CN105617785A - 中央空调用滤芯 - Google Patents

中央空调用滤芯 Download PDF

Info

Publication number
CN105617785A
CN105617785A CN201610188169.3A CN201610188169A CN105617785A CN 105617785 A CN105617785 A CN 105617785A CN 201610188169 A CN201610188169 A CN 201610188169A CN 105617785 A CN105617785 A CN 105617785A
Authority
CN
China
Prior art keywords
layer
central air
filter core
melt
layers
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610188169.3A
Other languages
English (en)
Inventor
陈映飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Shenyang Environment Protection Technology Co Ltd
Original Assignee
Jiangsu Shenyang Environment Protection Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Shenyang Environment Protection Technology Co Ltd filed Critical Jiangsu Shenyang Environment Protection Technology Co Ltd
Priority to CN201610188169.3A priority Critical patent/CN105617785A/zh
Publication of CN105617785A publication Critical patent/CN105617785A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种中央空调用滤芯，包括框体和设置在框体内的V型连续折转结构的过滤材料，所述过滤材料上贴合有支撑副，所述支撑副与过滤材料上的V型槽相垂直，所述支撑副的两端固定在框体上；所述过滤材料包括吸附层、聚酯骨架层、静电处理后的熔喷无纺布层和静电处理后的熔喷过滤棉层，所述聚酯骨架层为两层，分别位于吸附层两侧，所述熔喷无纺布层设置在聚酯骨架层上，所述熔喷过滤棉层设置在熔喷无纺布层上。其可以有效的实现PM2.5等粉尘物和甲醛等有害气体的过滤和吸收，保证良好的空气质量的同时，减少额外电器的购买和使用，从而更好的实现节能减排。

Description

中央空调用滤芯
技术领域
本发明涉及空气净化领域，特别是，涉及一种中央空调用滤芯。
背景技术
随着人民生活水平的提高，对空气质量的要求也逐渐提升，尤其是雾霾等现象的存在，空气净化装置似乎正逐渐成为每个家庭必备的电器，即使在办公区域，也越来越多的企业选择购买相应的空气过滤器以保证更好的工作环境。现有的中央空调还大多停留在调节温度的功能上，而忽略了其空气过滤的功能，其主要原因是没有合适的滤芯，如何找到合适的解决方法，实现中央空调对PM2.5等粉尘物和甲醛等有害气体的过滤和吸收，从而保证良好的空气环境的同时，更好的实现节能减排，是一个亟需解决的技术问题。
发明内容
为了克服现有技术的不足，本发明的目的在于提供一种中央空调用滤芯，其可以有效的实现PM2.5等粉尘物和甲醛等有害气体的过滤和吸收，保证良好的空气质量的同时，减少额外电器的购买和使用，从而更好的实现节能减排。
为解决上述问题，本发明所采用的技术方案如下：
中央空调用滤芯，包括框体和设置在框体内的V型连续折转结构的过滤材料，所述过滤材料上贴合有支撑副，所述支撑副与过滤材料上的V型槽相垂直，所述支撑副的两端固定在框体上；所述过滤材料包括吸附层、聚酯骨架层、静电处理后的熔喷无纺布层和静电处理后的熔喷过滤棉层，所述聚酯骨架层为两层，分别位于吸附层两侧，所述熔喷无纺布层设置在聚酯骨架层上，所述熔喷过滤棉层设置在熔喷无纺布层上。
优选的，还包括密封圈，所述密封圈贴合在框体上。
优选的，所述密封圈为两个，分别贴合在框体两侧。
优选的，所述过滤材料还包括负离子添加剂层，所述负离子添加剂层设置在熔喷无纺布层和熔喷过滤棉层之间。
优选的，所述负离子添加剂层由以下质量百分比的组分组成：H2O50％、SiO223％、Al2O318.5％、B2O35.5％、TiO21.5％、Fe2O30.7％、FeO0.4％、MgO0.2％、Li2O0.1％和MnO0.1％，所述负离子添加剂层厚度为0.05-0.1mm。
优选的，所述吸附层中吸附剂为活性炭、氧化铝、硅藻土中任一种或几种，所述吸附层厚度为1.2-1.5mm。
优选的，所述熔喷无纺布层材料为聚丙烯或聚对苯二甲酸乙二醇酯，所述熔喷无纺布层为两层，每层厚度为0.15-0.18mm。
优选的，所述熔喷过滤棉层材料为聚丙烯或聚对苯二甲酸乙二醇酯，所述熔喷过滤棉层为两层，每层厚度为0.3-0.45mm。
优选的，所述聚酯骨架层材料为聚对苯二甲酸乙二醇酯或聚对苯二甲酸丁二醇酯，每层厚度为0.2-0.25mm。
优选的，所述过滤材料中的每个V型槽高度h为1.0-2.5cm，宽度d为0.5-2.0cm。
相比现有技术，本发明的有益效果在于：
本发明有效的实现PM2.5等粉尘物和甲醛等有害气体的过滤和吸收，保证良好的空气质量的同时，减少额外电器的购买和使用，从而更好的实现节能减排；V型连续折转结构提供了更大的接触面积，提高了过滤的效率，支撑副的使用进一步加强了过滤材料的结构的稳定性，延长其使用寿命；聚酯骨架层具有良好的弹性，可对内部起吸附作用的材料起到良好的支撑和保护作用，提高过滤材料的强度，从而延长其使用寿命；熔喷无纺布和熔喷过滤棉经等离子处理和恒压电晕充电处理，可捕获空气中粉尘粒子，其内静电场的存在保证气流中的带电微粒通过材料纤维孔隙时，即被轻易捕获，从而大大提高了对固体污染物过滤效率；负离子添加剂层和吸附层可以实现TVOC、甲醛等有害气体污染物的过滤，实现了对空气净化的高净化效能；密封圈可以保证滤芯和中央空调的有效贴合，保证过滤的有效性。
附图说明
图1为本发明中中央空调用滤芯的结构示意图；
图2为图1中中央空调用滤芯A-A剖视图；
图3为图2中D处局部放大图；
图4为本发明中过滤材料结构示意图；
图5为实施例1中过滤材料结构示意图；
其中，1为框体、2为过滤材料、201为吸附层、202为聚酯骨架层、203为熔喷无纺布层、204为熔喷过滤棉层、205为负离子添加剂层、3为支撑副、4为密封圈、d为V型槽的宽度、h为V型槽的高度。
具体实施方式
下面结合附图和具体实施方式对本发明作进一步详细说明。
如图1-4所示，本发明中中央空调用滤芯包括框体1和设置在框体1内的V型连续折转结构的过滤材料2，过滤材料2上贴合有支撑副3，支撑副3与过滤材料2上的V型槽相垂直，支撑副3的两端固定在框体1上；过滤材料2包括吸附层201、聚酯骨架层202、静电处理后的熔喷无纺布层203和静电处理后的熔喷过滤棉层204，聚酯骨架层202为两层，分别位于吸附层201两侧，熔喷无纺布层203设置在聚酯骨架层202上，熔喷过滤棉层204设置在熔喷无纺布层203上。
优选方案中，该滤芯还包括密封圈4，密封圈4贴合在框体1上，密封圈4可以保证滤芯和中央空调的有效贴合，保证过滤的有效性。过滤材料2中的每个V型槽高度h为1.0-2.5cm，宽度d为0.5-2.0cm，V型连续折转结构提供了更大的接触面积，提高了过滤的效率。
实施例1
如图5所示，中央空调用滤芯包括框体1和设置在框体1内的V型连续折转结构的过滤材料2，过滤材料2上贴合有支撑副3，支撑副3与过滤材料2上的V型槽相垂直，支撑副3的两端固定在框体1上；过滤材料2包括吸附层201、聚酯骨架层202、静电处理后的熔喷无纺布层203、静电处理后的熔喷过滤棉层204和负离子添加剂层205，聚酯骨架层202为两层，分别位于吸附层201两侧，熔喷无纺布层203设置在聚酯骨架层202上，熔喷过滤棉层204设置在熔喷无纺布层203上，负离子添加剂层205设置在熔喷无纺布层203和熔喷过滤棉层204之间。该滤芯还包括密封圈4，密封圈4为两个，分别贴合在框体1两侧。
其中，负离子添加剂层205由以下质量百分比的组分组成：H2O50％、SiO223％、Al2O318.5％、B2O35.5％、TiO21.5％、Fe2O30.7％、FeO0.4％、MgO0.2％、Li2O0.1％和MnO0.1％，负离子添加剂层205厚度为0.6mm。
吸附层201中吸附剂为活性炭，吸附层201厚度为1.3mm。
聚酯骨架层202材料为聚对苯二甲酸丁二醇酯，每层厚度为0.22mm。
熔喷无纺布层203材料为聚丙烯，熔喷无纺布层203为两层，每层厚度为0.16mm。
熔喷过滤棉层204材料为聚对苯二甲酸乙二醇酯，熔喷过滤棉层204为两层，每层厚度为0.35mm。
过滤材料2中的每个V型槽高度h为1.5cm，宽度d为1.5cm。
对实施例1获得的滤芯进行检测，其在300m3/h的风量条件下，对PM2.5的一次性过滤效率高达93.2％，阻力仅为28Pa。安装于空调的回风口处进行测试，15min以内25平米的室内PM2.5的浓度从200ug/m3下降至20ug/m3，循环净化效率高达90％。
本发明有效的实现PM2.5等粉尘物和甲醛等有害气体的过滤和吸收，保证良好的空气质量的同时，减少额外电器的购买和使用，从而更好的实现节能减排；V型连续折转结构提供了更大的接触面积，提高了过滤的效率，支撑副的使用进一步加强了过滤材料的结构的稳定性，延长其使用寿命；聚酯骨架层具有良好的弹性，可对内部起吸附作用的材料起到良好的支撑和保护作用，提高过滤材料的强度，从而延长其使用寿命；熔喷无纺布和熔喷过滤棉经等离子处理和恒压电晕充电处理，可捕获空气中粉尘粒子，其内静电场的存在保证气流中的带电微粒通过材料纤维孔隙时，即被轻易捕获，从而大大提高了对固体污染物过滤效率；负离子添加剂层和吸附层可以实现TVOC、甲醛等有害气体污染物的过滤，实现了对空气净化的高净化效能；密封圈可以保证滤芯和中央空调的有效贴合，保证过滤的有效性。
对本领域的技术人员来说，可根据以上描述的技术方案以及构思，做出其它各种相应的改变以及形变，而所有的这些改变以及形变都应该属于本发明权利要求的保护范围之内。

Claims (10)

1.中央空调用滤芯，其特征在于，包括框体和设置在框体内的V型连续折转结构的过滤材料，所述过滤材料上贴合有支撑副，所述支撑副与过滤材料上的V型槽相垂直，所述支撑副的两端固定在框体上；所述过滤材料包括吸附层、聚酯骨架层、静电处理后的熔喷无纺布层和静电处理后的熔喷过滤棉层，所述聚酯骨架层为两层，分别位于吸附层两侧，所述熔喷无纺布层设置在聚酯骨架层上，所述熔喷过滤棉层设置在熔喷无纺布层上。
2.如权利要求1所述的中央空调用滤芯，其特征在于，还包括密封圈，所述密封圈贴合在框体上。
3.如权利要求2所述的中央空调用滤芯，其特征在于，所述密封圈为两个，分别贴合在框体两侧。
4.如权利要求1所述的中央空调用滤芯，其特征在于，所述过滤材料还包括负离子添加剂层，所述负离子添加剂层设置在熔喷无纺布层和熔喷过滤棉层之间。
5.如权利要求4所述的中央空调用滤芯，其特征在于，所述负离子添加剂层由以下质量百分比的组分组成：H2O50％、SiO223％、Al2O318.5％、B2O35.5％、TiO21.5％、Fe2O30.7％、FeO0.4％、MgO0.2％、Li2O0.1％和MnO0.1％，所述负离子添加剂层厚度为0.05-0.1mm。
6.如权利要求1所述的中央空调用滤芯，其特征在于，所述吸附层中吸附剂为活性炭、氧化铝、硅藻土中任一种或几种，所述吸附层厚度为1.2-1.5mm。
7.如权利要求1所述的中央空调用滤芯，其特征在于，所述熔喷无纺布层材料为聚丙烯或聚对苯二甲酸乙二醇酯，所述熔喷无纺布层为两层，每层厚度为0.15-0.18mm。
8.如权利要求1所述的中央空调用滤芯，其特征在于，所述熔喷过滤棉层材料为聚丙烯或聚对苯二甲酸乙二醇酯，所述熔喷过滤棉层为两层，每层厚度为0.3-0.45mm。
9.如权利要求1所述的中央空调用滤芯，其特征在于，所述聚酯骨架层材料为聚对苯二甲酸乙二醇酯或聚对苯二甲酸丁二醇酯，每层厚度为0.2-0.25mm。
10.如权利要求1-9任一项所述的中央空调用滤芯，其特征在于，所述过滤材料中的每个V型槽高度h为1.0-2.5cm，宽度d为0.5-2.0cm。
CN201610188169.3A 2016-03-29 2016-03-29 中央空调用滤芯 Pending CN105617785A (zh)