CN105648794B - A kind of dyeing and finishing processing method of the high-shrinkage filament fabric of imitative numb cotton - Google Patents

A kind of dyeing and finishing processing method of the high-shrinkage filament fabric of imitative numb cotton Download PDF

Info

Publication number
CN105648794B
CN105648794B CN201610135136.2A CN201610135136A CN105648794B CN 105648794 B CN105648794 B CN 105648794B CN 201610135136 A CN201610135136 A CN 201610135136A CN 105648794 B CN105648794 B CN 105648794B
Authority
CN
China
Prior art keywords
fabric
minutes
dyeing
cooled
speed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610135136.2A
Other languages
Chinese (zh)
Other versions
CN105648794A (en
Inventor
张卫东
奚炳华
李鹏
朱迎花
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU NEW-KASUM ENTERPRISE DEVELOPMENT Co Ltd
Original Assignee
JIANGSU NEW-KASUM ENTERPRISE DEVELOPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU NEW-KASUM ENTERPRISE DEVELOPMENT Co Ltd filed Critical JIANGSU NEW-KASUM ENTERPRISE DEVELOPMENT Co Ltd
Priority to CN201610135136.2A priority Critical patent/CN105648794B/en
Priority to PCT/CN2016/079005 priority patent/WO2017152461A1/en
Priority to US15/300,773 priority patent/US20170260687A1/en
Priority to KR1020167023839A priority patent/KR20170115433A/en
Priority to JP2016557133A priority patent/JP6383431B2/en
Publication of CN105648794A publication Critical patent/CN105648794A/en
Application granted granted Critical
Publication of CN105648794B publication Critical patent/CN105648794B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a kind of dyeing and finishing processing method of the high-shrinkage filament fabric of imitative numb cotton, comprise the following steps：Pre-treatment, pickling, dyeing and sizing so that fabric fully shrinks, there is provided imitate the texture of numb cotton.Through the above way, the dyeing and finishing processing method of the high-shrinkage filament fabric of imitative numb cotton of the present invention, cleaning treatment before being dyed using pre-treatment and pickling to fabric, it is easy to paint, reduces aberration and dyeing defect after dyeing, the opening and cooling that face liber is carried out during dyeing is shunk, obtain the product style of uniqueness, fabric feel is more biased towards that granular sensation is presented in imitative numb cotton effect, cloth cover, and finished product fabric is more like shuttle-woven fabric.

Description

A kind of dyeing and finishing processing method of the high-shrinkage filament fabric of imitative numb cotton
Technical field
The present invention relates to the dyeing and finishing field of high-shrinkage filament fabric, more particularly to a kind of high-shrinkage filament fabric of imitative numb cotton Dyeing and finishing processing method.
Background technology
Existing high-shrinkage filament fabric production technology is still immature, and aberration and dyeing defect often occurs, it is necessary to change in web surface Good dyeing.
In addition, the feel of existing high-shrinkage filament fabric is usually softness, it is smooth based on, the effect of imitative numb cotton can not be provided, Granular sensation can not be presented on cloth cover, it is necessary to improve.
The content of the invention
The present invention solves the technical problem of providing a kind of dyeing and finishing processing method of the high-shrinkage filament fabric of imitative numb cotton, The texture for imitating numb cotton is provided, avoids aberration and dyeing defect.
In order to solve the above technical problems, one aspect of the present invention is：A kind of high convergency of imitative numb cotton is provided The dyeing and finishing processing method of silk face fabric, comprises the following steps：
Pre-treatment：Fabric is put into progress first time heating treatment in dye vat, 3-5 g/l is added when being warming up to 35 DEG C Soda ash and 2-5 g/l of degreaser emulsion agent, bath raio control 1:8-12 then proceedes to second of heating treatment, temperature control To 100-120 DEG C, soaking time is 30-50 minutes；
Pickling：Pre-treatment carries out cooling processing after terminating, rate of temperature fall is controlled at 2-3 DEG C/min, when be cooled to 50 DEG C with Under, twice are washed after draining dye vat reclaimed water, intakes again and adds 1-3 g/l of glacial acetic acid, are then carried out at third time heating Reason, when being warming up to 50 DEG C, carries out the 15-30 minutes that wash cloth；
Dyeing：Normal temperature, which adds dye liquor and auxiliary agent, auxiliary agent, to be included：1-3 g/l of glacial acetic acid, the degreaser emulsion agent 1- of 98% concentration 1-4 g/l of 3 g/l, 1.5-5 g/l of levelling agent and stabilizer, bath raio are controlled 1:8~12, continue to heat up, heating rate control System is warming up to 85 DEG C at 2-5 DEG C/min, is incubated 2-5 minutes, continues to be warming up to 110-120 DEG C with 1-3 DEG C/min of speed, 10-15 minutes are incubated, continues to be warming up to 130-150 DEG C with 1-5 DEG C/min of speed and is incubated 30-40 minutes, insulation terminates Afterwards, 80-100 DEG C is cooled to 1.5-5 DEG C/min of speed, and after being cooled to 50-70 DEG C with 3-5 DEG C/min of speed, added Speed is cooled to normal temperature, increases fabric shrinkage factor, after draining dye vat reclaimed water, washes twice, per pass is washed 15-30 minutes, intake again And 1-3 g/l of 2-5 g/l of piece alkali and sodium hydrosulfite are added, adding piece alkali opens face liber, forms the fabric style of uniqueness, 85-100 DEG C is warming up to, 2-5 DEG C/min of heating rate, post processing insulation 20-30 minutes make cloth cover produce fold sense and level dyeing Effect, avoid producing dyeing defect and aberration phenomenon；It is incubated after terminating and is cooled to less than 50-70 DEG C with 1-3 DEG C/min of speed, row After exhaustion cylinder reclaimed water, wash twice, per pass washes 15-20 minutes, intake again and add 0.8-2 grams of the glacial acetic acid of 98% concentration/ Rise, be warming up to 60-80 DEG C, 2-5 DEG C/min of heating rate, be then incubated 20-30 minutes, the time in insulating process determines cloth Whether the fold sense in face is abundant；It is incubated after terminating and is cooled to less than 50-60 DEG C with 3-5 DEG C/min of speed, drains dye vat reclaimed water Afterwards, twice are washed, per pass washes 15-30 minutes, intakes again and adds 0.3-1 g/l of the glacial acetic acid of 98% concentration, operates 10-15 Band water goes out dye vat after minute；
Sizing：170-190 DEG C of setting temperature, the setting temperature purpose higher than common fabric are to make fabric contraction more abundant, Hydrophilic softening agent 0.3-1% is added, fabric is entered in shaping baking oven by padding machine.
In a preferred embodiment of the present invention, in the fixating shape step, the speed of padding machine is 21-25 ms/min.
In a preferred embodiment of the present invention, the dyestuff in the dye liquor that the staining procedure uses is depending on each color Its dosage.
In a preferred embodiment of the present invention, in the staining procedure, acceleration utilizes during being cooled to normal temperature to be added The cooling water of ice cools to accelerate to be cooled to the speed of normal temperature to dye vat, so as to increase fabric shrinkage factor.
The beneficial effects of the invention are as follows：A kind of dyeing and finishing processing side of the high-shrinkage filament fabric for imitative numb cotton that the present invention points out Method, the cleaning treatment before dyeing fabric using pre-treatment and pickling, it is easy to paint, reduces aberration and color after dyeing Flower, the opening and cooling that face liber is carried out during dyeing are shunk, and obtain the product style of uniqueness, fabric feel is more biased towards In imitative numb cotton effect, granular sensation is presented in cloth cover, and finished product fabric is more like shuttle-woven fabric.
Embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation Example is only the part of the embodiment of the present invention, rather than whole embodiments.It is common based on the embodiment in the present invention, this area All other embodiment that technical staff is obtained under the premise of creative work is not made, belong to the model that the present invention protects Enclose.
The embodiment of the present invention includes：
Embodiment 1：
A kind of dyeing and finishing processing method of the high-shrinkage filament fabric of imitative numb cotton, comprises the following steps：
Pre-treatment：Fabric is put into progress first time heating treatment in dye vat, 4 g/l are added when being warming up to 35 DEG C Soda ash and 3 g/l of degreaser emulsion agent, bath raio are controlled 1:8, then proceed to second of heating treatment, temperature control to 100 DEG C, soaking time is 30 minutes；
Pickling：Pre-treatment carries out cooling processing after terminating, rate of temperature fall is controlled at 2 DEG C/min, when being cooled to 45 DEG C, arranges Twice are washed after exhaustion cylinder reclaimed water, intakes again and adds 2 g/l of glacial acetic acid, third time heating treatment is then carried out, works as liter During 50 DEG C of Wen Zhizhi, wash cloth 15 minutes；
Dyeing：Normal temperature adds dye liquor and auxiliary agent, and the dyestuff in dye liquor its dosage, auxiliary agent depending on each color include：98% 2 g/l of 2 g/l of the glacial acetic acid of concentration, 1 g/l of degreaser emulsion agent, 3 g/l of levelling agent and stabilizer, bath raio are controlled 1: 10, continue to heat up, heating rate is controlled at 3 DEG C/min, is warming up to 85 DEG C, is incubated 4 minutes, is continued with 2 DEG C/min of speed 116 DEG C are warming up to, is incubated 10 minutes, continues to be warming up to 140 DEG C with 2 DEG C/min of speed and is incubated 30 minutes, insulation terminates Afterwards, 80 DEG C are cooled to 3 DEG C/min of speed, but after being cooled to 60 DEG C with 3 DEG C/min of speed, acceleration is cooled to normal temperature, Increase fabric shrinkage factor,（Acceleration is cooled to accelerate to be cooled to during being cooled to normal temperature using cooling water on the rocks to dye vat The speed of normal temperature, so as to increase fabric shrinkage factor）, after draining dye vat reclaimed water, twice are washed, per pass is washed 18 minutes, intake again And 2 g/l of 3 g/l of piece alkali and sodium hydrosulfite are added, adding piece alkali opens face liber, forms the fabric style of uniqueness, heating To 85 DEG C, 3 DEG C/min of heating rate, post processing insulation makes cloth cover produce fold sense and even dyeing effect for 20 minutes, avoids producing Dyeing defect and aberration phenomenon；It is incubated after terminating and is cooled to less than 55 DEG C with 2 DEG C/min of speed, after draining dye vat reclaimed water, washing two Road, per pass are washed 15 minutes, are intake again and are added 1 g/l of the glacial acetic acid of 98% concentration, are warming up to 65 DEG C, 3 DEG C/minute of heating rate Clock, 20 minutes then are incubated, the time in insulating process determines whether the fold sense of cloth cover is abundant；It is incubated after terminating with 3 DEG C/minute The speed of clock is cooled to less than 50 DEG C, after draining dye vat reclaimed water, washes twice, and per pass washes 20 minutes, intakes again and adds 98% 0.5 g/l of the glacial acetic acid of concentration, band water goes out dye vat after operating 10 minutes；
Sizing：170 DEG C of setting temperature, the setting temperature purpose higher than common fabric are to make fabric contraction more abundant, are added Hydrophilic softening agent 0.5%, fabric is entered in shaping baking oven by padding machine, and the speed of padding machine is 22 ms/min.
Embodiment 2：
A kind of dyeing and finishing processing method of the high-shrinkage filament fabric of imitative numb cotton, comprises the following steps：
Pre-treatment：Fabric is put into progress first time heating treatment in dye vat, 5 g/l are added when being warming up to 35 DEG C Soda ash and 4 g/l of degreaser emulsion agent, bath raio are controlled 1:12 then proceed to second of heating treatment, temperature control to 120 DEG C, soaking time is 50 minutes；
Pickling：Pre-treatment carries out cooling processing after terminating, rate of temperature fall is controlled at 3 DEG C/min, when being cooled to 46 DEG C, arranges Twice are washed after exhaustion cylinder reclaimed water, intakes again and adds 3 g/l of glacial acetic acid, third time heating treatment is then carried out, works as liter During 50 DEG C of Wen Zhizhi, wash cloth 30 minutes；
Dyeing：Normal temperature adds dye liquor and auxiliary agent, and the dyestuff in dye liquor its dosage, auxiliary agent depending on each color include：98% 4 g/l of 3 g/l of the glacial acetic acid of concentration, 3 g/l of degreaser emulsion agent, 5 g/l of levelling agent and stabilizer, bath raio are controlled 1: 12, continue to heat up, heating rate is controlled at 5 DEG C/min, is warming up to 85 DEG C, is incubated 5 minutes, is continued with 3 DEG C/min of speed 120 DEG C are warming up to, is incubated 15 minutes, continues to be warming up to 150 DEG C with 5 DEG C/min of speed and is incubated 40 minutes, insulation terminates Afterwards, 100 DEG C are cooled to 4 DEG C/min of speed, and after being cooled to 70 DEG C with 5 DEG C/min of speed, maximal rate is cooled to Normal temperature, fabric shrinkage factor is improved to greatest extent, after draining dye vat reclaimed water, wash twice, per pass is washed 30 minutes, intakes and add again Enter 3 g/l of 5 g/l of piece alkali and sodium hydrosulfite, adding piece alkali opens face liber, forms the fabric style of uniqueness, is warming up to 100 DEG C, 5 DEG C/min of heating rate, post processing insulation makes cloth cover produce fold sense and even dyeing effect for 30 minutes, avoids producing Dyeing defect and aberration phenomenon；It is incubated after terminating and is cooled to less than 70 DEG C with 3 DEG C/min of speed, after draining dye vat reclaimed water, washing two Road, per pass are washed 20 minutes, are intake again and are added 2 g/l of the glacial acetic acid of 98% concentration, are warming up to 80 DEG C, 5 DEG C/minute of heating rate Clock, 30 minutes then are incubated, the time in insulating process determines whether the fold sense of cloth cover is abundant；It is incubated after terminating with 5 DEG C/minute The speed of clock is cooled to less than 60 DEG C, after draining dye vat reclaimed water, washes twice, and per pass washes 30 minutes, intakes again and adds 98% 1 g/l of the glacial acetic acid of concentration, band water goes out dye vat after operating 15 minutes；
Sizing：190 DEG C of setting temperature, the setting temperature purpose higher than common fabric are to make fabric contraction more abundant, are added Hydrophilic softening agent 1%, fabric is entered in shaping baking oven by padding machine, and the speed of padding machine is 25 ms/min.
In summary, the dyeing and finishing processing method for the high-shrinkage filament fabric of a kind of imitative numb cotton that the present invention points out, make during dyeing Face liber is opened with piece alkali, forms the fabric style of uniqueness, fabric shrinkage factor is high, and granular sensation is presented in cloth cover, realizes imitative fiber crops Cotton effect is good more like shuttle-woven fabric, novelty.
Embodiments of the invention are the foregoing is only, are not intended to limit the scope of the invention, it is every to utilize this hair The equivalent structure or equivalent flow conversion that bright description is made, or directly or indirectly it is used in other related technology necks Domain, it is included within the scope of the present invention.

Claims (2)

1. a kind of dyeing and finishing processing method of the high-shrinkage filament fabric of imitative numb cotton, comprises the following steps：
Pre-treatment：Fabric is put into progress first time heating treatment in dye vat, 3-5 g/l of addition is pure when being warming up to 35 DEG C Alkali and 2-5 g/l of degreaser emulsion agent, bath raio are controlled 1:8-12 then proceedes to second of heating treatment, and temperature control is extremely 100-120 DEG C, soaking time is 30-50 minutes；
Pickling：Pre-treatment carries out cooling processing after terminating, rate of temperature fall is controlled at 2-3 DEG C/min, when being cooled to less than 50 DEG C, Twice are washed after draining dye vat reclaimed water, intakes again and adds 1-3 g/l of glacial acetic acid, then carry out third time heating treatment, When being warming up to 50 DEG C, the 15-30 minutes that wash cloth are carried out；
Dyeing：Normal temperature, which adds dye liquor and auxiliary agent, auxiliary agent, to be included：1-3 g/l of the glacial acetic acid of 98% concentration, 1-3 grams of degreaser emulsion agent/ Rise, 1.5-5 g/l of levelling agent and 1-4 g/l of stabilizer, bath raio are controlled 1:8~12, continue to heat up, heating rate control exists 2-5 DEG C/min, 85 DEG C are warming up to, is incubated 2-5 minutes, continues to be warming up to 110-120 DEG C with 1-3 DEG C/min of speed, insulation 10-15 minutes, continue to be warming up to 130-150 DEG C with 1-5 DEG C/min of speed and be incubated 30-40 minutes, after insulation terminates, with 1.5-5 DEG C/min of speed is cooled to 80-100 DEG C, and after being cooled to 50-70 DEG C with 3-5 DEG C/min of speed, accelerates cooling To normal temperature, increase fabric shrinkage factor, acceleration is cooled to accelerate during being cooled to normal temperature using cooling water on the rocks to dye vat The speed of normal temperature is cooled to, so as to increase fabric shrinkage factor, after draining dye vat reclaimed water, washes twice, per pass washes 15-30 minutes, Again intake and add 1-3 g/l of 2-5 g/l of piece alkali and sodium hydrosulfite, adding piece alkali opens face liber, forms uniqueness Fabric style, 85-100 DEG C is warming up to, 2-5 DEG C/min of heating rate, post processing insulation 20-30 minutes make cloth cover produce fold Sense and even dyeing effect, avoid producing dyeing defect and aberration phenomenon；It is incubated after terminating and 50-70 is cooled to 1-3 DEG C/min of speed Below DEG C, after draining dye vat reclaimed water, twice are washed, per pass washes 15-20 minutes, intakes again and adds the glacial acetic acid of 98% concentration 0.8-2 g/l, be warming up to 60-80 DEG C, 2-5 DEG C/min of heating rate, be then incubated 20-30 minutes, in insulating process when Between determine cloth cover fold sense it is whether abundant；It is incubated after terminating and is cooled to less than 50-60 DEG C with 3-5 DEG C/min of speed, drains After dye vat reclaimed water, twice are washed, per pass washes 15-30 minutes, intakes again and adds 0.3-1 g/l of the glacial acetic acid of 98% concentration, Band water goes out dye vat after operating 10-15 minutes；
Sizing：170-190 DEG C of setting temperature, the setting temperature purpose higher than common fabric are to make fabric contraction more abundant, are added Hydrophilic softening agent 0.3-1%, fabric are entered in shaping baking oven by padding machine, and the speed of padding machine is 21-25 ms/min.
2. the dyeing and finishing processing method of the high-shrinkage filament fabric of imitative numb cotton according to claim 1, it is characterised in that the dye Dyestuff in the dye liquor that color step uses its dosage depending on each color.
CN201610135136.2A 2016-03-10 2016-03-10 A kind of dyeing and finishing processing method of the high-shrinkage filament fabric of imitative numb cotton Active CN105648794B (en)