CN105729935A - Production process of metal texture plate synthetic glass - Google Patents
Production process of metal texture plate synthetic glass Download PDFInfo
- Publication number
- CN105729935A CN105729935A CN201610129754.6A CN201610129754A CN105729935A CN 105729935 A CN105729935 A CN 105729935A CN 201610129754 A CN201610129754 A CN 201610129754A CN 105729935 A CN105729935 A CN 105729935A
- Authority
- CN
- China
- Prior art keywords
- glass
- pressing
- metallic plate
- plate
- processes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a production process of metal texture plate synthetic glass. The metal texture plate synthetic glass is formed by the adhesive bonding of a metal plate with textures and glass. According to the production process, the metal texture plate synthetic glass is prepared through the five processes: glass pre-processing, metal plate pre-processing, metal plate and glass bonding, pre-pressing and pressing, metal plate and glass high-pressure processing and metal plate and glass post-processing. The production process provided by the invention has the advantages that small patterns can reappear on the metal texture plate synthetic glass produced by the production process; the texture can be embodied, and the weather resistance is extremely high, so that the product quality is stable; in addition, the input-output ratio is high, the product cost is low, and the development of new equipment is not needed.
Description
Technical field
The present invention relates to a kind of metal texture plate synthetic glass, particularly to the production technology of a kind of metal texture plate synthetic glass.
Background technology
Metal texture plate synthetic glass is a kind of desirably new decorative material, OCA double faced adhesive tape or PVB film is utilized to be undertaken bonding by the glass that metal texture plate and 1～4mm are thick, to reach case hardness height that on sheet metal, textured metal texture and glass possess, easy to clean, feature that surface gloss is high.Along with the people's asking most nature material, the production technology of metal texture plate synthetic glass is also just more and more concerned.
The production technology of metal texture plate synthetic glass currently mainly has by silk screen printing, UV transfer modes and what three kinds of techniques of pad pasting realized.
Existing silk-screen printing technique major defect is: (1) can not realize below 0.05mm texture, and general silk screen printing process can only realize more than 0.1mm tactile texture display, and the reflective difference of textured metal texture of silk-screen cannot represent real metal material effect；(2) because to realize texture and need to realize more than at least 3 times silk screen printings in silk-screen operation, 0.05mm input and output rate is low, reaches 75% only.
Existing UV transfer modes technique major defect is: (1) complex process, it is necessary to could realize through grinding tool making, pressing, membrane removal, solidification, magnetron sputtering plating, printing protection ink；(2) relevant environment is required harshness by transfer, filming process, and input and output rate is low, reaches 70% only.
Existing pad pasting mode technique major defect is: (1) pad pasting is imitation texture, it is impossible to perfection represents real metal material effect；(2) current Related product can not meet client's standard in water boiling resistance and acid and alkali-resistance physical and chemical index, as the test such as decocting in water cannot pass through 100 DEG C, 1 hour, the index such as 5%NaOH such as acid-fast alkali-proof be unable to reach coating crack-free after soaking 1 hour, expand, shrink, come off wait exception.
Therefore, research and development one can reproduce fine pattern, embody texture, stain resistant, and input and output rate is high, and constant product quality, product have the production technology of high weatherability and the low metal texture plate synthetic glass of product cost and be necessary.
Summary of the invention
The technical problem to be solved in the present invention is to provide one and can reproduce fine pattern, embody texture, stain resistant, and input and output rate is high, and constant product quality, product have high weatherability and the production technology of the low metal texture plate synthetic glass of product cost.
For solving above-mentioned technical problem, the technical scheme is that the production technology of a kind of metal texture plate synthetic glass, being combined formation metal texture plate synthetic glass by the metallic plate with texture with glassy bond, its innovative point is in that: described production technology prepares metal texture plate synthetic glass by glass preprocessing process, metallic plate preprocessing process, metallic plate precompressed pressing process bonding with glass, metallic plate and high-pressure glass process and metallic plate and five operations of glass post processing.
Further, the specifically comprising the following steps that of described production technology
(1) glass preprocessing processes: by chemically toughened glass that thickness is 1～2mm by cutting, edging matting be processed into the length dimension L1 of needs, or by common float glass that thickness is 2～4mm by cutting, edging, cleaning, physical toughened working procedure processing one-tenth needs length dimension L1；
(2) metallic plate preprocessing processes: metallic plate adopts thickness to be the various texture aluminium alloy of band or the rustless steel of 0.3～0.5mm, then passes through punching press, Digit Control Machine Tool is finish-ground to the metallic plate that length dimension is L1-1mm；
(3) metallic plate precompressed pressing bonding with glass processes: the glass after preprocessing being processed and the metallic plate after preprocessing process clean, and carry out bonding precompressed pressing again and process after cleaning；
(4) metallic plate processes with high-pressure glass: after metallic plate processes with glass pre-pressing pressing, autoclave equipment is adopted to carry out High Temperature High Pressure pressing again again, thoroughly getting rid of the bubble between sheet metal and glass assembly, technique is temperature: 135～140 DEG C, and temperature, pressure keeps three phases；First stage: pressure keeps: 0.8Mpa, temperature retention time: 10 ± 2 minutes, second stage: pressure keeps: 1.0Mpa, temperature retention time: 20 ± 3 minutes, the phase III: pressure keeps: 1.2Mpa, temperature retention time: 60 ± 5 minutes, then being vented to normal pressure, cooling down goes out product to 45 DEG C；
(5) metallic plate and glass post processing: the product intermediate layer redundance blade that in step (4), pressing is good is repaiied and removed or emery wheel grinding, makes product edge appearance transparent consistent.
Further, the bonding precompressed pressing in described step (3) processes as adopting OCA double faced adhesive tape bonding between metallic plate with glass, then passes through pressing machine by three's pressing, and pressing-in temp is room temperature, and pressing speed is 1～3m/M.
Further, it is 0.38 or 0.76mmPVB is gluing connects that bonding precompressed pressing in described step (3) processes as adopting film stock thickness between metallic plate and glass, then passing through pressing machine by three's pressing, pressing-in temp is 115～125 DEG C, and pressing speed is 1～2m/M.
It is an advantage of the current invention that:
(1) production technology of metal texture plate synthetic glass of the present invention, compared with traditional processing technology, the metal texture plate synthetic glass gone out by this explained hereafter can reproduce fine pattern；Texture can be embodied and there is high weatherability, and then making constant product quality；Additionally, high and this technique the product cost of this input and output rate is low, it is not necessary to the exploitation of new equipment；
(2) relative to traditional technique, the production technology of metal texture plate synthetic glass of the present invention can realize on chemically toughened glass, also can realize on common float glass so that product is unification no longer；
(3) production technology of metal texture plate synthetic glass of the present invention, metallic plate precompressed pressing bonding with glass is processed and can be realized by the gluing precompressed pressing two ways that connects of the bonding precompressed pressing of OCA double faced adhesive tape and PVB, so makes metallic plate precompressed pressing bonding with glass process and has more selectivity.
Detailed description of the invention
The following examples can make professional and technical personnel more fully understand the present invention, but does not therefore limit the present invention among described scope of embodiments.
The production technology of metal texture plate synthetic glass of the present invention, be combined formation metal texture plate synthetic glass with glassy bond by the metallic plate with texture, and this production technology is by glass preprocessing process, metallic plate preprocessing process, metallic plate precompressed pressing process bonding with glass, metallic plate and high-pressure glass process and metallic plate and the prepared metal texture plate synthetic glass of five operations of glass post processing.
Embodiment 1
The production technology of the present embodiment metal texture plate synthetic glass, this production technology specifically comprises the following steps that
(1) glass preprocessing processes: chemically toughened glass that thickness is 1～2mm is processed into the length dimension L1 of needs by cutting, edging matting；
(2) metallic plate preprocessing processes: metallic plate adopts thickness to be the various texture rustless steel of band of 0.3～0.5mm, then passes through punching press, Digit Control Machine Tool is finish-ground to the metallic plate that length dimension is L1-1mm；
(3) metallic plate precompressed pressing bonding with glass processes: the glass after preprocessing being processed and the metallic plate after preprocessing process clean, adopt OCA double faced adhesive tape bonding after cleaning between metallic plate with glass, then pass through pressing machine by three's pressing, pressing-in temp is room temperature, and pressing speed is 1～3m/M；
(4) metallic plate processes with high-pressure glass: after metallic plate processes with glass pre-pressing pressing, autoclave equipment is adopted to carry out High Temperature High Pressure pressing again again, thoroughly getting rid of the bubble between sheet metal and glass assembly, technique is temperature: 135～140 DEG C, and temperature, pressure keeps three phases；First stage: pressure keeps: 0.8Mpa, temperature retention time: 10 ± 2 minutes, second stage: pressure keeps: 1.0Mpa, temperature retention time: 20 ± 3 minutes, the phase III: pressure keeps: 1.2Mpa, temperature retention time: 60 ± 5 minutes, then being vented to normal pressure, cooling down goes out product to 45 DEG C；
(5) metallic plate and glass post processing: the product intermediate layer redundance blade that in step (4), pressing is good is repaiied and removed or emery wheel grinding, makes product edge appearance transparent consistent.
Embodiment 2
The production technology of the present embodiment metal texture plate synthetic glass, this production technology specifically comprises the following steps that
(1) glass preprocessing processes: by cutting, edging, cleaning, physical toughened working procedure processing, the common float glass that thickness is 2～4mm is become the length dimension L1 needed；
(2) metallic plate preprocessing processes: metallic plate adopts thickness to be the various texture rustless steel of band of 0.3～0.5mm, then passes through punching press, Digit Control Machine Tool is finish-ground to the metallic plate that length dimension is L1-1mm；
(3) metallic plate precompressed pressing bonding with glass processes: the glass after preprocessing being processed and the metallic plate after preprocessing process clean, adopt OCA double faced adhesive tape bonding after cleaning between metallic plate with glass, then pass through pressing machine by three's pressing, pressing-in temp is room temperature, and pressing speed is 1～3m/M；
(4) metallic plate processes with high-pressure glass: after metallic plate processes with glass pre-pressing pressing, autoclave equipment is adopted to carry out High Temperature High Pressure pressing again again, thoroughly getting rid of the bubble between sheet metal and glass assembly, technique is temperature: 135～140 DEG C, and temperature, pressure keeps three phases；First stage: pressure keeps: 0.8Mpa, temperature retention time: 10 ± 2 minutes, second stage: pressure keeps: 1.0Mpa, temperature retention time: 20 ± 3 minutes, the phase III: pressure keeps: 1.2Mpa, temperature retention time: 60 ± 5 minutes, then being vented to normal pressure, cooling down goes out product to 45 DEG C；
(5) metallic plate and glass post processing: the product intermediate layer redundance blade that in step (4), pressing is good is repaiied and removed or emery wheel grinding, makes product edge appearance transparent consistent.
Embodiment 3
The production technology of the present embodiment metal texture plate synthetic glass, this production technology specifically comprises the following steps that
(1) glass preprocessing processes: chemically toughened glass that thickness is 1～2mm is processed into the length dimension L1 of needs by cutting, edging matting；
(2) metallic plate preprocessing processes: metallic plate adopts thickness to be the various texture rustless steel of band of 0.3～0.5mm, then passes through punching press, Digit Control Machine Tool is finish-ground to the metallic plate that length dimension is L1-1mm；
(3) metallic plate precompressed pressing bonding with glass processes: the glass after preprocessing being processed and the metallic plate after preprocessing process clean, adopt film stock thickness to be that 0.76mmPVB is gluing after cleaning between metallic plate and glass to connect, then pass through pressing machine by three's pressing, pressing-in temp is 115～125 DEG C, and pressing speed is 1～2m/M；
(4) metallic plate processes with high-pressure glass: after metallic plate processes with glass pre-pressing pressing, autoclave equipment is adopted to carry out High Temperature High Pressure pressing again again, thoroughly getting rid of the bubble between sheet metal and glass assembly, technique is temperature: 135～140 DEG C, and temperature, pressure keeps three phases；First stage: pressure keeps: 0.8Mpa, temperature retention time: 10 ± 2 minutes, second stage: pressure keeps: 1.0Mpa, temperature retention time: 20 ± 3 minutes, the phase III: pressure keeps: 1.2Mpa, temperature retention time: 60 ± 5 minutes, then being vented to normal pressure, cooling down goes out product to 45 DEG C；
(5) metallic plate and glass post processing: the product intermediate layer redundance blade that in step (4), pressing is good is repaiied and removed or emery wheel grinding, makes product edge appearance transparent consistent.
Embodiment 4
The production technology of the present embodiment metal texture plate synthetic glass, this production technology specifically comprises the following steps that
(1) glass preprocessing processes: by cutting, edging, cleaning, physical toughened working procedure processing, the common float glass that thickness is 2～4mm is become the length dimension L1 needed；
(2) metallic plate preprocessing processes: metallic plate adopts thickness to be the various texture rustless steel of band of 0.3～0.5mm, then passes through punching press, Digit Control Machine Tool is finish-ground to the metallic plate that length dimension is L1-1mm；
(3) metallic plate precompressed pressing bonding with glass processes: the glass after preprocessing being processed and the metallic plate after preprocessing process clean, adopt film stock thickness to be that 0.38mmPVB is gluing after cleaning between metallic plate and glass to connect, then pass through pressing machine by three's pressing, pressing-in temp is 115～125 DEG C, and pressing speed is 1～2m/M；
(4) metallic plate processes with high-pressure glass: after metallic plate processes with glass pre-pressing pressing, autoclave equipment is adopted to carry out High Temperature High Pressure pressing again again, thoroughly getting rid of the bubble between sheet metal and glass assembly, technique is temperature: 135～140 DEG C, and temperature, pressure keeps three phases；First stage: pressure keeps: 0.8Mpa, temperature retention time: 10 ± 2 minutes, second stage: pressure keeps: 1.0Mpa, temperature retention time: 20 ± 3 minutes, the phase III: pressure keeps: 1.2Mpa, temperature retention time: 60 ± 5 minutes, then being vented to normal pressure, cooling down goes out product to 45 DEG C；
(5) metallic plate and glass post processing: the product intermediate layer redundance blade that in step (4), pressing is good is repaiied and removed or emery wheel grinding, makes product edge appearance transparent consistent.
Following table is the contrast of the color crystal glass that the metal texture plate synthetic glass obtained by embodiment 1～4 prepares with traditional handicraft:
Conclusion: by the production technology of the present invention, the metal texture plate synthetic glass produced can reproduce fine pattern；Texture can be embodied and there is high weatherability, and then making constant product quality；Additionally, this input and output rate is high, may be up to 96.5%, and the product cost of this technique is low, it is not necessary to the exploitation of new equipment；Meanwhile, by the comparison of each embodiment, scheme 4 is optimal case.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.Skilled person will appreciate that of the industry; the present invention is not restricted to the described embodiments; described in above-described embodiment and description is that principles of the invention is described; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements both fall within the claimed scope of the invention.Claimed scope is defined by appending claims and equivalent thereof.
Claims (4)
1. the production technology of a metal texture plate synthetic glass, formation metal texture plate synthetic glass is combined with glassy bond by the metallic plate with texture, it is characterised in that: described production technology is by glass preprocessing process, metallic plate preprocessing process, metallic plate precompressed pressing process bonding with glass, metallic plate and high-pressure glass process and metallic plate and the prepared metal texture plate synthetic glass of five operations of glass post processing.
2. the production technology of metal texture plate synthetic glass according to claim 1, it is characterised in that: specifically comprising the following steps that of described production technology
(1) glass preprocessing processes: by chemically toughened glass that thickness is 1～2mm by cutting, edging matting be processed into the length dimension L1 of needs, or by common float glass that thickness is 2～4mm by cutting, edging, cleaning, physical toughened working procedure processing one-tenth needs length dimension L1；
(2) metallic plate preprocessing processes: metallic plate adopts thickness to be the various texture aluminium alloy of band or the rustless steel of 0.3～0.5mm, then passes through punching press, Digit Control Machine Tool is finish-ground to the metallic plate that length dimension is L1-1mm；
(3) metallic plate precompressed pressing bonding with glass processes: the glass after preprocessing being processed and the metallic plate after preprocessing process clean, and carry out bonding precompressed pressing again and process after cleaning；
(4) metallic plate processes with high-pressure glass: after metallic plate processes with glass pre-pressing pressing, autoclave equipment is adopted to carry out High Temperature High Pressure pressing again again, thoroughly getting rid of the bubble between sheet metal and glass assembly, technique is temperature: 135～140 DEG C, and temperature, pressure keeps three phases；First stage: pressure keeps: 0.8Mpa, temperature retention time: 10 ± 2 minutes, second stage: pressure keeps: 1.0Mpa, temperature retention time: 20 ± 3 minutes, the phase III: pressure keeps: 1.2Mpa, temperature retention time: 60 ± 5 minutes, then being vented to normal pressure, cooling down goes out product to 45 DEG C；
(5) metallic plate and glass post processing: the product intermediate layer redundance blade that in step (4), pressing is good is repaiied and removed or emery wheel grinding, makes product edge appearance transparent consistent.
3. the production technology of metal texture plate synthetic glass according to claim 2, it is characterized in that: the bonding precompressed pressing in described step (3) processes as adopting OCA double faced adhesive tape bonding between metallic plate with glass, then pass through pressing machine by three's pressing, pressing-in temp is room temperature, and pressing speed is 1～3m/M.
4. the production technology of metal texture plate synthetic glass according to claim 2, it is characterized in that: it is 0.38 or 0.76mmPVB is gluing connects that bonding precompressed pressing in described step (3) processes as adopting film stock thickness between metallic plate and glass, then pass through pressing machine by three's pressing, pressing-in temp is 115～125 DEG C, and pressing speed is 1～2m/M.