CN103978525A - OSB ecological painting-free decorative surface furniture plate and preparing method thereof - Google Patents
OSB ecological painting-free decorative surface furniture plate and preparing method thereof Download PDFInfo
- Publication number
- CN103978525A CN103978525A CN201410207465.4A CN201410207465A CN103978525A CN 103978525 A CN103978525 A CN 103978525A CN 201410207465 A CN201410207465 A CN 201410207465A CN 103978525 A CN103978525 A CN 103978525A
- Authority
- CN
- China
- Prior art keywords
- osb
- veneer
- blanket
- painting
- thick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
An OSB ecological painting-free decorative surface furniture plate comprises at least one OSB blank plate; a decorative surface layer is composited on at least one surface of the OSB blank plate by at least one buffer balance layer in the middle; the preparing method comprises the following steps of a, manufacturing the OSB blank plate: machining a raw material into a thin long wood chip which is 40-120mm long, 5-20mm wide and 0.3-0.7mm thick along the grain direction, paving a three-layer or four-layer criss-cross structure by gluing, and manufacturing the blank plate by adopting a continuous hot press process; b, compositing by adopting a direct attaching mode: compositing the OSB blank plate and a veneer which is 0.1-3.0mm thick to manufacture an OSB base pate by using E0 glue, then attaching one layer of impregnated paper decorative surface layer on the surface of the OSB base plate; or the step b, compositing by using a repeated attaching mode: compositing the veneer which is 0.1-3.0mm thick and the impregnated paper to manufacture a paper board composite decorative surface layer, and gluing the paper board composite decorative surface layer to the OSB base plate by E0 glue. The furniture plate has a painting-free function, and has the excellent performances of environment friendliness, high stability, high carrying property, high nail keeping capacity and the like.
Description
Technical field
That the present invention relates to is the ecological non-painting veneer furniture-plates of a kind of OSB and preparation method, belongs to decorative materials technology.
Background technology
In decorative materials technology, decoration panel is widely used in furniture, and these decoration panels that are applied in furniture mainly contain fancy veneer thick china and melamine impregnated paper decoration panel (ecological board non-painting veneer plate).Because fancy veneer thick china also needs to paint after being used in furniture, in this process, both produced toxicity and dust, pollute environment, extend again house ornamentation flow process, increase cost.And melamine impregnated paper decoration panel is because of surperficial dipping ply of paper, can omit and cover or decorate with paint link, and its floral designs is huge many, enriched product line.At present, the utilization of melamine impregnated paper decoration panel in furniture is like a raging fire, has greatly the trend that replaces fancy veneer thick china.Current ecological non-painting veneer buttress mainly can be divided into the ecological non-painting veneer plate of glued board, the ecological non-painting veneer plate of core-board, the ecological non-painting veneer plate of particieboard, the ecological non-painting veneer plate of medium density fibre board (MDF) according to the difference of its base material.These four kinds common ecological non-painting veneer plates generally use urea-formaldehyde glue, and its environmental protection grade is generally lower, are generally E1 level or even E2 level in the market, seldom reach E0 level, and that furniture is used in is indoor, very high to environmental protection class requirement, General Requirements reaches E0 level.Its price of the ecological non-painting veneer plate of glued board is higher, and more yielding.The ecological non-painting veneer intralamellar part of core-board material is more loose, and it is poor to carry, and nail-holding ability is poor.Himself density of the ecological non-painting veneer plate of density board, particieboard is larger, carries poorly, and moisture expantion rate is larger, and dimensional stability is poor, and nail-holding ability is poor.
Summary of the invention
The object of the invention is to overcome the deficiency that prior art exists, exempt to paint function and provide one both to have, possess again the ecological non-painting veneer furniture-plates of OSB and the preparation method of the premium properties such as environmental protection, high stability, high-mechanic, high nail-holding ability.
The object of the invention is to complete by following technical solution, the ecological non-painting veneer furniture-plates of described OSB, it comprises at least one block of OSB blanket, it is characterized in that at least one surface of described OSB blanket is compounded with finish coat by least one deck cushioning balance layer of centre.
Described cushioning balance layer selects the natural veneer of 0.1-3.0mm or formaldehyde to discharge the recombinant decorative veneer of limitation for E0 level; Described finish coat is melamine-impregnated bond paper, decorative paper or natural veneer; Described OSB blanket is 40-120mmm by adopting length, wide 5-20mm, and the thin long wood chip of thick 0.3-0.7mm, mats formation into 3 layers or 4 layers of crisscross structure through applying glue, and makes through continuous hot-press.
The present invention is preferably: described OSB blanket is bonded by two, after having posted respectively natural veneer or recombinant decorative veneer on the surface of lower two fixed thick sandings thereon, form OSB substrate, then posted one deck impregnated paper finish coat at least one sanding surface of OSB substrate.
The present invention is preferably: described OSB blanket is bonded by two, posts respectively that to discharge limitation by natural veneer or formaldehyde be the recombinant decorative veneer of E0 level and cardboard composite decorative surface layer that impregnated paper is combined on the surface of the two fixed thick sandings up and down of this OSB blanket.
A preparation method for the ecological non-painting veneer furniture-plates of OSB as above, it comprises the steps:
A) making of OSB blanket, is processed into raw material along its grain direction and is processed as 40-120mmm, wide 5-20mm, and the thin long wood chip of thick 0.3-0.7mm, mats formation into 3 layers or 4 layers of crisscross structure through applying glue, adopts the technique of continuous hot-press to make;
B) directly paste method compound, above-mentioned OSB blanket and the thick veneer of 0.1-3.0mm are pasted again and make OSB substrate with E0 glue, and then the surface of described OSB substrate has been posted to one deck impregnated paper finish coat.
In described step b), the bonding hot pressing parameters of described OSB substrate and impregnated paper is unit pressure 0.5-1.5 MPa, time 3-15min, temperature 110-180 DEG C.
A preparation method for the ecological non-painting veneer furniture-plates of OSB as above, it comprises the steps:
A) making of OSB blanket, it is 40-120mmm that raw material are processed into long along its grain direction, wide 5-20mm, the thin long wood chip of thick 0.3-0.7mm, mats formation into 3 layers or 4 layers of crisscross structure through applying glue, adopts the technique of continuous hot-press to make;
B) paste again method compound, existing by veneer thick 0.1-3.0mm and the compound cardboard composite decorative surface layer of making of impregnated paper, then by described cardboard composite decorative surface layer use EO glue bond at described OSB blanket.
In described step b), the hot pressing parameters of veneer and impregnated paper compound tense is unit pressure 0.5-1.5 MPa, time 50-100s, temperature 110-180 DEG C, and the heat pressing process that described cardboard composite decorative surface layer and OSB blanket adopt is unit pressure 0.5-1.5 MPa, time 4-15min, temperature 90-150 DEG C.
The present invention is preferably: in described step a), the technique of described continuous hot-press comprises: hot pressing time-division three regions: press area, pressurize district, Ding Hou district, unload nip, hot pressing three elements, i.e. unit pressure and the time in each region are different, and density is controlled within the scope of 0.45-0.6g/cm3.
OSB blanket of the present invention, i.e. base material employing PMDI glue, there is not formaldehyde in it, has the very high feature of environmental protection; Matrix structure, through adjusting, adopts special thin long wood chip in addition, through crisscross three layers or four-layer structure, adopts the hot pressing mode of continuous press, makes Stability Analysis of Structures, intensity is higher and density is moderate OSB blanket; OSB blanket is carried out to surely thick sanding, blanket is carried out to following process facing, between base material and impregnated paper, paste again balance layer, both played cushioning effect, guaranteed again the flatness of final products.
OSB of the present invention, as the upgrading products of core-board, structural plywood, had both possessed both advantages, was greatly improved again in its performance.Ecological its formaldehyde of non-painting veneer plate of OSB that adopts OSB blanket to make discharges limitation and reaches without aldehyde level, and the more common sheet material of its humidity resistance improves a lot, and its physicochemical property is all higher than common medium density fibre board (MDF) and particieboard.
Brief description of the drawings
Fig. 1 is the structural representation of the ecological non-painting veneer furniture-plates of OSB of the present invention.
Detailed description of the invention
Below in conjunction with accompanying drawing, the present invention will be described in detail: shown in Fig. 1, the ecological non-painting veneer furniture-plates of OSB of the present invention, it comprises at least one block of OSB blanket 1, and at least one surface of described OSB blanket 1 is compounded with finish coat 3 by least one deck cushioning balance layer 2 of centre.
Cushioning balance layer 2 of the present invention selects the natural veneer of 0.1-3.0mm or formaldehyde to discharge the recombinant decorative veneer of limitation for E0 level; Described finish coat is melamine-impregnated bond paper, decorative paper or natural veneer; Described OSB blanket 1 is 40-120mmm by adopting length, wide 5-20mm, and the thin long wood chip of thick 0.3-0.7mm, mats formation into 3 layers or 4 layers of crisscross structure through applying glue, and makes through continuous hot-press.
A kind of embodiment of the present invention is: described OSB blanket 1 is bonded by two, after having posted respectively natural veneer or recombinant decorative veneer on the surface of lower two fixed thick sandings thereon, form OSB substrate, then posted one deck impregnated paper finish coat 3 at least one sanding surface of OSB substrate.
Another kind of embodiment of the present invention is: described OSB blanket 1 is bonded by two, posts respectively that to discharge limitation by natural veneer or formaldehyde be the recombinant decorative veneer of E0 level and cardboard composite decorative surface layer 3 that impregnated paper is combined on the surface of the two fixed thick sandings up and down of this OSB blanket.
Embodiment is taking monolithic OSB blanket 1 as example, by two or more than two the compound OSB blanket of the bonding composition of OSB blanket 1, as long as following examples are replaced and can be obtained other embodiment below.
Embodiment 1: the preparation method of the ecological non-painting veneer furniture-plates of a kind of OSB described above of the present invention, it comprises the steps:
A) making of OSB blanket, it is 40-120mmm that raw material are processed into long along its grain direction, wide 5-20mm, the thin long wood chip of thick 0.3-0.7mm, mats formation into 3 layers or 4 layers of crisscross structure through applying glue, adopts the technique of continuous hot-press to make;
B) directly paste method compound, above-mentioned OSB blanket and the thick veneer of 0.1-3.0mm are posted and make OSB substrate with E0 glue, and then the surface of described OSB substrate has been posted to one deck impregnated paper finish coat.
In described step b), the bonding hot pressing parameters of described OSB substrate and impregnated paper is unit pressure 0.5-1.5 MPa, time 3-15min, temperature 110-180 DEG C.
Embodiment 2: a kind of the above preparation method of the ecological non-painting veneer furniture-plates of OSB of the present invention, it comprises the steps:
A) making of OSB blanket, it is 40-120mmm that raw material are processed into long along its grain direction, wide 5-20mm, the thin long wood chip of thick 0.3-0.7mm, mats formation into 3 layers or 4 layers of crisscross structure through applying glue, adopts the technique of continuous hot-press to make;
B) paste again method compound, existing by veneer thick 0.1-3.0mm and the compound cardboard composite decorative surface layer of making of impregnated paper, then by described cardboard composite decorative surface layer use EO glue bond at described OSB blanket.
In described step b), the hot pressing parameters of veneer and impregnated paper compound tense is unit pressure 0.5-1.5 MPa, time 50-100s, temperature 110-180 DEG C, and the heat pressing process that described cardboard composite decorative surface layer and OSB blanket adopt is unit pressure 0.5-1.5 MPa, time 4-15min, temperature 90-150 DEG C.
In step a) described in the present invention in the above, the technique of described continuous hot-press comprises: hot pressing time-division three regions: press area, pressurize district, Ding Hou district, unload nip, hot pressing three elements, i.e. unit pressure and the time in each region are different, and density is controlled within the scope of 0.45-0.6g/cm3.
The present invention, by conventional OSB is carried out to certain structural adjustment, changes hot pressing parameters when continuous hot-press, reduce its density, and this had both met the function of Furniture panel, has reduced again the cost of OSB blanket.OSB blanket is carried out to surely thick sanding processing, then carry out multiple subsides facing processing, ensure its flatness, give it simultaneously and exempt from the facing function of paint, consumer can, according to the hobby of oneself, select the impregnated paper of different floral designs.Multiple subsides facing processing technology after just fixed thick sanding generally adopts straight subsides method and pastes again method, and this is similar with common ecological non-painting veneer furniture-plates.Straight subsides method plate face fineness is better, and cost is lower simultaneously.Paste again method production efficiency higher, but fineness is slightly poor.The brightness of soleplate face generally adopt straight subsides method in order to reduce production costs and to guarantee.
First the present invention considers to adopt the natural veneer of 0.1-3.0mm or formaldehyde to discharge the recombinant decorative veneer of limitation for E0 level for the balance layer between OSB blanket and impregnated paper, this had both ensured flatness and environmental-protecting performance that product is final, considered again the cost of product.
For the ecological non-painting veneer furniture-plates of described OSB has the needed aesthetic of good fire prevention, water resistance and furniture design, described impregnated bond paper adopts melamine impregnated paper simultaneously.
So-called straight subsides technique first by the veneer of 0.1-3.0mm on Double-face adhesive after fixed OSB substrate blanket thick sanding, make OSB base material after hot pressing sanding, after base material is cooling, paster is carried out on its surface again.The so-called technique of pasting is again first 0.1-3.0mm veneer and impregnated paper to be combined into cardboard, then with surely thick sanding after OSB blanket be combined into the ecological non-painting veneer board finished product of OSB
The ecological non-painting veneer furniture-plates of described OSB is generally two-sided facing, adopts straight subsides method technique generally to need twice pad pasting, and paste again, technique is general only need once be combined, double-sided cloth glue.
The ecological non-painting veneer furniture-plates of described OSB is made OSB substrate by paste veneer on OSB blanket, then on substrate, overlays melamine impregnated paper and make non-painting veneer plate, and it is easy to process.Its cost and core-board core, particieboard core, the ecological non-painting veneer plate of density board core are suitable, have substantial degradation compared with the ecological non-painting veneer furniture-plates of plywood core.Its finished product had both had OSB all superior mechanical property and environmental-protecting performance, in finishing use procedure, again without brushing paint, had reduced environmental pollution, and this product will be widely used in interior decoration field.
Claims (9)
1. the ecological non-painting veneer furniture-plates of OSB, it comprises at least one block of OSB blanket, it is characterized in that at least one surface of described OSB blanket is compounded with finish coat by least one deck cushioning balance layer of centre.
2. the ecological non-painting veneer furniture-plates of OSB according to claim 1, the cushioning balance layer described in it is characterized in that selects the natural veneer of 0.1-3.0mm or formaldehyde to discharge the recombinant decorative veneer that limitation is E0 level; Described finish coat is melamine-impregnated bond paper, decorative paper or natural veneer; Described OSB blanket is 40-120mmm by adopting length, wide 5-20mm, and the thin long wood chip of thick 0.3-0.7mm, mats formation into 3 layers or 4 layers of crisscross structure through applying glue, and makes through continuous hot-press.
3. the ecological non-painting veneer furniture-plates of OSB according to claim 1 and 2, it is characterized in that described OSB blanket is bonded by two, after having posted respectively natural veneer or recombinant decorative veneer on the surface of lower two fixed thick sandings thereon, form OSB substrate, then posted one deck impregnated paper finish coat at least one sanding surface of OSB substrate.
4. the ecological non-painting veneer furniture-plates of OSB according to claim 1 and 2, it is characterized in that described OSB blanket is bonded by two, on the surface of the two fixed thick sandings up and down of this OSB blanket, post respectively that to discharge limitation by natural veneer or formaldehyde be the recombinant decorative veneer of E0 level and cardboard composite decorative surface layer that impregnated paper is combined into.
5. a preparation method for the ecological non-painting veneer furniture-plates of OSB as claimed in claim 1 or 2 or 3 or 4, is characterized in that described preparation method comprises the steps:
A) making of OSB blanket, it is 40-120mmm that raw material are processed into long along its grain direction, wide 5-20mm, the thin long wood chip of thick 0.3-0.7mm, mats formation into 3 layers or 4 layers of crisscross structure through applying glue, adopts the technique of continuous hot-press to make;
B) directly paste method compound, above-mentioned OSB blanket and the thick veneer of 0.1-3.0mm are posted and make OSB substrate with E0 glue, and then the surface of described OSB substrate has been posted to one deck impregnated paper finish coat.
6. the preparation method of the ecological non-painting veneer furniture-plates of OSB according to claim 5, it is characterized in that in described step b), the bonding hot pressing parameters of described OSB substrate and impregnated paper is unit pressure 0.5-1.5 MPa, time 3-15min, temperature 110-180 DEG C.
7. a preparation method for the ecological non-painting veneer furniture-plates of OSB as claimed in claim 1 or 2 or 3 or 4, is characterized in that described preparation method comprises the steps:
A) making of OSB blanket, is processed into raw material along its grain direction processing and grows into 40-120mmm, wide 5-20mm, and the thin long wood chip of thick 0.3-0.7mm, mats formation into 3 layers or 4 layers of crisscross structure through applying glue, adopts the technique of continuous hot-press to make;
B) paste again method compound, existing by veneer thick 0.1-3.0mm and the compound cardboard composite decorative surface layer of making of impregnated paper, then by described cardboard composite decorative surface layer use EO glue bond at described OSB blanket.
8. the preparation method of the ecological non-painting veneer furniture-plates of OSB according to claim 7, it is characterized in that in described step b), the hot pressing parameters of veneer and impregnated paper compound tense is unit pressure 0.5-1.5 MPa, time 50-100s, temperature 110-180 DEG C, and the heat pressing process that described cardboard composite decorative surface layer and OSB blanket adopt is unit pressure 0.5-1.5 MPa, time 4-15min, temperature 90-150 DEG C.
9. according to the preparation method of the ecological non-painting veneer furniture-plates of the OSB described in claim 5,7, it is characterized in that in described step a), the technique of described continuous hot-press comprises: hot pressing time-division three regions: press area, pressurize district, Ding Hou district, unload nip, hot pressing three elements, i.e. unit pressure and the time in each region are different, and density is controlled within the scope of 0.45-0.6g/cm3.