CN105648782A - 一种石蜡相变微胶囊调温面料的制备方法 - Google Patents
一种石蜡相变微胶囊调温面料的制备方法 Download PDFInfo
- Publication number
- CN105648782A CN105648782A CN201610194541.1A CN201610194541A CN105648782A CN 105648782 A CN105648782 A CN 105648782A CN 201610194541 A CN201610194541 A CN 201610194541A CN 105648782 A CN105648782 A CN 105648782A
- Authority
- CN
- China
- Prior art keywords
- phase change
- fabric
- change microcapsule
- weight portion
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种石蜡相变微胶囊调温面料的制备方法,主要包括石蜡乳液制备步骤、混合液制备步骤、石蜡相变微胶囊制备步骤、石蜡相变微胶囊涂布步骤等,将此种相变调温微胶囊应用到织物表面,可以为人体提供相对普通织物更舒适的穿着环境,使人体始终处于一种舒适的状态。
Description
技术领域
本发明涉及一种调温面料,特别涉及一种石蜡相变微胶囊调温面料的制备方法。
背景技术
服装织物是人们日常生活中必不可少的物品,主要起到防寒保暖作用。通常情况下,服装织物温度依靠环境温度及人体的体温来调节,缺乏有效的保温效果,因此人们只能通过增加或者减少服装物料的厚薄多寡来调节所需的舒适温度,而有时过多过厚的衣物带来了诸如活动不便和臃肿的困扰。
相变调温微胶囊是一种将相变材料包裹在微小的胶囊球中,相变物质随着外界环境温度的变化发生相变以吸收或释放热量的方式来微小地调节周身温度。
但目前为止,很少研究将相变调温微胶囊与衣物相结合,所以研发相变微胶囊调温面料是有必要的。
发明内容
本发明的目的,就是为了解决上述问题而提供了一种石蜡相变微胶囊调温面料的制备方法,将相变调温微胶囊应用到织物表面,可以为人体提供相对普通织物更舒适的穿衣环境。
为实现上述目的,本发明的技术方案实施如下:
本发明的一种石蜡相变微胶囊调温面料的制备方法,包括以下制备步骤:
步骤1:将0.5-1重量份的均苯三甲酰氯和10-15重量份的石蜡共熔,并加入2-3重量份的油酸聚氧乙烯酯和10-15重量份的去离子水,在50-60℃的条件下,搅拌20-30min,随后加入乙酸搅拌,至PH为5-6时,获得石蜡乳液;
步骤2:在搅拌和30-40℃的条件下,向步骤1的石蜡乳液中加入0.1-0.3重量份的三聚氰胺-甲醛预聚体,温度升至60℃,保温2h后,将温度冷却至20-30℃之间,获得混合液;
步骤3:在搅拌和30-40℃的条件下,向步骤2的混合液中加入0.3-0.5重量份的三聚氰胺-甲醛预聚体,温度升至60℃,保温2h后,继续升温至80℃,保温2h,然后加入0.1-0.2重量份的尿素,获得石蜡相变微胶囊;
步骤4:将面料洗净后,在40-50℃下烘干20-30min;
步骤5:在经步骤4处理后的面料上均匀涂布一层涂层胶,随后涂布一层石蜡相变微胶囊,石蜡相变微胶囊的厚度为0.01-0.02mm;
步骤6:在60-70℃的温度下,将经步骤5处理后的面料烘干10-20min,随后在120-150℃的温度下,继续烘干5-10min,即获得本发明的调温面料。
本发明的有益效果如下:
将相变调温微胶囊应用到织物表面,可以为人体提供相对普通织物更舒适的穿衣环境。与现有技术相比,本发明将微胶囊与织物相结合,在不同环境条件下,织物可根据外界情况调节温度,可解决衣物穿着过多行动不便等问题。
具体实施方式
下面将结合实施例,对本发明作进一步说明。
实施例1
本实施例包括以下步骤:
步骤1:将0.5kg的均苯三甲酰氯和10kg的石蜡共熔,并加入2kg的油酸聚氧乙烯酯和10kg的去离子水,在50℃的条件下,搅拌20min,随后加入乙酸搅拌,至PH为5-6时,获得石蜡乳液;
步骤2:在搅拌和30℃的条件下,向步骤1的石蜡乳液中加入0.2kg的三聚氰胺-甲醛预聚体,温度升至60℃,保温2h后,将温度冷却至20-30℃之间,获得混合液;
步骤3:在搅拌和30℃的条件下,向步骤2的混合液中加入0.3kg的三聚氰胺-甲醛预聚体,温度升至60℃,保温2h后,继续升温至80℃,保温2h,然后加入0.1kg的尿素,获得石蜡相变微胶囊;
步骤4:将面料洗净后,在40℃下烘干30min;
步骤5:在经步骤4处理后的面料上均匀涂布一层涂层胶,随后涂布一层石蜡相变微胶囊,石蜡相变微胶囊的厚度为0.01-0.02mm;
步骤6:在60℃的温度下,将经步骤5处理后的面料烘干20min,随后在120℃的温度下,继续烘干5min,即获得调温面料1。
实施例1
本实施例包括以下步骤:
步骤1:将0.7kg的均苯三甲酰氯和12kg的石蜡共熔,并加入2kg的油酸聚氧乙烯酯和12kg的去离子水,在60℃的条件下,搅拌30min,随后加入乙酸搅拌,至PH为5-6时,获得石蜡乳液;
步骤2:在搅拌和40℃的条件下,向步骤1的石蜡乳液中加入0.3kg的三聚氰胺-甲醛预聚体,温度升至60℃,保温2h后,将温度冷却至20-30℃之间,获得混合液;
步骤3:在搅拌和40℃的条件下,向步骤2的混合液中加入0.4kg的三聚氰胺-甲醛预聚体,温度升至60℃,保温2h后,继续升温至80℃,保温2h,然后加入0.15kg的尿素,获得石蜡相变微胶囊;
步骤4:将面料洗净后,在50℃下烘干30min;
步骤5:在经步骤4处理后的面料上均匀涂布一层涂层胶,随后涂布一层石蜡相变微胶囊,石蜡相变微胶囊的厚度为0.01-0.02mm;
步骤6:在70℃的温度下,将经步骤5处理后的面料烘干20min,随后在130℃的温度下,继续烘干10min,即获得调温面料2。
将市售普通面料、调温面料1和调温面料2进行温度测试(室温为18℃),测试结果如下表所示:
通过上表可知,本发明的石蜡相变微胶囊调温面料与普通面料相比,在高温和低温条件下可在一定范围内调节温度,如果用该面料制成衣物,在40℃的环境温度下可使衣物温度控制在20-30℃之间,在0℃的环境温度下可使衣物温度控制在8-12℃之间。
以上实施例仅供说明本发明之用,而非对本发明的限制,有关技术领域的技术人员,在不脱离本发明的精神和范围的情况下,还可以作出各种变换或变型,因此所有等同的技术方案也应该属于本发明的范畴,应由各权利要求所限定。
Claims (1)
1.一种石蜡相变微胶囊调温面料的制备方法,其特征在于,包括以下制备步骤:
步骤1:将0.5-1重量份的均苯三甲酰氯和10-15重量份的石蜡共熔,并加入2-3重量份的油酸聚氧乙烯酯和10-15重量份的去离子水,在50-60℃的条件下,搅拌20-30min,随后加入乙酸搅拌,至PH为5-6时,获得石蜡乳液;
步骤2:在搅拌和30-40℃的条件下,向步骤1的石蜡乳液中加入0.1-0.3重量份的三聚氰胺-甲醛预聚体,温度升至60℃,保温2h后,将温度冷却至20-30℃之间,获得混合液;
步骤3:在搅拌和30-40℃的条件下,向步骤2的混合液中加入0.3-0.5重量份的三聚氰胺-甲醛预聚体,温度升至60℃,保温2h后,继续升温至80℃,保温2h,然后加入0.1-0.2重量份的尿素,获得石蜡相变微胶囊;
步骤4:将面料洗净后,在40-50℃下烘干20-30min;
步骤5:在经步骤4处理后的面料上均匀涂布一层涂层胶,随后涂布一层石蜡相变微胶囊,石蜡相变微胶囊的厚度为0.01-0.02mm;
步骤6:在60-70℃的温度下,将经步骤5处理后的面料烘干10-20min,随后在120-150℃的温度下,继续烘干5-10min,即获得本发明的调温面料。