CN105696322A - Method for improving softness of hemp fabric - Google Patents
Method for improving softness of hemp fabric Download PDFInfo
- Publication number
- CN105696322A CN105696322A CN201610144755.8A CN201610144755A CN105696322A CN 105696322 A CN105696322 A CN 105696322A CN 201610144755 A CN201610144755 A CN 201610144755A CN 105696322 A CN105696322 A CN 105696322A
- Authority
- CN
- China
- Prior art keywords
- parts
- fabric
- hemp fabric
- hemp
- finishing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a method for improving softness of hemp fabric. The method includes the following steps that firstly, water is added into a finishing agent to prepare steeping liquor, then the fabric is placed in the steeping liquor to be subjected to padding, the liquor detention rate is 45-70%, finally, washing is performed for 2-3 times, and dewatering and drying are performed. The finishing agent is prepared from, by weight, 13-16 parts of butyl titanate, 18-22 parts of ethylene glycol, 3-6 parts of chitosan, 11-18 parts of pentaerythritol stearate, 2-6 parts of sodium xylene sulfonate, 3-7 parts of didecyl dimethyl ammonium chloride, 5-9 parts of methyl hydrogen silicone oil, 2-8 parts of xylene, 4-8 parts of vinyl trimethoxy silane, 1-10 parts of talcum powder and 1-2 parts of aziridine. By means of the finishing method, the hemp fabric will be soft and elastic after being subjected to softening processing, the hemp fabric is safe and free of toxin, and the problem that the hemp fabric is rough and hard in hand feeling is solved.
Description
Technical field
The invention belongs to textile technology field, a kind of method being specifically related to softness improving hemp fabric。
Technical background
Hemp fabric is the woven fabric of china-hemp fibers, Fructus Cannabis, has another name called hemp, cold fiber crops, Urtica cannabina L. etc., and another name appellation is planted up to more than ten。History records carry, and fiber crops originate from China, have " king of natural fiber " good reputation, and the clothing finery being made up of it have the several functions such as moisture absorption, ventilative, pleasant, heat radiation, mildew-resistant, antibacterial, radioprotective, anti-ultraviolet, sound-absorbing, not only can be military but also can be civilian。And to make the effect of antimicrobial socks, just it is subject to extensive favorable comment。Fructus Cannabis be the mankind the earliest for the natural fiber of fabric, have " source is spun by state, 10000 years clothing ancestrals " good reputation, its plantation history have at least more than 8000 year。Fructus Cannabis spread is planted, and can effectively alleviate the present situation that China's fiber is in short supply, break the new road of a high added value for solving agriculture, rural areas and farmers problem, and its good characteristic will be lived with bringing revolutionary variation for following soldier's food and clothing。
Fructus Cannabis is the raw material of various military clothes, high-grade dress ornament, is expected to change world today's textile constructions;It is also possible to become the mineral succedaneum such as oil, coal in the future, reduces the environmental pollution that energy resource consumption causes。Fructus Cannabis is a kind of ecological, environmental protective, reproducible multi-purpose plant, through degumming, the operation such as reel off raw silk from cocoons, becomes as shining white cotton-wool, both can wool spinning, again can cotton spinning, also can blending, and with low cost。The dehumidifying of Fructus Cannabis is textile 3 times, and Fructus Cannabis fabric can by the killing bacteria of attachment in 1 hour;The ultraviolet of hemp fabric maskable more than 95%, colour-fast when 370 DEG C of high temperature, do not burn when 1000 DEG C, there is splendid heat-resisting, ultraviolet resistance;Fructus Cannabis bast with can be used for weaving。
Usual fabric is in the technical processs such as weaving, pre-treatment, it is coarse that several factors is likely to make fabric become feel, and the soft feel of comfortable is the client's decisive foundation when buying a textile, therefore, soft feel is considered as the most important factor affecting textile sales。But there is the problem such as cost height, single, the submissive less effective of performance in current softener。Therefore how overcoming the deficiencies in the prior art is the problem that current field of textiles needs solution badly。
Summary of the invention
To achieve these goals, a kind of method that the invention provides softness improving hemp fabric。
It is an object of the invention to be achieved through the following technical solutions:
A kind of method of softness improving hemp fabric, the method has following steps: first being added water by finishing agent is configured to impregnation liquid, is then put in impregnation liquid by fabric and pads, pick-up 45-70%, finally washing 2-3 time, last dewatered drying;Described finishing agent is made up of the component of following parts by weight: tetrabutyl titanate 13-16 part, ethylene glycol 18-22 part, chitosan 3-6 part, pentaerythritol stearate 11-18 part, sodium xylene sulfonate 2-6 part, DDAC 3-7 part, Methyl Hydrogen Polysiloxane Fluid 5-9 part, dimethylbenzene 2-8 part, vinyltrimethoxy silane 4-8 part, Pulvis Talci 1-10 part, aziridine 1-2 part。
The preparation method of finishing agent is common process, and those of ordinary skill in the art skillfully grasp。
Described fabric impregnates 20-30 minute at 50-85 DEG C。
Described drying temperature is 50-60 DEG C, and the time is 3 minutes。
The concentration of described aqueous solution is 800-1500ppm。
The method have the advantages that the method for sorting of the present invention makes hemp fabric also can soft and high resilience, safety non-toxic, the problem solving hemp fabric wiriness through soft sofening treatment feel。
Detailed description of the invention
The following stated is only the preferred embodiments of the present invention, it is not limited to the present invention, although the present invention being described in detail with reference to previous embodiment, for a person skilled in the art, technical scheme described in foregoing embodiments still can be modified by it, or wherein portion of techniques feature carries out equivalent replacement。All within the spirit and principles in the present invention, any amendment of making, equivalent replacement, improvement etc., should be included within protection scope of the present invention。
Embodiment 1
A kind of method of softness improving hemp fabric, it has following steps: first being added water by finishing agent is configured to impregnation liquid, is then put in impregnation liquid by fabric and pads, pick-up 45-70%, finally washing 2-3 time, last dewatered drying;Described finishing agent is made up of the component of following parts by weight: tetrabutyl titanate 13 parts, ethylene glycol 18 parts, chitosan 3 parts, pentaerythritol stearate 11 parts, sodium xylene sulfonate 2 parts, DDAC 3 parts, Methyl Hydrogen Polysiloxane Fluid 5 parts, dimethylbenzene 2 parts, vinyltrimethoxy silane 4 parts, Pulvis Talci 1 part, aziridine 1 part。
Described fabric impregnates 20-30 minute at 50-85 DEG C。
Described drying temperature is 50-60 DEG C, and the time is 3 minutes。
The concentration of described aqueous solution is 800-1500ppm。
Embodiment 2
A kind of method of softness improving hemp fabric, it has following steps: first being added water by finishing agent is configured to impregnation liquid, is then put in impregnation liquid by fabric and pads, pick-up 45-70%, finally washing 2-3 time, last dewatered drying;Described finishing agent is made up of the component of following parts by weight: tetrabutyl titanate 16 parts, ethylene glycol 22 parts, chitosan 6 parts, pentaerythritol stearate 18 parts, sodium xylene sulfonate 6 parts, DDAC 7 parts, Methyl Hydrogen Polysiloxane Fluid 9 parts, dimethylbenzene 8 parts, vinyltrimethoxy silane 8 parts, Pulvis Talci 10 parts, aziridine 2 parts。
Described fabric impregnates 20-30 minute at 50-85 DEG C。
Described drying temperature is 50-60 DEG C, and the time is 3 minutes。
The concentration of described aqueous solution is 800-1500ppm。
Embodiment 3
A kind of method of softness improving hemp fabric, it has following steps: first being added water by finishing agent is configured to impregnation liquid, is then put in impregnation liquid by fabric and pads, pick-up 45-70%, finally washing 2-3 time, last dewatered drying;Described finishing agent is made up of the component of following parts by weight: tetrabutyl titanate 15 parts, ethylene glycol 19 parts, chitosan 5 parts, pentaerythritol stearate 15 parts, sodium xylene sulfonate 4 parts, DDAC 5 parts, Methyl Hydrogen Polysiloxane Fluid 7 parts, dimethylbenzene 5 parts, vinyltrimethoxy silane 6 parts, Pulvis Talci 5 parts, aziridine 2 parts。
Described fabric impregnates 20-30 minute at 50-85 DEG C。
Described drying temperature is 50-60 DEG C, and the time is 3 minutes。
The concentration of described aqueous solution is 800-1500ppm。
Claims (4)
1. the method for the softness improving hemp fabric, it is characterized in that the step of described method is as follows: first being added water by finishing agent is configured to impregnation liquid, then fabric is put in impregnation liquid and pad, pick-up 45-70%, finally washing 2-3 time, last dewatered drying;Described finishing agent is made up of the component of following parts by weight: tetrabutyl titanate 13-16 part, ethylene glycol 18-22 part, chitosan 3-6 part, pentaerythritol stearate 11-18 part, sodium xylene sulfonate 2-6 part, DDAC 3-7 part, Methyl Hydrogen Polysiloxane Fluid 5-9 part, dimethylbenzene 2-8 part, vinyltrimethoxy silane 4-8 part, Pulvis Talci 1-10 part, aziridine 1-2 part。
2. the method for a kind of softness improving hemp fabric according to claim 1, it is characterised in that: described fabric impregnates 20-30 minute at 50-85 DEG C。
3. the method for a kind of softness improving hemp fabric according to claim 1, it is characterised in that: described drying temperature is 50-60 DEG C, and the time is 3 minutes。
4. the method for a kind of softness improving hemp fabric according to claim 1, it is characterised in that: the concentration of described aqueous solution is 800-1500ppm。