CN105713427A - Coating for metal foil - Google Patents
Coating for metal foil Download PDFInfo
- Publication number
- CN105713427A CN105713427A CN201610171831.4A CN201610171831A CN105713427A CN 105713427 A CN105713427 A CN 105713427A CN 201610171831 A CN201610171831 A CN 201610171831A CN 105713427 A CN105713427 A CN 105713427A
- Authority
- CN
- China
- Prior art keywords
- parts
- chlorite
- bauxite
- clay
- forming coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A coating for metal foil is prepared from chlorite, water glass, clay, cellulose nitrate, pentaerythritol, polyamide resin liquid, ethidene diamine, nitrocotton liquid, tricresyl phosphate, acetic ether, methylbenzene, alkaline silica gel and bauxite. The paint for the metal foil is bright in color and high in tinting strength, the expressive force reaches up to 91% to 95%, and the coating is completely dried within 0.9 s, and is low in cost.
Description
Technical field
The present invention relates to a kind of metal paint, particularly relate to a kind of metal forming coating.
Background technology
Chlorite chlorite family layer silicate mineral.Commonly called chlorite,
Refer to the mineral species of predominantly Mg and Fe, i.e. clinochlore, chamosite etc..It is that some are made
The metamorphic rock of rock mineral.Mafite in igneous rock such as biotite, hornblend, pyroxene etc. exist
It is easily formed chlorite under low-temperature water heating effect.Its color is that the depth is different with the number of iron-holder
Green.Glassy lustre is to matt, and cleavage surface can be in pearly luster.In Zhu Yaoshi, Low Temperature Thermal
The product of liquid effect, epimetamorphism and deposition.
The main output of chlorite protolith, among the place deep in the mountains of Upper Reaches of Dadu River, is by green
The cobble that basalt is formed, its hardness is about 2-2.5, and peak green to bottle green, in grain
Shape, tabular, bulk, owing to rock parcel is grown, be most easily formed various form.
Along with social city, technicalization, the development of hommization, metal has obtained flourishing sending out
Opening up, increasing metal species presses close to consumer's life etc., and the thing followed is metal paint
The increase of usage amount and metal paint water proofing property is poor, be dried slowly, glossiness is low and representability is low etc.
Showing of problem, and popularizing along with humanity concept, and the composition of novel harmonious society, if
Count the metal forming coating that a kind of color and luster is good, representability is excellent to be very important.
Summary of the invention
Solve the technical problem that: non-watertight for above-mentioned metal paint, be dried slow, glossiness is low
The shortcoming such as poor with representability, it is provided that a kind of metal forming coating.
Technical scheme: a kind of metal forming coating, its composition with mass fraction representation is:
100 parts of chlorite, waterglass 4.5-6.5 part, clay 3-5 part, NC Nitroncellulose 4-8 part,
Tetramethylolmethane 20-60 part, butyl acetate 10-50 part, ethylenediamine 0.3-0.7 part, nitrocotton
Liquid 5-25 part, tricresyl phosphate 2-8 part, ethyl acetate 1-5 part, toluene 10-30 part,
Alkaline silica sol 8-12 part, bauxite 4-16 part.
As a preferred technical solution of the present invention: described metal forming coating composition with
Mass fraction representation is: 100 parts of chlorite, waterglass 5-6 part, clay 3.5-4.5 part,
NC Nitroncellulose 5-7 part, tetramethylolmethane 30-50 part, butyl acetate 20-40 part, ethylenediamine
0.4-0.6 part, nitrocotton liquid 10-20 part, tricresyl phosphate 3-7 part, ethyl acetate 2-4
Part, toluene 15-25 part, alkaline silica sol 9-11 part, bauxite 6-14 part.
As a preferred technical solution of the present invention: described metal forming coating composition with
Mass fraction representation is: 100 parts of chlorite, waterglass 5 parts, clay 3.5 parts, nitro
Cellulose 5 parts, tetramethylolmethane 30 parts, butyl acetate 20 parts, ethylenediamine 0.4 part, nitrification
Cotton liquid 10 parts, tricresyl phosphate 3 parts, ethyl acetate 2 parts, toluene 15 parts, alkalescence silicon
Colloidal sol 9 parts, bauxite 6 parts.
As a preferred technical solution of the present invention: described metal forming coating composition with
Mass fraction representation is: 100 parts of chlorite, waterglass 6 parts, clay 4.5 parts, nitro
Cellulose 7 parts, tetramethylolmethane 50 parts, butyl acetate 40 parts, ethylenediamine 0.6 part, nitrification
Cotton liquid 20 parts, tricresyl phosphate 7 parts, ethyl acetate 4 parts, toluene 25 parts, alkalescence silicon
Colloidal sol 11 parts, bauxite 14 parts.
As a preferred technical solution of the present invention: described metal forming coating composition with
Mass fraction representation is: 100 parts of chlorite, waterglass 5.5 parts, clay 4 parts, nitro
Cellulose 6 parts, tetramethylolmethane 40 parts, butyl acetate 30 parts, ethylenediamine 0.5 part, nitrification
Cotton liquid 15 parts, tricresyl phosphate 5 parts, ethyl acetate 3 parts, toluene 20 parts, alkalescence silicon
Colloidal sol 10 parts, bauxite 10 parts.
Beneficial effect: the metal forming coating that the present invention provides, metal is with painting lovely luster,
Color power is strong, and representability is up to 91%-95%, absolutely dry and with low cost in 0.9s, viscosity 15-25s.
Detailed description of the invention
Illustrate present disclosure the most in further detail.
Embodiment 1:
A kind of metal forming coating, its composition with mass fraction representation is: chlorite
100 parts, waterglass 4.5 parts, clay 3 parts, NC Nitroncellulose 4 parts, tetramethylolmethane 20
Part, butyl acetate 10 parts, ethylenediamine 0.3 part, nitrocotton liquid 5 parts, tricresyl phosphate
2 parts, ethyl acetate 1 part, toluene 10 parts, alkaline silica sol 8 parts, bauxite 4 parts.
By nitrocotton liquid, alkaline silica sol, ethyl acetate, bauxite and 2/3rds mass parts
Chlorite load in reactor, with reflux condenser on reactor, open reflux condenser
Start stirring after cooling water, be subsequently adding polyamide liquid, tetramethylolmethane and ethylenediamine, rise
Temperature stops heating after 60 DEG C, continues stirring, cools the temperature to 40 DEG C after insulation 3h;Then
Add waterglass, clay and NC Nitroncellulose to stir, add tricresyl phosphate and toluene;
It is eventually adding remaining chlorite, after stirring, filters and i.e. obtain metal forming coating.
Metal is bright in colour with paint, strong coloring force, and representability is up to 91%, in 0.9s absolutely dry and
With low cost, viscosity 15s.
Embodiment 2:
A kind of metal forming coating, its composition with mass fraction representation is: chlorite
100 parts, waterglass 6.5 parts, clay 5 parts, NC Nitroncellulose 8 parts, tetramethylolmethane 60
Part, butyl acetate 50 parts, ethylenediamine 0.7 part, nitrocotton liquid 25 parts, tricresyl phosphate
8 parts, ethyl acetate 5 parts, toluene 30 parts, alkaline silica sol 12 parts, bauxite 16 parts.
By nitrocotton liquid, alkaline silica sol, ethyl acetate, bauxite and 2/3rds mass parts
Chlorite load in reactor, with reflux condenser on reactor, open reflux condenser
Start stirring after cooling water, be subsequently adding polyamide liquid, tetramethylolmethane and ethylenediamine, rise
Temperature stops heating after 60 DEG C, continues stirring, cools the temperature to 40 DEG C after insulation 3h;Then
Add waterglass, clay and NC Nitroncellulose to stir, add tricresyl phosphate and toluene;
It is eventually adding remaining chlorite, after stirring, filters and i.e. obtain metal forming coating.
Metal is bright in colour with paint, strong coloring force, and representability is up to 93%, in 0.9s absolutely dry and
With low cost, viscosity 25s.
Embodiment 3:
A kind of metal forming coating, its composition with mass fraction representation is: chlorite
100 parts, waterglass 5.5 parts, clay 4 parts, NC Nitroncellulose 6 parts, tetramethylolmethane 40
Part, butyl acetate 30 parts, ethylenediamine 0.5 part, nitrocotton liquid 15 parts, tricresyl phosphate
5 parts, ethyl acetate 3 parts, toluene 20 parts, alkaline silica sol 10 parts, bauxite 10 parts.
By nitrocotton liquid, alkaline silica sol, ethyl acetate, bauxite and 2/3rds mass parts
Chlorite load in reactor, with reflux condenser on reactor, open reflux condenser
Start stirring after cooling water, be subsequently adding polyamide liquid, tetramethylolmethane and ethylenediamine, rise
Temperature stops heating after 60 DEG C, continues stirring, cools the temperature to 40 DEG C after insulation 3h;Then
Add waterglass, clay and NC Nitroncellulose to stir, add tricresyl phosphate and toluene;
It is eventually adding remaining chlorite, after stirring, filters and i.e. obtain metal forming coating.
Metal is bright in colour with paint, strong coloring force, and representability is up to 95%, in 0.9s absolutely dry and
With low cost, viscosity 20s.
Above-described embodiment is only intended to be illustrated present disclosure rather than limit, because of
This any change in the implication suitable with claims of the present invention and scope, all should
It is considered to be included within the scope of the claims.
Claims (5)
1. a metal forming coating, it is characterised in that: its composition represents with mass fraction
Method is: 100 parts of chlorite, waterglass 4.5-6.5 part, clay 3-5 part, NC Nitroncellulose
4-8 part, tetramethylolmethane 20-60 part, butyl acetate 10-50 part, ethylenediamine 0.3-0.7 part,
Nitrocotton liquid 5-25 part, tricresyl phosphate 2-8 part, ethyl acetate 1-5 part, toluene 10-30
Part, alkaline silica sol 8-12 part, bauxite 4-16 part.
A kind of metal forming coating the most according to claim 1, it is characterised in that: its group
One-tenth composition with mass fraction representation is: 100 parts of chlorite, waterglass 5-6 part, clay
3.5-4.5 part, NC Nitroncellulose 5-7 part, tetramethylolmethane 30-50 part, butyl acetate 20-40
Part, ethylenediamine 0.4-0.6 part, nitrocotton liquid 10-20 part, tricresyl phosphate 3-7 part,
Ethyl acetate 2-4 part, toluene 15-25 part, alkaline silica sol 9-11 part, bauxite 6-14
Part.
A kind of metal forming coating the most according to claim 1, it is characterised in that: its group
One-tenth composition with mass fraction representation is: 100 parts of chlorite, waterglass 5 parts, clay 3.5
Part, NC Nitroncellulose 5 parts, tetramethylolmethane 30 parts, butyl acetate 20 parts, ethylenediamine 0.4
Part, nitrocotton liquid 10 parts, tricresyl phosphate 3 parts, ethyl acetate 2 parts, toluene 15 parts,
Alkaline silica sol 9 parts, bauxite 6 parts.
A kind of metal forming coating the most according to claim 1, it is characterised in that: its group
One-tenth composition with mass fraction representation is: 100 parts of chlorite, waterglass 6 parts, clay 4.5
Part, NC Nitroncellulose 7 parts, tetramethylolmethane 50 parts, butyl acetate 40 parts, ethylenediamine 0.6
Part, nitrocotton liquid 20 parts, tricresyl phosphate 7 parts, ethyl acetate 4 parts, toluene 25 parts,
Alkaline silica sol 11 parts, bauxite 14 parts.
A kind of metal forming coating the most according to claim 1, it is characterised in that: its group
One-tenth composition with mass fraction representation is: 100 parts of chlorite, waterglass 5.5 parts, clay 4
Part, NC Nitroncellulose 6 parts, tetramethylolmethane 40 parts, butyl acetate 30 parts, ethylenediamine 0.5
Part, nitrocotton liquid 15 parts, tricresyl phosphate 5 parts, ethyl acetate 3 parts, toluene 20 parts,
Alkaline silica sol 10 parts, bauxite 10 parts.