CN105734980A - Anti-wrinkle, anti-microbial and odor-resistant finishing agent for baffeta and preparation method thereof - Google Patents
Anti-wrinkle, anti-microbial and odor-resistant finishing agent for baffeta and preparation method thereof Download PDFInfo
- Publication number
- CN105734980A CN105734980A CN201610102042.5A CN201610102042A CN105734980A CN 105734980 A CN105734980 A CN 105734980A CN 201610102042 A CN201610102042 A CN 201610102042A CN 105734980 A CN105734980 A CN 105734980A
- Authority
- CN
- China
- Prior art keywords
- finishing agent
- parts
- bafta
- bacterial
- modified polyorganosiloxane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an anti-wrinkle, anti-microbial and odor-resistant finishing agent for baffeta. The finishing agent is prepared from, by weight, 60-80 parts of modified polysiloxane, 5-9 parts of surfactant, 8-12 parts of sodium oleate, 2-5 parts of thickener and 5-20 parts of water. The invention further discloses a preparation method of the finishing agent. According to the finishing agent, modified polysiloxane is used as a main functional ingredient, the anti-wrinkle effect is good, and meanwhile the finishing agent has an inhibiting effect on multiple bacteria and has strong anti-microbial and odor-resistant functions. The finishing agent can be powerfully connected with cotton fibers and can still maintain strong anti-wrinkle, anti-microbial and odor-resistant properties after being washed multiple times and abraded after being worn for a long time.
Description
Technical field:
The present invention relates to textile auxiliary field, particularly relate to the creasing anti-bacterial deodorant of a kind of bafta
Finishing agent and preparation method thereof.
Background technology:
It is along with improving constantly of people's living standard, more and more higher to the quality requirements of the articles for daily use,
The especially requirement to textile quality.Do not require nothing more than textile and there is higher aesthetics, the most right
In textile, healthy impact also had more concern.Bafta, due to its soft comfortable, comes
Source is natural, is constantly subjected to the favor of people.But the fiber of cotton thing processed is the most soft, in wearing process
Easily produce fold impact attractive in appearance, also make troubles to operational maintenance.And bafta easily causes carefully
Bacterium grows, and healthy to people threatens.
By carrying out crease-resistant to bafta, antimicrobial treatment is to improve the effective means of pure cotton fabric quality.
The crease-shedding finishing agent being made up of Lauxite and formaldehyde is relatively common anti-crease finishing way, but knits
Thing is Diazolidinyl Urea after using this finishing agent, greatly threatens the healthy of the mankind even to cause body
Body canceration.So the research about the crease-shedding finishing agent of formaldehydeless green health receives substantial amounts of pass
Note.Crease-shedding finishing agent also can play other useful healths while having the wrinkle resistance of brilliance simultaneously
Healthy effect, thus save the energy, improving production efficiency is also current popular research direction.
Chinese patent CN201510097071.2 discloses a kind of creasing anti-bacterial finishing agent and preparation side thereof
Method, purposes, finishing agent include Azelaic Acid, disodium hydrogen phosphate, carboxymethyl chitosan, hydroxy propyl-Beta-
Cyclodextrin, Fructus Perillae Frutescentis ethyl acetate extract, Rhizoma Kaempferiae ethanol extraction, polyglycerol monooleate and water；
Preparation method is such as: (1) prepares Fructus Perillae Frutescentis ethyl acetate extract；(2) Rhizoma Kaempferiae ethanol extraction is prepared；
(3) taking above-mentioned each composition the most respectively and carry out mix and blend, shear treatment, after shearing
Creasing anti-bacterial finishing agent for preparation.It is strong, suitable that the finishing agent of preparation has the good bacteriostasis property of anti-wrinkle effect
By the wide advantage of scope.But this creasing anti-bacterial finishing agent does not significantly improve with the adhesion of fiber,
The problem that after causing repeatedly washing, creasing anti-bacterial effect declines.
Summary of the invention:
It is an object of the invention to provide the creasing anti-bacterial deodorant finishing agent of a kind of bafta, this finishing agent
Utilizing modified polysiloxanes is main function composition, and anti-wrinkle effect is good, simultaneously to various bacteria
There is inhibitory action, there is stronger anti-bacterial anti-foul function.This inorganic agent can have stronger with cotton fiber
Attachment force, remains to keep stronger creasing anti-bacterial to prevent after repeatedly washing and long-time dress friction
Smelly performance.
It is a further object of the present invention to provide the preparation method of this creasing anti-bacterial deodorant finishing agent.
For achieving the above object, the present invention is by the following technical solutions:
A kind of creasing anti-bacterial deodorant finishing agent of bafta, in parts by weight, including following components:
Modified polyorganosiloxane 60-80 part, surfactant 5-9 part, enuatrol 8-12 part, thickening agent 2-5
Part, water 5-20 part.
A kind of creasing anti-bacterial deodorant finishing agent of bafta, in parts by weight, including following components:
Modified polyorganosiloxane 70-75 part, surfactant 6-8 part, enuatrol 9-10 part, thickening agent 3-4
Part, water 5-10 part.
Preferably, described modified polyorganosiloxane is quaternary ammonium salt and the mixed and modified polysiloxanes of ethoxy,
And after reacting with Polyethylene Glycol, the modified polyorganosiloxane prepared after removing Polyethylene Glycol.
Preferably, in described modified polyorganosiloxane, the mol ratio of quaternary ammonium salt and ethoxy is 1:2.
Preferably, described surfactant is dodecylbenzene sodium sulfonate, Cortex cocois radicis oleoyl monoethanolamine,
One or more in dodecyl dihydroxy ethyl glycine betaine or dodecanamide propyl decil lactone are mixed
Compound.
Preferably, described thickening agent is methyl hydroxyethylcellulose, ethylhydroxyethylcellulose or hydroxyl second
One or more mixture in base cellulose.
The preparation method of the creasing anti-bacterial deodorant finishing agent of a kind of bafta, it is characterised in that comprise
Following steps:
(1) modified polyorganosiloxane is added to the water with surfactant, control temperature at 60-80 DEG C,
High-speed stirred, prepares the emulsion of mix homogeneously；
(2) emulsion prepared in above-mentioned steps adds enuatrol and thickening agent, reduce mixture temperature
Degree, controls temperature at 0-5 DEG C, puts into high-speed grinder, be fully ground, mixture is risen to room
Temperature, prepares required creasing anti-bacterial deodorant finishing agent.
The invention have the advantages that, employing modified polyorganosiloxane is main body, modified poly-silica
Alkane can form network structure at fabric face, forms one layer of homogeneous thin film permissible with bafta
Combining well, resistance to water performance is strong.This modified polyorganosiloxane can rise at surface of cotton fabric
To good anti-folding, quaternary ammonium salt may also operate as good antibacterial deodourizing effect simultaneously.Cotton is knitted
Thing uses this finishing agent can simultaneously work as the crease-resistant and effect of antibacterial deodourizing, decreases bafta whole
The handling process of reason, can improve the quality of bafta.Meanwhile, this creasing anti-bacterial deodorant is used to arrange
After agent, bafta still can keep preferable flexibility, and the most stiff, feel is good.
Detailed description of the invention:
In order to be better understood from the present invention, below by embodiment, the present invention is further described, implements
Example is served only for explaining the present invention, and the present invention will not constitute any restriction.
Embodiment 1
Modified polyorganosiloxane 60 parts, 9 parts of surfactant, enuatrol 12 parts, thickening agent 5 parts,
14 parts of water.
Being added to the water with surfactant by modified polyorganosiloxane, control temperature is at 60-80 DEG C, at a high speed
Stirring, prepares the emulsion of mix homogeneously；In prepared emulsion, add enuatrol and thickening agent, reduce
Mixture temperature, controls temperature at 0-5 DEG C, puts into high-speed grinder, be fully ground, will mixing
Thing is warmed to room temperature, and prepares required creasing anti-bacterial deodorant finishing agent.
This creasing anti-bacterial deodorant finishing agent, can play good crease-resistant effect, can suppress thin simultaneously
Bacterium, plays the effect of deodorant.
Embodiment 2
Modified polyorganosiloxane 62 parts, 7 parts of surfactant, enuatrol 11.5 parts, thickening agent 3.5
Part, 16 parts of water.
Being added to the water with surfactant by modified polyorganosiloxane, control temperature is at 60-80 DEG C, at a high speed
Stirring, prepares the emulsion of mix homogeneously；In prepared emulsion, add enuatrol and thickening agent, reduce
Mixture temperature, controls temperature at 0-5 DEG C, puts into high-speed grinder, be fully ground, will mixing
Thing is warmed to room temperature, and prepares required creasing anti-bacterial deodorant finishing agent.
This creasing anti-bacterial deodorant finishing agent, can play good crease-resistant effect, can suppress thin simultaneously
Bacterium, plays the effect of deodorant.
Embodiment 3
Modified polyorganosiloxane 65 parts, 6 parts of surfactant, enuatrol 11 parts, thickening agent 4 parts,
14 parts of water.
Being added to the water with surfactant by modified polyorganosiloxane, control temperature is at 60-80 DEG C, at a high speed
Stirring, prepares the emulsion of mix homogeneously；In prepared emulsion, add enuatrol and thickening agent, reduce
Mixture temperature, controls temperature at 0-5 DEG C, puts into high-speed grinder, be fully ground, will mixing
Thing is warmed to room temperature, and prepares required creasing anti-bacterial deodorant finishing agent.
This creasing anti-bacterial deodorant finishing agent, can play good crease-resistant effect, can suppress thin simultaneously
Bacterium, plays the effect of deodorant.
Embodiment 4
Modified polyorganosiloxane 67 parts, 8 parts of surfactant, enuatrol 10.5 parts, thickening agent 4.5
Part, 10 parts of water.
Being added to the water with surfactant by modified polyorganosiloxane, control temperature is at 60-80 DEG C, at a high speed
Stirring, prepares the emulsion of mix homogeneously；In prepared emulsion, add enuatrol and thickening agent, reduce
Mixture temperature, controls temperature at 0-5 DEG C, puts into high-speed grinder, be fully ground, will mixing
Thing is warmed to room temperature, and prepares required creasing anti-bacterial deodorant finishing agent.
This creasing anti-bacterial deodorant finishing agent, can play good crease-resistant effect, can suppress thin simultaneously
Bacterium, plays the effect of deodorant.
Embodiment 5
Modified polyorganosiloxane 70 parts, 7 parts of surfactant, enuatrol 10 parts, thickening agent 4 parts,
9 parts of water.
Being added to the water with surfactant by modified polyorganosiloxane, control temperature is at 60-80 DEG C, at a high speed
Stirring, prepares the emulsion of mix homogeneously；In prepared emulsion, add enuatrol and thickening agent, reduce
Mixture temperature, controls temperature at 0-5 DEG C, puts into high-speed grinder, be fully ground, will mixing
Thing is warmed to room temperature, and prepares required creasing anti-bacterial deodorant finishing agent.
This creasing anti-bacterial deodorant finishing agent, can play good crease-resistant effect, can suppress thin simultaneously
Bacterium, plays the effect of deodorant.
Embodiment 6
Modified polyorganosiloxane 73 parts, 6 parts of surfactant, enuatrol 9.5 parts, thickening agent 3.5
Part, 8 parts of water.
Being added to the water with surfactant by modified polyorganosiloxane, control temperature is at 60-80 DEG C, at a high speed
Stirring, prepares the emulsion of mix homogeneously；In prepared emulsion, add enuatrol and thickening agent, reduce
Mixture temperature, controls temperature at 0-5 DEG C, puts into high-speed grinder, be fully ground, will mixing
Thing is warmed to room temperature, and prepares required creasing anti-bacterial deodorant finishing agent.
This creasing anti-bacterial deodorant finishing agent, can play good crease-resistant effect, can suppress thin simultaneously
Bacterium, plays the effect of deodorant.
Embodiment 7
Modified polyorganosiloxane 75 parts, 8 parts of surfactant, enuatrol 9 parts, thickening agent 3 parts, water
5 parts.
Being added to the water with surfactant by modified polyorganosiloxane, control temperature is at 60-80 DEG C, at a high speed
Stirring, prepares the emulsion of mix homogeneously；In prepared emulsion, add enuatrol and thickening agent, reduce
Mixture temperature, controls temperature at 0-5 DEG C, puts into high-speed grinder, be fully ground, will mixing
Thing is warmed to room temperature, and prepares required creasing anti-bacterial deodorant finishing agent.
This creasing anti-bacterial deodorant finishing agent, can play good crease-resistant effect, can suppress thin simultaneously
Bacterium, plays the effect of deodorant.
Embodiment 8
Modified polyorganosiloxane 78 parts, 6 parts of surfactant, enuatrol 8.5 parts, thickening agent 2.5
Part, 5 parts of water.
Being added to the water with surfactant by modified polyorganosiloxane, control temperature is at 60-80 DEG C, at a high speed
Stirring, prepares the emulsion of mix homogeneously；In prepared emulsion, add enuatrol and thickening agent, reduce
Mixture temperature, controls temperature at 0-5 DEG C, puts into high-speed grinder, be fully ground, will mixing
Thing is warmed to room temperature, and prepares required creasing anti-bacterial deodorant finishing agent.
This creasing anti-bacterial deodorant finishing agent, can play good crease-resistant effect, can suppress thin simultaneously
Bacterium, plays the effect of deodorant.
Embodiment 9
Modified polyorganosiloxane 80 parts, 5 parts of surfactant, enuatrol 8 parts, thickening agent 2 parts, water
5 parts.
Being added to the water with surfactant by modified polyorganosiloxane, control temperature is at 60-80 DEG C, at a high speed
Stirring, prepares the emulsion of mix homogeneously；In prepared emulsion, add enuatrol and thickening agent, reduce
Mixture temperature, controls temperature at 0-5 DEG C, puts into high-speed grinder, be fully ground, will mixing
Thing is warmed to room temperature, and prepares required creasing anti-bacterial deodorant finishing agent.
This creasing anti-bacterial deodorant finishing agent, can play good crease-resistant effect, can suppress thin simultaneously
Bacterium, plays the effect of deodorant.
Claims (7)
1. the creasing anti-bacterial deodorant finishing agent of a bafta, it is characterised in that in parts by weight,
Including following components: modified polyorganosiloxane 60-80 part, surfactant 5-9 part, enuatrol 8-12
Part, thickening agent 2-5 part, water 5-20 part.
2. the creasing anti-bacterial deodorant finishing agent of a bafta, it is characterised in that in parts by weight,
Including following components: modified polyorganosiloxane 70-75 part, surfactant 6-8 part, enuatrol 9-10
Part, thickening agent 3-4 part, water 5-10 part.
The creasing anti-bacterial deodorant finishing agent of bafta the most according to claim 1 and 2, it is special
Levying and be, described modified polyorganosiloxane is quaternary ammonium salt and the mixed and modified polysiloxanes of ethoxy, and with
After Polyethylene Glycol reaction, remove the modified polyorganosiloxane that Polyethylene Glycol prepares.
The creasing anti-bacterial deodorant finishing agent of bafta the most according to claim 1 and 2, it is special
Levying and be, in described modified polyorganosiloxane, quaternary ammonium salt is 1:2 with the mol ratio of ethoxy.
The creasing anti-bacterial deodorant finishing agent of bafta the most according to claim 1 and 2, it is special
Levying and be, described surfactant is dodecylbenzene sodium sulfonate, Cortex cocois radicis oleoyl monoethanolamine, 12
One or more mixing in alkyldihydxyethyl betaines or dodecanamide propyl decil lactone
Thing.
The creasing anti-bacterial deodorant finishing agent of bafta the most according to claim 1 and 2, it is special
Levying and be, described thickening agent is methyl hydroxyethylcellulose, and ethylhydroxyethylcellulose or ethoxy are fine
One or more mixture in dimension element.
7. the preparation method of the creasing anti-bacterial deodorant finishing agent of a bafta, it is characterised in that bag
Containing following steps:
(1) described modified polyorganosiloxane is added to the water with surfactant, controls temperature and exist
60-80 DEG C, high-speed stirred, prepare the emulsion of mix homogeneously；
(2) emulsion prepared in above-mentioned steps adds enuatrol and thickening agent, reduce mixture temperature
Degree, controls temperature at 0-5 DEG C, puts into high-speed grinder, be fully ground, be warmed to room temperature by mixture,
Prepare required creasing anti-bacterial deodorant finishing agent.