CN105506970A - Crude-fine fiber blended yarn - Google Patents
Crude-fine fiber blended yarn Download PDFInfo
- Publication number
- CN105506970A CN105506970A CN201510985509.0A CN201510985509A CN105506970A CN 105506970 A CN105506970 A CN 105506970A CN 201510985509 A CN201510985509 A CN 201510985509A CN 105506970 A CN105506970 A CN 105506970A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- weight portion
- blended yarn
- stir
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses crude-fine fiber blended yarn. The crude-fine fiber blended yarn is subjected to dipping treatment, and the dipping treatment comprises steps as follows: 1), 1-2 parts by weight of glycerol monostearate, 1.4 parts by weight of hydroxy propyl cellulose, 0.4 parts by weight of zinc sulfate and 1.2 parts by weight of trichloracetic aldehyde are added to 12.7 parts by weight of deionized water, and the materials are stirred uniformly; 2), 0.7 parts by weight of vinyltriethoxysilane, 0.4 parts by weight of potassium peroxodisulfate, 0.8 parts by weight of 2-n-octyl-4-isothiazolin-3-one and 0.9 parts by weight of dimethyl octadecyl hydroxyethyl ammonium nitrate are added simultaneously and slowly, the materials are stirred continuously until the materials are mixed sufficiently and uniformly, and a finishing liquid is prepared; 3), blended yarn is subjected to dipping treatment in the finishing liquid, and then is taken out for drying at the constant temperature. The crude-fine fiber blended yarn has excellent mould-proof, mothproof, anti-bacterial, anti-flaming and anti-static performance.
Description
Technical field
The present invention relates to thickness fiber blend yarn.
Background technology
The performance of existing thickness fiber blend yarn is single, can not meet the requirement of client.
Summary of the invention
The object of the present invention is to provide a kind of thickness fiber blend yarn, it has excellent mildew-resistant, mothproof, antibacterial, fire-retardant, antistatic property.
For achieving the above object, technical scheme of the present invention is a kind of thickness fiber blend yarn of design, and it is through padding process, and this pads process and comprises the steps:
1) in 12.7 parts by weight of deionized water, drop into 1 ~ 2 parts by weight glycerol monostearate, 1.4 weight portion hydroxypropyl celluloses, 0.4 parts sulfuric acid zinc, 1.2 weight portion trichloroacetaldehydes, stir;
2) slowly add 0.7 parts by weight of ethylene ethyl triethoxy silicane alkane, 0.4 weight portion potassium peroxydisulfate, 0.8 weight portion di-n-octyl-4-isothiazoline-3-ketone, 0.9 weight portion octadecyldimethyl ethoxy quaternary ammonium nitrate more simultaneously, continue to stir, to fully mixing, obtained dressing liquid;
3) blended yarn is padded process in dressing liquid, constant temperature drying after taking out.
Preferably, thickness fiber blend yarn, it is through padding process, and this pads process and comprises the steps:
1) in 12.7 parts by weight of deionized water, drop into 1 parts by weight glycerol monostearate, 1.4 weight portion hydroxypropyl celluloses, 0.4 parts sulfuric acid zinc, 1.2 weight portion trichloroacetaldehydes, stir;
2) slowly add 0.7 parts by weight of ethylene ethyl triethoxy silicane alkane, 0.4 weight portion potassium peroxydisulfate, 0.8 weight portion di-n-octyl-4-isothiazoline-3-ketone, 0.9 weight portion octadecyldimethyl ethoxy quaternary ammonium nitrate more simultaneously, continue to stir, to fully mixing, obtained dressing liquid;
3) blended yarn is padded process in dressing liquid, constant temperature drying after taking out.
Preferably, thickness fiber blend yarn, it is through padding process, and this pads process and comprises the steps:
1) in 12.7 parts by weight of deionized water, drop into 2 parts by weight glycerol monostearate, 1.4 weight portion hydroxypropyl celluloses, 0.4 parts sulfuric acid zinc, 1.2 weight portion trichloroacetaldehydes, stir;
2) slowly add 0.7 parts by weight of ethylene ethyl triethoxy silicane alkane, 0.4 weight portion potassium peroxydisulfate, 0.8 weight portion di-n-octyl-4-isothiazoline-3-ketone, 0.9 weight portion octadecyldimethyl ethoxy quaternary ammonium nitrate more simultaneously, continue to stir, to fully mixing, obtained dressing liquid;
3) blended yarn is padded process in dressing liquid, constant temperature drying after taking out.
Advantage of the present invention and beneficial effect are: provide a kind of thickness fiber blend yarn, and it has excellent mildew-resistant, mothproof, antibacterial, fire-retardant, antistatic property.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of thickness fiber blend yarn, it is through padding process, and this pads process and comprises the steps:
1) in 12.7 parts by weight of deionized water, drop into 1 ~ 2 parts by weight glycerol monostearate, 1.4 weight portion hydroxypropyl celluloses, 0.4 parts sulfuric acid zinc, 1.2 weight portion trichloroacetaldehydes, stir;
2) slowly add 0.7 parts by weight of ethylene ethyl triethoxy silicane alkane, 0.4 weight portion potassium peroxydisulfate, 0.8 weight portion di-n-octyl-4-isothiazoline-3-ketone, 0.9 weight portion octadecyldimethyl ethoxy quaternary ammonium nitrate more simultaneously, continue to stir, to fully mixing, obtained dressing liquid;
3) blended yarn is padded process in dressing liquid, constant temperature drying after taking out.
Embodiment 2
Thickness fiber blend yarn, it is through padding process, and this pads process and comprises the steps:
1) in 12.7 parts by weight of deionized water, drop into 1 parts by weight glycerol monostearate, 1.4 weight portion hydroxypropyl celluloses, 0.4 parts sulfuric acid zinc, 1.2 weight portion trichloroacetaldehydes, stir;
2) slowly add 0.7 parts by weight of ethylene ethyl triethoxy silicane alkane, 0.4 weight portion potassium peroxydisulfate, 0.8 weight portion di-n-octyl-4-isothiazoline-3-ketone, 0.9 weight portion octadecyldimethyl ethoxy quaternary ammonium nitrate more simultaneously, continue to stir, to fully mixing, obtained dressing liquid;
3) blended yarn is padded process in dressing liquid, constant temperature drying after taking out.
Embodiment 3
Thickness fiber blend yarn, it is through padding process, and this pads process and comprises the steps:
1) in 12.7 parts by weight of deionized water, drop into 2 parts by weight glycerol monostearate, 1.4 weight portion hydroxypropyl celluloses, 0.4 parts sulfuric acid zinc, 1.2 weight portion trichloroacetaldehydes, stir;
2) slowly add 0.7 parts by weight of ethylene ethyl triethoxy silicane alkane, 0.4 weight portion potassium peroxydisulfate, 0.8 weight portion di-n-octyl-4-isothiazoline-3-ketone, 0.9 weight portion octadecyldimethyl ethoxy quaternary ammonium nitrate more simultaneously, continue to stir, to fully mixing, obtained dressing liquid;
3) blended yarn is padded process in dressing liquid, constant temperature drying after taking out.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. thickness fiber blend yarn, is characterized in that, it is through padding process, and this pads process and comprises the steps:
1) in 12.7 parts by weight of deionized water, drop into 1 ~ 2 parts by weight glycerol monostearate, 1.4 weight portion hydroxypropyl celluloses, 0.4 parts sulfuric acid zinc, 1.2 weight portion trichloroacetaldehydes, stir;
2) slowly add 0.7 parts by weight of ethylene ethyl triethoxy silicane alkane, 0.4 weight portion potassium peroxydisulfate, 0.8 weight portion di-n-octyl-4-isothiazoline-3-ketone, 0.9 weight portion octadecyldimethyl ethoxy quaternary ammonium nitrate more simultaneously, continue to stir, to fully mixing, obtained dressing liquid;
3) blended yarn is padded process in dressing liquid, constant temperature drying after taking out.
2. thickness fiber blend yarn according to claim 1, is characterized in that, it is through padding process, and this pads process and comprises the steps:
1) in 12.7 parts by weight of deionized water, drop into 1 parts by weight glycerol monostearate, 1.4 weight portion hydroxypropyl celluloses, 0.4 parts sulfuric acid zinc, 1.2 weight portion trichloroacetaldehydes, stir;
2) slowly add 0.7 parts by weight of ethylene ethyl triethoxy silicane alkane, 0.4 weight portion potassium peroxydisulfate, 0.8 weight portion di-n-octyl-4-isothiazoline-3-ketone, 0.9 weight portion octadecyldimethyl ethoxy quaternary ammonium nitrate more simultaneously, continue to stir, to fully mixing, obtained dressing liquid;
3) blended yarn is padded process in dressing liquid, constant temperature drying after taking out.
3. thickness fiber blend yarn according to claim 1, is characterized in that, it is through padding process, and this pads process and comprises the steps:
1) in 12.7 parts by weight of deionized water, drop into 2 parts by weight glycerol monostearate, 1.4 weight portion hydroxypropyl celluloses, 0.4 parts sulfuric acid zinc, 1.2 weight portion trichloroacetaldehydes, stir;
2) slowly add 0.7 parts by weight of ethylene ethyl triethoxy silicane alkane, 0.4 weight portion potassium peroxydisulfate, 0.8 weight portion di-n-octyl-4-isothiazoline-3-ketone, 0.9 weight portion octadecyldimethyl ethoxy quaternary ammonium nitrate more simultaneously, continue to stir, to fully mixing, obtained dressing liquid;
3) blended yarn is padded process in dressing liquid, constant temperature drying after taking out.