CN105734776A - Machine knitted fabric with transparent appearance, and applications thereof - Google Patents
Machine knitted fabric with transparent appearance, and applications thereof Download PDFInfo
- Publication number
- CN105734776A CN105734776A CN201410760131.XA CN201410760131A CN105734776A CN 105734776 A CN105734776 A CN 105734776A CN 201410760131 A CN201410760131 A CN 201410760131A CN 105734776 A CN105734776 A CN 105734776A
- Authority
- CN
- China
- Prior art keywords
- fabric
- fiber
- transparent
- nylon
- woven fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a machine knitted fabric with transparent appearance, and applications thereof. The machine knitted fabric is prepared from transparent nylon fiber and an another fiber at a ratio of 1.5-1.8; the another fiber is one or a mixture of ingredients selected from viscose, cationic-dyeable polyester, cotton, and wool. The appearance of the machine knitted fabric is unique; surface transparency is excellent; handfeel is soft; wearability is excellent; and the machine knitted fabric is especially suitable to be used for preparing summer clothes of women.
Description
Technical field
The present invention relates to a kind of garment material, be specifically related to a kind of woven fabric with transparent appearance.
Background technology
Summer, dress shell fabric both required the dressing with comfortable ventilating, more require the outward appearance with unique fashion.Dress shell fabric in summer in the market, it does not have salient feature, novelty and stylishness are not strong, it is impossible to meet the market demand.A kind of there is transparent appearance effect in the urgent need to developing, summer women can be simulated like the husky sugar candy eaten to savor cold drink outward appearance；And after visual, can produce to eat the fabric of the cooling feeling of Sha Bing by Stimulation of The Brain nerve.
The fabric with transparent appearance released on market, great majority are to be formed by two shell fabric simple superposition sewings, such as top layer adopts the fabric formed by silkworm silk (raw silk), nexine adopts by fibroplastic fabric beautiful in colour, prepares fabric then through sewing, although such fabric surface is provided with transparent effect, but need to be sewed together two-layer, add production cost, and silkworm silk series products can not be machine-washed, and not easily arranges.Somebody proposes to adopt double-layered structure to obtain folded effect thoroughly in conjunction with specific yarn, a kind of double-layer jacquard stamp man textile fabric with folded effect disclosed in such as patent documentation CN201110101770.1, the white polyester of triangular cross-section or nylon monofilament are arranged in fabric top layer, white yarn or colored yarns are arranged in fabric nexine, obtain the thoroughly folded effect shrouded just as tulle, but such fabric transparent feel is not enough；And fabric employs monofilament, feel is partially hard, more abundant again, is not suitable for making summer clothes.
Additionally, existing dress shell fabric is much the mixed fabric of nylon, a kind of artificial silk hollow check pattern plus material disclosed in such as patent documentation CN201110153167.8, adopts double layer hollow structure, and Reasonable is equipped with light nylon, artificial silk and terylene, gained fabric has had the moisture pick-up properties that artificial silk is good concurrently, nylon and well-pressed, the slim and graceful quality of polyster fibre, bright color, is good women's dress fabric, but this web surface does not have transparent effect, novelty is not enough.
Summary of the invention
It is an object of the invention to overcome the deficiencies in the prior art, it is provided that the woven fabric with transparent appearance effect that a kind of with low cost and snugness of fit is good.This fabric is particularly suitable for making woman style summer clothes.
The technical solution of the present invention is:
The woven fabric with transparent appearance of the present invention, by nylon fiber and other processbearing astrocyte, wherein nylon fiber is transparent nylon fibre, other fiber is one or more of in viscose glue, the CDP fabrics, cotton and Pilus Caprae seu Ovis, and the ratio of the fiber number of the fiber number of nylon fiber/other fiber is 1.5～1.8.
The woven fabric with transparent appearance of the present invention, by the reasonable disposition of yarn and optimization technique, gives outward appearance and the soft feel of this fabric novelty fashion, particularly when wearing summer, easily make people associate husky sugar candy product, have cool feeling after visual, define the visual effect of a kind of uniqueness.Meanwhile, by internal layer yarn contaminates different colors, simulate various fruit sand ice, increase mood when women wears and experience.And, use single-layer fabric or double-layered structure's fabric just to reach the effect of two shell fabrics, save sewing expense, reduce production cost.
Detailed description of the invention
The woven fabric with transparent appearance of the present invention, by nylon fiber and other processbearing astrocyte, wherein nylon fiber is transparent nylon fibre, and other fiber is one or more of in viscose glue, the CDP fabrics, cotton and Pilus Caprae seu Ovis；And the ratio of the fiber number of the fiber number of nylon fiber/other fiber is 1.5～1.8.If ratio is less than 1.5, the nylon fiber of web surface is difficult to cover the fiber of the inside, and transparent feel is not enough；And ratio is more than 1.8, the space between the nylon fiber of web surface is excessive, degree of comfort decreased.When other fiber has multiple, calculate the ratio relation of the fiber number of nylon fiber and the fiber number sum of other fiber.
Why using nylon fiber as one of the fibrous raw material of the present invention mainly it is considered that all comparative superiorities such as the intensity of nylon fiber, wearability, hygroscopicity, be suitable for fabric in summer.In the present invention, nylon fiber used is transparent nylon fibre, by nylon chips without or obtain then through spinning after adding minimal amount of TITANIUM DIOXIDE DELUSTRANT particle.The content of titanium dioxide is preferably 0～0.50%, and within the scope of this, the transparent feel of fabric is good.If content of titanium dioxide is more than 0.50% in transparent nylon fibre, the transparent feel of fabric face can be affected.
In the present invention, other fibers used are one or more of in viscose glue, the CDP fabrics, cotton and Pilus Caprae seu Ovis.Wherein viscose glue belongs to regenerated celulose fibre, has the features such as smooth nice and cool, good skin-friendly and hygroscopicity；The CDP fabrics belongs to modified dacron, can obtain colourful color by simple dyeing, have the features such as good hygroscopicity；And both fiber cost are relatively low, therefore as preferably.In the present invention, the grammes per square metre of the fabric that other fibers employing viscose glue or the CDP fabrics are formed is preferably 100g/m2Below.
The preferred long filament of transparent nylon fibre form used by the present invention in the present invention, it is contemplated that the stability of volume production, its Denier range is preferably 60～180 daniers (D).
In transparent nylon fibre used by the present invention, the present invention other fibre morphologies used are not particularly limited, it is possible to be long filament, it is also possible to be chopped fiber.
The tissue of the woven fabric of the present invention is preferably satin weave, satin weave alternative construction or double-layered structure.These tissues can so that transparent nylon yarn is as far as possible many occurs in web surface, thus obtaining good transparent effect.
Wherein, warp (or parallel) flotation line of satin weave and alternative construction thereof is longer, and intertwined point is less, and the independent interlacing point spacing on adjacent two warp thread is farther out.Little through the number of times interweaved up and down of weft yarn, between two adjacent latitude interlacing points of a warp thread, warp thread floats over above several weft yarns continuously, thus have longer warp thread to cover web surface, and gained fabric texture is soft, and surface smooths neat and well spaced, is rich in gloss.In the present invention, warp thread uses transparent nylon fibre, and weft yarn uses other fibers above-mentioned, and gained fabric not only transparent appearance is good, and quality is light.
Double-layered structure by table, inner two systems warp thread respectively with the weft yarns of table, inner two systems, structurally form the fabric tissue of upper and lower two superimposed.Upper strata constitutes fabric upper layer through weft yarn, claims table organization；Nexine constitutes fabric lower floor through weft yarn, organizes in title.In connection table, two-layer fabrics claims access node.Tying method adopts self access node method.All using transparent nylon fibre by upper strata through weft yarn, nexine warp thread and connecting filament in the present invention, nexine weft yarn uses other fibers above-mentioned, it is possible in fabric, surface maximum covers transparent nylon fibre, and gained fabric transparent appearance is effective.
When the woven fabric of the present invention adopts satin weave or double-layered structure, the twist of nylon fiber used is 350～1600T/M.The twist is relevant with the contraction situation of yarn and lustrous surface.If the twist is lower than 350T/M, yarn shrinkage is only small, web surface undershrinking, and transparent feel reduces；And the twist is higher than 1600T/M, the twist is too high, and yarn shrinkage is very big, but lustrous surface sense weakens, and transparent style weakens.
The woven fabric of the present invention, it is preferable that warp-wise density is 117～182/inch, latitudinal density is 80～132/inch.Thread count is too low, and transparent feel is not enough；Thread count is too high, and fabric is blocked up, affects the frivolous sense of fabric.
The woven fabric of the present invention can be used for blouse in summer, T-shirt or the skirt etc. that make.
Embodiment
Physical property involved in the present invention is measured by following methods.
1. transparent feel
This fabric please being carried out 15 people ocular estimate, assessment item is transparent feel.More than 10 people, think that when evaluation fabric has transparent feel, ocular estimate is as well.When 7-9 people thinks that evaluation fabric has transparent feel, hand valuation result is better.When 4-6 people thinks that evaluation fabric has transparent feel, hand valuation result is general.When 0-3 people thinks that evaluation fabric has transparent feel, hand valuation result is for poor.
2. feel
This fabric please being carried out 15 people hand valuation, assessment item is comfort.More than 10 people, think that when evaluation fabric has comfort, hand valuation is as well.When 7-9 people thinks that evaluation fabric has comfort, hand valuation result is better.When 4-6 people thinks that evaluation fabric has comfort, hand valuation result is general.When 0-3 people thinks that evaluation fabric has comfort, hand valuation result is for poor.
By the examples below and comparative example the invention will be further described.
Embodiment 1
75D-34f-transparent nylon FDY selected by warp thread, weft yarn is 50D-24f-viscose glue FDY, after adopting satin weave weaving to obtain grey cloth, carry out that 95 degree concise, sizing in the middle of 180 degree, dyeing (adopt reactive dye list dye viscose glue, 70 degree * 50 minutes), water suction supple resin processing, arrange the woven fabric of the prepared present invention of sizing.
Wherein the ratio of the fiber number of the fiber number/viscose glue of nylon is 1.5, in transparent nylon FDY the content of titanium dioxide be 0, its twist be 350T/M；Warp-wise density is 182/inch, latitudinal density is 132/inch, and fabric grammes per square metre is 85g/m3.Concrete as shown in table 1.
Embodiment 2
90D-68f-transparent nylon FDY selected by warp thread, weft yarn is 50D-24f-the CDP fabrics FDY, after adopting satin weave weaving to obtain grey cloth, carry out that 95 degree concise, sizing in the middle of 180 degree, dyeing (adopt dye of positive ion list dye the CDP fabrics, 120 degree * 30 minutes), water suction supple resin processing, arrange the woven fabric of the prepared present invention of sizing.
Wherein the ratio of the fiber number of the fiber number/the CDP fabrics of nylon is 1.8, in transparent nylon FDY content of titanium dioxide be 0.10%, its twist be 1600T/M；Warp-wise density is 166/inch, latitudinal density is 110/inch, and grammes per square metre is 88g/m3.Concrete as shown in table 1.
Embodiment 3
150D-68f-transparent nylon FDY selected by warp thread, weft yarn is 60S cotton yarn, after adopting satin weave weaving to obtain grey cloth, carry out that 95 degree concise, sizing in the middle of 180 degree, dyeing (adopt reactive dye list dye cotton yarn, 90 degree * 50 minutes), supple resin processing, arrange the woven fabric of the prepared present invention of sizing.
Wherein the ratio of the fiber number of the fiber number/cotton of nylon is 1.7, in transparent nylon FDY content of titanium dioxide be 0.50%, its twist be 800T/M；Warp-wise density is 129/inch, latitudinal density is 83/inch, and grammes per square metre is 150g/m3.Concrete as shown in table 1.
Embodiment 4
160D-68f-transparent nylon FDY selected by warp thread, weft yarn is 55S Pilus Caprae seu Ovis, after adopting satin weave weaving to obtain grey cloth, carry out that 95 degree concise, sizing in the middle of 180 degree, dyeing (adopt reactive dye list dyeing wool, 98 degree * 50 minutes), felt proofing process of resin, arrange the woven fabric of the prepared present invention of sizing.
Wherein the ratio of the fiber number of the fiber number/cotton of nylon is 1.6, in transparent nylon FDY content of titanium dioxide be 0.30%, its twist be 1200T/M；Warp-wise density is 117/inch, latitudinal density is 83/inch, and grammes per square metre is 180g/m3.Concrete as shown in table 1.
Embodiment 5
75D-68f-transparent nylon FDY selected by warp thread, weft yarn 1 is 50D-24f-viscose glue FDY, weft yarn 2 is 110S cotton yarn, weft yarn assortment 1:1, after adopting satin weave weaving to obtain grey cloth, carry out that 95 degree concise, sizing in the middle of 180 degree, dyeing (adopt dye viscose glue and cotton yarn on reactive dye, 90 degree * 50 minutes), supple resin processing, arrange the woven fabric of the prepared present invention of sizing.
Wherein the ratio of the fiber number of the fiber number of nylon/(viscose glue+cotton) is 1.5, in transparent nylon FDY content of titanium dioxide be 0.05%, its twist be 900T/M；Warp-wise density is 175/inch, latitudinal density is 120/inch, and grammes per square metre is 99g/m3.Concrete as shown in table 1.
Embodiment 6
Top line, upper layer weft yarns, nexine warp thread and connecting filament all use 75D-68f-transparent nylon FDY, lower floor's weft yarn uses 50D-24f-viscose glue FDY, after adopting double-layered structure's weaving to obtain grey cloth, carry out that 95 degree concise, sizing in the middle of 180 degree, dyeing (adopt reactive dye list dye viscose glue, 70 degree * 50 minutes), water suction supple resin processing, arrange the woven fabric of the prepared present invention of sizing.
Wherein the ratio of the fiber number of the fiber number/viscose glue of nylon is 1.5, in transparent nylon FDY content of titanium dioxide be 0.02%, its twist be 600T/M；Warp-wise density is 180/inch, latitudinal density is 132/inch, and grammes per square metre is 195g/m3.Concrete as shown in table 1.
Embodiment 7
90D-68f-transparent nylon FDY selected by warp thread, 90D-68f-transparent nylon FDY selected by weft yarn 1,50D-24f-the CDP fabrics FDY selected by weft yarn 2, weft yarn assortment 1:1, after adopting filling-backed weave weaving to obtain grey cloth, carry out that 95 degree concise, sizing in the middle of 180 degree, dyeing (adopt dye of positive ion list dye the CDP fabrics, 120 degree * 30 minutes), water suction supple resin processing, arrange the prepared finished product of sizing.
Wherein the ratio of the fiber number of the fiber number/the CDP fabrics of nylon is 1.8, in transparent nylon yarn content of titanium dioxide be 0.10%, its twist be 1600T/M；Warp-wise density is 125/inch, latitudinal density is 110/inch, and grammes per square metre is 92g/m3.Concrete as shown in table 1.
Embodiment 8
160D-68f-transparent nylon FDY selected by warp thread, weft yarn is 55S Pilus Caprae seu Ovis, after adopting satin weave weaving to obtain grey cloth, carry out that 95 degree concise, sizing in the middle of 180 degree, dyeing (adopt reactive dye list dyeing wool, 98 degree * 50 minutes), felt proofing process of resin, arrange the woven fabric of the prepared present invention of sizing.
Wherein the ratio of the fiber number of the fiber number/viscose glue of nylon is 1.6, in transparent nylon yarn content of titanium dioxide be 0.03%, its twist be 1800T/M；Warp-wise density is 120/inch, latitudinal density is 83/inch, and grammes per square metre is 165g/m3.Concrete as shown in table 1.
Embodiment 9
160D-68f-transparent nylon FDY selected by warp thread, weft yarn is 55S Pilus Caprae seu Ovis, after adopting satin weave weaving to obtain grey cloth, carry out that 95 degree concise, sizing in the middle of 180 degree, dyeing (adopt reactive dye list dyeing wool, 98 degree * 50 minutes), felt proofing process of resin, arrange the woven fabric of the prepared present invention of sizing.
Wherein the ratio of the fiber number of the fiber number/viscose glue of nylon is 1.6, in transparent nylon yarn content of titanium dioxide be 0.04%, its twist be 100T/M.Warp-wise density is 117/inch, latitudinal density is 80/inch, and grammes per square metre is 152g/m3.Concrete as shown in table 1.
Adopt blouse in summer, T-shirt or skirt that embodiment 1-9 prepares.
Comparative example 1
90D-68f-transparent nylon FDY selected by warp thread, and 75D-24f-viscose glue FDY selected by weft yarn, and the ratio of the fiber number of the fiber number/viscose glue of nylon is 1.2；Warp-wise density is 165/inch, latitudinal density is 100/inch, and grammes per square metre is 95g/m3, all the other are with embodiment 1, specifically as shown in table 2.
Comparative example 2
160D-68f-transparent nylon FDY selected by warp thread, and 65S Pilus Caprae seu Ovis selected by weft yarn, and the ratio of the fiber number of the fiber number/Pilus Caprae seu Ovis of nylon is 2.0, and warp-wise density is 118/inch, latitudinal density is 81/inch, and grammes per square metre is 175g/m3, all the other are with embodiment 4, specifically as shown in table 2.
Claims (7)
1. a woven fabric with transparent appearance, it is characterized in that: this woven fabric is by nylon fiber and other processbearing astrocyte, wherein said nylon fiber is transparent nylon fibre, other fiber described is one or more of in viscose glue, the CDP fabrics, cotton and Pilus Caprae seu Ovis, and the ratio of the fiber number of the fiber number of described nylon fiber/other fiber described is 1.5～1.8.
2. the woven fabric with transparent appearance according to claim 1, is characterized in that: in described nylon fiber, the content of titanium dioxide is 0～0.50%.
3. the woven fabric with transparent appearance according to claim 1, is characterized in that: other fiber described is viscose glue or the CDP fabrics, and the grammes per square metre of this fabric is 100g/m2Below.
4. the woven fabric with transparent appearance according to any one of claims 1 to 3, is characterized in that: this fabric be organized as satin weave or double-layered structure.
5. the woven fabric with transparent appearance according to claim 4, is characterized in that: this fabric be organized as satin weave, the twist of described nylon fiber is 350～1600T/M.
6. the woven fabric with transparent appearance according to claim 4, is characterized in that: the warp-wise density of this fabric is 117～182/inch, and latitudinal density is 80～132/inch.
7. blouse in summer, T-shirt or the skirt that the woven fabric with transparent appearance adopted described in claim 1 prepares.