CN1664024A - Light putty - Google Patents
Light putty Download PDFInfo
- Publication number
- CN1664024A CN1664024A CN 200510009810 CN200510009810A CN1664024A CN 1664024 A CN1664024 A CN 1664024A CN 200510009810 CN200510009810 CN 200510009810 CN 200510009810 A CN200510009810 A CN 200510009810A CN 1664024 A CN1664024 A CN 1664024A
- Authority
- CN
- China
- Prior art keywords
- putty
- talcum powder
- weight ratio
- superfine talcum
- following compositions
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Disclosed is sliding atom ash, relating to a kind of polymeric putty. According to the shortage of insufficient fineness and smooth after coating and polishing of the current, the invention provides the sliding atom ash with high fineness and smooth, which comprises main body ash and firming agent with the proportion of 100:2 in mass, and the main body ash comprising the following components with the proportion in mass to be: unsaturated polyester resin, 100; accelerant, 3~5; phenylethene,3~5; pigment, 4~6; ultra-fine talcum powder, 70~90; the firming agent comprising the following components with the proportion in mass to be: initiating agent, 100; pigment, 2~4; stuffing, 4~6. The product possesses the following advantages compared with current adhesive power with the metal, fine and smooth putty surface, replenishing the opening and crack more than 5mm for one time, small degree of shrinkage, fast drying speed, heat-proof temperature being is not less than 120 DEG C, possessing a certain degree of tarnish proofness, good air seasoning property, convenient polishing, and mating with various oil paint.
Description
Technical field:
The present invention relates to a kind of polymerization putty.
Background technology:
The atom ash is a kind of pointing material, and formal name used at school is a polymerization putty, and it is mainly used in filleting before application of metal, non-metal material surface, fills and leads up, in the hope of smooth, slick outward appearance.The atom ash is based on unsaturated polyester, is that with the difference of existing other synthetic resins putty it can regulate curing speed with solidifying agent, and can fast setting, and its maximum application market is mainly automobile making and overhaul industry at present.Continuous development along with the domestic automobile industry, being on the increase of automobile kind and output, competition between industry is growing more intense, visual appearance is noticeable all the more, specification of quality to the atom ash is more and more higher, the kind that can satisfy the atom ash under the special machine condition is required also to get more and more, become extremely urgent scientific research mission so develop serial atom ash goods of new generation.The shortcoming of present polymerization putty is that smooth, the fine and smooth degree after the coating polishing is not enough, is difficult to satisfy the demand of Hyundai Motor manufacturing and maintenance industry.
Summary of the invention:
The present invention is directed to the not enough shortcoming of smooth, fine and smooth degree after there is coating polishing in existing polymerization putty, a kind of exquisiteness, slick light putty are provided, to adapt to industrial multifarious demand such as Hyundai Motor.Light putty of the present invention is made up of main putty, two kinds of components of solidifying agent, the weight ratio of main putty and solidifying agent is 100: 2, and wherein main putty is made up of according to weight ratio following compositions: unsaturated polyester resin: 100, promotor: 3～5, vinylbenzene: 3～5, pigment: 4～6, superfine talcum powder: 70～90; Solidifying agent is made up of according to weight ratio following compositions: initiator: 100, pigment: 2～4, filler: 4～6.The present invention is a body material with resins for universal use or hybrid resin, except that adding universal pigment, filler (titanium dioxide, talcum powder, water-ground limestone, aerosil), also add superfine talcum powder, make prepared super moist polymerization putty, with the manufacturing of satisfying modern sedan limousine with repair needs.The present invention compares with existing polymerization putty, has following advantage:
1, the sticking power with metal is good, easy to use, preparation easily, blade coating smoothness, arbitrarily moulding;
2, the putty surface is fine and smooth, smooth;
3, once can fill up 5mm above hole or crackle, shrinking percentage is little;
4, rate of drying fast (dry 15min below 20 ℃);
5, heat resisting temperature ≮ 120 ℃, ultimate temperature can reach 140 ℃ (1h, 2mm is thick)
6, have certain rust inhibition, can be without priming paint;
7, air-drying property is good, and polishing is convenient, and dry grinding, wet-milling all can;
8, with the supporting use of various paint, as can be supporting with all kinds of coating such as alkyd, nitro, vinylformic acid, amino, Resins, epoxy.
Embodiment:
Embodiment one: the light putty of present embodiment is made up of main putty, two kinds of components of solidifying agent, the weight ratio of main putty and solidifying agent is 100: 2, and wherein main putty is made up of according to weight ratio following compositions: unsaturated polyester resin: 100, promotor: 3～5, vinylbenzene: 3～5, pigment: 4～6, superfine talcum powder: 70～90; Solidifying agent is made up of according to weight ratio following compositions: initiator: 100, pigment: 2～4, filler: 4～6.Described unsaturated polyester resin is the air drying type unsaturated polyester resin; Promotor is cobalt iso-octoate and N, methylphenylamine; Initiator is cyclohexanone peroxide and methylethyl ketone peroxide; Pigment in the main putty is nano titanium oxide; Pigment in the solidifying agent is that yellow ultramarine is stuck with paste, and filler is an aerosil.
Embodiment two: what present embodiment and embodiment one were different is that main putty is made up of according to weight ratio following compositions: the air drying type unsaturated polyester resin: 100, cobalt iso-octoate and xylidine: 2～4, vinylbenzene: 8～10, nano titanium oxide: 5, superfine talcum powder 1800
#: 50, superfine talcum powder 1200
#: 20, superfine talcum powder 800
#: 10; Solidifying agent is made up of according to weight ratio following compositions: cyclohexanone peroxide and methylethyl ketone peroxide: 100, yellow ultramarine is stuck with paste: 3, aerosil: 5.
Embodiment three: the light putty of present embodiment is made up of main putty, two kinds of components of solidifying agent, and the weight ratio of main putty and solidifying agent is 100: 2, and its concrete proportioning sees Table 1.
Table 1
| System forms | Weight (g) | ||||||
| A component main putty | Air drying type unsaturated polyester resin CN-225 | ????100 | ????100 | ????100 | ????100 | ????100 | ????100 |
| Cobalt iso-octoate+xylidine | ????3 | ????4 | ????2 | ????3 | ????2 | ????4 | |
| Nano titanium oxide | ????5 | ????5 | ????5 | ????4 | ????6 | ????5 | |
| Vinylbenzene | ????9 | ????8 | ????10 | ????10 | ????9 | ????8 | |
| Superfine talcum powder 1800 # | ????50 | ????50 | ????50 | ????45 | ????40 | ????55 | |
| Superfine talcum powder 1200 # | ????20 | ????20 | ????20 | ????15 | ????25 | ????20 | |
| Superfine talcum powder 800 # | ????10 | ????10 | ????10 | ????20 | ????15 | ????5 | |
| B component solidifying agent | Cyclohexanone peroxide+methylethyl ketone peroxide | ????100 | ????100 | ????100 | ????100 | ????100 | ????100 |
| Yellow ultramarine is stuck with paste | ????3 | ????3 | ????3 | ????4 | ????3 | ????2 | |
| Aerosil | ????5 | ????5 | ????5 | ????4 | ????5 | ????6 | |
Claims (10)
1, light putty, it is made up of main putty, two kinds of components of solidifying agent, the weight ratio of main putty and solidifying agent is 100: 2, it is characterized in that main putty is made up of according to weight ratio following compositions: unsaturated polyester resin: 100, promotor: 3～5, vinylbenzene: 3～5, pigment: 4～6, superfine talcum powder: 70～90; Solidifying agent is made up of according to weight ratio following compositions: initiator: 100, pigment: 2～4, filler: 4～6.
2, light putty according to claim 1 is characterized in that described unsaturated polyester resin is the air drying type unsaturated polyester resin.
3, light putty according to claim 1 is characterized in that described promotor is cobalt iso-octoate and N, methylphenylamine.
4, light putty according to claim 1 is characterized in that described initiator is cyclohexanone peroxide and methylethyl ketone peroxide.
5, light putty according to claim 1 is characterized in that the pigment in the main putty is nano titanium oxide.
6, light putty according to claim 1 is characterized in that the pigment in the solidifying agent is that yellow ultramarine is stuck with paste, and filler is an aerosil.
7, light putty according to claim 1 is characterized in that main putty is made up of according to weight ratio following compositions: the air drying type unsaturated polyester resin; 100, cobalt iso-octoate and xylidine: 2～4, vinylbenzene: 8～10, nano titanium oxide: 5, superfine talcum powder 1800
#: 50, superfine talcum powder 1200
#: 20, superfine talcum powder 800
#: 10; Solidifying agent is made up of according to weight ratio following compositions: cyclohexanone peroxide and methylethyl ketone peroxide: 100, yellow ultramarine is stuck with paste: 3, aerosil: 5.
8, light putty according to claim 1, it is characterized in that main putty is made up of according to weight ratio following compositions: the air drying type unsaturated polyester resin: 100, cobalt iso-octoate and xylidine: 3, vinylbenzene: 9, nano titanium oxide: 5, superfine talcum powder 1800
#: 50, superfine talcum powder 1200
#: 20, superfine talcum powder 800
#: 10; Solidifying agent is made up of according to weight ratio following compositions: cyclohexanone peroxide and methylethyl ketone peroxide: 100, yellow ultramarine is stuck with paste: 3, aerosil: 5.
9, light putty according to claim 1, it is characterized in that main putty is made up of according to weight ratio following compositions: the air drying type unsaturated polyester resin: 100, cobalt iso-octoate and xylidine: 4, vinylbenzene: 8, nano titanium oxide: 5, superfine talcum powder 1800
#: 50, superfine talcum powder 1200
#: 20, superfine talcum powder 800
#: 10; Solidifying agent is made up of according to weight ratio following compositions: cyclohexanone peroxide and methylethyl ketone peroxide: 100, yellow ultramarine is stuck with paste: 3, aerosil: 5.
10, light putty according to claim 1, it is characterized in that main putty is made up of according to weight ratio following compositions: the air drying type unsaturated polyester resin: 100, cobalt iso-octoate and xylidine: 2, vinylbenzene: 10, nano titanium oxide: 5, superfine talcum powder 1800
#: 50, superfine talcum powder 1200
#: 20, superfine talcum powder 800
#: 10; Solidifying agent is made up of according to weight ratio following compositions: cyclohexanone peroxide and methylethyl ketone peroxide: 100, yellow ultramarine is stuck with paste: 3, aerosil: 5.