CN105599522B - A kind of combined process of potsherd and noble metal - Google Patents
A kind of combined process of potsherd and noble metal Download PDFInfo
- Publication number
- CN105599522B CN105599522B CN201511011267.1A CN201511011267A CN105599522B CN 105599522 B CN105599522 B CN 105599522B CN 201511011267 A CN201511011267 A CN 201511011267A CN 105599522 B CN105599522 B CN 105599522B
- Authority
- CN
- China
- Prior art keywords
- potsherd
- noble metal
- blind hole
- moulding
- hole
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of combined process of potsherd and noble metal carries out a moulding to potsherd first, and processes blind hole on the side wall of potsherd；Then noble metal is surrounded into fitting along the edge of potsherd, while processes the through-hole to match with the blind hole on potsherd on noble metal；Finally is passed through in through-hole merging blind hole and welded precious metal and noble metal, the finished product combined with noble metal up to potsherd after secondary moulding with precious metal.Technique of the present invention, pass through the repeat style of potsherd and noble metal, noble metal and potsherd are combined into a new entirety in a welding manner, technique is fine and terse, entire technological process also need not expend the too many time, meet very much modern crafts and make efficient feature, and the art work that finished product is new as one, imparts the new enjoying value of potsherd, artistic value and economic value.
Description
Technical field
The present invention relates to field of ceramic processing, the combined process of specially a kind of potsherd and noble metal.
Background technology
China is the place of origin of ware, and the collection to ware is liking for numerous compatriots.Antique pottery tile refers to China
Ancient pottery and porcelain device spreads a part of relic so far, and wherein most is that ruins grave is unearthed.On the age of antique pottery tile so far
In quotient's week, down toward Ming and Qing, good antique pottery tile should have opening's edge and integral bottom, and can restore according to this, while some are good
Ancient pottery and porcelain on piece there are many ancient times artistic colour painting works, slightly it is more complete with art drawing antique pottery tile suffer from it is high
Reserve value.In the collection of modern antique pottery tile, the reserve value of pottery piece and your tile, which is that people are sincere, to be gasp in admirationd, custom
Talk about " there is ten thousand strings of cash in family, not as good as pottery a piece of ", and your porcelain is also listed in first of five big kilns of Song Dynasty, just made by imperial order when Song for
The hired porcelain in imperial palace.Regrettably, reveal that soil deposits your porcelain of generation and pottery is substantially relic, none is complete, collector and art
Family can only collect some you porcelain and pottery relic, be considered as delicacy to these ancient art treasures, but be also to be only limited to collect.If
If the ancient times treasure that can these " quiet to lie " uses again, their new life and economic value are assigned, this will be pole
Significant.But in the prior art, there is no the precedents that truly full utilization of antique pottery tile is got up, for this purpose, anxious
A kind of new technique is needed to assign the new life of these antique pottery tiles and value.
Invention content
To solve the above-mentioned problems, the purpose of the present invention is to propose to the combined process of a kind of potsherd and noble metal, pass through
Noble metal and potsherd are combined as a whole by specified technology, particular for antique pottery tile, make the antique pottery tile of relic shape
Shine new artistic value and life.
The technical solution that the present invention is taken to solve the above-mentioned problems is：A kind of combination work of potsherd and noble metal
Skill carries out a moulding to potsherd first, and processes blind hole on the side wall of potsherd；Then by noble metal along potsherd
Edge around fitting, while the through-hole to match with the blind hole on potsherd is processed on noble metal；Finally use noble metal
Silk passes through in through-hole merging blind hole and welds precious metal and noble metal, up to potsherd and noble metal after secondary moulding
In conjunction with finished product.
The combined process of a kind of potsherd and noble metal, includes the following steps：
1）Moulding of potsherd and noble metal
Potsherd is chosen, and it is cut, is polished and moulding, and is processed on the potsherd side wall after moulding blind
Hole obtains blank, spare, chooses noble metal, is processed the moulding to match with blank, obtain auxiliary base, spare；
2）Fitting and punching
By step 1）In obtained auxiliary base carried out around blank edge it is seamless applying, processed on auxiliary base after fitting with it is former
The matched through-hole of blind hole on base, and extra auxiliary blank is cut, blank is obtained, it is spare；
3）Welding
Selection and through-hole and the matched precious metal of blind hole pass through precious metal in through-hole merging blind hole, by noble metal
Silk is welded as a whole with auxiliary base, obtains semi-finished product, spare,
4）Secondary moulding
To step 3）In obtained semi-finished product carry out secondary moulding, up to potsherd and noble metal after polishing, polishing
In conjunction with finished product.
The step 1）Middle blind hole at least there are two and each blind hole aperture be 0.1-0.3mm, bruting process is respectively gradually
Polished potsherd 5-10min with the diamond dust of 500 mesh, 1000 mesh, 2000 mesh and 5000 mesh, until potsherd integrally it is mellow and full it is smooth,
Without bur, while it is 0.3-0.5mm and the moulding that matches with potsherd that noble metal is processed to thickness in a mold.
The step 3）Precious metal material used in middle welding is identical as auxiliary blank material matter.
The step 4）In be taken up in order of priority and polished surface of semi-finished, polished by cotton piece buff and wool wheel.
Beneficial effects of the present invention：
Noble metal after moulding directly is surrounded to be fitted in and be made by the combined process of potsherd and noble metal of the present invention
Potsherd surrounding after type, this process are pure manual operations, and fineness is high, can play ceramics and your gold to the maximum extent
Belong to the artistic characteristics after the two combines, then gets blind hole together on the noble metal after fitting and potsherd wall again, and utilize
Wire is inserted into blind hole and welds, and noble metal is firmly fitted in potsherd surrounding by welding, makes noble metal
It combines closely and is integral with potsherd, technique is fine and terse, without complicated preparation and later stage work, entire technological process
Also the too many time need not be expended, meets very much modern crafts and makes efficient feature；
In addition, from artistic angle, noble metal such as gold, silver etc. are used as ornament and the art work, are all people all the time
Extremely like and be keen to, and potsherd itself just has certain enjoying value, artistic value and economic value, this hair
The combined process of the bright potsherd and noble metal, by the repeat style of potsherd and noble metal, by noble metal and antique pottery
Tile is combined into a new entirety, and decoration and the wearing of human body can be slightly directly used in after modification processing, new between becoming one
The art work, this directly imparts the new enjoying value of potsherd, artistic value and economic value, especially inherently have very
The antique pottery tile of high artistic value, through the invention the technique can be detached from the destiny only collected, repeating transmission is radiated vigour,
So that the ancient pottery and porcelain art of Chinese tradition is shone new brilliance again, is to have an epoch-marking significance for traditional Chinese art
's.
Specific implementation mode
With reference to specific embodiment, invention is further described in detail, and the present embodiment is with technical solution of the present invention
Premise gives detailed embodiment and specific operating process, but protection scope of the present invention is not limited to following implementation
Example.
The combined process of a kind of potsherd and noble metal of the present invention carries out a moulding to potsherd first, and
Blind hole is processed on the side wall of potsherd；Then noble metal is surrounded into fitting along the edge of potsherd, while on noble metal
Process the through-hole to match with the blind hole on potsherd；Finally passed through in through-hole merging blind hole and by noble metal with precious metal
Silk is welded with noble metal, the finished product combined with noble metal up to potsherd after secondary moulding.
The combined process of a kind of potsherd and noble metal, includes the following steps：
1）Moulding of potsherd and noble metal
Choose potsherd, especially ancient times incomplete potsherd, such as the pottery in period Song Dynasty, your porcelain, and to its into
Row cutting, polishing and moulding, potsherd is created the shape rich in aesthetic by modeling process according to aesthetics completely, and is being made
Blind hole is processed on potsherd side wall after type, the processing of blind hole is needed by distinctive pneumatic drilling machine in Ceramic manufacturing industry,
The aperture of blind hole obtains blank after processing is completed without excessive, spare, chooses noble metal, such as gold, silver, noble metal need basis
Aesthetics and artistic characteristic after potsherd moulding are selected, and are processed the moulding to match with blank, matched
Moulding refers to noble metal directly being processed to the annular that can be directly carried out with potsherd around being bonded, or be processed into bar shaped,
By the noble metal of bar shaped around being fitted in potsherd edge, then to the two ends of bar shaped noble metal welded also can, noble metal
Auxiliary base is obtained after moulding, it is spare；
2）Fitting and punching
By step 1）In obtained auxiliary base carried out around blank edge seamless applying, fitting process fully relies on artificial behaviour
Make, machinery is avoided to scratch noble metal during fitting, is processed on auxiliary base after fitting matched logical with the blind hole in blank
Hole, the processing of the through-hole are processed according to the position of blind hole on blank side wall, make through-hole and blind hole be combined into one it is new
Blind hole, and cut extra auxiliary blank, the cutting of extra auxiliary blank includes cleaning and item by the metal fragment after processing
The cutting of shape noble metal clout after the connection of two ends after fitting, it is spare up to blank after the completion of fitting and punching；
3）Welding
Selection and through-hole and the matched precious metal of blind hole, your gold that the material of the precious metal must be bonded with blank edge
It is identical to belong to material, and the diameter of precious metal is suitable with the internal diameter of through-hole and blind hole, passes through through-hole to be placed in precious metal blind
Precious metal and auxiliary base are welded as a whole by Kong Zhong, soldering appliance be electric iron or other metal molten soldering appliances, if
Step 1）It is middle that noble metal is processed as bar shaped, then it needs to weld after docking the head and the tail interface of noble metal, obtains semi-finished product, it is spare,
4）Secondary moulding
To step 3）In obtained semi-finished product carry out secondary moulding, secondary moulding include in semi-finished product ceramics combined with metal
Polishing between position and polishing also can weld a hanging ring, as ornament, the hanging ring on the top of semi-finished product with noble metal
It can be used for wire rope handling extension to wear, the finished product combined with noble metal up to potsherd after polishing, polishing.
For the above-mentioned processing step being previously mentioned, the step 1）Middle blind hole at least there are two and each blind hole aperture be
0.1-0.3mm, aperture is excessive to be easy that noble metal is made to be broken, and aperture is too small, is unfavorable for being inserted into welded wire in hole, polishing
Process is respectively gradually with the diamond dust polishing antique pottery tile 5-10min of 500 mesh, 1000 mesh, 2000 mesh and 5000 mesh, four kinds of differences
The time that the diamond dust polishing of mesh number is used gradually increases, until potsherd integrally it is mellow and full it is smooth, exist without bur, while by noble metal
It is 0.3-0.5mm and the moulding that matches with potsherd that thickness is processed in mold.
For the above-mentioned processing step being previously mentioned, the step 3）Precious metal material used in middle welding and auxiliary blank material
Matter is identical.
For the above-mentioned processing step being previously mentioned, the step 4）In be taken up in order of priority through cotton piece buff and wool wheel to semi-finished product
It polished, polished in surface.
Claims (4)
1. the combined process of a kind of potsherd and noble metal, it is characterised in that：A moulding is carried out to potsherd first, and is being made pottery
Blind hole is processed on the side wall of tile；Then noble metal is surrounded into fitting along the edge of potsherd, while is processed on noble metal
Go out the through-hole to match with the blind hole on potsherd；Finally with precious metal pass through through-hole merging blind hole in and by precious metal with
Noble metal welds, the finished product combined with noble metal up to potsherd after secondary moulding；Specific process step is as follows：
1）Moulding of potsherd and noble metal
Potsherd is chosen, and it is cut, is polished and moulding, and blind hole is processed on the potsherd side wall after moulding,
Blank is obtained, it is spare, noble metal is chosen, the moulding to match with blank is processed, obtains auxiliary base, it is spare；
2）Fitting and punching
By step 1）In obtained auxiliary base carried out around blank edge it is seamless applying, processed on auxiliary base after fitting in blank
The matched through-hole of blind hole, and cut extra auxiliary blank, obtain blank, it is spare；
3）Welding
Selection with through-hole and the matched precious metal of blind hole, by precious metal pass through through-hole merging blind hole in, by precious metal with
Auxiliary base is welded as a whole, and obtains semi-finished product, spare,
4）Secondary moulding
To step 3）In obtained semi-finished product carry out secondary moulding, combined with noble metal up to potsherd after polishing, polishing
Finished product.
2. a kind of combined process of potsherd and noble metal as described in claim 1, it is characterised in that：The step 1）In it is blind
Hole at least there are two and each blind hole aperture be 0.1-0.3mm, bruting process respectively gradually with 500 mesh, 1000 mesh, 2000 mesh and
The diamond dust of 5000 mesh is polished antique pottery tile 5-10min, until potsherd integrally it is mellow and full it is smooth, exist without bur, while by noble metal
It is 0.3-0.5mm and the moulding that matches with potsherd that thickness is processed in mold.
3. a kind of combined process of potsherd and noble metal as described in claim 1, it is characterised in that：The step 3）Middle weldering
Precious metal material is identical as auxiliary blank material matter used in connecing.
4. a kind of combined process of potsherd and noble metal as described in claim 1, it is characterised in that：The step 4）Middle elder generation
It is polished surface of semi-finished by cotton piece buff and surface of semi-finished is polished by wool wheel again.