CN105694642A - 一种丙烯酸酯防水涂料乳液及其制备方法 - Google Patents
一种丙烯酸酯防水涂料乳液及其制备方法 Download PDFInfo
- Publication number
- CN105694642A CN105694642A CN201510382431.3A CN201510382431A CN105694642A CN 105694642 A CN105694642 A CN 105694642A CN 201510382431 A CN201510382431 A CN 201510382431A CN 105694642 A CN105694642 A CN 105694642A
- Authority
- CN
- China
- Prior art keywords
- parts
- initiator
- acrylate
- stirring
- waterproof paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开的是一种丙烯酸酯防水涂料乳液及其制备方法,所述乳液,包括甲基丙烯酸甲酯3-10份、丙烯酸丁酯30-60份、丙烯腈2-10份、丙烯酸1-5份、保护胶PM0.2-0.5份、碳酸氢钠0.5-1份、去离子水50-80份、引发剂0.1-0.4份、乳化剂3-10份、氨水适量。制备方法如下:首先,向2L烧瓶中加入部分去离子水、碳酸氢钠、乳化剂,搅拌使其溶解,搅拌后,再加入甲基丙烯酸甲酯、丙烯酸丁酯、丙烯腈、丙烯酸进行预乳化,再加入部分引发剂,搅拌,再次向烧瓶加入剩余的去离子水、保护胶并升温至80~85℃,加部分引发剂并滴加预乳化单体,继续保温2h,最后加氨水调pH至8~9,过滤,即得。
Description
技术领域
本发明涉及一种丙烯酸酯防水涂料乳液及其制备方法,属于涂料领域。
背景技术
防水涂料是指能防止雨水或地下水渗漏的一类涂料,主要用于屋面、地下建筑、厨房、浴室、卫生间、粮仓等多水潮湿场所的防雨、防水和防潮。此类涂料所用的基础乳液要求具备较高的弹性、较佳的耐酸碱、低温柔韧性和优异的耐候、耐久性等特点。常用的有VAE共聚乳液和丙烯酸酯共聚乳液等。丙烯酸酯共聚乳液的耐水、耐候、耐酸碱性、附着性和弹性等均优于VAE乳液而成为防水涂料的首先基础乳液,被越来越多地应用于许多重要的工业与民用建筑,特别是高层建筑屋面的防水处理,有效年限可达20年以上。目前,在越来越多的大、中、小城市,沥青类聚氨酯防水涂料已被禁用,取而代之的是以水性丙烯酸酯防水涂料为代表的新型绿色环保型产品。
丙烯酸酯防水涂料乳液是制备丙烯酸酯防水涂料的首先基础乳液,涂料乳液的性能对丙烯酸酯防水涂料的使用效果具有决定性的影响,因此,一种丙烯酸酯防水涂料乳液及其制备方法是很有必要的。
发明内容
本发明目的是,用来弥补现有配方的不足,而提供一种丙烯酸酯防水涂料乳液及其制备方法。
为了实现上述目的,本发明的技术方案如下:
一种丙烯酸酯防水涂料乳液,其特征在于,以重量份数计,包括甲基丙烯酸甲酯3-10份、丙烯酸丁酯30-60份、丙烯腈2-10份、丙烯酸1-5份、保护胶PM0.2-0.5份、碳酸氢钠0.5-1份、去离子水50-80份、引发剂0.1-0.4份、乳化剂3-10份、氨水适量。
所述引发剂为过硫酸胺。
所述乳化剂为OP-10和SDS混合乳化剂。
所述的丙烯酸酯防水涂料乳液的制备方法,其特征在于,包括以下几个步骤:
(A)向2L三颈烧瓶中加入部分去离子水、碳酸氢钠、乳化剂,搅拌使其溶解;
(B)加大搅拌器的速度,加入甲基丙烯酸甲酯、丙烯酸丁酯、丙烯腈、丙烯酸进行预乳化;
(C)最后加入部分引发剂溶液,搅拌后均匀倒出,再次向三颈烧瓶加入剩余的去离子水、保护胶并升温至80~85℃,加入部分引发剂并滴加预乳化单体,全部预乳化单体在4h左右滴加完,继续保温2h,在滴加过程中,应保持较低的搅拌强度;
(D)最后待体系温度降到50℃以下,加氨水调pH至8~9,过滤,即得本乳液。
本发明的有益效果如下:
本发明制备工艺简单,制备出来的丙烯酸酯防水涂料乳液具有拉伸强度大、断裂伸长率高的优点,且其化学稳定性强,无毒、无味,是一种理想的乳液。经实验证明,其拉伸强度大于0.6MPa,断裂伸长率大于600%。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的易于明白了解,下面结合具体实施例,进一步阐述本发明。
实施例1:
本实施例中,一种丙烯酸酯防水涂料乳液,以重量份数计,包括甲基丙烯酸甲酯6份、丙烯酸丁酯45份、丙烯腈8份、丙烯酸3份、保护胶PM0.3份、碳酸氢钠0.6份、去离子水70份、引发剂0.3份、乳化剂8份、氨水适量。
所述的丙烯酸酯防水涂料乳液的制备方法,其特征在于,包括以下几个步骤:
(A)向2L三颈烧瓶中加入部分去离子水、碳酸氢钠、乳化剂,搅拌使其溶解;
(B)加大搅拌器的速度,加入甲基丙烯酸甲酯、丙烯酸丁酯、丙烯腈、丙烯酸进行预乳化;
(C)最后加入部分引发剂溶液,搅拌后均匀倒出,再次向三颈烧瓶加入剩余的去离子水、保护胶并升温至82℃,加入部分引发剂并滴加预乳化单体,全部预乳化单体在4h左右滴加完,继续保温2h,在滴加过程中,应保持较低的搅拌强度;
(D)最后待体系温度降到50℃以下,加氨水调pH至8,过滤,即得本乳液。
本发明制备工艺简单,制备出来的丙烯酸酯防水涂料乳液具有拉伸强度大、断裂伸长率高的优点,且其化学稳定性强,无毒、无味,是一种理想的乳液。经实验证明,其拉伸强度为0.64MPa,断裂伸长率为708%。
实施例2:
本实施例中,一种丙烯酸酯防水涂料乳液,以重量份数计,包括甲基丙烯酸甲酯5份、丙烯酸丁酯40份、丙烯腈5份、丙烯酸3份、保护胶PM0.35份、碳酸氢钠0.8份、去离子水65份、引发剂0.25份、乳化剂5份、氨水适量。
所述的丙烯酸酯防水涂料乳液的制备方法,其特征在于,包括以下几个步骤:
(A)向2L三颈烧瓶中加入部分去离子水、碳酸氢钠、乳化剂,搅拌使其溶解;
(B)加大搅拌器的速度,加入甲基丙烯酸甲酯、丙烯酸丁酯、丙烯腈、丙烯酸进行预乳化;
(C)最后加入部分引发剂溶液,搅拌后均匀倒出,再次向三颈烧瓶加入剩余的去离子水、保护胶并升温至85℃,加入部分引发剂并滴加预乳化单体,全部预乳化单体在4h左右滴加完,继续保温2h,在滴加过程中,应保持较低的搅拌强度;
(D)最后待体系温度降到50℃以下,加氨水调pH至8,过滤,即得本乳液。
本发明制备工艺简单,制备出来的丙烯酸酯防水涂料乳液具有拉伸强度大、断裂伸长率高的优点,且其化学稳定性强,无毒、无味,是一种理想的乳液。经实验证明,其拉伸强度为0.71MPa,断裂伸长率为680%。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (4)
1.一种丙烯酸酯防水涂料乳液,其特征在于,以重量份数计,包括甲基丙烯酸甲酯3-10份、丙烯酸丁酯30-60份、丙烯腈2-10份、丙烯酸1-5份、保护胶PM0.2-0.5份、碳酸氢钠0.5-1份、去离子水50-80份、引发剂0.1-0.4份、乳化剂3-10份、氨水适量。
2.根据权利要求1所述的丙烯酸酯防水涂料乳液,其特征在于,所述引发剂为过硫酸胺。
3.根据权利要求1所述的丙烯酸酯防水涂料乳液,其特征在于,所述乳化剂为OP-10和SDS混合乳化剂。
4.根据权利要求1所述的丙烯酸酯防水涂料乳液的制备方法,其特征在于,包括以下几个步骤:
(A)向2L三颈烧瓶中加入部分去离子水、碳酸氢钠、乳化剂,搅拌使其溶解;
(B)加大搅拌器的速度,加入甲基丙烯酸甲酯、丙烯酸丁酯、丙烯腈、丙烯酸进行预乳化;
(C)最后加入部分引发剂溶液,搅拌后均匀倒出,再次向三颈烧瓶加入剩余的去离子水、保护胶并升温至80~85℃,加入部分引发剂并滴加预乳化单体,全部预乳化单体在4h左右滴加完,继续保温2h,在滴加过程中,应保持较低的搅拌强度;
(D)最后待体系温度降到50℃以下,加氨水调pH至8~9,过滤,即得本乳液。