CN105712666A - Vetrified tiles high-efficiency purifying clay - Google Patents
Vetrified tiles high-efficiency purifying clay Download PDFInfo
- Publication number
- CN105712666A CN105712666A CN201410398176.7A CN201410398176A CN105712666A CN 105712666 A CN105712666 A CN 105712666A CN 201410398176 A CN201410398176 A CN 201410398176A CN 105712666 A CN105712666 A CN 105712666A
- Authority
- CN
- China
- Prior art keywords
- clay
- vitrified tile
- vetrified
- tiles
- bonding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a vetrified tiles high-efficiency purifying clay, which belongs to the technical field of a building material. An application method comprises the following steps: mixing a component A and a component B according to a weight ratio of 1: 0.5, uniformly stirring the components, and directly smearing the components on a back side of the vetrified tiles or a bonding base layer for bonding the vetrified tiles. The vetrified tiles high-efficiency purifying clay can resist, alleviate and eliminate various stress impact, permanent and firm bonding between the vetrified tiles and the bonding clay and the bonding base layer can be realized. The zeolite powder, diatomite and meerschaum fiber in the clay can absorb, decompose, and eliminate formaldehyde, indoor peculiar smell and harmful substances in air. The purifying clay has the effects for regulating indoor humidity and improving living environment.
Description
Technical field
The invention belongs to building material technical field, especially relate to a kind of vitrified tile high-efficient purification clay, specifically double-component vitrified tile bonding cement with purification air quality performance of a kind of flexibility and preparation method thereof.
Background technology
Vitrified tile, as a kind of important ornament materials, is widely used in the indoor and outdoor decoration engineerings such as kitchen and toilet wall ground.The densification of vitrified tile quality, the rare hole in surface, interface is smooth, water absorption rate is low, " can lock " firmly cement mortar almost without micropore or pit.Adding binding material by moisture expansion and drying shrinkage, expand with heat and contract with cold, curing shrinkage, constantly impacting of construction vibrations iso-stress makes to exist between basic unit, tack coat, vitrified tile very big interaction force.Common cement mortar or one-component binding agent are difficult to infiltration attachment and are difficult to be formed effectively firmly mortar interlocking mechanism, and hollowing, the problem that comes off often have generation.It addition, the ornament materials being entirely free of formaldehyde at present is considerably less, people are to environmental protection, healthy attention and require more and more higher.So, invention one can overcome clears up swell-shrinking stress, it is achieved vitrified tile securely bonds and has the vitrified tile high-efficient purification clay and preparation method thereof purifying air quality performance is very necessary.
Summary of the invention
It is an object of the invention to overcome vitrified tile because of water absorption rate is low, interface is smooth and various stress causes vitrified tile to come off problem; there is provided a kind of flexibility be capable of vitrified tile secure bond and the vitrified tile high-efficient purification clay with the quality that purifies the air of a room; including component A and B component, described component A includes: cement, quartz sand, zeolite powder, kieselguhr, sepiolite fibre, hydroxypropyl methyl cellulose；Described B component includes: tap water, dispersant, acrylic emulsion, antibacterial, defoamer.
The present invention is realized by techniques below scheme, described component A is made up of by weight proportion following raw materials according, cement 30～50%, quartz sand 45～55%, zeolite powder 3～8%, kieselguhr 3～8%, sepiolite fibre 3～8%, hydroxypropyl methyl cellulose 0.1～0.3%.Described B component is made up of by weight proportion following raw materials according, tap water 30～60%, dispersant 0.3～0.5%, acrylic emulsion 40～60%, antibacterial 0.1～0.3%, defoamer 0.05～0.15%.
Measure cement, quartz sand, zeolite powder, kieselguhr, sepiolite fibre, hydroxypropyl methyl cellulose by aforementioned ratio, add in powder stirrer and be stirred, mix homogeneously, it is packaged into A material；
Measure tap water, dispersant, acrylic emulsion, antibacterial, defoamer by aforementioned ratio, add in liquid stirrers and be stirred, mix homogeneously, it is packaged into B material；
Carry out mixing, being uniformly mixing to obtain vitrified tile high-efficient purification clay according to the ratio of weight ratio 1: 0.5 by A material and B material.During use, the clay mixed is applied directly to the vitrified tile back side or bonding basic unit can carry out the stickup of vitrified tile.
Vitrified tile high-efficient purification clay of the present invention can be resisted, alleviates, eliminate various stress impact, it is achieved the permanent secure bond between vitrified tile and bonding cement and bonding basic unit.The harmful substance that zeolite powder contained by clay, kieselguhr, sepiolite fibre can absorb, decompose, eliminate in formaldehyde, foreign flavor indoors and air.And there is conditioning chamber humidity, improve the effect of living environment.
Detailed description of the invention
Embodiment 1
A kind of vitrified tile high-efficient purification clay; it is made up of two components of A, B; wherein component A is made up of by weight proportion following raw materials according, cement 30%, quartz sand 45.9%, zeolite powder 8%, kieselguhr 8%, sepiolite fibre 8%, hydroxypropyl methyl cellulose 0.1%.B component is made up of by weight proportion following raw materials according, tap water 49.3%, dispersant 0.4%, acrylic emulsion 50%, antibacterial 0.2%, defoamer 0.1%.
This vitrified tile high-efficient purification clay preparation method is: measure cement, quartz sand, zeolite powder, kieselguhr, sepiolite fibre, 6 kinds of dry mash mix homogeneously in powder stirrer of hydroxypropyl methyl cellulose respectively according to aforementioned weight ratio, is packaged into A material；Measure tap water, dispersant, acrylic emulsion, antibacterial, 5 kinds of liquid material mix homogeneously in liquid stirrers of defoamer respectively according to aforementioned weight ratio, be packaged into B material；
This vitrified tile high-efficient purification clay using method is: carry out mixing, stirring according to the ratio of weight ratio 1: 0.5 by A material and B material, the clay mixed is applied directly to the vitrified tile back side or bonding basic unit can carry out the stickup of vitrified tile.Carry out the vitrified tile pasted through this vitrified tile high-efficient purification clay, its adhesion strength is up to 2.3Mpa.
Embodiment 2
A kind of vitrified tile high-efficient purification clay; it is made up of two components of A, B; wherein component A is made up of by weight proportion following raw materials according, cement 35%, quartz sand 46.8%, zeolite powder 6%, kieselguhr 6%, sepiolite fibre 6%, hydroxypropyl methyl cellulose 0.2%.B component is made up of by weight proportion following raw materials according, tap water 39.3%, dispersant 0.3%, acrylic emulsion 60.2%, antibacterial 0.1%, defoamer 0.1%.
This vitrified tile high-efficient purification clay preparation method is: measure cement, quartz sand, zeolite powder, kieselguhr, sepiolite fibre, 6 kinds of dry mash mix homogeneously in powder stirrer of hydroxypropyl methyl cellulose respectively according to aforementioned weight ratio, is packaged into A material；Measure tap water, dispersant, acrylic emulsion, antibacterial, 5 kinds of liquid material mix homogeneously in liquid stirrers of defoamer respectively according to aforementioned weight ratio, be packaged into B material；
This vitrified tile high-efficient purification clay using method is: carry out mixing, stirring according to the ratio of weight ratio 1: 0.5 by A material and B material, the clay mixed is applied directly to the vitrified tile back side or bonding basic unit can carry out the stickup of vitrified tile.Carry out the vitrified tile pasted through this vitrified tile high-efficient purification clay, its adhesion strength is up to 2.7Mpa.
Embodiment 3
A kind of vitrified tile high-efficient purification clay; it is made up of two components of A, B; wherein component A is made up of by weight proportion following raw materials according, cement 40%, quartz sand 44.8%, zeolite powder 5%, kieselguhr 5%, sepiolite fibre 5%, hydroxypropyl methyl cellulose 0.2%.B component is made up of by weight proportion following raw materials according, tap water 29.1%, dispersant 0.5%, acrylic emulsion 70%, antibacterial 0.3%, defoamer 0.1%.
This vitrified tile high-efficient purification clay preparation method is: measure cement, quartz sand, zeolite powder, kieselguhr, sepiolite fibre, 6 kinds of dry mash mix homogeneously in powder stirrer of hydroxypropyl methyl cellulose respectively according to aforementioned weight ratio, is packaged into A material；Measure tap water, dispersant, acrylic emulsion, antibacterial, 5 kinds of liquid material mix homogeneously in liquid stirrers of defoamer respectively according to aforementioned weight ratio, be packaged into B material；
This vitrified tile high-efficient purification clay using method is: carry out mixing, stirring according to the ratio of weight ratio 1: 0.5 by A material and B material, the clay mixed is applied directly to the vitrified tile back side or bonding basic unit can carry out the stickup of vitrified tile.Carry out the vitrified tile pasted through this vitrified tile high-efficient purification clay, its adhesion strength is up to 3.2Mpa.
Claims (1)
1. a vitrified tile high-efficient purification clay, is made up of two kinds of components of A, B.Wherein component A is made up of by weight proportion following raw materials according, cement 30～50%, quartz sand 45～55%, zeolite powder 3～8%, kieselguhr 3～8%, sepiolite fibre 3～8%, hydroxypropyl methyl cellulose 0.1～0.3%.Wherein B component is made up of by weight proportion following raw materials according, tap water 30～60%, dispersant 0.3～0.5%, acrylic emulsion 40～60%, antibacterial 0.1～0.3%, defoamer 0.05～0.15%.
Measure cement, quartz sand, zeolite powder, kieselguhr, sepiolite fibre, hydroxypropyl methyl cellulose by aforementioned ratio, add in powder stirrer and be stirred, mix homogeneously, it is packaged into A material；
Measure tap water, dispersant, acrylic emulsion, antibacterial, defoamer by aforementioned ratio, add in liquid stirrers and be stirred, mix homogeneously, it is packaged into B material；
Carry out mixing, being uniformly mixing to obtain vitrified tile high-efficient purification clay according to the ratio of weight ratio 1: 0.5 by A material and B material.During use, the clay mixed is applied directly to the vitrified tile back side or bonding basic unit can carry out the stickup of vitrified tile.