CN105669152B - Indoor wall basalis, which is used, has the levelling mud of purification function and preparation, construction method - Google Patents
Indoor wall basalis, which is used, has the levelling mud of purification function and preparation, construction method Download PDFInfo
- Publication number
- CN105669152B CN105669152B CN201610016406.8A CN201610016406A CN105669152B CN 105669152 B CN105669152 B CN 105669152B CN 201610016406 A CN201610016406 A CN 201610016406A CN 105669152 B CN105669152 B CN 105669152B
- Authority
- CN
- China
- Prior art keywords
- mud
- levelling
- mesh
- purification function
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of indoor wall basalis with having the levelling mud of purification function and preparation, construction method, belong to building base material technical field, leveling putty includes the raw material of following parts by weight：20 50 parts of gypsum, 200 400 5 20 parts of mesh calcium oxide, 100 200 20 50 parts of mesh quartz sands, 200 400 10 30 parts of mesh coarse whitings, 80 200 10 30 parts of mesh diatomite, 80 200 5 10 parts of mesh volcanic ash, 5 20 parts of the non-calcinated diatomite of 100 200 mesh, 100 200 1 10 parts of mesh attapulgites, 200 800 1 10 parts of mesh aluminium-magnesium silicates, 10 0.5 10 parts of 30nm nano zine oxides, 10 0.5 10 parts of 30nm nano titanium oxides etc..The levelling mud of the present invention has a variety of environment-friendly functions such as damping insulation, purification air, decomposing formaldehyde.
Description
Technical field
The present invention relates to building base material technical field, more particularly to a kind of indoor wall basalis is with having purification function
The levelling mud of property and preparation, construction method.
Background technology
Economic condition is become better and better, and living environment is consequently also stepping up.But many ornament materials largely contain
Harmful components, constantly pollute us and seem beautiful comfortable space, existing developing stage carrys out many diseases because of finishing, ornamental tape
Disease, such as leukaemia, lung cancer, fetal anomaly, these are all endangering us all the time.
Country wants index to step up ornament materials.Although have has Con trolling index at this stage to environment friendly decorative material,
But if meeting life requirement, ornament materials materials are stepped up, all environmental protection indexs or exceeded of adding up, can cause
Serious room air pollution.
Existing indoor wall basalis is levelling mainly to be had：White cement, stone slurry, coarse whiting, talcum powder, gypsum, composition be
Monomer bonds, and only levelling effect, also encloses wall, if subjected to the influence of external high humidity can also bulge, peeling, peeling
Deng.Its decorative surface is destroyed, does not possess feature also.
Therefore need to provide it is a kind of can thick-layer, part, the alignment material with purification function of overall metope and construction make
Use method.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of energy thick-layer, part, the indoor wall basalis use of overall metope
With the levelling mud of purification function and preparation, construction method.
In order to solve the above technical problems, present invention offer technical scheme is as follows：
A kind of indoor wall basalis is provided with having the levelling mud of purification function, the levelling mud drum includes following parts by weight
Raw material：
Diatomite in the present invention has porous, has double-deck value, is both functional structure paint vehicle and lubricating substance；It is de-
Sulfuric acid gypsum is applied as the byproduct of industry, the important foundation of city's environmental emission reduction, at the same embody its use value (including
Caking property)；Non-calcinated diatomite belongs to rare earth scope, and while as this constitution paint material, its feature is also embodied in micro-
The oxidation material of amount；Nano zine oxide has the performance of the purification air under normal room temperature state；Nano titanium oxide can be with
As photocatalyst material, play a part of sterilization, purification under ultraviolet light or sunlight；Calcium oxide has strong oxidizing property, right
It is particularly evident in the decomposition of formaldehyde；Good water conservation is played present invention uses guar gum, algin, hydroxymethyl cellulose
Property, reach excellent application property, and hardening process does not have harmful substance residual；The interior decoration wall base intermediate layer of the present invention
With the levelling mud of purification function, can adsorb and effectively remove the harmful substance in air, and can be profound be applicable the present invention
In all ornament materials；The present invention applies a large amount of mineral exploration and exploitation products from failing, and utilizes the purification function of nano zine oxide, nanometer
The oxidation mechanism of the photocatalyst of titanium dioxide, numerous oxides, so as to obtain damping insulation, purification air, decomposing formaldehyde etc.
The base treatment material of a variety of environment-friendly functions；Dosage of the present invention is big, easy to use, has great promotional value.
Further, the levelling mud drum includes the raw material of following parts by weight：
Further, the levelling mud drum includes the raw material of following parts by weight：
Further, the gypsum is desulfurated plaster.
Preferably, the ratio of the diatomite and volcanic ash is 2:1~1:1.
On the other hand, there is provided a kind of preparation method of indoor wall basalis with the levelling mud of purification function, by described in
The raw material mixing of the levelling mud of purification function, stirs, that is, obtains described having the levelling mud of purification function.
Furthermore, there is provided a kind of construction method of indoor wall basalis with the levelling mud of purification function, by the purification
The levelling mud of feature adds water 40%-80% by weight percentage, mechanical or manual to be uniformly mixed, and reaches and is adapted to construction by hand
Conventional experience viscosity, you can construction, by the levelling mud indoors wall base bottom be sprayed onto it is smooth.
In summary, beneficial effects of the present invention are shown as：
1) diatomite in the present invention has porous, has double-deck value, is both functional structure paint vehicle and lubricating substance；
Desulfurization acid gypsum is applied as the byproduct of industry, the important foundation of city's environmental emission reduction, while embodies its use value (bag
Include caking property)；Non-calcinated diatomite belongs to rare earth scope, and while as this constitution paint material, its feature, which is also embodied in, to be had
Micro oxidation material；Nano zine oxide has the performance of the purification air under normal room temperature state；Nano titanium oxide can
As photocatalyst material, to play a part of sterilization, purification under ultraviolet light or sunlight；Calcium oxide has strong oxidizing property,
Decomposition for formaldehyde is particularly evident；Good water conservation is played present invention uses guar gum, algin, hydroxymethyl cellulose
Property, reach excellent application property, and hardening process does not have harmful substance residual；
2) purification function levelling mud in interior decoration wall base intermediate layer of the invention, it can adsorb and effectively remove in air
Harmful substance, and can be profound the present invention is applied to all ornament materials；
3) present invention applies a large amount of mineral exploration and exploitation products from failing, and utilizes purification function, the nano-silica of nano zine oxide
Change photocatalyst, the oxidation mechanism of numerous oxides of titanium, it is a variety of so as to obtain damping insulation, purification air, decomposing formaldehyde etc.
The base treatment material of environment-friendly function；
4) dosage of the present invention is big, easy to use, has great promotional value.
Embodiment
To make embodiments of the invention technical problems to be solved, technical scheme and advantage clearer, below in conjunction with
Specific embodiment is described in detail.But the present invention is limited to absolutely not these examples.As described below is only that the present invention is preferably implemented
Example, only to explain the present invention, therefore it can not be interpreted as the limitation of the scope of the claims of the present invention.It is it should be pointed out that all
All any modification, equivalent and improvement done within the spirit and principles in the present invention etc., it should be included in the guarantor of the present invention
Within the scope of shield.Therefore, the protection domain of patent of the present invention should be determined by the appended claims.
Embodiment one
Levelling mud is prepared by the raw material of following parts by weight：
By gypsum 20kg, 200-400 mesh calcium oxide 5kg, 100-200 mesh quartz sand 50kg, 200-400 mesh coarse whiting 10kg,
80-200 mesh diatomite 10kg, 80-200 the mesh volcanic ash non-calcinated diatomite 5kg of 5kg, 100-200 mesh, 100-200 mesh concave convex rods
Native 1kg, 200-800 mesh aluminium-magnesium silicate 1kg, 10-30nm nano zine oxide 0.5kg, 10-30nm nano titanium oxide 0.5kg,
300-1250 mesh kaolin 1kg, bentonite 5kg, citric acid 0.1kg, guar gum 0.9kg, algin 0.8kg and methylol are fine
Plain 0.5kg mixing is tieed up, is stirred, that is, obtains described there is the levelling mud of purification function.
Embodiment two
Levelling mud is prepared by the raw material of following parts by weight：
By gypsum 50kg, 200-400 mesh calcium oxide 5kg, 100-200 mesh quartz sand 20kg, 200-400 mesh coarse whiting 10kg,
80-200 mesh diatomite 20kg, 80-200 the mesh volcanic ash non-calcinated diatomite 5kg of 10kg, 100-200 mesh, 100-200 mesh are concavo-convex
Rod soil 10kg, 200-800 mesh aluminium-magnesium silicate 5kg, 10-30nm nano zine oxide 10kg, 10-30nm nano titanium oxide 0.5kg,
300-1250 mesh kaolin 10kg, bentonite 5kg, citric acid 0.5kg, guar gum 0.3kg, algin 4kg and methylol are fine
Plain 0.5kg mixing is tieed up, is stirred, that is, obtains described there is the levelling mud of purification function.
Embodiment three
Levelling mud is prepared by the raw material of following parts by weight：
By gypsum 30kg, 200-400 mesh calcium oxide 10kg, 100-200 mesh quartz sand 20kg, 200-400 mesh coarse whiting 30kg,
80-200 mesh diatomite 30kg, 80-200 the mesh volcanic ash non-calcinated diatomite 20kg of 6kg, 100-200 mesh, 100-200 mesh are concavo-convex
Rod soil 5kg, 200-800 mesh aluminium-magnesium silicate 10kg, 10-30nm nano zine oxide 0.5kg, 10-30nm nano titanium oxide 10kg,
300-1250 mesh kaolin 5kg, bentonite 10kg, citric acid 0.5kg, guar gum 0.3kg, algin 0.8kg and methylol
Cellulose 5kg is mixed, and is stirred, that is, obtains described having the levelling mud of purification function.
Example IV
Levelling mud is prepared by the raw material of following parts by weight：
By gypsum 25kg, 200-400 mesh calcium oxide 15kg, 100-200 mesh quartz sand 20kg, 200-400 mesh coarse whiting 10kg,
80-200 mesh diatomite 11kg, 80-200 the mesh volcanic ash non-calcinated diatomite 5kg of 10kg, 100-200 mesh, 100-200 mesh are concavo-convex
Rod soil 2kg, 200-800 mesh aluminium-magnesium silicate 3kg, 10-30nm nano zine oxide 0.5kg, 10-30nm nano titanium oxide 0.5kg,
300-1250 mesh kaolin 3kg, bentonite 5kg, citric acid 0.1kg, guar gum 0.9kg, algin 1.5kg and methylol are fine
Plain 2kg mixing is tieed up, is stirred, that is, obtains described there is the levelling mud of purification function.
Embodiment five
Leveling putty is prepared by the raw material of following parts by weight：
By gypsum 40kg, 200-400 mesh calcium oxide 10kg, 100-200 mesh quartz sand 22kg, 200-400 mesh coarse whiting 13kg,
80-200 mesh diatomite 10kg, 80-200 the mesh volcanic ash non-calcinated diatomite 10kg of 5kg, 100-200 mesh, 100-200 mesh are concavo-convex
Rod soil 5kg, 200-800 mesh aluminium-magnesium silicate 3kg, 10-30nm nano zine oxide 4kg, 10-30nm nano titanium oxide 0.5kg,
300-1250 mesh kaolin 3kg, bentonite 5kg, citric acid 0.5kg, guar gum 0.5kg, algin 4kg and hydroxylmethyl cellulose
Plain 1.5kg mixing, stirs, that is, obtains described having the levelling mud of purification function.
Embodiment six
Leveling putty is prepared by the raw material of following parts by weight：
By gypsum 30kg, 400 mesh calcium oxide 5kg, 200 mesh quartz sand 40kg, 200 mesh coarse whiting 11kg, 200 mesh diatomite
12kg, 80 mesh volcanic ash 8kg, 200 mesh non-calcinated diatomite 10kg, 100 mesh attapulgite 2kg, 800 mesh aluminium-magnesium silicate 5kg,
10nm nano zine oxides 0.8kg, 30nm nano titanium oxide 4kg, 300 mesh kaolin 3kg, bentonite 5kg, citric acid 0.2kg,
Guar gum 0.9kg, algin 1kg and hydroxymethyl cellulose 2kg are mixed, and are stirred, that is, obtain described having purification function
The levelling mud of property.
Embodiment seven
Leveling putty is prepared by the raw material of following parts by weight：
By gypsum 30kg, 200 mesh calcium oxide 10kg, 100 mesh quartz sand 25kg, 400 mesh coarse whiting 20kg, 80 mesh diatomite
20kg, 200 mesh volcanic ash 5kg, 100 mesh non-calcinated diatomite 8kg, 200 mesh attapulgite 1kg, 200 mesh aluminium-magnesium silicate 1kg,
30nm nano zine oxides 0.8kg, 10nm nano titanium oxide 0.8kg, 1250 mesh kaolin 8kg, bentonite 5kg, citric acid
0.1kg, guar gum 0.3kg, algin 0.8kg and hydroxymethyl cellulose 2kg are mixed, and are stirred, that is, obtain described having
The levelling mud of purification function.
Embodiment eight
Leveling putty is prepared by the raw material of following parts by weight：
By gypsum 30kg, 200-400 mesh calcium oxide 10kg, 100-200 mesh quartz sand 20kg, 200-400 mesh coarse whiting 10kg,
80-200 mesh diatomite 10kg, 80-200 the mesh volcanic ash non-calcinated diatomite 5kg of 5kg, 100-200 mesh, 100-200 mesh concave convex rods
Native 4kg, 200-800 mesh aluminium-magnesium silicate 3kg, 10-30nm nano zine oxide 0.5kg, 10-30nm nano titanium oxide 0.5kg,
300-1250 mesh kaolin 5kg, bentonite 5kg, citric acid 0.15kg, guar gum 0.5kg, algin 1.5kg and methylol
Cellulose 2kg is mixed, and is stirred, that is, obtains described having the levelling mud of purification function.
The levelling mud 100kg of purification function of above-described embodiment is taken, adds water 45kg to dilute, mechanical agitation is equal to mixing
Even, job execution can be scratched and be detected by reaching required working viscosity (experience viscosity).The detection foundation of surface drying density
For GB/T20473-2006, the detection foundation GB/T20473-2006 of thermal conductivity factor, the foundation of 28 adhesion strengths is SJG11-
The detection of 2004. moisture adsorption and releasing characteristics eliminates according to GB/T20312-2006, burst size of methanal detection according to being GB18580-2001
Formaldehyde examination is according to GB/T16129-1995.As a result such as table 1.
The detection data of eight embodiments of the present invention of table 1
As shown in Table 1, the purification function leveling putty that prepared by the present invention can adsorb and effectively remove having in air
Evil material (formaldehyde etc.), and there is good workability, adhesion strength meets demand, and has certain heat insulating ability
Energy, moisture absorption and desorption property.
In summary, the diatomite in the present invention has porous, has double-deck value, is both functional structure paint vehicle
It is lubricating substance；Desulfurization acid gypsum is applied as the byproduct of industry, the important foundation of city's environmental emission reduction, while embodies its use
It is worth (including caking property)；Non-calcinated diatomite belongs to rare earth scope, and while as this constitution paint material, its feature also embodies
With micro oxidation material；Nano zine oxide has the performance of the purification air under normal room temperature state；Nano-silica
Photocatalyst material can be used as by changing titanium, play a part of sterilization, purification under ultraviolet light or sunlight；Calcium oxide has strong oxygen
The property changed, the decomposition for formaldehyde is particularly evident；Present invention uses guar gum, algin, hydroxymethyl cellulose to play well
Water-retaining property, reach excellent application property, and hardening process does not have harmful substance residual；The interior decoration wall base of the present invention
The levelling mud of intermediate layer purification function, can adsorb and effectively remove the harmful substance in air, and can be profound make this hair
It is bright to be applied to all ornament materials；The present invention applies a large amount of mineral exploration and exploitation products from failing, and utilizes the purification work(of nano zine oxide
Energy, the photocatalyst of nano titanium oxide, the oxidation mechanism of numerous oxides, so as to obtain damping insulation, purification air, decompose
The base treatment material of a variety of environment-friendly functions such as formaldehyde；Dosage of the present invention is big, easy to use, has great promotional value.
Described above is the preferred embodiment of the present invention, it is noted that for those skilled in the art
For, on the premise of principle of the present invention is not departed from, some improvements and modifications can also be made, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (7)
1. a kind of indoor wall basalis, which is used, has the levelling mud of purification function, it is characterised in that the levelling mud is by following weight
The raw material composition of part：
2. indoor wall basalis according to claim 1, which is used, has the levelling mud of purification function, it is characterised in that described to look for
Flat mud is made up of the raw material of following parts by weight：
3. indoor wall basalis according to claim 1 or 2, which is used, has the levelling mud of purification function, it is characterised in that institute
It is desulfurated plaster to state gypsum.
4. indoor wall basalis according to claim 1 or 2, which is used, has the levelling mud of purification function, it is characterised in that institute
The viscosity for stating hydroxymethyl cellulose is 100,000.
5. indoor wall basalis according to claim 4, which is used, has the levelling mud of purification function, it is characterised in that the silicon
Diatomaceous earth and the ratio of volcanic ash are 2:1~1:1.
6. any preparation method of the described indoor wall basalis with the levelling mud of purification function of claim 1 to 5, it is special
Sign is, the raw material of the levelling mud of the purification function is mixed, stirred, that is, obtains described levelling with purification function
Mud.
7. construction party of the indoor wall basalis that the method described in claim 6 is prepared with the levelling mud of purification function
Method, the levelling mud of the purification function is added into water 40%-80% by weight percentage, it is mechanical or manual to be uniformly mixed, reach
To the suitable conventional experience viscosity constructed by hand, you can construction, by the levelling mud indoors wall base bottom be sprayed onto it is smooth.