CN105544919A - Oxygen anion membrane environment-friendly decorative plate and preparation method thereof - Google Patents
Oxygen anion membrane environment-friendly decorative plate and preparation method thereof Download PDFInfo
- Publication number
- CN105544919A CN105544919A CN201510981037.1A CN201510981037A CN105544919A CN 105544919 A CN105544919 A CN 105544919A CN 201510981037 A CN201510981037 A CN 201510981037A CN 105544919 A CN105544919 A CN 105544919A
- Authority
- CN
- China
- Prior art keywords
- oxygen ion
- negative oxygen
- carrier material
- negative
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an oxygen anion membrane environment-friendly decorative plate and a preparation method thereof. The oxygen anion membrane environment-friendly decorative plate is composed of a base plate body, an oxygen anion membrane material and a facing layer. The decorative plate has the advantages that non-woven fabric or dipping kraft paper or decorative paper is used as the carrier material to prepare the oxygen anion membrane material, the selected material is environmentally friendly, cost is low, and adsorption performance is high; the carrier material is immersed in bonding resin containing anion powder, and a secondary infiltration and drying method is adopted to obtain the oxygen anion membrane material containing anion powder, so that the content of anions in the membrane material is increased; the oxygen anion membrane material is bonded with the base plate body in a hot pressing mode, the preparation process is simple, efficiency is high, and the prepared decorative plate can release anions for a long period, so that the content of the anions indoors is increased, and the decorative plate is beneficial to human health.
Description
Technical field
The present invention relates to a kind of environment friendly decoration board, particularly relate to a kind of negative oxygen ion film environment friendly decoration board and preparation method thereof.
Background technology
In air, negative ion concentration is the important parameter weighing air quality indexes.Medical research shows, in air, electronegative particulate can increase the oxygen content in blood of human body, contribute to blood Oxygen deliver, absorption and utilization, there is the effect promoting human metabolism, improve human immunological competence, strengthen human body flesh energy, regulate human body function balance.Far infrared rays and the human body of the radiation of anion mineral crystal can be coordinated very well, all can be absorbed by human body.Generally speaking, people needs about 13,000,000,000 anions every day, and the indoor environments such as our room, office, public place of entertainment, can only provide about 1 ~ 2,000,000,000 anion, this and the desired level of human body to anion greatly differ from each other.But for most people, most time is all rest on indoor, supply falls short of demand will affect the state of mind and the physical and mental health of human body for thus long-term anion.
In prior art, in upholstery material, food fresh keeping material, anion material has obtained applying comparatively widely, as Chinese patent CN2011104214006 anion water-based emulsion coating and preparation method thereof, it prepares the coating that can discharge anion, oxonium ion by the method for adding anion material in aqueous emulsion paint, this coating can absorb the hazardous substancess such as various benzene, formaldehyde, uranium, reach the object of effective clean room environment, the physical and mental health of guarantor in living space.In addition, Chinese patent CN2014102605117 anion releasing multifunctional fresh-keeping material and preparation method thereof, it by mixing anionic additive with resin in batch mixer, then in double screw extruder, the multifunctional fresh-keeping material of anion releasing is made in granulation, and this anion preservative film has the function of antibacterial bacteriostatic, fresh-keeping taste removal, prolongation effective period of food quality.Above two prior aries are all utilize the effects such as anion can purify air, attracts bacteria, the two method adopted in order to the material obtained containing anion is all anion material or anionic additive are directly added in carrier material (coating, resin), then obtains the material containing anion through processes such as mixing, granulations.
Summary of the invention
The object of the invention is: in order to improve indoor anion concentration, make the life better and working environment, promote the state of mind and the physical and mental health of human body, the present invention by the method for adding negative oxygen ion membrane material in indoor decoration decorative panel obtain can anion releasing, oxonium ion novel decoration building materials, the invention provides a kind of negative oxygen ion film environment friendly decoration board and preparation method thereof.
In order to realize above goal of the invention, the present invention by the following technical solutions:
A kind of negative oxygen ion film environment friendly decoration board, be made up of substrate, negative oxygen ion membrane material and finish coat, described substrate is veneer, core-board, shaving board or fiberboard; Described finish coat is fancy veneer, slicing veneer, facing paper or paint; Described negative oxygen ion membrane material is made up of carrier material, negative ion powder and binder resin.
As a kind of preferred embodiment of technique scheme, described carrier material adopts non-woven fabrics, dipping kraft or facing paper, wherein kraft or facing paper quantitative requirement 60-120g/m
2, non-woven fabrics quantitative requirement 40-80g/m
2; Described negative ion powder is by the close tourmaline powder of fineness and living beings carbon dust in mass ratio (20-50): (80-50) mechanical mixture is made, and wherein tourmaline powder fineness is 500-1250 order, and biomass carbon powder fineness is 500-1250 order; Described binder resin is the melamine resin or Trimeric β peptide that are suitable for flooding, and wherein resin solid content is at least 40%.
Preferably, described living beings carbon dust is bamboo charcoal powder.
The technical problem that the present invention will solve further is, provides a kind of preparation method of negative oxygen ion film environment friendly decoration board, and when the negative oxygen ion film that employing is carrier material with non-woven fabrics or kraft, preparation method comprises following steps:
(1) by fixed for substrate thick sanding;
(2) respectively lay in substrate upper and lower surface the negative oxygen ion film that is carrier material with non-woven fabrics or kraft;
(3) one deck facing layer material is laid at the extexine of upper and lower negative oxygen ion film;
(4) sent in hot press by the slab that above-mentioned steps obtains, at temperature 120-150 DEG C, hot pressing 1-5min under the condition of unit pressure 1.0-2.0MPa, release is also processed into negative oxygen ion film environment friendly decoration board through subsequent mechanical.
When adopt take facing paper as the negative oxygen ion film of carrier material time, preparation method comprises following steps:
(1) by fixed for substrate thick sanding;
(2) respectively lay in substrate upper and lower surface the negative oxygen ion film that take facing paper as carrier material;
(3) sent in hot press by the slab that above-mentioned steps obtains, at temperature 120-150 DEG C, hot pressing 0.5-2min under the condition of unit pressure 1.0-2.0MPa, release is also processed into negative oxygen ion film environment friendly decoration board through subsequent mechanical.
Further, the preparation method of the negative oxygen ion membrane material adopted in the present invention is as follows:
(1) negative ion powder is added to the low molecular poly solution that mass fraction is 10-50% or mass fraction is in the polyacrylamide solution of 5-10%, high-speed stirred forms negative ion powder dispersion and sticks with paste, disperse paste to add in binder resin negative ion powder again to stir, make negative ion powder binder resin; Wherein negative ion powder mixes with mass ratio 1: 1 with polyglycol solution or polyacrylamide solution, and the addition that anion dispersion is stuck with paste in binder resin is the 20-30% of resin quality;
(2) once infiltrate: carrier material is soaked in not containing in the binder resin of negative ion powder, when carrier material be kraft or facing paper time, the mass content of binder resin is 50-80%, and when carrier material is non-woven fabrics, the mass content of binder resin is 60-90%;
(3) carrier material of immersion binder resin step (2) obtained is placed in continuous drier, dry under 70-120 DEG C of temperature condition, makes the volatile content of carrier material be reduced to 16-12%;
(4) secondary infiltrates: through step (3) dried carrier material be soaked in that step (1) obtains containing in the binder resin of negative ion powder, when carrier material be kraft or facing paper time, the mass content of binder resin is 80-110%, when carrier material is non-woven fabrics, the mass content of binder resin is 90-120%;
(5) carrier material that the immersion that step (4) obtains contains the binder resin of negative ion powder is placed in continuous drier, dry under 70-120 DEG C of temperature condition, the volatile content of carrier material is made to be reduced to 14-10%, the final obtained negative oxygen ion membrane material containing negative ion powder.
After resin adds negative ion powder, permeability declines, therefore first time dipping be the resin not adding negative ion powder of good penetrability, resin is made fully to penetrate into support material internal, thus ensure that anionic film has good adhesive property, what second time was flooded is the resin adding negative ion powder, make negative ion powder by resin go out viscous homogeneous stick to surfaces of carrier materials, give full play to the function of negative ion powder.Polyethylene glycol or polyacrylamide are high absorbency material, and its aqueous solution has good mobility and viscosity, and negative ion powder thus can be made to be dispersed in wherein and can not to precipitate or layering.
Negative oxygen ion membrane material of the present invention can discharge anion, oxonium ion, the oxygen content in blood of human body can be increased, contribute to blood Oxygen deliver, absorption and utilization, there is the effect promoting human metabolism, improve human immunological competence, strengthen human body flesh energy, regulate human body function balance.In addition, membrane material of the present invention is applied in upholstery material, play surface degerming, eliminate peculiar smell and pernicious gas, the effect purified the air of a room.Due to the far infrared band that the piezoelectricity of tourmaline powder and bamboo charcoal powder produces, can activating human body cells, conditioning physiological activity, therefore has good health care.
Beneficial effect
The present invention compared with prior art, has following good effect:
(1) adopt non-woven fabrics, dipping kraft or facing paper as carrier material, selection environmental protection, cost is low, absorption property is strong;
(2) adopt polyglycol solution or polyacrylamide solution to be dissolved in binder resin as medium by negative ion powder, make negative ion powder and binder resin Homogeneous phase mixing;
(3) carrier material is soaked in the binder resin containing negative ion powder, and the two-sided negative oxygen ion membrane material containing negative ion powder of method acquisition adopting secondary to infiltrate, dry, improve the content of anion in membrane material;
(4) by negative oxygen ion membrane material with hot pressing mode and base plate bonding, preparation technology is simple, efficiency is high;
(5) decorative panel that obtains of the present invention can long-acting negative ion release, thus improves indoor anion concentration, is conducive to health.
Detailed description of the invention
Be described further the preferred embodiment of the present invention below in conjunction with embodiment, wherein embodiment 1 is the example of the preferred embodiment using non-woven fabrics as carrier material; Wherein embodiment 2 is examples of the preferred embodiment using kraft as carrier material; Embodiment 3 is examples of the preferred embodiment using facing paper as carrier material.
Embodiment 1:
(1) negative oxygen ion membrane material is prepared
With 65g/m
2non-woven fabrics as carrier material, with fineness be 800 object tourmaline powders and bamboo charcoal powder in mass ratio 30: 60 mechanical mixture obtain negative ion powder, and select resin content be the melamine resin of 50% as binder resin, prepare negative oxygen ion membrane material according to the following steps:
(1) negative ion powder is added to the low molecular poly solution that mass fraction is 10%, high-speed stirred forms negative ion powder dispersion and sticks with paste, then disperses paste to add in binder resin negative ion powder to stir, make negative ion powder binder resin; Wherein negative ion powder mixes with mass ratio 1: 1 with polyglycol solution, and the addition that anion dispersion is stuck with paste in binder resin is 25% of resin quality;
(2) once infiltrate: carrier material is soaked in not containing in the binder resin of negative ion powder, the mass content of binder resin in carrier material is controlled 75%;
(3) carrier material of immersion binder resin step (2) obtained is placed in continuous drier, dry under 110 DEG C of temperature condition, makes the volatile content of carrier material be reduced to 13%;
(4) secondary infiltrates: through step (3) dried carrier material be soaked in that step (1) obtains containing in the binder resin of negative ion powder, the mass content of binder resin in carrier material is controlled 110%;
(5) carrier material that the immersion that step (4) obtains contains the binder resin of negative ion powder is placed in continuous drier, dry under 115 DEG C of temperature condition, the volatile content of carrier material is made to be reduced to 12%, the final obtained negative oxygen ion membrane material containing negative ion powder.(2) negative oxygen ion film environment friendly decoration board is prepared
Negative oxygen ion film environment friendly decoration board of the present invention, select core-board as substrate, fancy veneer as finish coat, negative oxygen ion membrane material is by using non-woven fabrics as carrier material, and negative ion powder and binder resin are prepared from, and concrete preparation method is as described in (one).Prepare negative oxygen ion film environment friendly decoration board according to the following steps:
(1) by fixed for substrate thick sanding;
(2) respectively lay in substrate upper and lower surface the negative oxygen ion film that is carrier material with non-woven fabrics or kraft;
(3) one deck facing layer material is laid at the extexine of upper and lower negative oxygen ion film;
(4) sent in hot press by the slab that above-mentioned steps obtains, hot pressing 5min under the condition of temperature 120 DEG C, unit pressure 1.0MPa, release is also processed into negative oxygen ion film environment friendly decoration board through subsequent mechanical.
After testing, anion releasing quantity is 900-1200/(s.cm to the environment friendly decoration board that the present embodiment obtains
2), the negative ion concentration in distance 50cm place, plate face air reaches 400-500/cm
3, and there is good far infrared radiation characteristic.
Embodiment 2:
(1) negative oxygen ion membrane material is prepared
With 60g/m
2kraft as carrier material, with fineness be 700 object tourmaline powders and bamboo charcoal powder in mass ratio 20: 80 mechanical mixture obtain negative ion powder, and select resin content be the melamine resin of 45% as binder resin, prepare negative oxygen ion membrane material according to the following steps:
(1) negative ion powder being added to mass fraction is in the polyacrylamide solution of 5%, and high-speed stirred forms negative ion powder dispersion and sticks with paste, then disperses paste to add in binder resin negative ion powder to stir, make negative ion powder binder resin; Wherein negative ion powder mixes with mass ratio 1: 1 with polyacrylamide solution, and the addition that anion dispersion is stuck with paste in binder resin is 30% of resin quality;
(2) once infiltrate: carrier material is soaked in not containing in the binder resin of negative ion powder, the mass content of binder resin in carrier material is controlled 60%;
(3) carrier material of immersion binder resin step (2) obtained is placed in continuous drier, dry under 120 DEG C of temperature condition, makes the volatile content of carrier material be reduced to 12%;
(4) secondary infiltrates: through step (3) dried carrier material be soaked in that step (1) obtains containing in the binder resin of negative ion powder, the mass content of binder resin in carrier material is controlled 110%;
(5) carrier material that the immersion that step (4) obtains contains the binder resin of negative ion powder is placed in continuous drier, dry under 120 DEG C of temperature condition, the volatile content of carrier material is made to be reduced to 10%, the final obtained negative oxygen ion membrane material containing negative ion powder.
(2) negative oxygen ion film environment friendly decoration board is prepared
Negative oxygen ion film environment friendly decoration board of the present invention, select veneer as substrate, slicing veneer as finish coat, negative oxygen ion membrane material is by using kraft as carrier material, and negative ion powder and binder resin are prepared from, and concrete preparation method is as described in (one).Prepare negative oxygen ion film environment friendly decoration board according to the following steps:
(1) by fixed for substrate thick sanding;
(2) respectively lay in substrate upper and lower surface the negative oxygen ion film that is carrier material with non-woven fabrics or kraft;
(3) one deck facing layer material is laid at the extexine of upper and lower negative oxygen ion film;
(4) sent in hot press by the slab that above-mentioned steps obtains, hot pressing 1min under the condition of temperature 150 DEG C, unit pressure 2.0MPa, release is also processed into negative oxygen ion film environment friendly decoration board through subsequent mechanical.
After testing, anion releasing quantity is 1700-2300/(s.cm to the environment friendly decoration board that the present embodiment obtains
2), the negative ion concentration in distance 50cm place, plate face air reaches 1500-2100/cm
3, and there is good far infrared radiation characteristic.
Embodiment 3:
(1) negative oxygen ion membrane material is prepared
With 120g/m
2facing paper as carrier material, with fineness be 1250 object tourmaline powders and living beings carbon dust in mass ratio 45: 75 mechanical mixture obtain negative ion powder, and select resin content be the Trimeric β peptide of 60% as binder resin, prepare negative oxygen ion membrane material according to the following steps:
(1) negative ion powder being added to mass fraction is in the low molecular poly solution of 50%, and high-speed stirred forms negative ion powder dispersion and sticks with paste, then disperses paste to add in binder resin negative ion powder to stir, make negative ion powder binder resin; Wherein negative ion powder mixes with mass ratio 1: 1 with low molecular poly solution, and the addition that anion dispersion is stuck with paste in binder resin is 20% of resin quality;
(2) once infiltrate: carrier material is soaked in not containing in the binder resin of negative ion powder, the mass content of binder resin in carrier material is controlled 80%;
(3) carrier material of immersion binder resin step (2) obtained is placed in continuous drier, dry under 110 DEG C of temperature condition, makes the volatile content of carrier material be reduced to 12%;
(4) secondary infiltrates: through step (3) dried carrier material be soaked in that step (1) obtains containing in the binder resin of negative ion powder, the mass content of binder resin in carrier material is controlled 100%;
(5) carrier material that the immersion that step (4) obtains contains the binder resin of negative ion powder is placed in continuous drier, dry under 120 DEG C of temperature condition, the volatile content of carrier material is made to be reduced to 10%, the final obtained negative oxygen ion membrane material containing negative ion powder.
(2) negative oxygen ion film environment friendly decoration board is prepared
Negative oxygen ion film environment friendly decoration board of the present invention, selects fiberboard as substrate, and negative oxygen ion membrane material is by using facing paper as carrier material, and negative ion powder and binder resin are prepared from, and concrete preparation method is as described in (one).Prepare negative oxygen ion film environment friendly decoration board according to the following steps:
(1) by fixed for substrate thick sanding;
(2) respectively lay in substrate upper and lower surface the negative oxygen ion film that take facing paper as carrier material;
(3) sent in hot press by the slab that above-mentioned steps obtains, hot pressing 0.5min under the condition of temperature 150 DEG C, unit pressure 2.0MPa, release is also processed into negative oxygen ion film environment friendly decoration board through subsequent mechanical.
After testing, anion releasing quantity is 2600-3000/(s.cm to the environment friendly decoration board that the present embodiment obtains
2), the negative ion concentration in distance 50cm place, plate face air reaches 2100-2600/cm
3, and there is obvious far infrared radiation characteristic.
Above in conjunction with detailed description of the invention to invention has been detailed description, but the present invention is not limited to this, and any those skilled in the art, in possessed ken, without prejudice under the prerequisite of present inventive concept, can make various distortion and amendment to it.
Claims (5)
1. a negative oxygen ion film environment friendly decoration board, is characterized in that, by substrate, subsides and the negative oxygen ion membrane material on substrate, and the finish coat composition outside negative oxygen ion membrane material that is laid in, described substrate is veneer, core-board, shaving board or fiberboard; Described finish coat is fancy veneer, slicing veneer, facing paper or paint; Described negative oxygen ion membrane material is made up of carrier material, negative ion powder and binder resin.
2. a kind of negative oxygen ion film environment friendly decoration board according to claim 1, is characterized in that, described carrier material adopts non-woven fabrics, dipping kraft or facing paper, wherein kraft or facing paper quantitative requirement 60-120g/m
2, non-woven fabrics quantitative requirement 40-80g/m
2; Described negative ion powder is by the close tourmaline powder of fineness and living beings carbon dust in mass ratio (20-50): (80-50) mechanical mixture is made, and wherein tourmaline powder fineness is 500-1250 order, and biomass carbon powder fineness is 500-1250 order; Described binder resin is the melamine resin or Trimeric β peptide that are suitable for flooding, and wherein resin solid content is at least 40%.
3. a kind of negative oxygen ion film environment friendly decoration board according to claim 2, it is characterized in that, described living beings carbon dust is bamboo charcoal powder.
4. the preparation method of a kind of negative oxygen ion film environment friendly decoration board described in claim 1,2 or 3, is characterized in that, comprise following steps:
(1) by fixed for substrate thick sanding;
(2) respectively lay in substrate upper and lower surface the negative oxygen ion film that is carrier material with non-woven fabrics or kraft;
(3) one deck facing layer material is laid at the extexine of upper and lower negative oxygen ion film;
(4) sent in hot press by the slab that above-mentioned steps obtains, at temperature 120-150 DEG C, hot pressing 1-5min under the condition of unit pressure 1.0-2.0MPa, release is also processed into negative oxygen ion film environment friendly decoration board through subsequent mechanical.
5. the preparation method of a kind of negative oxygen ion film environment friendly decoration board described in claim 1,2 or 3, is characterized in that, comprise following steps:
(1) by fixed for substrate thick sanding;
(2) respectively lay in substrate upper and lower surface the negative oxygen ion film that take facing paper as carrier material;
(3) sent in hot press by the slab that above-mentioned steps obtains, at temperature 120-150 DEG C, hot pressing 0.5-2min under the condition of unit pressure 1.0-2.0MPa, release is also processed into negative oxygen ion film environment friendly decoration board through subsequent mechanical.