CN105713473A - 一种皮革涂饰剂 - Google Patents
一种皮革涂饰剂 Download PDFInfo
- Publication number
- CN105713473A CN105713473A CN201410730559.XA CN201410730559A CN105713473A CN 105713473 A CN105713473 A CN 105713473A CN 201410730559 A CN201410730559 A CN 201410730559A CN 105713473 A CN105713473 A CN 105713473A
- Authority
- CN
- China
- Prior art keywords
- parts
- leather
- water
- acrylamide
- amount
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于皮革加工技术领域，具体是一种皮革涂饰剂，它由下述重量份原料组成：丙烯酸2-6，丙烯腈50-80，丙烯酸丁酯60-80，苯乙烯1-5，丙烯酰胺10-40，EDTA0.1-0.5，丙烯酰胺10-30，过硫酸钾0.1-0.3，浓氨水0.01-0.1，十二烷基硫酸钠0.5-2，水80-120，甲醛0.5-1.5；制备时，将水和2/3量的乳化剂加入反应釜内，升温至70-90℃，再滴加1/3量的乳化剂、引发剂、混合单体，控制聚合温度为80-85℃，在1h内滴加完毕，于90℃下保温2-3小时，冷却至45-50℃，加氨水调节pH至5-6即可；本发明皮革涂饰剂能够适用于各种皮革的涂饰，涂饰后的皮革光泽柔和自然，手感丰满滋润，能提高皮革表面的耐摩擦能力。
Description
技术领域
本发明皮革加工技术领域，具体是一种皮革涂饰剂。
背景技术
丙烯酸树脂是目前世界上使用量最大的一类皮革涂饰剂材料，年产量占皮革涂饰剂的70%左顺，从生产成本、工艺过程及综合性能诸方面来看，丙烯酸树脂作为涂饰材料较之其它化工材料可谓优点多多，但世无完物，其唯一缺陷就是热粘冷脆，使其在使用上受到气候条件的限制。1987年以来，美国RohmandHass公司相继研发出新产品，第二代丙烯酸树脂(sGA)，在热粘冷脆方面有了突破性进展。随后我国在丙烯酸材料改性面也陆续取得了一定成果。但其研制方法大都是引入官能单体与丙烯酸单体进行多元共聚、接枝共聚、或外加交联剂，使线性结构变为网状结构，从而提高涂膜的耐热耐寒性能，所采用的技术手段停留在分子结构的层面上，热粘冷脆性能虽有改善，但仍显不足。因此，研发一种能够有效改善上述问题的丙烯酸树脂涂饰剂十分必要。
发明内容
本发明的目的就是针对目前丙烯酸树脂在存在上述诸多缺陷，导致其不适宜在寒冷地方使用的问题，提供一种皮革涂饰剂，本发明的丙烯酸皮革涂饰剂可用于寒冷的北方使用。
本发明的一种皮革涂饰剂，由下述重量份原料组成：
丙烯酸2-6丙烯腈50-80
丙烯酸丁酯60-80苯乙烯1-5
丙烯酰胺10-40EDTA0.1-0.5
丙烯酰胺10-30过硫酸钾0.1-0.3
浓氨水0.01-0.1十二烷基硫酸钠0.5-2
水80-120甲醛0.5-1.5；
制备时，将水和2/3量的乳化剂加入反应釜内，升温至70-90℃，再滴加1/3量的乳化剂、引发剂、混合单体，控制聚合温度为80-85℃，在1h内滴加完毕，于90℃下保温2-3小时，冷却至45-50℃，加氨水调节pH至5-6即可。
本发明皮革涂饰剂水溶性很好，乳液稳定，长期存放不分层、无浮蜡，能够适用于各种皮革的涂饰，涂饰后的皮革光泽柔和自然，手感丰满滋润，能提高皮革表面的耐摩擦能力。
具体实施方式
实施例1
一种皮革涂饰剂，由下述重量份原料组成：
丙烯酸4丙烯腈55
丙烯酸丁酯70苯乙烯3
丙烯酰胺25EDTA0.3
丙烯酰胺20过硫酸钾0.2
浓氨水0.08十二烷基硫酸钠1.5
水120甲醛1.2；
制备时，将水和2/3量的乳化剂加入反应釜内，升温至85℃，再滴加1/3量的乳化剂、引发剂、混合单体，控制聚合温度为85℃，在1h内滴加完毕，于90℃下保温2小时，冷却至45℃，加氨水调节pH至5即可。
实施例2
一种皮革涂饰剂，由下述重量份原料组成：
丙烯酸5丙烯腈60
丙烯酸丁酯70苯乙烯3
丙烯酰胺25EDTA0.2
丙烯酰胺22过硫酸钾0.15
浓氨水0.05十二烷基硫酸钠0.1
水100甲醛1.0；
制备时，将水和2/3量的乳化剂加入反应釜内，升温至80℃，再滴加1/3量的乳化剂、引发剂、混合单体，控制聚合温度为82℃，在1h内滴加完毕，于90℃下保温3小时，冷却至50℃，加氨水调节pH至6即可。
Claims (1)
1.一种皮革涂饰剂，其特征在于由下述重量份原料组成：
丙烯酸2-6丙烯腈50-80
丙烯酸丁酯60-80苯乙烯1-5
丙烯酰胺10-40EDTA0.1-0.5
丙烯酰胺10-30过硫酸钾0.1-0.3
浓氨水0.01-0.1十二烷基硫酸钠0.5-2
水80-120甲醛0.5-1.5；
制备时，将水和2/3量的乳化剂加入反应釜内，升温至70-90℃，再滴加1/3量的乳化剂、引发剂、混合单体，控制聚合温度为80-85℃，在1h内滴加完毕，于90℃下保温2-3小时，冷却至45-50℃，加氨水调节pH至5-6即可。