CN108329864A - Healthy rupture membrane of anion - Google Patents
Healthy rupture membrane of anion Download PDFInfo
- Publication number
- CN108329864A CN108329864A CN201810323914.XA CN201810323914A CN108329864A CN 108329864 A CN108329864 A CN 108329864A CN 201810323914 A CN201810323914 A CN 201810323914A CN 108329864 A CN108329864 A CN 108329864A
- Authority
- CN
- China
- Prior art keywords
- layer
- parts
- negative ion
- anion
- fixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a negative ion health anti-explosion film, which comprises a decorative film body, wherein the decorative film body comprises an adhesive layer serving as a bottom layer, a water-resisting layer arranged on the upper surface of the adhesive layer, a base material layer arranged on the upper surface of the water-resisting layer and fixed with the water-resisting layer and used for storing water, a negative ion coating layer arranged on the upper surface of the base material layer and fixed with the base material layer, and a protective layer arranged on the upper surface of the negative ion coating layer, attached and fixed with the negative ion coating layer and capable of preventing the negative ion coating layer from being scratched; this healthy rupture membrane of anion can effectively protect the anion dope layer through water barrier and protective layer, in addition, can make the decoration membrane permanently release in the air after using be favorable to the anion and the transmission far infrared ray of human normal needs content through the anion dope layer, can replace current decorative paint vehicle, reduce the content of harmful substance such as formaldehyde, toluene, have simple structure, environmental protection pollution-free and the long advantage of live time.
Description
Technical field
The present invention relates to a kind of anion healthy rupture pressure discs.
Background technology
With the improvement of living standards, the living environment of health is more valued by the people.Health, length of the anion to people
The significant impact of longevity and ecology, is verified by domestic and international medical field expert by clinical trial, it is known as " air vitamin "
Title.Therefore, according to the demand of people, the miscellaneous decorative product rich in anion has been expedited the emergence of in the market.Especially make
New material for interior decoration.
The product of interior decoration is mostly paint vehicle and decorating film at present, and paint vehicle usage amount is maximum, and right after paint vehicle use
Air is also maximum to the harm of human body.Existing paint vehicle contains a large amount of formaldehyde, and irritating formaldehyde is evaporate into air,
The formaldehyde of human body inhalation of low concentration can cause to continue the light symptoms such as headache, inability, insomnia.Human body, which once sucks, can excessively cause
Respiratory tract and oedema, long-term exposure can cause dermatitis, lung, dysfunction of liver, immunologic dysfunction, central nervous system by
It influences, inhereditary material that can also be in damaging cells, sucking then can be carcinogenic for a long time.Therefore, present room is after finishing, all
It needs to place more than half a year, until the volatilization of indoor formaldehyde finishes, can just move in.And the use of decorating film is then instead of paint vehicle
Use, shorten the standing time that house is moved in, but existing decorating film is mostly common decorating film, both cannot be to room
Interior air is purified, its service life used can not be extended, therefore, in conclusion there are environment-friendly functions for existing decorating film
The short problem of difference, usage time.
Invention content
In view of this, it is an object of the present invention to provide a kind of anions simple in structure, environment friendly and pollution-free and usage time length
Healthy rupture pressure disc.
In order to solve the above-mentioned technical problem, the technical scheme is that:
A kind of anion healthy rupture pressure disc, including decoration membrane body, the decoration membrane body include it is as bottom, can be with decoration
Position is bonded fixed adhesive layer, and be arranged it is in adhesive layer upper surface and with adhesive-layer it is fixed, the water proof of infiltration can be prevented
Layer, and be arranged it is in water barrier upper surface and with water barrier is fixed, substrate layer for storing moisture, and be arranged in base material
Layer upper surface and with the fixed negative ion paint layer of substrate layer, and be arranged it is in negative ion paint layer upper surface and with bear from
Sub- dope layer is bonded protective layer that is fixed, can preventing negative ion paint layer scratching.
Further, the adhesive layer is polyvinyl acetate adhesive layer.
Further, the first card slot of setting be recessed inwardly, rectangular is provided on the upper surface of the adhesive layer.
Further, the water barrier is glass thin-film layers.
Further, the lower end of the water barrier, which is extended, the first chimeric raised line corresponding with the first card slot, described
The upper end of water barrier, which is extended, the second raised line.
Further, the substrate layer 13 is nonwoven layer.
Further, the lower end of the substrate layer be provided with setting be recessed inwardly, rectangular, can be with the second raised line pair
The second card slot that should be fitted into.
Further, the protective layer is polyester layer.
Further, the anion coating is made of the raw material of following weight:13-15 parts of phenolic resin gathers
11-15 parts of ester resin, 7-9 parts of dicyandiamide, 8-12 parts of Boron Trifluoride Ethylamine, 5-7 parts of polycarbonate powder, 5-7 parts of latex powder,
10-14 parts of bamboo charcoal powder, 6-8 parts of titanium dioxide, 2-4 parts of barium sulfate, 1-2 parts of calcium carbonate, 2-6 parts of ester based quaternary ammonium salt, coconut palm palm fibre 11-13
Part, 2-5 parts of lauryl sodium sulfate dispersant, 2-3 parts of vinyl triamine curing agent and tris phosphite antioxidant 1.3-2.5
Part.
Another technical problem to be solved by the invention is to provide 1)Take 5-7 parts of polycarbonate powder, 5-7 parts of latex powder, bamboo
2-6 parts of 10-14 parts of powdered carbon, 6-8 parts of titanium dioxide, 2-4 parts of barium sulfate, 1-2 parts of calcium carbonate and ester based quaternary ammonium salt are carried out with grinder
Grinding stirring so that above-mentioned material is uniformly mixed, and pulverulent filler is made, spare;
2)8-12 parts of 13-15 parts of phenolic resin, 11-15 parts of polyester resin, 7-9 parts of dicyandiamide and Boron Trifluoride Ethylamine are taken, is added
Enter into reaction kettle, adjust the temperature to 120 DEG C, and starts the blender in reaction kettle and be stirred, mixing speed 40r/
Min, mixing time 15min;
3)Reactor temperature is increased to 135 DEG C, then adds step 1 into reaction kettle)Filler obtained passes through guarantor after addition
It holds blender 40r/mi speed and is stirred 45min, then keep the temperature spare;
4)Take 11-13 parts of coconut palm palm fibre to be added in cutter machine, adjust in cutter machine knife away from for 2cm, start cutter machine will plus
The coconut palm palm fibre entered is cut, and the coconut palm monofilament of section shape is obtained, spare;
5)Take 2-5 parts of lauryl sodium sulfate dispersant, 2-3 parts of vinyl triamine curing agent and tris phosphite antioxidant
1.3-2.5 parts and step 4)Step 3 is added in coconut palm monofilament obtained)In reaction kettle in, adjust temperature and be reduced to 80 DEG C, and
It is stirred with blender, mixing speed 120r/min, mixing time 45min, obtains uniformly mixed paint binder, it is standby
With;
6)Step 5)In paint binder stirring after the completion of be warming up to 100 DEG C, vacuumize heat preservation 1h, be then cooled to 40 DEG C, stop
Only vacuum;And after stopping vacuum, the paint binder in reaction kettle is transferred in high-speed shearing machine, paint binder is cut
Processing is cut, the paint binder of dispersion is made in shearing rotating speed 3000r/min, shear time 50min, spare;
7)By step 6)Paint binder obtained is uniformly sprayed at base material layer surface by spray gun, after substrate layer absorb saturation after
Base material layer surface forms negative ion paint layer, you can.
The technology of the present invention effect major embodiment is in the following areas:The anion healthy rupture pressure disc passes through water barrier and protective layer
Can effective protection negative ion paint layer, in addition, enabling to decorating film after use can be to air by negative ion paint layer
In permanently release be beneficial to human normal need content anion and transmitting far ir ray, existing decorative paint can be replaced
Material reduces the content of the harmful substances such as formaldehyde, toluene, has the advantages that simple in structure, environment friendly and pollution-free and usage time length, this
Outside, by phenolic resin, polyester resin, dicyandiamide, Boron Trifluoride Ethylamine, polycarbonate powder, latex powder, bamboo charcoal powder, titanium white
Coconut palm palm fibre and the lauryl sodium sulfate point of section shape is made in slurries made of powder, barium sulfate, calcium carbonate and ester based quaternary ammonium salt, addition
Powder, vinyl triamine curing agent and tris phosphite antioxidant are formed negative by being sprayed on substrate layer after shearing dispersion
Ionic coating so that decorating film has the advantages that antioxidant effect is good, is convenient for release anion and transmitting far ir ray, is applicable in
In interior decoration.
Description of the drawings
Fig. 1 is a kind of sectional view of anion healthy rupture pressure disc of the present invention.
Specific implementation mode
Below in conjunction with attached drawing, the specific implementation mode of the present invention is described in further detail, so that technical solution of the present invention is more
It should be readily appreciated that and grasp.
In embodiment, it is to be understood that term " centre ", "upper", "lower", " top ", " right side ", " left end ", " on
Side ", " back side ", " middle part ", etc. instructions orientation or positional relationship be based on the orientation or positional relationship shown in the drawings, be only
It is of the invention for ease of description, it does not indicate or imply the indicated device or element must have a particular orientation, with specific
Azimuth configuration and operation, therefore be not considered as limiting the invention.
Embodiment 1
A kind of anion healthy rupture pressure disc, as shown in Figure 1, including decoration membrane body 1, the decoration membrane body 1 includes being used as bottom
Layer, fixed adhesive layer 11 can be bonded by glue with decorative position, and in 11 upper surface of adhesive layer and and viscose glue is set
Layer 11 is bonded water barrier 12 that is fixed, can preventing infiltration by glue, and in 12 upper surface of water barrier and and water proof is arranged
Layer 12 is bonded substrate layer 13 fixed, for storing moisture by glue, and in 13 upper surface of substrate layer and and base is arranged
Material layer 13 is bonded fixed negative ion paint layer 14 by glue, and be arranged it is in 14 upper surface of negative ion paint layer and with it is negative
Ion dope layer 14 is bonded protective layer 15 that is fixed, can preventing 14 scratching of negative ion paint layer by glue.The adhesive layer
11 be polyvinyl acetate adhesive layer.The first of setting be recessed inwardly, rectangular is provided on the upper surface of the adhesive layer 11
Card slot 111.The water barrier 12 is glass thin-film layers.The lower end of the water barrier 12 be extended have it is right with the first card slot 111
The first raised line 121 that should be fitted into, the upper end of the water barrier 12, which is extended, the second raised line 122.The substrate layer 13 is nothing
Woven fabric layer.The lower end of the substrate layer 13 be provided with setting be recessed inwardly, rectangular, can be corresponding embedding with the second raised line 122
The second card slot 131 closed.The protective layer 15 is polyester layer.
The anion coating is made of the raw material of following weight:It is 15 parts of phenolic resin, 11 parts of polyester resin, double
7 parts of cyanamide, 8 parts of Boron Trifluoride Ethylamine, 5 parts of polycarbonate powder, 5 parts of latex powder, 10 parts of bamboo charcoal powder, 6 parts of titanium dioxide, sulfuric acid
2 parts of barium, 1 part of calcium carbonate, 2 parts of ester based quaternary ammonium salt, 11 parts of coconut palm palm fibre, 2 parts of lauryl sodium sulfate dispersant, vinyl triamine solidification
1.3 parts of 2 parts of agent and tris phosphite antioxidant.
A kind of preparation method of anion coating, includes the following steps:
1)Take 5 parts of polycarbonate powder, 5 parts of latex powder, 10 parts of bamboo charcoal powder, 6 parts of titanium dioxide, 2 parts of barium sulfate, 1 part of calcium carbonate and
2 parts of ester based quaternary ammonium salt is ground stirring with grinder so that above-mentioned material is uniformly mixed, and pulverulent filler is made, spare;
2)8 parts of 15 parts of phenolic resin, 11 parts of polyester resin, 7 parts of dicyandiamide and Boron Trifluoride Ethylamine are taken, reaction kettle is added to
In, 120 DEG C are adjusted the temperature to, and start the blender in reaction kettle and be stirred, mixing speed 40r/min, mixing time
For 15min;
3)Reactor temperature is increased to 135 DEG C, then adds step 1 into reaction kettle)Filler obtained passes through guarantor after addition
It holds blender 40r/mi speed and is stirred 45min, then keep the temperature spare;
4)It takes 11 parts of coconut palm palm fibre to be added in cutter machine, adjusts in cutter machine knife away from for 2cm, starting cutter machine by addition
Coconut palm palm fibre is cut, and the coconut palm monofilament of section shape is obtained, spare;
5)Take 1.3 parts of 2 parts of lauryl sodium sulfate dispersant, 2 parts of vinyl triamine curing agent and tris phosphite antioxidant
And step 4)Step 3 is added in coconut palm monofilament obtained)In reaction kettle in, adjust temperature be reduced to 80 DEG C, be used in combination blender into
Row stirring, mixing speed 120r/min, mixing time 45min obtain uniformly mixed paint binder, spare;
6)Step 5)In paint binder stirring after the completion of be warming up to 100 DEG C, vacuumize heat preservation 1h, be then cooled to 40 DEG C, stop
Only vacuum;And after stopping vacuum, the paint binder in reaction kettle is transferred in high-speed shearing machine, paint binder is cut
Processing is cut, the paint binder of dispersion is made in shearing rotating speed 3000r/min, shear time 50min, spare;
7)By step 6)Paint binder obtained is uniformly sprayed at base material layer surface by spray gun, after substrate layer absorb saturation after
Base material layer surface forms negative ion paint layer, you can.
Embodiment 2
A kind of anion healthy rupture pressure disc, as shown in Figure 1, including decoration membrane body 1, the decoration membrane body 1 includes being used as bottom
Layer, fixed adhesive layer 11 can be bonded by glue with decorative position, and in 11 upper surface of adhesive layer and and viscose glue is set
Layer 11 is bonded water barrier 12 that is fixed, can preventing infiltration by glue, and in 12 upper surface of water barrier and and water proof is arranged
Layer 12 is bonded substrate layer 13 fixed, for storing moisture by glue, and in 13 upper surface of substrate layer and and base is arranged
Material layer 13 is bonded fixed negative ion paint layer 14 by glue, and be arranged it is in 14 upper surface of negative ion paint layer and with it is negative
Ion dope layer 14 is bonded protective layer 15 that is fixed, can preventing 14 scratching of negative ion paint layer by glue.The adhesive layer
11 be polyvinyl acetate adhesive layer.The first of setting be recessed inwardly, rectangular is provided on the upper surface of the adhesive layer 11
Card slot 111.The water barrier 12 is glass thin-film layers.The lower end of the water barrier 12 be extended have it is right with the first card slot 111
The first raised line 121 that should be fitted into, the upper end of the water barrier 12, which is extended, the second raised line 122.The substrate layer 13 is nothing
Woven fabric layer.The lower end of the substrate layer 13 be provided with setting be recessed inwardly, rectangular, can be corresponding embedding with the second raised line 122
The second card slot 131 closed.The protective layer 15 is polyester layer.
The anion coating is made of the raw material of following weight:It is 13 parts of phenolic resin, 15 parts of polyester resin, double
9 parts of cyanamide, 12 parts of Boron Trifluoride Ethylamine, 7 parts of polycarbonate powder, 7 parts of latex powder, 14 parts of bamboo charcoal powder, 8 parts of titanium dioxide, sulphur
4 parts of sour barium, 2 parts of calcium carbonate, 6 parts of ester based quaternary ammonium salt, 13 parts of coconut palm palm fibre, 5 parts of lauryl sodium sulfate dispersant, vinyl triamine are solid
2.5 parts of 3 parts of agent and tris phosphite antioxidant.
A kind of preparation method of anion coating, includes the following steps:
1)Take 7 parts of polycarbonate powder, 7 parts of latex powder, 14 parts of bamboo charcoal powder, 8 parts of titanium dioxide, 4 parts of barium sulfate, 2 parts of calcium carbonate and
6 parts of ester based quaternary ammonium salt is ground stirring with grinder so that above-mentioned material is uniformly mixed, and pulverulent filler is made, spare;
2)12 parts of 13 parts of phenolic resin, 15 parts of polyester resin, 9 parts of dicyandiamide and Boron Trifluoride Ethylamine are taken, reaction kettle is added to
In, 120 DEG C are adjusted the temperature to, and start the blender in reaction kettle and be stirred, mixing speed 40r/min, mixing time
For 15min;
3)Reactor temperature is increased to 135 DEG C, then adds step 1 into reaction kettle)Filler obtained passes through guarantor after addition
It holds blender 40r/mi speed and is stirred 45min, then keep the temperature spare;
4)Take 11-13 parts of coconut palm palm fibre to be added in cutter machine, adjust in cutter machine knife away from for 2cm, start cutter machine will plus
The coconut palm palm fibre entered is cut, and the coconut palm monofilament of section shape is obtained, spare;
5)Take 2.5 parts of 5 parts of lauryl sodium sulfate dispersant, 3 parts of vinyl triamine curing agent and tris phosphite antioxidant
And step 4)Step 3 is added in coconut palm monofilament obtained)In reaction kettle in, adjust temperature be reduced to 80 DEG C, be used in combination blender into
Row stirring, mixing speed 120r/min, mixing time 45min obtain uniformly mixed paint binder, spare;
6)Step 5)In paint binder stirring after the completion of be warming up to 100 DEG C, vacuumize heat preservation 1h, be then cooled to 40 DEG C, stop
Only vacuum;And after stopping vacuum, the paint binder in reaction kettle is transferred in high-speed shearing machine, paint binder is cut
Processing is cut, the paint binder of dispersion is made in shearing rotating speed 3000r/min, shear time 50min, spare;
7)By step 6)Paint binder obtained is uniformly sprayed at base material layer surface by spray gun, after substrate layer absorb saturation after
Base material layer surface forms negative ion paint layer, you can.
Embodiment 3
A kind of anion healthy rupture pressure disc, as shown in Figure 1, including decoration membrane body 1, the decoration membrane body 1 includes being used as bottom
Layer, fixed adhesive layer 11 can be bonded by glue with decorative position, and in 11 upper surface of adhesive layer and and viscose glue is set
Layer 11 is bonded water barrier 12 that is fixed, can preventing infiltration by glue, and in 12 upper surface of water barrier and and water proof is arranged
Layer 12 is bonded substrate layer 13 fixed, for storing moisture by glue, and in 13 upper surface of substrate layer and and base is arranged
Material layer 13 is bonded fixed negative ion paint layer 14 by glue, and be arranged it is in 14 upper surface of negative ion paint layer and with it is negative
Ion dope layer 14 is bonded protective layer 15 that is fixed, can preventing 14 scratching of negative ion paint layer by glue.The adhesive layer
11 be polyvinyl acetate adhesive layer.The first of setting be recessed inwardly, rectangular is provided on the upper surface of the adhesive layer 11
Card slot 111.The water barrier 12 is glass thin-film layers.The lower end of the water barrier 12 be extended have it is right with the first card slot 111
The first raised line 121 that should be fitted into, the upper end of the water barrier 12, which is extended, the second raised line 122.The substrate layer 13 is nothing
Woven fabric layer.The lower end of the substrate layer 13 be provided with setting be recessed inwardly, rectangular, can be corresponding embedding with the second raised line 122
The second card slot 131 closed.The protective layer 15 is polyester layer.
The anion coating is made of the raw material of following weight:It is 14 parts of phenolic resin, 13 parts of polyester resin, double
8 parts of cyanamide, 10 parts of Boron Trifluoride Ethylamine, 6 parts of polycarbonate powder, 6 parts of latex powder, 12 parts of bamboo charcoal powder, 7 parts of titanium dioxide, sulphur
3 parts of sour barium, 1.5 parts of calcium carbonate, 4 parts of ester based quaternary ammonium salt, 12 parts of coconut palm palm fibre, 3.5 parts of lauryl sodium sulfate dispersant, vinyl three
1.7 parts of 2.5 parts of amine hardener and tris phosphite antioxidant.
A kind of preparation method of anion coating, includes the following steps:
1)Take 6 parts of polycarbonate powder, 6 parts of latex powder, 12 parts of bamboo charcoal powder, 7 parts of titanium dioxide, 3 parts of barium sulfate, 1.5 parts of calcium carbonate
It is ground stirring with grinder for 4 parts with ester based quaternary ammonium salt so that above-mentioned material is uniformly mixed, and pulverulent filler is made, spare;
2)10 parts of 14 parts of phenolic resin, 13 parts of polyester resin, 8 parts of dicyandiamide and Boron Trifluoride Ethylamine are taken, reaction kettle is added to
In, 120 DEG C are adjusted the temperature to, and start the blender in reaction kettle and be stirred, mixing speed 40r/min, mixing time
For 15min;
3)Reactor temperature is increased to 135 DEG C, then adds step 1 into reaction kettle)Filler obtained passes through guarantor after addition
It holds blender 40r/mi speed and is stirred 45min, then keep the temperature spare;
4)It takes 12 parts of coconut palm palm fibre to be added in cutter machine, adjusts in cutter machine knife away from for 2cm, starting cutter machine by addition
Coconut palm palm fibre is cut, and the coconut palm monofilament of section shape is obtained, spare;
5)Take 3.5 parts of lauryl sodium sulfate dispersant, 2.5 parts of vinyl triamine curing agent and tris phosphite antioxidant
1.7 parts and step 4)Step 3 is added in coconut palm monofilament obtained)In reaction kettle in, adjust temperature be reduced to 80 DEG C, be used in combination and stir
It mixes device to be stirred, mixing speed 120r/min, mixing time 45min, obtains uniformly mixed paint binder, it is spare;
6)Step 5)In paint binder stirring after the completion of be warming up to 100 DEG C, vacuumize heat preservation 1h, be then cooled to 40 DEG C, stop
Only vacuum;And after stopping vacuum, the paint binder in reaction kettle is transferred in high-speed shearing machine, paint binder is cut
Processing is cut, the paint binder of dispersion is made in shearing rotating speed 3000r/min, shear time 50min, spare;
7)By step 6)Paint binder obtained is uniformly sprayed at base material layer surface by spray gun, after substrate layer absorb saturation after
Base material layer surface forms negative ion paint layer, you can.
Experimental example:
Choose epoxy coating as a control group one, choose asphalt paint as a control group two and the application anion
Coating is as experimental group.
Following table is the assay method and standard of three groups of coating:
Density | Test GB/T6750-86 |
Fineness | Test GB/T1724-79 |
State | It is transparent, micro- muddy, muddy |
Volatile performance | Test GB/T9272-88 |
Drying time | Test GB/T1728-79 |
Flexibility | Test GB/T1731-93 |
Experimental subjects chooses three pieces area, material and the identical non-woven fabrics of specification.
Requirement of experiment:Non-woven fabrics is sprayed using above-mentioned three groups of coating respectively, specific detection data is as follows:
Following table is the experimental result of three groups of coating:
In conjunction with upper table, comparison control group one, control group two and experimental group, negative ion paint of the invention is as experimental group, institute
The data measured are superior to control group one and control group two, therefore, compared to than control group one and control group two, the application bear from
Sub- coating is more suitable for should be in interior decoration.
The technology of the present invention effect major embodiment is in the following areas:The anion healthy rupture pressure disc passes through water barrier and protective layer
Can effective protection negative ion paint layer, in addition, enabling to decorating film after use can be to air by negative ion paint layer
In permanently release be beneficial to human normal need content anion and transmitting far ir ray, existing decorative paint can be replaced
Material reduces the content of the harmful substances such as formaldehyde, toluene, has the advantages that simple in structure, environment friendly and pollution-free and usage time length, this
Outside, by phenolic resin, polyester resin, dicyandiamide, Boron Trifluoride Ethylamine, polycarbonate powder, latex powder, bamboo charcoal powder, titanium white
Coconut palm palm fibre and the lauryl sodium sulfate point of section shape is made in slurries made of powder, barium sulfate, calcium carbonate and ester based quaternary ammonium salt, addition
Powder, vinyl triamine curing agent and tris phosphite antioxidant are formed negative by being sprayed on substrate layer after shearing dispersion
Ionic coating so that decorating film has the advantages that antioxidant effect is good, is convenient for release anion and transmitting far ir ray, is applicable in
In interior decoration.
Certainly, the representative instance of the above only present invention, in addition to this, the present invention can also have other a variety of specific implementations
Mode, all technical solutions formed using equivalent substitution or equivalent transformation, is all fallen within the scope of protection of present invention.
Claims (8)
1. a kind of anion healthy rupture pressure disc, including decoration membrane body, it is characterised in that:The decoration membrane body includes being used as bottom
Layer, fixed adhesive layer can be bonded with decorative position, and be arranged it is in adhesive layer upper surface and with adhesive-layer it is fixed, can
Prevent the water barrier of infiltration, and be arranged it is in water barrier upper surface and with water barrier is fixed, base material for storing moisture
Layer, and be arranged it is in substrate layer upper surface and with the fixed negative ion paint layer of substrate layer, and be arranged on negative ion paint layer
Surface and protective layer fixed, that negative ion paint layer scratching can be prevented is bonded with negative ion paint layer.
2. a kind of anion healthy rupture pressure disc as described in claim 1, it is characterised in that:The adhesive layer is polyvinyl acetate
Adhesive layer.
3. a kind of anion healthy rupture pressure disc as described in claim 1, it is characterised in that:It is set on the upper surface of the adhesive layer
It is equipped with the first card slot of setting be recessed inwardly, rectangular.
4. a kind of anion healthy rupture pressure disc as described in claim 1, it is characterised in that:The water barrier is glass film
Layer.
5. a kind of anion healthy rupture pressure disc as described in claim 1, it is characterised in that:The lower end of the water barrier, which extends, to be set
It is equipped with the first chimeric raised line corresponding with the first card slot, the upper end of the water barrier, which is extended, the second raised line.
6. a kind of anion healthy rupture pressure disc as described in claim 1, it is characterised in that:The substrate layer 13 is non-woven fabrics
Layer.
7. a kind of anion healthy rupture pressure disc as described in claim 1, it is characterised in that:The lower end of the substrate layer is provided with
Setting be recessed inwardly, rectangular, can the second chimeric card slot corresponding with the second raised line.
8. a kind of anion healthy rupture pressure disc as described in claim 1, it is characterised in that:The protective layer is polyester layer.