CN105734768A - Woven nylon anti-stitch slipping sportswear fabric and weaving method thereof - Google Patents
Woven nylon anti-stitch slipping sportswear fabric and weaving method thereof Download PDFInfo
- Publication number
- CN105734768A CN105734768A CN201610230049.5A CN201610230049A CN105734768A CN 105734768 A CN105734768 A CN 105734768A CN 201610230049 A CN201610230049 A CN 201610230049A CN 105734768 A CN105734768 A CN 105734768A
- Authority
- CN
- China
- Prior art keywords
- fabric
- slippage
- warp
- nylon
- sportswear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a woven nylon anti-stitch slipping sportswear fabric. Raw materials used for the fabric are nylon fully-drawn yarns and are formed by weaving, dyeing and after-treatment processing; warp yarns of the nylon fully-drawn yarns are 70D/24F, and weft yarns of the nylon fully-drawn yarns are 200D/48F; the warp density of the anti-stitch slipping fabric is 180 pieces/inch, and the weft density of the anti-stitch slipping fabric 92 pieces/inch; the fabric structure is a two-top two-down left twill; the woven fabric is 120-130 g/m<2>. According to the woven nylon anti-stitch slipping sportswear fabric provided by the invention, through the fabric structure, the warp and weft density design and the after-treatment processing after dyeing, the anti-stitch slipping strength of the fabric is significantly enhanced; the fabric is simple in weaving process; a coating is arranged in the after-treatment processing, so that no additional production cost is increased.
Description
Technical field
The invention belongs to textile material field, particularly relate to a kind of anti-slippage sportswear fabric of woven nylon and method for weaving thereof.
Background technology
When slippage refers to the pulling force effect that sutured fabric is subject to vertical sealing, the yarn in a direction produces sliding, the de-seam presented or breach on the yarn in another direction.Garment material has to pass through quilting process could couple together the clothing becoming real by the garment piece of the different parts cut, and in the wearing process of sportswear particularly autumn and winter series close-fitting sports garment, the position (such as ancon, shoulder, oxter etc.) bearing individually bigger load can produce the sliding of yarn due to stress in suture site, cloth cover produces slippage, not only directly affect the attractive in appearance of clothing, reduce the quality of clothing;Serious meeting causes garment piece to be mutually disengaged, and causes inevitable embarrassment to wearer, and therefore the splitting parameter of fabric is suffered from strict requirement by the especially high-grade sportswear fabric of garment material.
The patent of the anti-slippage fabric announced at present only has Chinese invention patent application number for CN201610011782.8, patent name proposes the method for weaving of a kind of real silk twill-weave with anti-slippage performance for " a kind of anti-slippage frivolous fancy crepe georgette fabric and method for weaving thereof ", is solved the slippage problem of real silk woven fabric by the design of organizational structure.But the current sportswear overwhelming majority adopts chemical fibre, for instance nylon, terylene etc..The performance of chemical fibre and real silk have larger difference, and fancy crepe georgette fabric also cannot meet the requirement of sportswear simultaneously.
Woven nylon fabric in the market can meet the requirement of high-end sportswear fabric in fabric weight, color fastness etc., but slippage intensity always cannot be up to standard.Testing through third party testing agency (Tongbiao Standard Technology Service Co., Ltd, SGS), method of testing adopts " AdidasMethod4.13 ", and the slippage intensity of result display warp-wise and broadwise only has about 80N.Minima 200N from customer requirement also has bigger gap.
Therefore, for above-mentioned technical problem, it is necessary to provide a kind of high-grade anti-slippage sportswear fabric of woven nylon and method for weaving thereof, to overcome drawbacks described above.
Summary of the invention
In view of this, it is an object of the invention to provide a kind of high-grade anti-slippage sportswear fabric of woven nylon and method for weaving thereof, this fabric is the market demand for high-grade sportswear fabric at present, select nylon fiber, select and thread count design through organizational structure, a series of production processes such as dyeing Final finishing processing, process.
For achieving the above object, the present invention provides following technical scheme:
A kind of anti-slippage sportswear fabric of woven nylon, it is characterized in that: described fabric is raw materials used for nylon fully drawn yarn, the warp thread of described nylon fully drawn yarn is 70D/24F, the weft yarn of described nylon fully drawn yarn is 200D/48F, the end count of described anti-slippage fabric is 180 pieces/inch, and the filling density of described anti-slippage fabric is 92 pieces/inch.
Preferably, in the anti-slippage sportswear fabric of above-mentioned woven nylon, described fabric structure is 2 times twills on 2, and the fabric weight weaved is 120~130g/m2。
A kind of woven nylon anti-slippage sportswear face weave method, it is characterised in that: include step:
Select raw material: selecting nylon fully drawn yarn is the raw material of fabric, and wherein warp thread is 70D/24F, and weft yarn is 200D/48F;
Warping: warp thread carries out warping by warp warping machine, yarn is parallel to each other and is wound on warp beam closely, and percentage elongation controls 0.5%~0.8%;
Starching: warp sizing, slurry is mainly the polyacrylate of 3% and the PVA-205 of 2.5%, adds the antistatic additive of 0.2%, the oil emulsion of 0.5%, and the rate of sizing is 3~5%;
Weaving: warp thread sizing well after gait denting according to pegging plan and warp count designing requirement, loom adopts air-jet loom, and fabric structure is 2 times twills on 2, and the fabric weight weaved is 120~130g/m2;
Dry and grey cloth inspection: after drying, length and door width have retraction, and grey cloth verifier vehicle speed is 15m/min;
Cold pad--batch: first by grey cloth at room temperature alkali immerging, then clot on the cloth beam of draw off mechanism, yardage roll plastic sheeting wraps up, it is prevented that cloth cover is air-dry, last yardage roll is at room temperature banked up 72 hours, and period keeps yardage roll to turn round with the speed of 6-8r/min;
Washing: yardage roll good for cold pad--batch is washed 0.5~1 hour in the hot water of 60 DEG C;
Dyeing: middle acid dyeing, first regulate Value in Dyeing Process to 4~6 with acetic acid, and add the levelling agent of 1~2%, start dyeing after dye bath temperature to 40 DEG C, heat up and rise to 80~85 degree with the speed of 1 degree/2 minutes, heat up again after being incubated 15 minutes, after dye bath temperature is increased to 95 DEG C, dye of boiling 70~90 minutes, then lowers the temperature gradually and drops to 40 DEG C with the speed of 1 degree/min, adds 1~color fixing agent of 2% simultaneously;
Dry: dry and carry out in the cylinder group that surface temperature is 80~90 DEG C, 10~25 seconds time that cloth cover is fitted with cylinder;
Thermal finalization: in the tank before forming machine, adds anti-agent 1~3% of becoming unwoven or untiwisted, antistatic additive 0.5%, waterproofing agent 1~2% by proportioning, often shapes 800~1000 meters, quantitatively supplements waterproofing agent, and setting temperature is 130~140 DEG C, and machine rotational speed is 50 yards;
Inspection clot, packaging.
Preferably, in above-mentioned woven nylon anti-slippage sportswear face weave method, the end count of described anti-slippage fabric is 180 pieces/inch.
Preferably, in above-mentioned woven nylon anti-slippage sportswear face weave method, the filling density of described anti-slippage fabric is 92 pieces/inch.
Compared with prior art, the invention has the beneficial effects as follows:
(1) present invention is by the processing of fabric structure and thread count design, dyeing Final finishing, fabric slippage intensity is made to be obviously enhanced, through (Tongbiao Standard Technology Service Co., Ltd of third party testing agency, SGS) test, method of testing adopts " AdidasMethod4.13 ", and the slippage intensity of result display warp-wise and broadwise is all more than 200N;
(2) this face weave technique is simple, does not have coating, it does not have additionally increase production cost in Final finishing processing;
(3) this fabric is except anti-slippage, it is also possible to anti-hook silk, and fabric is slim and graceful, ventilative, and added value of product is high, it is easy to marketing.
Accompanying drawing explanation
Fig. 1 is the flow chart of woven nylon of the present invention anti-slippage sportswear face weave method.
Fig. 2 is the organization chart of the anti-slippage sportswear fabric of woven nylon of the present invention.
Detailed description of the invention
The invention discloses a kind of anti-slippage sportswear fabric of woven nylon and method for weaving thereof, this fabric is the market demand for high-grade sportswear fabric at present, select nylon fiber, select and thread count design through organizational structure, a series of production processes such as dyeing Final finishing processing, process.
As shown in Figure 2, the anti-slippage sportswear fabric of woven nylon disclosed by the invention, its fabric is raw materials used for nylon fully drawn yarn, the warp thread of described nylon fully drawn yarn is 70D/24F, the weft yarn of described nylon fully drawn yarn is 200D/48F, the end count of described anti-slippage fabric is 180 pieces/inch, and the filling density of described anti-slippage fabric is 92 pieces/inch.Described fabric structure is 2 times twills on 2, and the fabric weight weaved is 120~130g/m2。
As it is shown in figure 1, woven nylon disclosed by the invention anti-slippage sportswear face weave method, it includes step:
Select raw material: selecting nylon fully drawn yarn is the raw material of fabric, and wherein warp thread is 70D/24F, and weft yarn is 200D/48F;
Warping: warp thread carries out warping by warp warping machine, yarn is parallel to each other and is wound on warp beam closely, and percentage elongation controls 0.5%~0.8%;
Starching: warp sizing, slurry is mainly the polyacrylate of 3% and the PVA-205 of 2.5%, adds the antistatic additive of 0.2%, the oil emulsion of 0.5%, and the rate of sizing is 3~5%;
Weaving: warp thread sizing well after gait denting according to pegging plan and warp count designing requirement, loom adopts air-jet loom, and fabric structure is 2 times twills on 2, and the fabric weight weaved is 120~130g/m2;
Dry and grey cloth inspection: after drying, length and door width have retraction, are beneficial to the shrinkage problem controlling dyeing and finishing process, are beneficial to raising thread count, and grey cloth verifier vehicle speed is 15m/min;
Cold pad--batch: first by grey cloth at room temperature alkali immerging, then clot on the cloth beam of draw off mechanism, yardage roll plastic sheeting wraps up, it is prevented that cloth cover is air-dry, last yardage roll is at room temperature banked up 72 hours, and period keeps yardage roll to turn round with the speed of 6-8r/min;
Washing: yardage roll good for cold pad--batch is washed 0.5~1 hour in the hot water of 60 DEG C;
Dyeing: middle acid dyeing, first regulate Value in Dyeing Process to 4~6 with acetic acid, and add the levelling agent of 1~2%, start dyeing after dye bath temperature to 40 DEG C, heat up and rise to 80~85 degree with the speed of 1 degree/2 minutes, heat up again after being incubated 15 minutes, after dye bath temperature is increased to 95 DEG C, dye of boiling 70~90 minutes, then lowers the temperature gradually and drops to 40 DEG C with the speed of 1 degree/min, adds 1~color fixing agent of 2% simultaneously;
Dry: dry and carry out in the cylinder group that surface temperature is 80~90 DEG C, 10~25 seconds time that cloth cover is fitted with cylinder, reach the effect of basic drying, purpose has two, one is that the auxiliary agent in the tank before forming machine is easier to absorb by the fabric dried, being conducive to the accuracy of auxiliary agent proportioning, two is the washing shrinkage dried and can efficiently control fabric simultaneously;
Thermal finalization: in the tank before forming machine, adds anti-agent 1~3% of becoming unwoven or untiwisted, antistatic additive 0.5%, waterproofing agent 1~2% by proportioning, often shapes 800~1000 meters, quantitatively supplements waterproofing agent, and setting temperature is 130~140 DEG C, and machine rotational speed is 50 yards;
Inspection clot, packaging.
The end count of described anti-slippage fabric is 180 pieces/inch of filling densities is 92 pieces/inch.
Below in conjunction with detailed description of the invention, it is further elucidated with the present invention.
Embodiment 1:
A kind of high-grade anti-slippage sportswear fabric of woven nylon is to adopt nylon fully drawn yarn, processes through woven, dyeing, Final finishing.
Step 1, above-mentioned fabric is raw materials used for nylon fully drawn yarn (FDY), and wherein warp thread is 70D/24F, and weft yarn is 200D/48F;
Step 2, warping: warp thread carries out warping by warp warping machine, yarn is parallel to each other and is wound on warp beam closely, and percentage elongation controls 0.5%;
Step 3, starching: warp sizing, slurry is mainly the polyacrylate of 3% and the PVA-205 of 2.5%, adds the antistatic additive of 0.2%, the oil emulsion of 0.5%.The rate of sizing is 5%;
Step 4, weaving: warp thread sizing well after gait denting according to pegging plan and warp count designing requirement, loom adopts air-jet loom, fabric structure is 2 times twills on 2, the end count of fabric is 180 pieces/inch, and filling density is 92 pieces/inch, and the fabric weight weaved is 125g/m2;
Step 5, grey cloth is checked, and locomotive speed is 15m/min;
Step 6, cold pad--batch: first by grey cloth at room temperature alkali immerging (NaOH5g/L, 35%H2O28ml/L), then clot on the cloth beam of draw off mechanism, yardage roll plastic film and other material is wrapped up, it is prevented that cloth cover is air-dry.Last yardage roll is at room temperature banked up 72 hours, and period keeps yardage roll (6r/min) at a slow speed revolution;
Step 7, washing: yardage roll good for cold pad--batch is washed 0.5 hour in the hot water of 60 DEG C;
Step 8, dyeing: middle acid dyeing, first regulate Value in Dyeing Process to 4 with acetic acid, and add the levelling agent of 1%.Dye bath temperature starts dyeing after being increased to 40 DEG C, heat up and rise to 80 degree with the speed of 1 degree/2 minutes, heat up after being incubated 15 minutes again, after dye bath temperature is increased to 95 DEG C, dye of boiling 1 hour, then cools to 40 DEG C with the speed of 1 degree/1 minute, the color fixing agent simultaneously adding 1% gradually;
Step 9, dries: dries and carries out in the cylinder group that surface temperature is 80 DEG C, the 20 seconds time that cloth cover is fitted with cylinder, reaches the effect of basic drying;
Step 10, thermal finalization: in the tank before forming machine, add anti-agent 1% of becoming unwoven or untiwisted, antistatic additive 0.5%, waterproofing agent 1%, often sizing 1000 meters by proportioning, quantitatively supplement waterproofing agent, setting temperature is 140 DEG C, and machine rotational speed is 50 yards;
Step 11, checks clot, packaging.
Embodiment 2:
A kind of high-grade anti-slippage sportswear fabric of woven nylon is to adopt nylon fully drawn yarn, processes through woven, dyeing, Final finishing.
Step 1, above-mentioned fabric is raw materials used for nylon fully drawn yarn (FDY), and wherein warp thread is 70D/24F, and weft yarn is 200D/48F,
Step 2, warping: warp thread carries out warping by warp warping machine, yarn is parallel to each other and is wound on warp beam closely, and percentage elongation controls 0.6%,
Step 3, starching: warp sizing, slurry is mainly the polyacrylate of 3% and the PVA-205 of 2.5%, adds the antistatic additive of 0.2%, the oil emulsion of 0.5%, and the rate of sizing is 4%,
Step 4, weaving: warp thread sizing well after gait denting according to pegging plan and warp count designing requirement, loom adopts air-jet loom, fabric structure is 2 times twills on 2, the end count of fabric is 180 pieces/inch, and filling density is 91 pieces/inch, and the fabric weight weaved is 124g/m2,
Step 5, grey cloth is checked, and locomotive speed is 15m/min,
Step 6, cold pad--batch: first by grey cloth at room temperature alkali immerging (NaOH6g/L, 35%H2O28ml/L), then clot on the cloth beam of draw off mechanism, yardage roll plastic film and other material is wrapped up, it is prevented that cloth cover is air-dry, and last yardage roll is at room temperature banked up 72 hours, and period keeps yardage roll (8r/min) at a slow speed revolution.
Step 7, washing: yardage roll good for cold pad--batch is washed 1 hour in the hot water of 60 DEG C;
Step 8, dyeing: middle acid dyeing, first regulate Value in Dyeing Process to 5 with acetic acid, and add the levelling agent of 1%.Dye bath temperature starts dyeing after being increased to 40 DEG C, heat up and rise to 80 degree with the speed of 1 degree/2 minutes, heat up after being incubated 15 minutes again, after dye bath temperature is increased to 95 DEG C, dye of boiling 70 minutes, then lowers the temperature gradually and drops to 40 DEG C with the speed of 1 degree/min, the color fixing agent color simultaneously adding 1%;
Step 9, dries: dries and carries out in the cylinder group that surface temperature is 85 DEG C, the 25 seconds time that cloth cover is fitted with cylinder, reaches the effect of basic drying;
Step 10, thermal finalization: in the tank before forming machine, add anti-agent 2% of becoming unwoven or untiwisted, antistatic additive 0.5%, waterproofing agent 1%, often sizing 800 meters by proportioning, quantitatively supplement waterproofing agent.Setting temperature is 150 DEG C, and machine rotational speed is 50 yards;
Step 11, checks clot, packaging.
Embodiment 3:
A kind of high-grade anti-slippage sportswear fabric of woven nylon is to adopt nylon fully drawn yarn, processes through woven, dyeing, Final finishing.
Step 1, above-mentioned fabric is raw materials used for nylon fully drawn yarn (FDY), and wherein warp thread is 70D/24F, and weft yarn is 200D/48F;
Step 2, warping: warp thread carries out warping by warp warping machine, yarn is parallel to each other and is wound on warp beam closely, and percentage elongation controls 0.5%;
Step 3, starching: warp sizing, slurry is mainly the polyacrylate of 3% and the PVA-205 of 2.5%, adds the antistatic additive of 0.2%, the oil emulsion of 0.5%, and the rate of sizing is 3%;
Step 4, weaving: warp thread sizing well after gait denting according to pegging plan and warp count designing requirement, loom adopts air-jet loom, and fabric structure is 2 times twills on 2, the end count of fabric is 180 pieces/inch, and filling density is 93 pieces/inch of fabric weights weaved is 128g/m2;
Step 5, grey cloth is checked, and locomotive speed is 15m/min;
Step 6, cold pad--batch: first by grey cloth at room temperature alkali immerging (NaOH6g/L, 35%H2O210ml/L), then clot on the cloth beam of draw off mechanism, yardage roll plastic film and other material is wrapped up, it is prevented that cloth cover is air-dry, and last yardage roll is at room temperature banked up 72 hours, and period keeps yardage roll (6r/min) at a slow speed revolution;
Step 7, washing: yardage roll good for cold pad--batch is washed 0.5 hour in the hot water of 60 DEG C;
Step 8, dyeing: middle acid dyeing, first regulate Value in Dyeing Process to 5 with acetic acid, and add the levelling agent of 1%.Dye bath temperature starts dyeing after being increased to 40 DEG C, heat up and rise to 80 degree with the speed of 1 degree/2 minutes, heat up after being incubated 15 minutes again, after dye bath temperature is increased to 95 DEG C, dye of boiling 50 minutes, then lowers the temperature gradually and drops to 40 DEG C with the speed of 1 degree/min, the color fixing agent simultaneously adding 2%;
Step 9, dries: dries and carries out in the cylinder group that surface temperature is 80 DEG C, the 25 seconds time that cloth cover is fitted with cylinder, reaches the effect of basic drying;
Step 10, thermal finalization: in the tank before forming machine, add anti-agent 1% of becoming unwoven or untiwisted, antistatic additive 0.5%, waterproofing agent 1%, often sizing 1000 meters by proportioning, quantitatively supplement waterproofing agent, setting temperature is 150 DEG C, and machine rotational speed is 50 yards;
Step 11, checks clot, packaging.
The high-grade anti-slippage sportswear fabric of woven nylon disclosed by the invention is through (Tongbiao Standard Technology Service Co., Ltd of third party testing agency, SGS) test, method of testing adopts " AdidasMethod4.13 ", and the slippage intensity of result display warp-wise and broadwise has all exceeded 200N.Above three embodiment of the present invention is measured voluntarily by inside, and result is as follows:
Compared with prior art, the invention has the beneficial effects as follows:
(1) present invention is by the processing of fabric structure and thread count design, dyeing Final finishing, fabric slippage intensity is made to be obviously enhanced, through (Tongbiao Standard Technology Service Co., Ltd of third party testing agency, SGS) test, method of testing adopts " AdidasMethod4.13 ", and the slippage intensity of result display warp-wise and broadwise is all more than 200N;
(2) this face weave technique is simple, does not have coating, it does not have additionally increase production cost in Final finishing processing.
(3) this fabric is except anti-slippage, it is also possible to anti-hook silk, and fabric is slim and graceful, ventilative, and added value of product is high, it is easy to marketing.
Claims (5)
1. the anti-slippage sportswear fabric of woven nylon, it is characterized in that: described fabric is raw materials used for nylon fully drawn yarn, the warp thread of described nylon fully drawn yarn is 70D/24F, the weft yarn of described nylon fully drawn yarn is 200D/48F, the end count of described anti-slippage fabric is 180 pieces/inch, and the filling density of described anti-slippage fabric is 92 pieces/inch.
2. the anti-slippage sportswear fabric of woven nylon according to claim 1, it is characterised in that: described fabric structure is 2 times twills on 2, and the fabric weight weaved is 120 ~ 130g/m2。
3. a woven nylon anti-slippage sportswear face weave method, it is characterised in that: include step:
Select raw material: selecting nylon fully drawn yarn is the raw material of fabric, and wherein warp thread is 70D/24F, and weft yarn is 200D/48F;
Warping: warp thread carries out warping by warp warping machine, yarn is parallel to each other and is wound on warp beam closely, and percentage elongation controls 0.5% ~ 0.8%;
Starching: warp sizing, slurry is mainly the polyacrylate of 3% and the PVA-205 of 2.5%, adds the antistatic additive of 0.2%, the oil emulsion of 0.5%, and the rate of sizing is 3 ~ 5%;
Weaving: warp thread sizing well after gait denting according to pegging plan and warp count designing requirement, loom adopts air-jet loom, and fabric structure is 2 times twills on 2, and the fabric weight weaved is 120 ~ 130g/m2;
Dry and grey cloth inspection: after drying, length and door width have retraction, and grey cloth verifier vehicle speed is 15m/min;
Cold pad--batch: first by grey cloth at room temperature alkali immerging, then clot on the cloth beam of draw off mechanism, yardage roll plastic sheeting wraps up, it is prevented that cloth cover is air-dry, last yardage roll is at room temperature banked up 72 hours, and period keeps yardage roll to turn round with the speed of 6-8r/min;
Washing: by yardage roll good for cold pad--batch 60oThe hot water of C is washed 0.5 ~ 1 hour;
Dyeing: middle acid dyeing, first regulates Value in Dyeing Process to 4-6 with acetic acid, and adds the levelling agent of 1-2%, and dye bath temperature is to 40oStarting dyeing after C, heat up and rise to 80 ~ 85 degree with the speed of 1 degree/2 minutes, heat up after being incubated 15 minutes again, dye bath temperature is increased to 95oAfter C, dye of boiling 70 ~ 90 minutes, then lower the temperature gradually and drop to 40 with the speed of 1 degree/minoC, adds 1 ~ color fixing agent of 2% simultaneously;
Dry: drying in surface temperature is 80 ~ 90oThe cylinder group of C carries out, 10 ~ 25 seconds time that cloth cover is fitted with cylinder;
Thermal finalization: in the tank before forming machine, adds anti-agent 1 ~ 3% of becoming unwoven or untiwisted, antistatic additive 0.5%, waterproofing agent 1 ~ 2% by proportioning, often shapes 800 ~ 1000 meters, quantitatively supplements waterproofing agent, and setting temperature is 130 ~ 140oC, machine rotational speed is 50 yards;
Inspection clot, packaging.
4. the anti-slippage sportswear fabric of woven nylon according to claim 3, it is characterised in that: the end count of described anti-slippage fabric is 180 pieces/inch.
5. the anti-slippage sportswear fabric of woven nylon according to claim 3, it is characterised in that: the filling density of described anti-slippage fabric is 92 pieces/inch.