CN105712628A - Glaze special for underglaze colour depicted knife, horse person coloured pottery - Google Patents
Glaze special for underglaze colour depicted knife, horse person coloured pottery Download PDFInfo
- Publication number
- CN105712628A CN105712628A CN201610160108.6A CN201610160108A CN105712628A CN 105712628 A CN105712628 A CN 105712628A CN 201610160108 A CN201610160108 A CN 201610160108A CN 105712628 A CN105712628 A CN 105712628A
- Authority
- CN
- China
- Prior art keywords
- glaze
- pottery
- underglaze colour
- special
- clay
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides glaze special for underglaze colour depicted knife, horse person coloured pottery. The glaze is prepared from, by weight, 25-35 g of ferromolybdenum, 24-26 g bone meal, 15-25 g of shells, 25-35 g of clay, 5-50 g of cobaltous oxide, 4-6 g of titanium carbide, 4-6 g of silicon carbide, 3-5 g of procyanidine, 2-4 g of tea alkaloids, 7-9 g of natural sea stone, 7-9 g of hauynite, 5-7 g of lepidolite, 4-6 g of pear skin mud, 2-4 g of boric oxide, 7-9 g of magnesite and 7-9 g of potassium feldspar. According to the glaze, lead-removed glaze is adopted in cooperation with high temperature sintering, glaze cannot flow, a product is pure in color, original shapes of knives, horses and persons are maintained, and the preservation time is long.
Description
Technical field
The present invention relates to ancient painted pottery manufacture technology field, being specifically related to a kind of underglaze colour, to portray armed horseback figure's ancient painted pottery special
Use glaze.
Background technology
China is pottery ancient country, talks about pottery, and foreigner just expects China.Pottery art is a kind of biomorphogenic.
The stock of pottery form is soil, water, fire.People has only grasped the plasticity of water and soil kneading, rheology
Property, and forming method and sintering rule, just can facilitate generation and the evolution of pottery art form, make ware
The raw beautiful form of produce.Focus on the combination of moulding and decoration simultaneously, the inspiration sharp by people and
Creativity consciousness, catches and discloses plasticity U.S. beautiful, pliable and tough and the performance vigor of earth, thus occur in that
Brand-new pottery art form, the people by wisdom is grasped, is developed, is innovated.Any artistic development is to certain rank
Section, all can form complete skill.
Ceramic art rises of the remote past in China, and complexion is various, the ceramic skill of China in world's history
Art always has suitable representativeness, also due to pass on of the remote past, technology is constantly updated, and adds and goes through
Alternating through the dynasty, different nationalities and life style have impact on the developing direction of Chinese pottery.Along with the dynasty
And the evolution of ceramics, the value that pottery is practical in the life of the mankind, simultaneously because of
For the differentiation of culture, pottery becomes an important art culture gradually, diversified style and different
Kenel purposes, representative is that human aesthetic sees and the change of quality of the life.Owing to the modern times are former for chemical industry
The progress of material knowledge, and the development of glaze burning technology, add manufacture and invention, the pottery art of machine after industrialization
Manufacturing technology also constantly promoting.
Along with expanding economy and the raising of people's living standard, people's decoration technology requirement to porcelain
More and more higher.But owing to being limited to by high temperature decorating colour, glaze, technique, ceramic limits to use always
Leaded glaze, and use low-firing (800 DEG C-900 DEG C), leaded glaze causes not environmentally, outlet
Also restriction is received.
Summary of the invention
The technical problem to be solved be provide one can high-temperature firing, glaze does not flows, system
The underglaze colour of product holding time length portrays the special glaze of armed horseback figure's ancient painted pottery.
The technical problem to be solved realizes by the following technical solutions:
A kind of underglaze colour portrays the special glaze of armed horseback figure's ancient painted pottery, is made up of the component of following weight: molybdenum-iron
25-35g, bone meal 24-26g, shell 15-25g, clay 25-35g, cobalt oxide 5-50g, titanium carbide 4-6g,
Carborundum 4-6g, procyanidin 3-5g, Folium Camelliae sinensis alkaloid 2-4g, natural marine stone 7-9g, hauynite 7-9g,
Lepidolite 5-7g, this mountain green mud 4-6g, boron oxide 2-4g, magnesite 7-9g, potassium feldspar 7-9g；
The preferable weight of each component is: be made up of the component of following weight: molybdenum-iron 30g, bone meal 25g, shellfish
Shell 20g, clay 30g, cobalt oxide 20g, titanium carbide 5g, carborundum 5g, procyanidin 4g, Folium Camelliae sinensis are biological
Alkali 3g, natural marine stone 8g, hauynite 8g, lepidolite 6g, this mountain green mud 5g, boron oxide 3g, magnesite
Ore deposit 8g, potassium feldspar 8g；During preparation, said components is prepared in proportion, put into continuously grinding 4 in ball mill
Hour, fineness reaches 450-500 mesh sieve, sieves and is configured to.
A kind of using above-mentioned glaze that ancient painted pottery is carried out the technique of glazing, its step is as follows:
(1) use Kaolin as raw material, Kaolin be dried, pulverize, then add water and make mud,
Through pugging, molding, dry in the shade, repair type and polishing after prepare ceramic body；
(2) according to the color required for goods, ceramic body is carried out upper coloured silk, makes pigment be attached on base substrate,
Then ceramic body is dried in the shade, carry out picking flower process according to moulding, obtain semi-finished product ceramic body；
(3) by semi-finished product ceramic body feeding low-temperature enamel firing kiln carry out low temperature baking, by the pigment on base substrate with
Base substrate combines；Wherein cryogenic temperature controls at 180-230 DEG C；
(4) get on the base substrate after low temperature baking lead glaze, and the base substrate of upper lead glaze in the past is sent into high temperature also
Former flame kiln, carries out high-temperature firing, cool kiln, kiln discharge, makes under-glaze decoration ceramic；
The firing temperature of above-mentioned reducing flame kiln is 1250 DEG C-1270 DEG C, use high-temperature firing make glaze with
Base substrate fully fuses, will not peeling；Using simultaneously and go lead glaze to coordinate high-temperature firing, glaze will not produce stream
Dynamic, goods pure color, remain the original shape of armed horseback figure, and the holding time is long.
The invention has the beneficial effects as follows:
1) lead material is thoroughly removed by the present invention, adds the compositions such as clay, bone meal, titanium, silicon, the most leaded,
Can export, add the surface strength of glaze colours, smoothness, good hand touch simultaneously；
2) using high temperature reduction flame to fire, glaze will not flow, figure good forming effect, good looking appearance,
The pottery simultaneously prepared never peeling, it is simple to persistence.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and effect and be readily apparent from
Solve, below in conjunction with specific embodiment, the present invention is expanded on further.
Embodiment 1
A kind of underglaze colour portrays the special glaze of armed horseback figure's ancient painted pottery, is made up of the component of following weight: molybdenum-iron 30g,
Bone meal 25g, shell 20g, clay 30g, cobalt oxide 20g, titanium carbide 5g, carborundum 5g, procyanidin
4g, Folium Camelliae sinensis alkaloid 3g, natural marine stone 8g, hauynite 8g, lepidolite 6g, this mountain green mud 5g, oxygen
Change boron 3g, magnesite 8g, potassium feldspar 8g；During preparation, said components is prepared in proportion, put into ball milling
Continuously grinding 4 hours in machine, fineness reaches 450-500 mesh sieve, sieves and be configured to.
Embodiment 2
A kind of underglaze colour portrays the special glaze of armed horseback figure's ancient painted pottery, is made up of the component of following weight: molybdenum-iron 35g,
Bone meal 24g, shell 25g, clay 25g, cobalt oxide 50g, titanium carbide 4g, carborundum 6g, procyanidin
3g, Folium Camelliae sinensis alkaloid 4g, natural marine stone 7g, hauynite 9g, lepidolite 5g, this mountain green mud 6g, oxygen
Change boron 2g, magnesite 9g, potassium feldspar 7g；During preparation, said components is prepared in proportion, put into ball milling
Continuously grinding 4 hours in machine, fineness reaches 450-500 mesh sieve, sieves and be configured to.
Embodiment 3
A kind of underglaze colour portrays the special glaze of armed horseback figure's ancient painted pottery, is made up of the component of following weight: molybdenum-iron 25g,
Bone meal 26g, shell 15g, clay 35g, cobalt oxide 5g, titanium carbide 6g, carborundum 4g, procyanidin 5g,
Folium Camelliae sinensis alkaloid 2g, natural marine stone 9g, hauynite 7g, lepidolite 7g, this mountain green mud 4g, boron oxide
4g, magnesite 7g, potassium feldspar 9g；During preparation, said components is prepared in proportion, put in ball mill
Continuously grinding 4 hours, fineness reaches 450-500 mesh sieve, sieves and is configured to.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.One's own profession
Skilled person will appreciate that of industry, the present invention is not restricted to the described embodiments, above-described embodiment and explanation
The principle that the present invention is simply described described in book, without departing from the spirit and scope of the present invention,
The present invention also has various changes and modifications, and these changes and improvements both fall within claimed invention model
In enclosing.Claimed scope is defined by appending claims and equivalent thereof.
Claims (2)
1. a underglaze colour portrays the special glaze of armed horseback figure's ancient painted pottery, it is characterised in that by the group of following weight
Point make: molybdenum-iron 25-35g, bone meal 24-26g, shell 15-25g, clay 25-35g, cobalt oxide 5-50g,
Titanium carbide 4-6g, carborundum 4-6g, procyanidin 3-5g, Folium Camelliae sinensis alkaloid 2-4g, natural marine stone 7-9g,
Hauynite 7-9g, lepidolite 5-7g, this mountain green mud 4-6g, boron oxide 2-4g, magnesite 7-9g, potassium are long
Stone 7-9g.
Underglaze colour the most according to claim 1 portrays the special glaze of armed horseback figure's ancient painted pottery, it is characterised in that
It is made up of the component of following weight: be made up of the component of following weight: molybdenum-iron 30g, bone meal 25g, shell
20g, clay 30g, cobalt oxide 20g, titanium carbide 5g, carborundum 5g, procyanidin 4g, Folium Camelliae sinensis alkaloid
3g, natural marine stone 8g, hauynite 8g, lepidolite 6g, this mountain green mud 5g, boron oxide 3g, magnesite
8g, potassium feldspar 8g.