CN105714560A - Acid-resisting finishing method for chinlon fabric - Google Patents
Acid-resisting finishing method for chinlon fabric Download PDFInfo
- Publication number
- CN105714560A CN105714560A CN201610144376.9A CN201610144376A CN105714560A CN 105714560 A CN105714560 A CN 105714560A CN 201610144376 A CN201610144376 A CN 201610144376A CN 105714560 A CN105714560 A CN 105714560A
- Authority
- CN
- China
- Prior art keywords
- parts
- fabric
- acid
- acidproof
- sorting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an acid-resisting finishing method for chinlon fabric. The method comprises the following steps that water is firstly added to a finishing agent to be prepared into impregnation liquid, the fabric is placed in the impregnation liquid for padding, and the liquid detention rate ranges from 45% to 70%; finally, washing is carried out two or three times, and dewatering and drying are carried out. The finishing agent is prepared from, by weight, 50-60 parts of water, 14-18 parts of sodium polystyrenesulfonate, 3-10 parts of plifenate, 3-6 parts of diphenol propane, 5-8 parts of soap powder, 10-14 parts of licorice powder, 1-6 parts of acrylamide, 3-6 parts of butanol, 3-6 parts of methyl siloxane, 3-6 parts of chitosan, 1-5 parts of glycerol monostearate, 2-8 parts of fatty alcohol-polyoxyethylene ether, 3-6 parts of vinyltriethoxysilane and 1-8 parts of cinnamyl aldehyde. According to the finishing method, the chinlon fabric can be prevented from being wetted or permeated by acid liquor, erosion of strong acid can be resisted, and the advantages of being breathable, comfortable, soft, light, easy to wash and the like are achieved.
Description
Technical field
The invention belongs to textile technology field, be specifically related to a kind of acidproof arrangement side of nylon fabric
Method.
Technical background
Chinlon is exactly the nylon fiber generally said, nylon fabric pulls into nylon material the thinnest
Fiber, then weave cotton cloth, the concrete formal name used at school of nylon is called polyamide, is broad-spectrum work
Engineering plastics.Polyamide (PA) is the resin that DuPont is developed for fiber at first,
Industrialization is realized in nineteen thirty-nine.Start exploitation the 1950's and produce injection-molded item,
Meet downstream industry goods lightweight with substituted metal, reduce the requirement of cost.The kind of PA
Various, there are PA6, PA66, PAll, PAl2, PA46, PA610, PA612, PAl010 etc.,
And a lot of new varieties such as the semi-aromatic nylon PA6T developed in recent years and extraordinary nylon.Root
Material according to nylon is different, it can be common that chinlon 6 and chinlon 66, namely with nylon 6 He
The fiber that nylon66 fiber is made.
Nylon fabric is famous with the wearability of its excellence, and it is not only down jackets, anorak dress material
Optimum selection, and often and other fiber blend or intertexture, to improve intensity and the heavily fortified point of fabric
Fastness.The anti-wear performance of nylon fabric occupies first of each kind fabric, knits than other fiber of like product
Much higher times of thing, therefore, its ruggedness is splendid.The hygroscopicity of nylon fabric is knitted at synthetic fibers
Belonging to preferable kind in thing, the clothing therefore made of chinlon are more comfortable and easy to wear than terylene clothes.Brocade
Synthetic fibre fabric belongs to light fabric, after being only listed in polypropylene, acrylic fabric in synthetic fabrics,
Therefore, it is suitable for making anorak, water clothes etc..
Along with the quickening of economic construction paces, the range of application of acid and consumption are also constantly expanding,
According to incompletely statistics, current China three acid (sulphuric acid, nitric acid, hydrochloric acid) Year's consumption reaches 300,000
About Dun, range relates to oil, chemical industry, machinery, plating, nonferrous smelting, accumulator
Etc. industry.During sour production, transporting, store and use, it is corrosive because of it and soaks
Property thoroughly, the staff contacted with acid need to wear acid-proof protective garment, to ensure the person and to produce peace
Entirely.If the acid resistance of working clothing is poor, when by acid liquid corrosion, working clothing can be produced
Certain corrosion, serious may erode to employee.Nylon fabric has good hygroscopicity
And wearability, but its acid resistance is the highest, limits its range of application.The most how to improve brocade
The acid resistance of synthetic fibre fabric is the problem that current textile technology field needs solution badly.
Summary of the invention
To achieve these goals, the invention provides a kind of acidproof method for sorting of nylon fabric.
It is an object of the invention to be achieved through the following technical solutions:
A kind of acidproof method for sorting of nylon fabric, the method has following steps: first by finishing agent
Add water and be configured to impregnation liquid, then fabric is put in impregnation liquid and pad, pick-up 45-70%,
Finally washing 2-3 time, last dewatered drying；Described finishing agent is by following parts by weight
Component forms: water 50-60 part, kayexalate 14-18 part, acetofenate 3-10
Part, diphenol propane 3-6 part, soap powder 5-8 part, Radix Glycyrrhizae powder 10-14 part, acrylamide
1-6 part, butanol 3-6 part, methyl cyclosiloxane 3-6 part, chitosan 3-6 part, stearic acid
Monoglyceride 1-5 part, fatty alcohol-polyoxyethylene ether 2-8 part, VTES
3-6 part, cinnamic aldehyde 1-8 part.
The preparation technology of finishing agent is common process, skillfully slaps for those of ordinary skill in the art
Hold.
Described fabric impregnates 20-30 minute at 50-85 DEG C.
Described drying temperature is 50-60 DEG C, and the time is 3 minutes.
The concentration of described aqueous solution is 800-1500ppm.
The method have the advantages that the method for sorting that the present invention provides can prevent chinlon from knitting
Thing, by the moistening of acid solution and infiltration, can be resisted the erosion of strong acid, and have concurrently ventilative comfortable, soft
The advantages such as soft light, uncomplicated laundering.
Detailed description of the invention
The following stated is only the preferred embodiments of the present invention, is not limited to the present invention,
Although the present invention being described in detail with reference to previous embodiment, for the technology of this area
For personnel, the technical scheme described in foregoing embodiments still can be modified by it,
Or wherein portion of techniques feature is carried out equivalent.All the spirit and principles in the present invention it
In, any modification, equivalent substitution and improvement etc. made, should be included in the protection of the present invention
Within the scope of.
Embodiment 1
A kind of acidproof method for sorting of nylon fabric, it has following steps: first added water by finishing agent
It is configured to impregnation liquid, then fabric is put in impregnation liquid and pad, pick-up 45-70%,
Rear washing 2-3 time, last dewatered drying；Described finishing agent is by the group of following parts by weight
It is grouped into: 50 parts of water, kayexalate 14 parts, acetofenate 3 parts, diphenylol
3 parts of propane, soap powder 5 parts, Radix Glycyrrhizae powder 10 parts, acrylamide 1 part, 3 parts of butanol, first
Cyclosiloxane 3 parts, chitosan 3 parts, glycerol monostearate 1 part, fatty alcohol polyoxy second
2 parts of alkene ether, VTES 3 parts, cinnamic aldehyde 1 part.
Described fabric impregnates 20-30 minute at 50-85 DEG C.
Described drying temperature is 50-60 DEG C, and the time is 3 minutes.
The concentration of described aqueous solution is 800-1500ppm.
Embodiment 2
A kind of acidproof method for sorting of nylon fabric, it has following steps: first added water by finishing agent
It is configured to impregnation liquid, then fabric is put in impregnation liquid and pad, pick-up 45-70%,
Rear washing 2-3 time, last dewatered drying；Described finishing agent is by the group of following parts by weight
It is grouped into: 60 parts of water, kayexalate 18 parts, acetofenate 10 parts, diphenol
6 parts of base propane, soap powder 8 parts, Radix Glycyrrhizae powder 14 parts, acrylamide 6 parts, 6 parts of butanol,
Methyl cyclosiloxane 6 parts, chitosan 6 parts, glycerol monostearate 5 parts, fatty alcohol polyoxy
Vinyl Ether 8 parts, VTES 6 parts, cinnamic aldehyde 8 parts.
Described fabric impregnates 20-30 minute at 50-85 DEG C.
Described drying temperature is 50-60 DEG C, and the time is 3 minutes.
The concentration of described aqueous solution is 800-1500ppm.
Embodiment 3
A kind of acidproof method for sorting of nylon fabric, it has following steps: first added water by finishing agent
It is configured to impregnation liquid, then fabric is put in impregnation liquid and pad, pick-up 45-70%,
Rear washing 2-3 time, last dewatered drying；Described finishing agent is by the group of following parts by weight
It is grouped into: 55 parts of water, kayexalate 16 parts, acetofenate 6 parts, diphenylol
5 parts of propane, soap powder 6 parts, Radix Glycyrrhizae powder 12 parts, acrylamide 4 parts, 5 parts of butanol, first
Cyclosiloxane 4 parts, chitosan 5 parts, glycerol monostearate 3 parts, fatty alcohol polyoxy second
5 parts of alkene ether, VTES 5 parts, cinnamic aldehyde 5 parts.
Described fabric impregnates 20-30 minute at 50-85 DEG C.
Described drying temperature is 50-60 DEG C, and the time is 3 minutes.
The concentration of described aqueous solution is 800-1500ppm.
Claims (4)
1. the acidproof method for sorting of nylon fabric, it is characterised in that the step of described method is such as
Under: first finishing agent is added water and be configured to impregnation liquid, then fabric is put in impregnation liquid and pad,
Pick-up 45-70%, finally washing 2-3 time, last dewatered drying；Described finishing agent
Be made up of the component of following parts by weight: water 50-60 part, kayexalate 14-18 part,
Acetofenate 3-10 part, diphenol propane 3-6 part, soap powder 5-8 part, Radix Glycyrrhizae powder 10-14
Part, acrylamide 1-6 part, butanol 3-6 part, methyl cyclosiloxane 3-6 part, chitosan
3-6 part, glycerol monostearate 1-5 part, fatty alcohol-polyoxyethylene ether 2-8 part, vinyl
Triethoxysilane 3-6 part, cinnamic aldehyde 1-8 part.
The most according to claim 1, a kind of acidproof method for sorting of nylon fabric, its feature exists
In: described fabric impregnates 20-30 minute at 50-85 DEG C.
The most according to claim 1, a kind of acidproof method for sorting of nylon fabric, its feature exists
In: described drying temperature is 50-60 DEG C, and the time is 3 minutes.
The most according to claim 1, a kind of acidproof method for sorting of nylon fabric, its feature exists
In: the concentration of described aqueous solution is 800-1500ppm.