CN105599072B - A kind of sheet material restorative procedure - Google Patents
A kind of sheet material restorative procedure Download PDFInfo
- Publication number
- CN105599072B CN105599072B CN201511020328.0A CN201511020328A CN105599072B CN 105599072 B CN105599072 B CN 105599072B CN 201511020328 A CN201511020328 A CN 201511020328A CN 105599072 B CN105599072 B CN 105599072B
- Authority
- CN
- China
- Prior art keywords
- parts
- defect
- sheet material
- smooth surface
- solidification glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of sheet material restorative procedure, comprise the following steps：1) plate face of sheet material is cleared up；2) check whether sheet material is smooth surface defect, defect on back side be present and lack to expect defect；The use of atomized ash and solidification glue is 100 in mass ratio if smooth surface defect be present：1.5~2.5 the first mixtures of composition, scrape the first mixture using greasy knife and smooth surface defect is repaired；The use of atomized ash and solidification glue is 100 in mass ratio if defect on back side be present：2.5~3.5 the second mixtures of composition, scrape the second mixture using greasy knife and smooth surface defect is repaired；Material defect is lacked if existing, the use of atomized ash and solidification glue is 100 in mass ratio：3.5~4.5 the 3rd mixtures of composition, scrape the 3rd mixture using greasy knife and smooth surface defect is repaired.The present invention is repaired using greasy knife with different proportion atomized ash and solidification glue to defect, and quality is preferable after reparation, small with the aberration of script, difficult for drop-off in the environment of moist high temperature.
Description
Technical field
The present invention relates to sheet material to repair field, more particularly to a kind of sheet material restorative procedure.
Background technology
After sheet material manufactures, because machine or it is artificial the reason for, be likely to result in sheet material breakage, it is therefore desirable to breakage
Sheet material repaired, still, existing restorative procedure has that repairing quality is poor, has larger color with script after reparation
Difference, and easily come off in the environment of moist high temperature.
The information for being disclosed in the background section is merely intended to understanding of the increase to the general background of the present invention, without answering
It has been the prior art well known to persons skilled in the art when being considered as recognizing or implying the information structure in any form.
The content of the invention
It is an object of the invention to provide a kind of sheet material restorative procedure, and matter is repaired so as to overcome existing restorative procedure to exist
Measure poor, there is larger aberration with script after reparation, and the shortcomings that easily come off in the environment of moist high temperature.
To achieve the above object, the invention provides a kind of sheet material restorative procedure, comprise the following steps：1) sheet material is cleared up
Plate face；2) check whether the sheet material is smooth surface defect, defect on back side be present and lack to expect defect；If smooth surface defect be present, make
It is 100 in mass ratio with atomized ash and solidification glue：1.5~2.5 the first mixtures of composition, the first mixture pair is scraped using greasy knife
Smooth surface defect is repaired；The use of atomized ash and solidification glue is 100 in mass ratio if defect on back side be present：2.5~3.5 compositions
Second mixture, scrape the second mixture using greasy knife and smooth surface defect is repaired；Material defect is lacked if existing, uses atomized ash
It is 100 in mass ratio with solidification glue：3.5~4.5 the 3rd mixtures of composition, the 3rd mixture is scraped to smooth surface defect using greasy knife
Repaired.
Preferably, in above-mentioned technical proposal, the surface of sheet material is cleared up using whisk broom and rag in step 1).
Preferably, in above-mentioned technical proposal, during smooth surface defect mending step, quality is pressed with atomized ash and solidification glue in summer
Than for 100：1.5~2 are matched.
Preferably, in above-mentioned technical proposal, during smooth surface defect mending step, quality is pressed with atomized ash and solidification glue in the winter time
Than for 100：2~2.5 are matched.
Preferably, in above-mentioned technical proposal, the solidification glue includes following components by weight：Epoxy resin 40-50
Part, borax 10-20 parts, polysulfone resin 9-15 parts, polyvinyl alcohol 10-15 parts, epoxy acrylic resin 10-13 parts, aliphatic poly
Urethane acrylate 2-6 parts, aerosil 3-5 parts, mercaptopropionic acid 2-4 parts, hexanediyl ester 2-6 parts, coupling
Agent 5-8 parts and diluent 2-4 parts.
Compared with prior art, the present invention has the advantages that：
The present invention determines the species of defect first, and defect is entered using the atomized ash and solidification glue of different proportion using greasy knife
Row is repaired, and repaiies that rear quality is preferable, smaller with the aberration of script and difficult for drop-off in the environment of moist high temperature.
Brief description of the drawings
Fig. 1 is the schematic flow sheet according to sheet material restorative procedure of the present invention.
Embodiment
Below in conjunction with the accompanying drawings, the embodiment of the present invention is described in detail, it is to be understood that the guarantor of the present invention
Shield scope is not limited by embodiment.
Explicitly indicated that unless otherwise other, otherwise in entire disclosure and claims, term " comprising " or its change
Change such as "comprising" or " including " etc. and will be understood to comprise stated part, and do not exclude other composition portions
Point.
Embodiment 1：
Fig. 1 shows the schematic flow sheet of sheet material restorative procedure according to the preferred embodiment of the present invention.As shown in figure 1,
Sheet material restorative procedure comprises the following steps：
(1) plate face of sheet material is cleared up；
Specifically, the surface of sheet material is cleared up using whisk broom and rag.
(2) check whether sheet material is smooth surface defect, defect on back side be present and lack to expect defect；
Putty collocation method is during repairing：
A small amount of atomized ash is taken in trowel centre position using greasy knife, and proportionally squeezes supporting solidification glue in trowel one end
Stir into puttylike.
The use of atomized ash and solidification glue is 100 in mass ratio if smooth surface defect be present：1.5~2.5 the first mixing of composition
Thing, scrape the first mixture using greasy knife and (as filled up using greasy knife to sand holes or hole) repaired to smooth surface defect,
If not repairing once in place, secondary repairing need to be carried out；Wherein, in summer preferably with atomized ash and solidification glue in mass ratio for 100：
1.5~2 are matched, in the winter time preferably with atomized ash and solidification glue in mass ratio for 100：2~2.5 are matched.
The use of atomized ash and solidification glue is 100 in mass ratio if defect on back side be present：2.5~3.5 the second mixing of composition
Thing, scrape the second mixture using greasy knife and smooth surface defect is repaired, if not repairing once in place, secondary repairing need to be carried out.
Material defect is lacked if existing, the use of atomized ash and solidification glue is 100 in mass ratio：The mixing of 3.5~4.5 composition the 3rd
Thing, scrape the 3rd mixture using greasy knife and smooth surface defect is repaired, if not repairing once in place, secondary repairing need to be carried out.
In this embodiment, solidification glue preferably includes following components by weight：40 parts of epoxy resin, 10 parts of borax,
9 parts of polysulfone resin, 10 parts of polyvinyl alcohol, 10 parts of epoxy acrylic resin, 2 parts of aliphatic urethane acrylate, gas phase dioxy
2 parts of 3 parts of SiClx, 2 parts of mercaptopropionic acid, 2 parts of hexanediyl ester, 5 parts of coupling agent and diluent.
It is stirred by above-mentioned component and produces solidification glue, merging the solidification glue by putty is repaired, and is had preferable
Viscosity, it is difficult for drop-off in the environment of moist high temperature.
The present invention determines the species of defect first, and defect is entered using the atomized ash and solidification glue of different proportion using greasy knife
Row is repaired, and repaiies that rear quality is preferable, smaller with the aberration of script and difficult for drop-off in the environment of moist high temperature.
Embodiment 2：
Sheet material restorative procedure is substantially consistent with embodiment 1 in the embodiment, and its difference is the ratio of solidification glue
Difference, solidification glue preferably include following components by weight：50 parts of epoxy resin, 20 parts of borax, 15 parts of polysulfone resin, poly- second
15 parts of enol, 13 parts of epoxy acrylic resin, 6 parts of aliphatic urethane acrylate, 5 parts of aerosil, mercaptopropionic acid 4
Part, 6 parts of hexanediyl ester, 8 parts of coupling agent and 4 parts of diluent.
Embodiment 3：
Sheet material restorative procedure is substantially consistent with embodiment 1 in the embodiment, and its difference is the ratio of solidification glue
Difference, solidification glue preferably include following components by weight：45 parts of epoxy resin, 15 parts of borax, 12 parts of polysulfone resin, poly- second
12 parts of enol, 11 parts of epoxy acrylic resin, 4 parts of aliphatic urethane acrylate, 4 parts of aerosil, mercaptopropionic acid 3
Part, 4 parts of hexanediyl ester, 6 parts of coupling agent and 3 parts of diluent.
The description of the foregoing specific illustrative embodiment to the present invention is to illustrate and the purpose of illustration.These descriptions
It is not wishing to limit the invention to disclosed precise forms, and it will be apparent that according to above-mentioned teaching, can be much changed
And change.The purpose of selecting and describing the exemplary embodiment is that explain that the certain principles of the present invention and its reality should
With so that those skilled in the art can realize and utilize the present invention a variety of exemplaries and
Various chooses and changes.The scope of the present invention is intended to be limited by claims and its equivalents.
Claims (4)
1. a kind of sheet material restorative procedure, it is characterised in that comprise the following steps：
1) plate face of sheet material is cleared up；
2) check whether the sheet material is smooth surface defect, defect on back side be present and lack to expect defect；
The use of atomized ash and solidification glue is 100 in mass ratio if smooth surface defect be present：1.5~2.5 the first mixtures of composition, profit
The first mixture is scraped with greasy knife to repair smooth surface defect；
The use of atomized ash and solidification glue is 100 in mass ratio if defect on back side be present：2.5~3.5 the second mixtures of composition, profit
The second mixture is scraped with greasy knife to repair smooth surface defect；
Material defect is lacked if existing, the use of atomized ash and solidification glue is 100 in mass ratio：3.5~4.5 the 3rd mixtures of composition, profit
The 3rd mixture is scraped with greasy knife to repair smooth surface defect；
The solidification glue includes following components by weight：Epoxy resin 40-50 parts, borax 10-20 parts, polysulfone resin 9-15
Part, aliphatic urethane acrylate 2-6 parts, polyvinyl alcohol 10-15 parts, epoxy acrylic resin 10-13 parts, gas phase titanium dioxide
Silicon 3-5 parts, mercaptopropionic acid 2-4 parts, hexanediyl ester 2-6 parts, coupling agent 5-8 parts and diluent 2-4 parts.
2. sheet material restorative procedure according to claim 1, it is characterised in that using whisk broom and rag to sheet material in step 1)
Surface cleared up.
3. sheet material restorative procedure according to claim 1, it is characterised in that during smooth surface defect mending step, summer with
Atomized ash is 100 in mass ratio with solidification glue：1.5~2 are matched.
4. sheet material restorative procedure according to claim 1, it is characterised in that during smooth surface defect mending step, in the winter time with
Atomized ash is 100 in mass ratio with solidification glue：2~2.5 are matched.