CN105733143A - 一种高阻燃性聚乙烯醇/木粉生物质复合材料 - Google Patents

一种高阻燃性聚乙烯醇/木粉生物质复合材料 Download PDF

Info

Publication number
CN105733143A
CN105733143A CN201410746938.8A CN201410746938A CN105733143A CN 105733143 A CN105733143 A CN 105733143A CN 201410746938 A CN201410746938 A CN 201410746938A CN 105733143 A CN105733143 A CN 105733143A
Authority
CN
China
Prior art keywords
composite material
polyvinyl alcohol
flame
wood powder
retardancy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410746938.8A
Other languages
English (en)
Inventor
刘申
张博霖
代汝军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Heilongjiang Xinda Enterprise Group Co Ltd
Original Assignee
Heilongjiang Xinda Enterprise Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Heilongjiang Xinda Enterprise Group Co Ltd filed Critical Heilongjiang Xinda Enterprise Group Co Ltd
Priority to CN201410746938.8A priority Critical patent/CN105733143A/zh
Publication of CN105733143A publication Critical patent/CN105733143A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种高阻燃性聚乙烯醇和木粉复合材料及其制备方法。该发明材料是一种新型环保复合材料。制备该复合材料的技术工艺的创新性体现在：通过和聚聚磷酸铵和木粉协同阻燃，并且聚乙烯醇提高复合材料的阻燃性，以及利用聚丙烯提高复合材料流动性和成型，进而将聚乙烯醇和木粉复合材料通过双螺杆挤出机共混挤出，牵引、冷却、切粒后得到改性高阻燃性的聚乙烯醇/木粉复合材料。在室内外环保装饰材料领域，高阻燃性的聚乙烯醇和木粉复合材料与木质材料和塑料相比，具有良好的阻燃性和使用质感，同时兼顾较高的尺寸稳定性和耐磨性、耐候性，另外还有可以材料的使用寿命等优点。

Description

一种高阻燃性聚乙烯醇/木粉生物质复合材料
技术领域
本发明涉及可再生环保复合材料，可用于室内外装饰、装潢、地板和家具等领域。具体涉及一种高阻燃性的聚乙烯醇和木粉复合材料及其制备方法，主要应用于环保装饰材料。
背景技术
木塑复合材料是国内外近年蓬勃兴起的一类新型复合材料，利用聚乙烯、聚丙烯和聚氯乙烯等，代替通常的树脂胶粘剂，与木粉、稻壳、秸秆等废植物纤维混合成新的木质材料，再经挤压、模压、注射成型等塑料加工工艺，生产出的板材或型材。主要用于建材、家具、物流包装等行业。
发明内容
本发明制备了一种高阻燃性的聚乙烯醇和木粉复合材料，该材料用于家具、室外装饰、室内装潢、非承重板材、码头地板等，利用聚丙烯增加复合材料的流动性，提高生产效率。聚磷酸铵提高复合材料的阻燃性。该复合材料不仅具有较好的力学性能，耐腐蚀性，而且具有良好的可塑性、阻燃性、耐候性。
技术方案
上述高阻燃性的聚乙烯醇和木粉复合材料的制备方法包括：
步骤一、聚乙烯醇在110～1200C下进行1小时烘干；
步骤二、木粉在90～1000C下进行3小时烘干；
步骤三、将干燥好的聚乙烯醇和木粉、阻燃剂、润滑剂、聚丙烯、相容剂放入高速混合机中，在常温下搅拌5～10分钟；
步骤四、将步骤三混合后的物料加入到双螺杆挤出机的料筒中，经过熔融共混挤出、水冷、风刀冷却、造粒；
其中，双螺杆挤出机的温度设置为：后段温度为240～2500C，中段和前段温度为220～2500C，螺杆转速为110～150r/min。
本发明解决了木塑复合材料的易燃性问题，同时复配聚丙烯增强体系流动性和成型行，可有效提高复合材料的阻燃性、耐候性，并使得材料具有良好的尺寸稳定性，满足于环保阻燃装饰材料的应用。
具体实例
为便于进一步说明本发明，下面结合具体实例对本发明进行说明：
主要原料聚乙烯醇塑脂粉末，密度为1.320g/cm3；木粉为目数为80目的杨木粉；助剂包括阻燃剂的聚磷酸铵；润滑剂为石蜡和硬质酸钙。双螺杆挤出机料筒温度一区温度：220～2250C，二区温度220～2250C，三区温度225～2300C，四区温度225～2300C，五区温度230～2350C，六区温度230～2350C，压力为10～16MPa，螺杆长径比35～40，主机转速110～150r/min。将各组分按配比混合均匀置于双螺杆挤出机中，经熔融混合挤出造粒。
本发明各实施例中所得的阻燃聚乙烯醇/木粉复合材料，按一下注塑条件注塑成测试样条。注塑条件：注塑温度220～2400C，注塑压力50～60MPa，注塑速度40～50mm/s。
各实施例具体检测标准如下：
缺口冲击强度ISO179
拉伸强度ISO527（5mm/min）
弯曲强度ISO178（3mm/min）
弯曲模量ISO178（3mm/min）
阻燃等级UL-94
实施例1～4对应的各组分用量、实施例性能检测结果（见表1和表2）
表1实施例1～4的配方表
实施例1 实施例2 实施例3 实施例4
原料 用量（份） 用量（份） 用量（份） 用量（份）
聚乙烯醇 55 55 55 55
木粉 15 15 15 15
聚丙烯 20 20 20 20
相容剂 5 5 5 5
阻燃剂 5 10 15
润滑剂 5 5 5 5
表2各实施例样品对应的性能
检测项目 实施例1 实施例2 实施例3 实施例4
拉伸强度MPa 32 30 27 26
弯曲强度MPa 45 41 40 38
弯曲模量MPa 2100 7120 7130 7230
无缺口冲击强度KJ/ m2 20 23 21 15
缺口冲击强度KJ/ m2 11 7 6.5 3.5
阻燃等级（UL-94） V1 V1 V0 V0
密度g/ m3 1.22 1.22 1.23 1.23
本发明采用几种不同比例的阻燃剂和聚乙烯醇/木粉复合材料复配体系，制备出不同综合性能的高阻燃性复合材料，从表2可知，随阻燃剂聚磷酸铵含量提高，复合材料的阻燃性也提高。证明其此种阻燃剂适合与聚乙烯醇/木粉复合材料复配使用，并且满足该复合材料的性能标准要求，所以制备的高阻燃性的聚乙烯醇和木粉复合材料可作为室外阻燃装饰材料使用。

Claims (6)

1.高阻燃性聚乙烯醇和木粉复合材料复合材料的配方组成如下所示：
聚乙烯醇50%～70%
木粉10%～15%
聚丙烯20%～30%
接枝聚丙烯4%～6%
阻燃剂2%～5%
润滑剂2%～4%。
2.根据权利要求1所述的高阻燃性的聚乙烯醇和木粉复合材料，其特征在于：所述的聚乙烯醇为白色粉末状的纯原料树脂，密度1.30g/cm3。
3.根据权利要求1所述的高阻燃性的聚乙烯醇和木粉复合材料，其特征在于：所述的木粉为杨木粉，目数为80目。
4.根据权利要求1所述的高阻燃性的聚乙烯醇和木粉复合材料，其特征在于：所述的聚丙烯为白色颗粒状的原料树脂，密度0.9g/cm3。
5.根据权利要求1所述的高阻燃性的聚乙烯醇和木粉复合材料，其特征在于：所述的阻燃剂为聚磷酸胺，含磷量30％～32％。
6.根据权利要求1所述的高阻燃性的聚乙烯醇和木粉复合材料，其特征在于：所述的润滑剂为主要由石蜡、硬质酸钙、耐高温抗氧剂按一定比例配混而成。
CN201410746938.8A 2014-12-10 2014-12-10 一种高阻燃性聚乙烯醇/木粉生物质复合材料 Pending CN105733143A (zh)