CN1055713C - 一种涂料脱除剂及应用于马口铁花次板的翻新 - Google Patents
一种涂料脱除剂及应用于马口铁花次板的翻新 Download PDFInfo
- Publication number
- CN1055713C CN1055713C CN97107036A CN97107036A CN1055713C CN 1055713 C CN1055713 C CN 1055713C CN 97107036 A CN97107036 A CN 97107036A CN 97107036 A CN97107036 A CN 97107036A CN 1055713 C CN1055713 C CN 1055713C
- Authority
- CN
- China
- Prior art keywords
- tinplate
- removing agent
- agent
- defective
- paint removing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明是关于涂料脱除剂的改进,尤其是一种成本低、广普性好、对基板损伤小的涂料脱除剂及用该脱除剂翻新马口铁花次板。脱除剂由0.3-15%(重量百分比,以下同)的强碱或强碱弱酸盐,0.5-30%的苯胺,余量为水组成。将其加温至50-80℃,将需脱漆的马口铁花次板浸泡其中,捞起抹去表面松动的漆膜。
Description
本发明涉及一种表面涂装涂料的脱除剂,尤其是马口铁花次板脱漆翻新用脱除剂及应用。
公知的脱除金属表面涂料的脱除剂,一类是无机型脱除剂,主要有强酸、强碱组成;另一类是有机型脱除剂,它是由多种有机溶剂和助剂组成。上述脱除剂的主要缺点是,一是对基材腐蚀性大,易损伤腐蚀基材表面;二是广普性差,一般只能脱除一种或几种涂料,脱除效率低,不能适应各种涂料、油漆的脱除。特别是有些有机型脱除剂,虽脱除了涂料漆膜但自身易粘附在基材表面,影响再次涂装。中国专利88105220公开了一种有机无机结合的脱漆剂,它是采用重铬酸钾(或重铬酸钠),浓流酸,N、N-二甲基甲酰胺,二氯甲烷或三氯甲烷混合搅拌而成。其缺点一是原料配比多、复杂,成本高;二是广普性仍较差,对多种涂料仍缺乏理想的脱除效果;三是脱除剂中使用有强氧化剂,对基材表面存在着一定程度的腐蚀损伤。
然而以马口铁板为基材,制造各种包装容器如罐头、包装盒等,需要在马口铁板上进行各种需要的涂装及印刷各种图案、文字,因而使用有多种涂料、油漆、保护剂等,以达到美观耐用及一些特殊效果。而在实际印铁、涂装的过程中,不可避免地会因种种原因导致印铁质量事故,产生花次板。由于马口铁板表面锡层一般不耐腐蚀,而现有的各种涂料脱除剂,均因存在广普性差及腐蚀损伤马口铁基板,尤其是破坏马口铁板的锡层的缺点,所以一般不适用于马口铁花次板涂料的脱除处理。长期以来各印铁制罐厂在马口铁花次板翻新上苦于缺乏有效的涂料脱除剂,以致产生大量花次板积压,造成马口铁板的不必要浪费和贬值。
本发明的目的在于克服上述已有涂料脱除剂的不足,提供一种广普性好,能适应去除各种涂料,且对基材破坏损伤小,配制简单成本低的涂料脱除剂,尤其是适用于马口铁花次板翻新的涂料脱除剂。
本发明的另一目的是提供一种应用上述涂料脱除剂,翻新马口铁花次板。
本发明第一目的实现,其改进是将强碱或强碱弱酸盐例如氢氧化钠、氢氧化钾、氢氧化钙、碳酸钠、碳酸钾与苯胺组成脱除剂水溶液。具体说,本发明涂料脱除剂,由0.3--15%(重量百分比,以下同)的强碱或强碱弱酸盐,0.5--30%的苯胺,余量为水组成。本发明中强碱或强碱弱酸盐用量增加会损伤基材,所以强碱或强碱弱酸盐的加量应有适当的限定;但苯胺用量增加,仅是成本的增加,一般对去除涂料及保护基材不受损伤无害处,但用量增加导致成本增加,且其又是易挥发性物质,用量过多也是一种浪费,因此认为30%已可以。本发明涂料脱除剂中的强的碱性物质对涂料中的有机成膜物质有破坏作用,苯胺对涂料中有机成膜物质也有极强的渗透和溶解能力,因此两者组配后对各种涂料显示出较强的脱除作用。同时碱性物质也是一种去污清洗剂,有较强的洗涤去污能力,苯胺是一种易挥发性的有机溶剂,因此两者组成的脱除剂,极易得到清洗,不易积留在基材表面,因此不会影响再次涂装。
本发明涂料脱除剂,最好使用强碱,尤其是氢氧化钠,组配的脱除剂有较强的脱除涂料的能力,而且广普性好,尤其是氢氧化钠与苯胺混合后能反应生成少量的酚钠,其对有机及无机物都有一定的渗透溶解能力,使得脱除效果更好。
本发明中强碱或强碱弱酸盐的加量最好为1--6%,苯胺的加量最好为5-10%,这样既经济又不会损伤基材。
本发明第二目的实现,将强碱或强碱弱酸盐与苯胺按上述比例要求混合组成脱除剂水溶液并加温至50-80℃,采用热浸脱除,将花次板浸没在加温后的脱除剂中便可使涂料松动与基板分离,达到脱除效果。脱除剂加温主要作用是降低脱除剂与涂料反应的活化能,加快反应速度,缩短浸泡时间,提高生产能力;同时又可避免因浸泡时间长,强的碱性物质损伤马口铁板的锡层,加温最好控制在75-80℃之间,温度低浸泡时间长,温度离浸泡时间短。
实施例1:将1%的氢氧化钠、5%的苯胺、94%的水,充分混合即得涂料脱除剂。
实施例2:将0.5%的氢氧化钠、10%的苯胺、89.5%的水充分混合即得涂料脱除剂。
实施例3:将1.5%的氢氧化钠、1%的苯胺、97.5%的水充分混合即得涂料脱除剂。
实施例4:将5%的氢氧化钠、10%的苯胺、85%的水充分混合即得涂料脱除剂。
实施例5:将12%的碳酸钠、28%的苯胺、60%的水充分混合即得涂料脱除剂。
脱除剂中碱及苯胺的加量视涂料的种类而定。实施例1、2及3配方尤其适合马口铁花次板的翻新。马口铁花次板的翻新,将上述脱除剂加温至75℃,然后将马口铁花次板浸没于脱除剂中浸泡,待涂料松动后捞起抹除即脱除。
用氢氧化钾、氢氧化钙及其弱酸盐取代上述氢氧化钠,同样可制成脱除剂
本发明涂料脱除剂,原料易得,组配简单成本底,以翻新花次马口铁板为例,每吨马口铁花次板翻新药剂成本仅150元左右,而且使用方便,适应范围广,对各类涂料、油漆、油墨及各类树脂漆都有较好的去除效果,脱除效率高,且对基材无损伤。该脱除剂尤其适用马口铁花次板涂料的脱除翻新,以达到重新使用,减少马口铁板的浪费。
为描述方便,本发明说明书中所说漆与涂料为同意语。
Claims (8)
1、一种涂料脱除剂,其特征在于由0.3-15%(重量百分比,以下同)的强碱或强碱弱酸盐,0.5-30%的苯胺,余量为水。
2、根据权利要求1所述涂料脱除剂,其特征在于所说强碱或强碱弱酸盐为1-6%。
3、根据权利要求1或2所述涂料脱除剂,其特征在于所说苯胺为5-10%。
4、根据权利要求3所述涂料脱除剂,其特征在于所说强碱或强碱弱酸盐为强碱。
5、根据权利要求4所述涂料脱除剂,其特征在于所说强碱为烧碱。
6、一种马口铁花次板的翻新方法,包括(1)将权利要求1所述涂料脱除剂加热至50-80℃,(2)将花次板浸入加热后的上述脱除剂中,(3)捞起花次板抹去表面松动的涂料。
7、根据权利要求6所述马口铁花次板的翻新方法,其特征在于所说脱除剂为1-6%的烧碱与5-10%的苯胺及水组成。
8、根据权利要求6或7所述马口铁花次板的翻新方法,其特征在于所说脱除剂加热温度为75-80℃。