CN105603753A - Multifunctional blended yarn - Google Patents
Multifunctional blended yarn Download PDFInfo
- Publication number
- CN105603753A CN105603753A CN201510985493.3A CN201510985493A CN105603753A CN 105603753 A CN105603753 A CN 105603753A CN 201510985493 A CN201510985493 A CN 201510985493A CN 105603753 A CN105603753 A CN 105603753A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- weight
- parts
- blended yarn
- stir
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses multifunctional blended yarn. The multifunctional blended yarn is subjected to padding processing, and the padding processing comprises steps as follows: 1), 1-2 parts by weight of fatty alcohol-polyoxyethylene ether, 0.8 parts by weight of hexyldecanol, 0.2 parts by weight of calcium carbonate and 1.1 parts by weight of sodium sulfate are added to 17.6 parts by weight of deionized water and are uniformly stirred; 2), 0.7 parts by weight of magnesium chloride, 0.9 parts by weight of potassium persulfate, 1.3 parts by weight of polyoxyethylene ether and 0.9 parts by weight of dimethyl octadecyl hydroxy ethyl ammonium nitrate are added slowly and simultaneously and are stirred continuously until the components are mixed uniformly and sufficiently, and a finishing liquid is prepared; 3), the blended yarn is subjected to padding processing in the finishing liquid and then is taken out for drying at the constant temperature. The multifunctional blended yarn has excellent mildew-proof, mothproof, antibacterial, flame-retardant and anti-static properties.
Description
Technical field
The present invention relates to multifunctional blended yarn.
Background technology
The performance of existing multifunctional blended yarn is single, can not meet client's requirement.
Summary of the invention
The object of the present invention is to provide a kind of multifunctional blended yarn, it has excellent mildew-resistant, mothproof, antibacterial, fire-retardant, antistatic property.
For achieving the above object, technical scheme of the present invention is a kind of multifunctional blended yarn of design, and it is through padding processing, and this pads to process and comprises the steps:
1) in 17.6 parts by weight of deionized water, drop into 1～2 weight portion AEO, 0.8 weight portion hexyl decyl alcohol, 0.2 weight portion calcium carbonate, 1.1 weight portion sodium sulphate, stir;
2) slowly add again 0.7 weight portion magnesium chloride, 0.9 weight portion potassium peroxydisulfate, 1.3 weight portion APEOs, 0.9 weight portion octadecyl dimethyl ethoxy quaternary ammonium nitrate simultaneously, continue to stir, to fully mixing, make dressing liquid;
3) mixed yarn is padded in dressing liquid to processing, constant temperature drying after taking out.
Preferably, multifunctional blended yarn, it is through padding processing, and this pads to process and comprises the steps:
1) in 17.6 parts by weight of deionized water, drop into 1 weight portion AEO, 0.8 weight portion hexyl decyl alcohol, 0.2 weight portion calcium carbonate, 1.1 weight portion sodium sulphate, stir;
2) slowly add again 0.7 weight portion magnesium chloride, 0.9 weight portion potassium peroxydisulfate, 1.3 weight portion APEOs, 0.9 weight portion octadecyl dimethyl ethoxy quaternary ammonium nitrate simultaneously, continue to stir, to fully mixing, make dressing liquid;
3) mixed yarn is padded in dressing liquid to processing, constant temperature drying after taking out.
Preferably, multifunctional blended yarn, it is through padding processing, and this pads to process and comprises the steps:
1) in 17.6 parts by weight of deionized water, drop into 2 weight portion AEOs, 0.8 weight portion hexyl decyl alcohol, 0.2 weight portion calcium carbonate, 1.1 weight portion sodium sulphate, stir;
2) slowly add again 0.7 weight portion magnesium chloride, 0.9 weight portion potassium peroxydisulfate, 1.3 weight portion APEOs, 0.9 weight portion octadecyl dimethyl ethoxy quaternary ammonium nitrate simultaneously, continue to stir, to fully mixing, make dressing liquid;
3) mixed yarn is padded in dressing liquid to processing, constant temperature drying after taking out.
Advantage of the present invention and beneficial effect are: a kind of multifunctional blended yarn is provided, and it has excellent mildew-resistant, mothproof, antibacterial, fire-retardant, antistatic property.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described. Following examples are only for technical scheme of the present invention is more clearly described, and can not limit the scope of the invention with this.
The concrete technical scheme of implementing of the present invention is:
Embodiment 1
A kind of multifunctional blended yarn, it is through padding processing, and this pads to process and comprises the steps:
1) in 17.6 parts by weight of deionized water, drop into 1～2 weight portion AEO, 0.8 weight portion hexyl decyl alcohol, 0.2 weight portion calcium carbonate, 1.1 weight portion sodium sulphate, stir;
2) slowly add again 0.7 weight portion magnesium chloride, 0.9 weight portion potassium peroxydisulfate, 1.3 weight portion APEOs, 0.9 weight portion octadecyl dimethyl ethoxy quaternary ammonium nitrate simultaneously, continue to stir, to fully mixing, make dressing liquid;
3) mixed yarn is padded in dressing liquid to processing, constant temperature drying after taking out.
Embodiment 2
Multifunctional blended yarn, it is through padding processing, and this pads to process and comprises the steps:
1) in 17.6 parts by weight of deionized water, drop into 1 weight portion AEO, 0.8 weight portion hexyl decyl alcohol, 0.2 weight portion calcium carbonate, 1.1 weight portion sodium sulphate, stir;
2) slowly add again 0.7 weight portion magnesium chloride, 0.9 weight portion potassium peroxydisulfate, 1.3 weight portion APEOs, 0.9 weight portion octadecyl dimethyl ethoxy quaternary ammonium nitrate simultaneously, continue to stir, to fully mixing, make dressing liquid;
3) mixed yarn is padded in dressing liquid to processing, constant temperature drying after taking out.
Embodiment 3
Multifunctional blended yarn, it is through padding processing, and this pads to process and comprises the steps:
1) in 17.6 parts by weight of deionized water, drop into 2 weight portion AEOs, 0.8 weight portion hexyl decyl alcohol, 0.2 weight portion calcium carbonate, 1.1 weight portion sodium sulphate, stir;
2) slowly add again 0.7 weight portion magnesium chloride, 0.9 weight portion potassium peroxydisulfate, 1.3 weight portion APEOs, 0.9 weight portion octadecyl dimethyl ethoxy quaternary ammonium nitrate simultaneously, continue to stir, to fully mixing, make dressing liquid;
3) mixed yarn is padded in dressing liquid to processing, constant temperature drying after taking out.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, do not departing under the prerequisite of the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. multifunctional blended yarn, is characterized in that, it is through padding processing, and this pads to process and comprises the steps:
1) in 17.6 parts by weight of deionized water, drop into 1～2 weight portion AEO, 0.8 weight portion hexyl decyl alcohol, 0.2 weight portion calcium carbonate, 1.1 weight portion sodium sulphate, stir;
2) slowly add again 0.7 weight portion magnesium chloride, 0.9 weight portion potassium peroxydisulfate, 1.3 weight portion APEOs, 0.9 weight portion octadecyl dimethyl ethoxy quaternary ammonium nitrate simultaneously, continue to stir, to fully mixing, make dressing liquid;
3) mixed yarn is padded in dressing liquid to processing, constant temperature drying after taking out.
2. multifunctional blended yarn according to claim 1, is characterized in that, it is through padding processing, and this pads to process and comprises the steps:
1) in 17.6 parts by weight of deionized water, drop into 1 weight portion AEO, 0.8 weight portion hexyl decyl alcohol, 0.2 weight portion calcium carbonate, 1.1 weight portion sodium sulphate, stir;
2) slowly add again 0.7 weight portion magnesium chloride, 0.9 weight portion potassium peroxydisulfate, 1.3 weight portion APEOs, 0.9 weight portion octadecyl dimethyl ethoxy quaternary ammonium nitrate simultaneously, continue to stir, to fully mixing, make dressing liquid;
3) mixed yarn is padded in dressing liquid to processing, constant temperature drying after taking out.
3. multifunctional blended yarn according to claim 1, is characterized in that, it is through padding processing, and this pads to process and comprises the steps:
1) in 17.6 parts by weight of deionized water, drop into 2 weight portion AEOs, 0.8 weight portion hexyl decyl alcohol, 0.2 weight portion calcium carbonate, 1.1 weight portion sodium sulphate, stir;
2) slowly add again 0.7 weight portion magnesium chloride, 0.9 weight portion potassium peroxydisulfate, 1.3 weight portion APEOs, 0.9 weight portion octadecyl dimethyl ethoxy quaternary ammonium nitrate simultaneously, continue to stir, to fully mixing, make dressing liquid;
3) mixed yarn is padded in dressing liquid to processing, constant temperature drying after taking out.