CN105729557A - 一种改善pcb钻孔毛刺的方法 - Google Patents
一种改善pcb钻孔毛刺的方法 Download PDFInfo
- Publication number
- CN105729557A CN105729557A CN201610142611.9A CN201610142611A CN105729557A CN 105729557 A CN105729557 A CN 105729557A CN 201610142611 A CN201610142611 A CN 201610142611A CN 105729557 A CN105729557 A CN 105729557A
- Authority
- CN
- China
- Prior art keywords
- resin
- pcb
- burr
- boring
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开一种改善PCB钻孔毛刺的方法,其中,在与垫板接触的PCB板面涂覆一层树脂,树脂固化后,用于PCB钻孔。本发明通过在翘曲变形大的PCB板金属面涂覆一层树脂,利用树脂固化后的高硬度、强粘结力的特性,抑制钻孔毛刺的产生,同时降低了PCB板钻孔加工品质对PCB板翘曲变形和垫板质量的要求,钻孔后再将树脂层采用退洗液退洗的方法去除即可。
Description
技术领域
本发明涉及PCB钻孔加工领域,尤其涉及一种改善PCB钻孔毛刺的方法。
背景技术
在印制电路板(简称PCB)加工制造工序中,受材料、结构设计、线路设计、压制工艺与设备等诸多因素的影响,压制工序加工出来的PCB板会存在一定程度的变形,放置在平整的大理石平台上有着不同程度的翘曲形变。PCB板的翘曲形变对其钻孔加工有较大的影响,若PCB板较薄(3.0mm以下),钻孔加工时则通过适当加大压力脚的压力,可以改变PCB板钻孔位置的翘曲形变,使得PCB板与垫板紧贴,钻孔不会产生过大的毛刺;若PCB板较厚(3.0mm以上),压力脚的压力难以改变PCB板的翘曲形变,PCB板与垫板无法紧贴而存在间隙,钻孔易产生较大的毛刺及其它钻孔问题,其过大的毛刺会影响到后工序加工,严重的甚至会影响PCB板成品品质而报废。总之,PCB板的翘曲形变或表面的平整性不足,在压力脚的压力无法改变的情况,钻孔加工时易产生毛刺等钻孔问题。
现有对PCB板钻孔加工中产生的毛刺,小的毛刺一般经去毛刺机刷磨即可;过大的毛刺须先经人工处理,再经去毛刺机刷磨,但有时存在毛刺去除不尽而刷磨时将毛刺刷入孔内,严重影响后工序加工和成品品质。
因此,现有技术还有待于改进和发展。
发明内容
鉴于上述现有技术的不足,本发明的目的在于提供一种改善PCB钻孔毛刺的方法,旨在解决现有PCB板钻孔加工中易产生毛刺的问题。
本发明的技术方案如下:
一种改善PCB钻孔毛刺的方法,其中,在与垫板接触的PCB板面涂覆一层树脂,树脂固化后,用于PCB钻孔。
所述的改善PCB钻孔毛刺的方法,其中,涂覆的树脂固化后的硬度达到5B以上,粘结力达到百格法测试2mm95%以上。
所述的改善PCB钻孔毛刺的方法,其中,所述树脂为环氧及其改性树脂、聚氨酯及其改性树脂、丙烯酸酯及其改性树脂、不饱和聚酯及其改性树脂中的一种或多种树脂的混合物。
所述的改善PCB钻孔毛刺的方法,其中,涂覆的树脂的厚度为20-250μm。
所述的改善PCB钻孔毛刺的方法,其中,涂覆的方式为滚涂、刮涂、喷涂或淋涂。
所述的改善PCB钻孔毛刺的方法,其中,钻孔后,树脂层采用退洗液退洗的方式去除。
有益效果:本发明通过在翘曲变形大的PCB板金属面涂覆一层树脂,利用树脂固化后的高硬度、强粘结力的特性,抑制钻孔毛刺的产生,同时降低了PCB板钻孔加工品质对PCB板翘曲变形和垫板质量的要求。
具体实施方式
本发明提供一种改善PCB钻孔毛刺的方法,为使本发明的目的、技术方案及效果更加清楚、明确,以下对本发明进一步详细说明。应当理解,此处所描述的具体实施例仅仅用以解释本发明,并不用于限定本发明。
本发明提供一种改善PCB钻孔毛刺的方法,其中,在与垫板接触的PCB板面涂覆一层树脂,树脂固化后,用于PCB钻孔。由于PCB板和垫板都是板状刚性体,在钻孔加工时,PCB板的翘曲形变会使得其难以与垫板紧贴,产生的间隙易导致钻孔毛刺生成。本发明通过在与垫板接触的PCB板面涂覆一层树脂,利用树脂固化后的高硬度、强粘结力的特性,抑制钻孔毛刺的产生,钻孔后再将树脂层采用特殊的方法去除即可。这是因为树脂的强粘结力利于固化后树脂与PCB板金属面强力粘结,钻孔时树脂层不易与金属面分离;而高硬度则利于树脂层在钻孔钻针入钻及毛刺产生时难以发生形变,达到抑制毛刺的效果。
优选地,本发明涂覆的树脂固化后的硬度达到5B以上,粘结力达到百格法测试2mm95%以上。本发明利用树脂固化后的高硬度、强粘结力的特性,抑制钻孔毛刺的产生。
优选地,本发明涂覆的树脂的厚度可以为20-250μm。这是因为树脂涂覆厚度不能太薄,太薄会影响树脂与金属面的粘结力及树脂对毛刺的抑制强度等;树脂涂覆厚度亦不能太厚,太厚会增加制品的成本、涂覆或去膜工艺难度等。更优选地,本发明涂覆的树脂的厚度为50-200μm,以进一步提高树脂对毛刺的抑制强度。
优选地,本发明所述树脂可以为但不限于环氧及其改性树脂、聚氨酯及其改性树脂、丙烯酸酯及其改性树脂、不饱和聚酯及其改性树脂中的一种或多种树脂的混合物。上述树脂涂覆于PCB板面固化后,树脂层的硬度均能达到5B以上,粘结力达到百格法测试2mm95%以上,实现抑制钻孔毛刺的效果。
优选地,本发明涂覆的方式可以为但不限于滚涂、刮涂、喷涂或淋涂等。
优选地,本发明所述树脂的固化条件可依据选择树脂的自身固化条件和PCB工艺条件来调整,更优选的固化温度为150~180℃,时间为10~60min。
优选地,钻孔后,树脂层采用退洗液高温退洗方式去除。退洗液包括但不限于碱液、氨水、自来水及其它特制退洗液等,退洗温度一般为45℃~90℃。
下面通过具体实施例对本发明进行详细说明。
实施例1
选用一种改性环氧树脂为主树脂,搭配辅助材料及助剂(为现有技术,在此不再赘述),控制一定的粘度约2000~50000mpa.s,在翘曲变形大的PCB板金属面上,分别辊涂涂覆50um、100um、150um厚度的树脂层,175℃的高温烘烤50min。涂覆有改性环氧树脂混合物的PCB板钻孔后,在85℃下采用强碱溶液退洗120min。
实施例2
选用一种聚氨酯树脂为主树脂,搭配辅助材料及助剂(为现有技术,在此不再赘述),控制一定的粘度约2000~50000mpa.s,在翘曲变形大PCB板金属面上,分别喷涂涂覆50um、100um、150um厚度的树脂层,160℃的高温烘烤50min。涂覆有聚氨酯树脂混合物的PCB板钻孔后,在80℃下采用弱碱溶液退洗20min。
将上述涂覆有树脂的PCB板进行钻孔测试,实验结果如下:
从上述实验结果来看,翘曲变形大的PCB板金属面涂覆一层高硬度、强粘结力的树脂,利用树脂固化后的高硬度、强粘结力的特性,有效达到了抑制毛刺的效果。
综上所述,本发明的一种改善PCB钻孔毛刺的方法,本发明通过在翘曲变形大的PCB板金属面涂覆一层高硬度、强粘结力的树脂,利用树脂固化后的高硬度、强粘结力的特性,抑制钻孔毛刺的产生,同时降低了PCB板钻孔加工品质对PCB板翘曲变形和垫板质量的要求,钻孔后再将树脂层采用退洗液高温退洗的方法去除即可。
应当理解的是,本发明的应用不限于上述的举例,对本领域普通技术人员来说,可以根据上述说明加以改进或变换,所有这些改进和变换都应属于本发明所附权利要求的保护范围。
Claims (6)
1.一种改善PCB钻孔毛刺的方法,其特征在于,在与垫板接触的PCB板面涂覆一层树脂,树脂固化后,用于PCB钻孔。
2.根据权利要求1所述的改善PCB钻孔毛刺的方法,其特征在于,涂覆的树脂固化后的硬度达到5B以上,粘结力达到百格法测试2mm95%以上。
3.根据权利要求1所述的改善PCB钻孔毛刺的方法,其特征在于,所述树脂为环氧及其改性树脂、聚氨酯及其改性树脂、丙烯酸酯及其改性树脂、不饱和聚酯及其改性树脂中的一种或多种树脂的混合物。
4.根据权利要求1所述的改善PCB钻孔毛刺的方法,其特征在于,涂覆的树脂的厚度为20-250μm。
5.根据权利要求1所述的改善PCB钻孔毛刺的方法,其特征在于,涂覆的方式为滚涂、刮涂、喷涂或淋涂。
6.根据权利要求1所述的改善PCB钻孔毛刺的方法,其特征在于,钻孔后,树脂层采用退洗液退洗的方式去除。