CN108608785A - A kind of noble metal paillon UV color printings, gloss oil protection product manufacture craft - Google Patents
A kind of noble metal paillon UV color printings, gloss oil protection product manufacture craft Download PDFInfo
- Publication number
- CN108608785A CN108608785A CN201810445940.XA CN201810445940A CN108608785A CN 108608785 A CN108608785 A CN 108608785A CN 201810445940 A CN201810445940 A CN 201810445940A CN 108608785 A CN108608785 A CN 108608785A
- Authority
- CN
- China
- Prior art keywords
- noble metal
- product
- paillon
- pattern
- manufacture craft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses the manufacture crafts that a kind of noble metal paillon UV color printings, gloss oil protect product, are related to noble metal products technical field；The manufacture craft includes the following steps：A, sawing sheet；B, Mold Making manufactures corresponding mold according to the shape of product；C, product is suppressed；D, plastic packaging glued membrane will suppress the noble metal paillon of good pattern, and by plastic packaging, one layer of glued membrane is sealed in product surface；Product obtained in step D is printed preset pattern by UV printers and prints transparent light oil reservoir by the E, making of light oil reservoir；The beneficial effects of the invention are as follows：The pattern accuracy higher printed by UV, ink adhesive force is stronger, and light oil reservoir permeability is more preferable, can preferably show the gradual change of noble metal true qualities and color printing pattern color, the enhancing of gloss oil bright property.
Description
Technical field
The present invention relates to noble metal products technical fields, more particularly, it relates to which a kind of noble metal paillon UV is color
The manufacture craft of print, gloss oil protection product.
Background technology
As the rapid development of sociaty and economy, noble metal jewelry, noble metal collectibles, noble metal investment goods etc. noble metal
Product accounted in the production and living of people proportion is increasing." that thing which is rare is dear " noble metal because its is rare and precious,
How the characteristics such as permanent quality, the weight of holding noble metal are not turned into hot spot of people's attention.
Precious metal surface coating technique mainly has noble metal nano plated film, noble metal vacuum coating at present.Noble metal nano
Plated film is exactly the conducting polymer coating in precious metal surface plating last layer diamond grade hardness, nanometer grade thickness, to which your gold made
Metal surface has the characteristics such as good wearability, corrosion resistance, anti-oxidation.But this coating technique must be in simulation nanometer experiment
It is operated in the environment of room, environmental condition requires harshness, and complex manufacturing technology, the most serious is nano-coatings to be easy to cause noble metal
The variation of attribute itself, therefore nano-coating is suitable for the fields such as industrial golden finger, pcb board plated film, is not suitable for noble metal
The fields such as collection, investment.Equally, noble metal vacuum coating can not directly apply to there is also disadvantage as described above and keep expensive
The constant field of metallic character.
Invention content
For overcome the deficiencies in the prior art, the present invention provides a kind of noble metal paillon UV color printings, gloss oil protection product
Manufacture craft, the pattern accuracy higher which is printed by UV, ink adhesive force is stronger, and light oil reservoir permeability is more preferable, energy
The preferably gradual change of display noble metal true qualities and color printing pattern color, the enhancing of gloss oil bright property.
The technical solution adopted by the present invention to solve the technical problems is：A kind of noble metal paillon UV color printings, gloss oil protection
The manufacture craft of product, thes improvement is that：The manufacture craft includes the following steps：
A, sawing sheet chooses precious metal raw material, passes sequentially through thick pressure rolling, middle pressure rolling and pressure-sizing and roll, by precious metal raw material pressure
The noble metal paillon for 0.004-0.3mm is rolled, preset shape is cut into；
B, Mold Making manufactures corresponding mold according to the shape of product；
C, product is suppressed, and the noble metal paillon that will have been cut is put into the cavity of the mold prepared in step B, passes through
Cold pressing, compacted products form pattern in product surface, and oil pressure tonnage is 30-3500 tons；
D, plastic packaging glued membrane will suppress the noble metal paillon of good pattern, and by plastic packaging, one layer of glued membrane is sealed in product surface,
In the process, hot melt adhesive is carried on glued membrane, and by the way that 110-160 DEG C of glued membrane is added, after so that hot melt adhesive is dissolved, glued membrane is compounded in
On noble metal paillon；
In step D, if the thickness of noble metal paillon is 0.004-0.006mm, monolithic to noble metal paillon or
Two-sided carry out plastic packaging；When the thickness of noble metal paillon is 0.006-0.1mm, plastic packaging is carried out to the monolithic of noble metal paillon；When
When the thickness of noble metal paillon is 0.1-0.3mm, noble metal paillon is without carrying out plastic cement sealer；
Product obtained in step D is printed preset pattern and printing by the E, making of light oil reservoir by UV printers
Transparent light oil reservoir specifically includes following step：
E1, by computer graphics, drawn pattern is input in UV printers；
E2, by UV printing inks on the surface of product surface print pattern or plastic cement glued membrane, pass through high temperature ultraviolet lamp
UV curing ink；
E3, the product that will print good pattern print transparent light oil reservoir again by UV printers, increase the gloss of product
Degree prevents product oxidation and UV ink from scratching.
Further, in the step B, include the following steps：
Steel are cut into preset shape, the shape is according to product by a1, the steel for selecting mold by line cutting mill tool
Depending on shape；
A2, it is drawn a design by computer, by the pattern input CNC engraving machines of drafting, is carved by CNC engraving machines
Copper is public；
A3, embossing pattern is formed on die steel by electric discharge corrosion die steel using the copper public affairs carved；
A4, pass through sandblasting, polishing and laser engraving, the bright sand face of processing mold；
A5, mold is assembled.
Further, in the step B, include the following steps：
Steel are cut into preset shape, the shape is according to product by b1, the steel for selecting mold by line cutting mill tool
Depending on shape；
B2, it is drawn a design by computer, drawn pattern is input in laser engraving machine, laser engraving machine is passed through
Device engraved die steel, form embossing pattern on die steel；
B3, pass through sandblasting, polishing and laser engraving, the bright sand face of processing mold；
B4, mold is assembled.
Further, in the step B, include the following steps：
Steel are cut into preset shape, the shape is according to product by c1, the steel for selecting mold by line cutting mill tool
Depending on shape；
C2, the mold that step c1 center lines are cut to completion are polished, and die surface is finished to minute surface；
C3, it is drawn a design by computer, by drawn pattern input laser engraving machine, passes through laser engraving machine
The minute surface on engraved die surface forms bright sand pattern texture.
Further, it in the step A, is rolled by thick pressure rolling, middle pressure rolling and pressure-sizing, is by precious metal raw material pressure rolling
The noble metal paillon of 0.004mm.
Further, it in the step A, is rolled by thick pressure rolling, middle pressure rolling and pressure-sizing, is by precious metal raw material pressure rolling
The noble metal paillon of 0.012mm.
Further, it in the step A, is rolled by thick pressure rolling, middle pressure rolling and pressure-sizing, is by precious metal raw material pressure rolling
The noble metal paillon of 0.3mm.
Further, in the step D, the heating temperature of glued membrane is 110 DEG C.
Further, in the step D, the heating temperature of glued membrane is 135 DEG C.
Further, in the step D, the heating temperature of glued membrane is 160 DEG C.
The beneficial effects of the invention are as follows：A kind of noble metal paillon UV color printings of the present invention, the making work of gloss oil protection product
Skill, the pattern accuracy higher which is printed by UV, ink adhesive force is stronger, and light oil reservoir permeability is more preferable, can be preferably
Show the gradual change of noble metal true qualities and color printing pattern color, the enhancing of gloss oil bright property；Light oil reservoir can protect noble metal paillon, make
Noble metal paillon is not oxidizable, and crumple when avoiding contact with staves, and is conducive to collection, storage；And gloss oil ratio and encapsulating material
Noble metal true qualities and the color of color printing can more be embodied.
Description of the drawings
Fig. 1 protects the process flow chart of the manufacture craft of product for a kind of noble metal paillon UV color printings of the present invention, gloss oil.
Specific implementation mode
Present invention will be further explained below with reference to the attached drawings and examples.
The technique effect of the design of the present invention, concrete structure and generation is carried out below with reference to embodiment and attached drawing clear
Chu is fully described by, to be completely understood by the purpose of the present invention, feature and effect.Obviously, described embodiment is this hair
Bright a part of the embodiment, rather than whole embodiments, based on the embodiment of the present invention, those skilled in the art are not being paid
The other embodiment obtained under the premise of creative work, belongs to the scope of protection of the invention.In addition, being arrived involved in patent
All connection/connection relations, not singly refer to component and directly connect, and refer to can according to specific implementation situation, by addition or
Couple auxiliary is reduced, to form more preferably coupling structure.Each technical characteristic in the invention, in not conflicting conflict
Under the premise of can be with combination of interactions.
Embodiment 1
Referring to Fig.1 shown in, present invention is disclosed a kind of noble metal paillon UV color printings, gloss oil protect product manufacture craft,
Specifically, the manufacture craft includes the following steps：
A, sawing sheet chooses precious metal raw material, passes sequentially through thick pressure rolling, middle pressure rolling and pressure-sizing and roll, by precious metal raw material pressure
The noble metal paillon for 0.1mm is rolled, preset shape is cut into；
B, Mold Making manufactures corresponding mold according to the shape of product；In the present embodiment, step B further includes specifically
Following step：
Steel are cut into preset shape, the shape is according to product by a1, the steel for selecting mold by line cutting mill tool
Depending on shape；
A2, it is drawn a design by computer, by the pattern input CNC engraving machines of drafting, is carved by CNC engraving machines
Copper is public；
A3, embossing pattern is formed on die steel by electric discharge corrosion die steel using the copper public affairs carved；
A4, pass through sandblasting, polishing and laser engraving, the bright sand face of processing mold；
A5, mold is assembled；
C, product is suppressed, and the noble metal paillon that will have been cut is put into the cavity of the mold prepared in step B, passes through
Cold pressing, compacted products form pattern in product surface, and oil pressure tonnage is 30-3500 tons；In practical operation, the tonnage of oil pressure
It is adjusted according to actual conditions；
Product obtained in step C is printed preset pattern and printing by the D, making of light oil reservoir by UV printers
Transparent light oil reservoir specifically includes following step：
E1, by computer graphics, drawn pattern is input in UV printers；
E2, by UV printing inks in two printout surface patterns of product, pass through high temperature ultraviolet lamp UV curing ink；
E3, the product that will print good pattern increase production again by UV printers in two transparent light oil reservoirs of printout surface of product
The glossiness of product prevents product oxidation and UV ink from scratching.
It should be noted that in the present embodiment, the thickness of precious metal raw material may be used between 0.1-0.3mm
Technique in embodiment 1.
Embodiment 2
Referring to Fig.1 shown in, present invention is disclosed a kind of noble metal paillon UV color printings, gloss oil protect product manufacture craft,
Specifically, the manufacture craft includes the following steps：
A, sawing sheet chooses precious metal raw material, passes sequentially through thick pressure rolling, middle pressure rolling and pressure-sizing and roll, by precious metal raw material pressure
The noble metal paillon for 0.006mm is rolled, preset shape is cut into；
B, Mold Making manufactures corresponding mold according to the shape of product；In the present embodiment, step B includes below
Step：
Steel are cut into preset shape, the shape is according to product by b1, the steel for selecting mold by line cutting mill tool
Depending on shape；
B2, it is drawn a design by computer, drawn pattern is input in laser engraving machine, laser engraving machine is passed through
Device engraved die steel, form embossing pattern on die steel；
B3, pass through sandblasting, polishing and laser engraving, the bright sand face of processing mold；
B4, mold is assembled.
C, product is suppressed, and the noble metal paillon that will have been cut is put into the cavity of the mold prepared in step B, passes through
Cold pressing, compacted products form pattern in product surface, and oil pressure tonnage is 30-3500 tons；In practical operation, the tonnage of oil pressure
It is adjusted according to actual conditions；
D, plastic packaging glued membrane will suppress the noble metal paillon of good pattern, and by plastic packaging, one layer of glued membrane is sealed in product surface,
In the process, hot melt adhesive is carried on glued membrane, and by the way that 135 DEG C of glued membrane is added, after so that hot melt adhesive is dissolved, your gold glued membrane is compounded in
Belong on paillon；
In the step D, since the thickness of the paillon of noble metal is 0.006mm, at this time to the list of noble metal paillon
Face carries out plastic packaging；But it should be noted that when the thickness of the paillon of noble metal is between 0.006-0.1mm, to noble metal paillon
Single side carry out plastic packaging；
Product obtained in step D is printed preset pattern and printing by the E, making of light oil reservoir by UV printers
Transparent light oil reservoir specifically includes following step：
E1, by computer graphics, drawn pattern is input in UV printers；
E2, by UV printing inks in a printout surface pattern of the non-plastic cement sealer of product, pass through high temperature ultraviolet
Lamp UV curing ink；
E3, the product that will print good pattern print transparent light oil reservoir again by UV printers, increase the gloss of product
Degree prevents product oxidation and UV ink from scratching.
Embodiment 3
Referring to Fig.1 shown in, present invention is disclosed a kind of noble metal paillon UV color printings, gloss oil protect product manufacture craft,
Specifically, the manufacture craft includes the following steps：
A, sawing sheet chooses precious metal raw material, passes sequentially through thick pressure rolling, middle pressure rolling and pressure-sizing and roll, by precious metal raw material pressure
The noble metal paillon for 0.004mm is rolled, preset shape is cut into；
B, Mold Making manufactures corresponding mold according to the shape of product；
Steel are cut into preset shape, the shape is according to product by c1, the steel for selecting mold by line cutting mill tool
Depending on shape；
C2, the mold that step c1 center lines are cut to completion are polished, and die surface is finished to minute surface；
C3, it is drawn a design by computer, by drawn pattern input laser engraving machine, passes through laser engraving machine
The minute surface on engraved die surface forms bright sand pattern texture；
C, product is suppressed, and the noble metal paillon that will have been cut is put into the cavity of the mold prepared in step B, passes through
Cold pressing, compacted products form pattern in product surface, and oil pressure tonnage is 30-3500 tons；In practical operation, the tonnage of oil pressure
It is adjusted according to actual conditions；
D, plastic packaging glued membrane will suppress the noble metal paillon of good pattern, and by plastic packaging, one layer of glued membrane is sealed in product surface,
In the process, hot melt adhesive is carried on glued membrane, and by the way that 160 DEG C of glued membrane is added, after so that hot melt adhesive is dissolved, your gold glued membrane is compounded in
Belong on paillon；
In the step D, since the thickness of the paillon of noble metal is 0.004mm, at this time to the double of noble metal paillon
Face carries out plastic packaging glued membrane；But it should be noted that when the thickness of the paillon of noble metal is between 0.004-0.006mm, to your gold
Belong to the two-sided carry out plastic packaging of paillon；
Product obtained in step D is printed preset pattern and printing by the E, making of light oil reservoir by UV printers
Transparent light oil reservoir specifically includes following step：
E1, by computer graphics, drawn pattern is input in UV printers；
E2, by UV printing inks in two printout surface patterns of product, pass through high temperature ultraviolet lamp UV curing ink；
E3, the product that good pattern will be printed, again by UV printers, in two transparent gloss oil of printout surface of product
Layer, increases the glossiness of product, prevents product oxidation and UV ink from scratching.
Shown in sum up, the adhesive force of pattern accuracy higher, UV ink that the present invention is printed by UV printers is more
By force, light oil reservoir translucency is more preferable, can preferably show the gradual change of the true qualities and color printing pattern color of noble metal；In addition, printing
When light oil reservoir, posting is printed first with UV printers, then product is put into posting to good position, passes through absorption platform
Precious metal sheets are fixed on table top.Machine calibrates printing level automatically, is then printed, and when color printing passes through ultraviolet radiator
UV ink is fixed on product surface by photocuring, and UV ink has stronger adhesive force, gloss oil is printed after UV ink solidifications
Layer, light oil reservoir range are printed according to pre-set dimension, and gloss oil layer thickness can control by adjusting ink-jet numerical values recited.Light oil reservoir can be with
Noble metal paillon is protected, keeps noble metal paillon not oxidizable, crumple when avoiding contact with staves, and is conducive to collection, storage；And
Gloss oil ratio can more embody noble metal true qualities and the color of color printing with encapsulating material.
It is to be illustrated to the preferable implementation of the present invention, but the invention is not limited to the implementation above
Example, those skilled in the art can also make various equivalent variations or be replaced under the premise of without prejudice to spirit of that invention
It changes, these equivalent deformations or replacement are all contained in the application claim limited range.
Claims (10)
1. the manufacture craft of a kind of noble metal paillon UV color printings, gloss oil protection product, it is characterised in that：The manufacture craft include with
Under step：
A, sawing sheet chooses precious metal raw material, passes sequentially through thick pressure rolling, middle pressure rolling and pressure-sizing and roll, be by precious metal raw material pressure rolling
The noble metal paillon of 0.004-0.3mm, is cut into preset shape；
B, Mold Making manufactures corresponding mold according to the shape of product；
C, product is suppressed, and the noble metal paillon that will have been cut is put into the cavity of the mold prepared in step B, by being cold-pressed,
Compacted products form pattern in product surface, and oil pressure tonnage is 30-3500 tons；
D, plastic packaging glued membrane will suppress the noble metal paillon of good pattern, by plastic packaging, seal one layer of glued membrane in product surface, herein
In the process, hot melt adhesive is carried on glued membrane, and by the way that 110-160 DEG C of glued membrane is added, after so that hot melt adhesive is dissolved, your gold glued membrane is compounded in
Belong on paillon；
In step D, if the thickness of noble metal paillon is 0.004-0.006mm, the monolithic or two-sided to noble metal paillon
Carry out plastic packaging；When the thickness of noble metal paillon is 0.006-0.1mm, plastic packaging is carried out to the monolithic of noble metal paillon；When your gold
When the thickness for belonging to paillon is 0.1-0.3mm, noble metal paillon is without carrying out plastic cement sealer；
Product obtained in step D is printed preset pattern by UV printers and printed transparent by the E, making of light oil reservoir
Light oil reservoir specifically includes following step：
E1, by computer graphics, drawn pattern is input in UV printers；
E2, by UV printing inks on the surface of product surface print pattern or plastic cement glued membrane, cured by high temperature ultraviolet lamp
UV ink；
E3, the product that will print good pattern print transparent light oil reservoir again by UV printers, increase the glossiness of product, prevent
Only product oxidation and UV ink scratch.
2. the manufacture craft of a kind of noble metal paillon UV color printings according to claim 1, gloss oil protection product, feature exist
In：In the step B, include the following steps：
Steel are cut into preset shape by a1, the steel for selecting mold by line cutting mill tool, and the shape is according to the shape of product
Depending on；
A2, it is drawn a design by computer, by the pattern input CNC engraving machines of drafting, copper is carved by CNC engraving machines
It is public；
A3, embossing pattern is formed on die steel by electric discharge corrosion die steel using the copper public affairs carved；
A4, pass through sandblasting polishing and laser engraving, the bright sand face of processing mold；
A5, mold is assembled.
3. the manufacture craft of a kind of noble metal paillon UV color printings according to claim 1, gloss oil protection product, feature exist
In：In the step B, include the following steps：
Steel are cut into preset shape by b1, the steel for selecting mold by line cutting mill tool, and the shape is according to the shape of product
Depending on；
B2, it is drawn a design by computer, drawn pattern is input in laser engraving machine, carved by laser engraving machine
Die steel is carved, forms embossing pattern on die steel；
B3, pass through sandblasting, polishing and laser engraving, the bright sand face of processing mold；
B4, mold is assembled.
4. the manufacture craft of a kind of noble metal paillon UV color printings according to claim 1, gloss oil protection product, feature exist
In：In the step B, include the following steps：
Steel are cut into preset shape by c1, the steel for selecting mold by line cutting mill tool, and the shape is according to the shape of product
Depending on；
C2, the mold that step c1 center lines are cut to completion are polished, and die surface is finished to minute surface；
C3, it is drawn a design by computer, by drawn pattern input laser engraving machine, is carved by laser engraving machine
The minute surface of die surface forms bright sand pattern texture.
5. the manufacture craft of a kind of noble metal paillon UV color printings according to claim 1, gloss oil protection product, feature exist
In：Your in the step A, rolled by thick pressure rolling, middle pressure rolling and pressure-sizing, by the gold that precious metal raw material pressure rolling is 0.004mm
Belong to paillon.
6. the manufacture craft of a kind of noble metal paillon UV color printings according to claim 1, gloss oil protection product, feature exist
In：Your in the step A, rolled by thick pressure rolling, middle pressure rolling and pressure-sizing, by the gold that precious metal raw material pressure rolling is 0.012mm
Belong to paillon.
7. the manufacture craft of a kind of noble metal paillon UV color printings according to claim 1, gloss oil protection product, feature exist
In：It in the step A, is rolled by thick pressure rolling, middle pressure rolling and pressure-sizing, by the noble metal that precious metal raw material pressure rolling is 0.3mm
Paillon.
8. the manufacture craft of a kind of noble metal paillon UV color printings according to claim 1, gloss oil protection product, feature exist
In：In the step D, the heating temperature of glued membrane is 110 DEG C.
9. the manufacture craft of a kind of noble metal paillon UV color printings according to claim 1, gloss oil protection product, feature exist
In：In the step D, the heating temperature of glued membrane is 135 DEG C.
10. the manufacture craft of a kind of noble metal paillon UV color printings according to claim 1, gloss oil protection product, feature
It is：In the step D, the heating temperature of glued membrane is 160 DEG C.