CN105568216A - Surface treatment process of metal product - Google Patents
Surface treatment process of metal product Download PDFInfo
- Publication number
- CN105568216A CN105568216A CN201610055257.6A CN201610055257A CN105568216A CN 105568216 A CN105568216 A CN 105568216A CN 201610055257 A CN201610055257 A CN 201610055257A CN 105568216 A CN105568216 A CN 105568216A
- Authority
- CN
- China
- Prior art keywords
- metal product
- metal products
- metal
- treatment
- surface treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a surface treatment process of a metal product. The process comprises the following steps: (a) pretreatment of the metal product: the surface of the metal product to be treated is cleaned; and then, the burr and polishing treatment is performed; (b) cooling of the metal product: the pretreated metal product is cooled in a cooler; and (c) surface treatment of the metal product: the double-surface corona treatment is performed for the cooled metal product; the metal surface is uniformly coated with a wear resistant agent; a layer is plated by using a vacuum film plating method; and the surface treatment of the metal product is finished to obtain a finished product. The process has the following beneficial effects: the method is adopted to treat the surface of the metal product, in particular, the metal product is firstly cooled in the treatment process, so that the metal product is more stable in performance in the treatment process; the surface treatment is more smooth; the wear resistant agent is easy to be absorbed on the surface of the metal product; and the process is simple and reliable.
Description
Technical field
The present invention relates to a kind of process of surface treatment, particularly relate to a kind of process of surface treatment of metal products.
Background technology
Along with improving constantly of standard of living, the surface decoration of people to artwork, ornament etc. proposes more and more higher requirement, such as, there is the metal productss such as the metal zip fastener of good aesthetic property, five metals button, five metals case and bag accessory and obtain generally liking of people.
For attractive in appearanceization of metal products in prior art, electric plating method is traditionally adopted the plated surface last layer of metal products to be had the rete of aesthetic.Plating is exactly the process utilizing electrolysis principle to plate other metal or alloy of skim on metal products, be utilize electrolytic action to make the technique of the surface attachment layer of metal film of metal or other material thus play to prevent corrosion, improve the effects such as wear resistance, electroconductibility, reflective and having improved aesthetic appearance.But this plating mode surface in the long use procedure of metal products is easily coarse, and degree of tarnishing, substantially reduces work-ing life.
Therefore, for solving the problem, spy provides a kind of new technical scheme.
Summary of the invention
The invention provides a kind of process of surface treatment of metal products.
The technical solution used in the present invention is:
A process of surface treatment for metal products, comprises following processing step:
A, metal products pre-treatment: needing surface of metal product to be processed to clean up, then carry out burr and polished finish;
The cooling process of b, metal products: pretreated metal products is cooled in water cooler;
C, surface of metal product process: metal products cooling process completed carries out two-sided corona treatment, then by anti-anti-wear agent uniform application in metallic surface, utilize Vacuum Coating method to carry out coating, the surface treatment of metal products is completed, can finished product be obtained.
Further, the cooling conditions in the cooling process of described metal products: cooling temperature is-10 ~-30 DEG C, cooling time is 1-2 hour.
The invention has the beneficial effects as follows: adopt the surface of this kind of method to metal products to process, particularly first metal products is cooled in the process of process, make metal products performance in treating processes more stable, surface treatment is more smooth and easy, easily anti-anti-wear agent is adsorbed on the surface of metal products, simple and reliable process.
Embodiment
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, and this embodiment, only for explaining the present invention, does not form the restriction to protection scope of the present invention.
Embodiment 1
A process of surface treatment for metal products, comprises following processing step:
A, metal products pre-treatment: needing surface of metal product to be processed to clean up, then carry out burr and polished finish;
The cooling process of b, metal products: pretreated metal products is cooled in water cooler, cooling temperature is-10 DEG C, and cooling time is 1 hour;
C, surface of metal product process: metal products cooling process completed carries out two-sided corona treatment, then by anti-anti-wear agent uniform application in metallic surface, utilize Vacuum Coating method to carry out coating, the surface treatment of metal products is completed, can finished product be obtained.
Embodiment 2
A process of surface treatment for metal products, comprises following processing step:
A, metal products pre-treatment: needing surface of metal product to be processed to clean up, then carry out burr and polished finish;
The cooling process of b, metal products: pretreated metal products is cooled in water cooler, cooling temperature is-20 DEG C, and cooling time is 1.5 hours;
C, surface of metal product process: metal products cooling process completed carries out two-sided corona treatment, then by anti-anti-wear agent uniform application in metallic surface, utilize Vacuum Coating method to carry out coating, the surface treatment of metal products is completed, can finished product be obtained.
Embodiment 3
A process of surface treatment for metal products, comprises following processing step:
A, metal products pre-treatment: needing surface of metal product to be processed to clean up, then carry out burr and polished finish;
The cooling process of b, metal products: pretreated metal products is cooled in water cooler, cooling temperature is-30 DEG C, and cooling time is 2 hours;
C, surface of metal product process: metal products cooling process completed carries out two-sided corona treatment, then by anti-anti-wear agent uniform application in metallic surface, utilize Vacuum Coating method to carry out coating, the surface treatment of metal products is completed, can finished product be obtained.
The invention has the beneficial effects as follows: adopt the surface of this kind of method to metal products to process, particularly first metal products is cooled in the process of process, make metal products performance in treating processes more stable, surface treatment is more smooth and easy, easily anti-anti-wear agent is adsorbed on the surface of metal products, simple and reliable process.
The above is only preferred embodiment of the present invention, is not restriction the present invention being made to any other form, and any amendment done according to technical spirit of the present invention or equivalent variations, still belong to the present invention's scope required for protection.
Claims (2)
1. a process of surface treatment for metal products, is characterized in that: comprise following processing step:
A, metal products pre-treatment: needing surface of metal product to be processed to clean up, then carry out burr and polished finish;
The cooling process of b, metal products: pretreated metal products is cooled in water cooler;
C, surface of metal product process: metal products cooling process completed carries out two-sided corona treatment, then by anti-anti-wear agent uniform application in metallic surface, utilize Vacuum Coating method to carry out coating, the surface treatment of metal products is completed, can finished product be obtained.
2. the process of surface treatment of a kind of metal products according to claim 1, is characterized in that: the cooling conditions in the cooling process of described metal products: cooling temperature is-10 ~-30 DEG C, and cooling time is 1-2 hour.