80-85 parts of calcite in powder, 30-
45 parts of olive mountain flours, 50-55 parts of Giallo Cecilia stone material powder, 5-8 parts of diatom oozes, 3-5 parts of dimethyl silicone polymers, 8-10 parts of carboxymethyls
Sodium cellulosate, 6-8 parts of hydroxyethyl celluloses, 5-8 parts of rosin, 6-8 parts of glycerine, 10-12 parts of lime stones.
Further, formed by the polished firing of component of following number：100 parts of mullite powders, 50 parts of quartz powders,
80 parts of calcite in powder, 30 parts of olive mountain flours, 50 parts of Giallo Cecilia stone material powder, 5 parts of diatom oozes, 3 parts of dimethyl silicone polymers, 8 parts of carboxylics
Sodium carboxymethylcellulose pyce, 6 parts of hydroxyethyl celluloses, 5 parts of rosin, 6 parts of glycerine, 10 parts of lime stones.
Either, formed by the polished firing of component of following number：150 parts of mullite powders, 60 parts of quartz powders, 85
Part calcite in powder, 45 parts of olive mountain flours, 55 parts of Giallo Cecilia stone material powder, 8 parts of diatom oozes, 5 parts of dimethyl silicone polymers, 10 parts of carboxylic first
Base sodium cellulosate, 8 parts of hydroxyethyl celluloses, 8 parts of rosin, 8 parts of glycerine, 12 parts of lime stones.
In conclusion the mixing feldspar material of the present invention has high heat conductance, high radiation coefficient, low cost can batch
The features such as production, solve the high cost of existing aluminium oxide ceramics, low yield energy, the lower thermal conductivity of steatite ceramic, radiation coefficient is low to be lacked
Point.Raw material passes through working process, then by hot pressing or dry pressuring forming process, high heat conductance is prepared into after high-temperature firing, height dissipates
Heat, inexpensive special ceramic material, suitable for high power and the LED lamps and lanterns of low-power, including lamp cap, LED stents, substrate
Or COB substrates, it is widely used in the fields such as commercial lighting, room lighting.
Embodiment
Embodiment 1
The described a kind of mixing feldspar material of the embodiment of the present invention 1, by the polished firing of the component of following number
Form：100 parts of mullite powders, 50 parts of quartz powders, 80 parts of calcite in powder, 30 parts of olive mountain flours, 50 parts of Giallo Cecilia stone material powder, 5
Part diatom ooze, 3 parts of dimethyl silicone polymers, 8 parts of sodium carboxymethylcelluloses, 6 parts of hydroxyethyl celluloses, 5 parts of rosin, 6 parts of glycerine,
10 parts of lime stones.
Embodiment 2
The described a kind of mixing feldspar material of the embodiment of the present invention 2, by the polished firing of the component of following number
Form：150 parts of mullite powders, 60 parts of quartz powders, 85 parts of calcite in powder, 45 parts of olive mountain flours, 55 parts of Giallo Cecilia stone material powder, 8
Part diatom ooze, 5 parts of dimethyl silicone polymers, 10 parts of sodium carboxymethylcelluloses, 8 parts of hydroxyethyl celluloses, 8 parts of rosin, 8 parts sweet
Oil, 12 parts of lime stones.
Above-described embodiment is only some preferred embodiments of the present invention, is not limited the scope of the invention according to this, therefore：
All various equivalence changes done according to the principle of the present invention etc., are covered by the protection scope of the present invention.
Claims (3)
1. one kind mixing feldspar material, it is characterised in that formed by the polished firing of the component of following number：100-150
Part mullite powder, 50-60 parts of quartz powders, 80-85 parts of calcite in powder, 30-45 parts of olive mountain flours, 50-55 parts of Giallo Cecilia stone materials
Powder, 5-8 parts of diatom oozes, 3-5 parts of dimethyl silicone polymers, 8-10 parts of sodium carboxymethylcelluloses, 6-8 parts of hydroxyethyl celluloses, 5-8
Part rosin, 6-8 parts of glycerine, 10-12 parts of lime stones.
2. a kind of mixing feldspar material according to claim 1, it is characterised in that the component by following number is ground
Fire and form afterwards：100 parts of mullite powders, 50 parts of quartz powders, 80 parts of calcite in powder, 30 parts of olive mountain flours, 50 parts of Giallo Cecilia stones
Material powder, 5 parts of diatom oozes, 3 parts of dimethyl silicone polymers, 8 parts of sodium carboxymethylcelluloses, 6 parts of hydroxyethyl celluloses, 5 parts of rosin, 6
Part glycerine, 10 parts of lime stones.
3. a kind of mixing feldspar material according to claim 1, it is characterised in that the component by following number is ground
Fire and form afterwards：150 parts of mullite powders, 60 parts of quartz powders, 85 parts of calcite in powder, 45 parts of olive mountain flours, 55 parts of Giallo Cecilia stones
Material powder, 8 parts of diatom oozes, 5 parts of dimethyl silicone polymers, 10 parts of sodium carboxymethylcelluloses, 8 parts of hydroxyethyl celluloses, 8 parts of rosin, 8
Part glycerine, 12 parts of lime stones.