CN105623266A - 一种新型复合高性能导电橡胶 - Google Patents
一种新型复合高性能导电橡胶 Download PDFInfo
- Publication number
- CN105623266A CN105623266A CN201410611251.3A CN201410611251A CN105623266A CN 105623266 A CN105623266 A CN 105623266A CN 201410611251 A CN201410611251 A CN 201410611251A CN 105623266 A CN105623266 A CN 105623266A
- Authority
- CN
- China
- Prior art keywords
- parts
- new type
- composite high
- performance
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种新型复合高性能导电橡胶，该发明的配方由以下重量份组成：硅橡胶40-60；硅烷偶联剂5-10；硬脂酸镁10-15；纳米氧化锌15-20；导电颗粒10-15；硫磺5-15；硫化剂1-5；阻燃剂2-5；防焦剂0.1-0.5；防老剂1-7；减磨剂1-5；松香1-5；石蜡1-5。该发明制成了导电橡胶的优点是：导电效率高，不易老化，物理机械性能、及屏蔽效能很好，且使用寿命长，成本低。
Description
技术领域
本发明涉及一种新型复合高性能导电橡胶。
背景技术
目前,导电橡胶制品作为功能性橡胶制品发展很好,应用范围日趋广泛。但是，市场上主要多以乙炔碳黑作为导电介质的导电材料，高分子基础料主要是天然橡胶，三元乙丙橡胶等，他们导电性能低，易老化，物理机械性能、及屏蔽效能较差，不能满足用户的要求。
发明内容
本发明的目的就在于克服上述不足，提供一种新型复合高性能导电橡胶。为实现上述目的，本发明的配方由以下重量份组成：
硅橡胶40-60
硅烷偶联剂5-10
硬脂酸镁10-15
纳米氧化锌15-20
导电颗粒10-15
硫磺5-15
硫化剂1-5
阻燃剂2-5
防焦剂0.1-0.5
防老剂1—7
减磨剂1-5
松香1-5
石蜡1-5
进一步的优化方案，一种新型复合高性能导电橡胶由以下重量份组成：
硅橡胶50-60
硅烷偶联剂5-10
硬脂酸镁10-15
纳米氧化锌15-20
导电颗粒10-15
硫磺5-15
阻燃剂2-5
防焦剂0.1-0.5
防老剂1-7
松香1-5
减磨剂1-5
进一步优化方案：导电颗粒为铜粉、铝粉、镁粉按重量分数比2：2：1的混合物。
进一步优化方案：防老剂为6-乙氧基-2，2，4-三甲基-1，2二氢化喹啉、N-苯基-a-苯胺按重量比1：1的混合物。
进一步优化方案：硅橡胶为高温硫化硅橡胶。
进一步优化方案：防焦剂为N-环己基硫代邻苯二甲酰胺或邻苯二甲酸酐或水杨酸。
进一步优化方案：阻燃剂为四溴双酚A。
该发明制成了导电橡胶的优点是：导电效率高，不易老化，物理机械性能、及屏蔽效能很好，且使用寿命长，成本低。
具体实施方式
下面结合具体实施例，进一步来介绍本发明。这些实施例子不用于限制本发明的范围。
实施例1
该一种新型复合高性能导电橡胶，本发明的配方由以下重量份组成：
硅橡胶60
硅烷偶联剂10
硬脂酸镁10
纳米氧化锌15
导电颗粒10
硫磺15
硫化剂1
四溴双酚A2
N-环己基硫代邻苯二甲酰胺0.1
防老剂1
减磨剂2
松香2
石蜡2
实施例2
该一种新型复合高性能导电橡胶由以下重量份组成：
高温硫化硅橡胶50
硅烷偶联剂5
硬脂酸镁10
纳米氧化锌15
导电颗粒10
硫磺5
四溴双酚A2
水杨酸0.1
防老剂1
松香1
减磨剂1。
Claims (7)
1.一种新型复合高性能导电橡胶，其特征在于：该配方由以下重量份组成：
硅橡胶40-60
硅烷偶联剂5-10
硬脂酸镁10-15
纳米氧化锌15-20
导电颗粒10-15
硫磺5-15
硫化剂1-5
阻燃剂2-5
防焦剂0.1-0.5
防老剂1—7
减磨剂1-5
松香1-5
石蜡1-5。
2.根据权利要求1所述的一种新型复合高性能导电橡胶，其特征在于：
硅橡胶50-60
硅烷偶联剂5-10
硬脂酸镁10-15
纳米氧化锌15-20
导电颗粒10-15
硫磺5-15
阻燃剂2-5
防焦剂0.1-0.5
防老剂1-7
松香1-5
减磨剂1-5。
3.根据权利要求1所述的一种新型复合高性能导电橡胶，其特征在于：所述导电颗粒为铜粉、铝粉、镁粉按重量分数比2：2：1的混合物。
4.根据权利要求1所述的一种新型复合高性能导电橡胶，其特征在于：所述防老剂为6-乙氧基-2，2，4-三甲基-1，2二氢化喹啉、N-苯基-a-苯胺按重量比1：1的混合物。
5.根据权利要求1所述的一种新型复合高性能导电橡胶，其特征在于：所述硅橡胶为高温硫化硅橡胶。
6.根据权利要求1所述的一种新型复合高性能导电橡胶，其特征在于：所述防焦剂为N-环己基硫代邻苯二甲酰胺或邻苯二甲酸酐或水杨酸。
7.根据权利要求1所述的一种新型复合高性能导电橡胶，其特征在于：所述阻燃剂为四溴双酚A。