CN105534221A - Safe artistic glass cup and making method thereof - Google Patents
Safe artistic glass cup and making method thereof Download PDFInfo
- Publication number
- CN105534221A CN105534221A CN201610122924.8A CN201610122924A CN105534221A CN 105534221 A CN105534221 A CN 105534221A CN 201610122924 A CN201610122924 A CN 201610122924A CN 105534221 A CN105534221 A CN 105534221A
- Authority
- CN
- China
- Prior art keywords
- cup
- adhesive film
- glass
- idiosome
- wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a safe artistic glass cup which comprises an inner cup and an outer cup. A PVB adhesive film layer, ornamentals and an outer PVB adhesive film layer are sequentially arranged between the inner cup and the outer cup. The ornamentals are dried petals and/or plant stems and leaves, the outer surfaces of the ornamentals are coated with a layer of high-temperature-resisting flame-retardant high-transparency adhesive, the ornamentals are directly arranged on the outer wall of the inner cup, the PVB adhesive film layer is a single-layer PVB adhesive film layer, the ornamentals are at least one of heat-transfer-printed patterns, paintings and glass spray-carved works, the outer wall of the outer cup is coated with a layer of photosensitive color-changeable ink, and the outer wall of the inner cup and the inner wall of the outer cup are mutually parallel and are of inverted circular truncated cone structures. Correspondingly, a making method of the safe artistic glass cup comprises the steps of material selection, adding of the ornamentals and the PVB adhesive film layers, adhesion of the inner cup and the outer cup, opening sealing, annealing and the like. The arranged PVB adhesive film can ensure that even through the cup is broken, glass fragments are also tightly adhered to the PVB adhesive film and do not hurt a user, and beautiful visual enjoyment is brought to the user while the safety is ensured.
Description
Technical field
The present invention relates to glass container and manufacture field thereof, particularly safe art glass cup of one and preparation method thereof.
Background technology
Along with growth in the living standard, the requirement of people to quality of the life is more and more higher, not only pursues the practicality of article, and also wishing that it has concurrently can appreciating.With regard to glass, because it is inexpensive, practical, nonhazardous and the application obtained in daily life widely, also there is the glass of various Various Functions.But glass is frangible, be easy to bundle during glass fragment cleaning in one's hands, and not easily clean out, some fractionlet being scattered in corner may be hurted sb.'s feelings accidentally.For convenience of using, glass is generally all placed on the position that dining table, desk etc. easily contact, and this just considerably increases it by the risk smashed because of carelessness, allows a lot of people more particularly have the family of child always cannot relievedly to use.Chinese invention patent CN102860730A discloses a kind of glass of Anti-breaking; it has one deck flexible protective film on cup outer wall; although this flexible protective film can play certain cushioning effect when cup drops on the ground; but glass can not be avoided to be broken into pieces when major part, still there is the risk of hurting sb.'s feelings in the glass fragment that is scattered.Also have artificial this problem of solution, at outer setting plastics or the metal glass holder of glass, although resistance to the falling property of glass can be improved, greatly have impact on the attractive in appearance of glass, weaken visual enjoyment when it uses.
Summary of the invention
For the defect that above-mentioned prior art exists, also can not disperse even if technical problem to be solved by this invention is to provide a kind of broken glass fragment, can use safety be ensured and there is the safe art glass cup of higher value of art appreciation.
Corresponding therewith, also can not disperse even if another technical problem that will solve of the present invention is to provide a kind of broken glass fragment, can use safety be ensured and there is the preparation method of the safe art glass cup of higher value of art appreciation.
The present invention is that the safe art glass cup of one solve the technical problem comprises inner cup and the outer cup, is provided with PVB adhesive film and ornament between described inner cup and the outer cup.
As a modification of the present invention, interior PVB adhesive film, ornament and outer PVB adhesive film is provided with successively between described inner cup and the outer cup, described ornament is arranged between two-layer PVB adhesive film, described ornament is petal and/or the plant base of leaf of drying process, described ornament outer surface one deck heat-resistant fireproof high transparency glue.
Improve as another kind of the present invention, described ornament is arranged on interior cup outer wall, and described PVB adhesive film is individual layer PVB adhesive film, and described ornament is at least the one in thermally transferred pattern, paint and glass spray carving works.
The outer wall of described outer cup preferably sprays one deck sensitization discoloration ink.
The outer wall of described interior cup is preferably parallel to each other with the inwall of outer cup and all becomes the structure of reverse frustoconic.
Accordingly, the preparation method of this safe art glass cup of the present invention comprises the following steps:
1) identical, two glasses varying in size of selected shape are as interior cup idiosome and outer cup idiosome, and inside and outside cup idiosome 2 ~ 5cm higher than finished glass cup;
2) on interior cup outer wall, be close to PVB adhesive film in one deck, be pasted onto on interior PVB adhesive film after ornament outer surface one deck heat-resistant fireproof high transparency glue, and then be close to the outer PVB adhesive film of one deck;
3) be inserted in outer cup idiosome by outer wall being provided with cup idiosome in PVB glued membrane, heat and keep temperature to be 60 ~ 80 DEG C, internal cup idiosome inner bottom part applies and keeps pressure to be 0.3 ~ 0.5MPa, described pressure is held time as 15-20min, makes described interior cup idiosome and outer cup idiosome be bonded together and discharge air therebetween;
4) glass autoclave is utilized to remove air remaining between inside and outside wall of cup and PVB glued membrane;
5) glass sealing machine is utilized to carry out sealing process;
6) anneal, lower the temperature;
7) reduce to after room temperature until temperature, outer cup outer wall sprays one deck sensitization discoloration ink, this layer of sensitization discoloration ink is 2 ~ 3cm apart from rim of a cup distance.
One as a kind of preparation method of safe art glass cup is improved, and its step is as follows:
1) identical, two glasses varying in size of selected shape are as interior cup idiosome and outer cup idiosome, and inside and outside cup idiosome 2 ~ 5cm higher than finished glass cup;
2) on interior cup outer wall, directly carry out thermally transferred pattern, drawing and/or spray carving, and then be close to individual layer PVB adhesive film;
3) be inserted in outer cup idiosome by outer wall being provided with cup idiosome in PVB glued membrane, heat and keep temperature to be 60 ~ 80 DEG C, internal cup idiosome inner bottom part applies and keeps pressure to be 0.3 ~ 0.5MPa, the time that described pressure maintains is 15-20min, makes described interior cup idiosome and outer cup idiosome be bonded together and discharge air therebetween;
4) glass autoclave is utilized to remove air remaining between glass wall of cup and PVB glued membrane;
5) glass sealing machine is utilized to carry out sealing process;
6) anneal, lower the temperature;
7) reduce to after room temperature until temperature, outer cup outer wall sprays one deck sensitization discoloration ink, this layer of sensitization discoloration ink is 2 ~ 3cm apart from rim of a cup distance.
Beneficial effect of the present invention is: between inner cup and the outer cup, arrange PVB adhesive film, and inside and outside glass can be made closely to stick together, even if break, glass fragment also can be bonded on PVB glued membrane, can effectively prevent glass fragment from hurting sb.'s feelings.Between two-layer PVB glued membrane, be provided with the petal, plant stem-leaf etc. of drying process, the moment that fresh flower, plant etc. is beautiful is kept in glass used in everyday, more adds its value of art appreciation.In addition, outer cup outer wall sprays one deck sensitization discoloration ink, glass can be made under light irradiates to present different colors, more add visual enjoyment.In the present invention, cup outer wall is preferably parallel to each other with outer cup inwall and all becomes the structure of reverse frustoconic, is conducive to fitting tightly between inside and outside cup and PVB glued membrane.One deck heat-resistant fireproof high transparency glue is applied on the surface of ornament, can effectively prevent high temperature failure ornament in the processes such as glass subsequent heat, sealing, thus make some burning-points lower but zingy ornament such as dry petal etc. appears in glass, increase glass artistic treat in use.
Accompanying drawing explanation
Fig. 1 is the schematic diagram of a kind of safe art glass cup of the embodiment of the present invention 1;
Fig. 2 is the schematic diagram of a kind of safe art glass cup of the embodiment of the present invention 2;
In figure, each label implication is: 1 is sensitization discoloration ink; 2 is outer cups; 3a is outer PVB adhesive film; 4 is interior PVB adhesive films; 5 is interior cups; 6 is ornaments; 7 is interior cup outer walls; 8 is outer cup inwalls; 9 is outer cup outer walls; 3b is individual layer PVB adhesive film.
Detailed description of the invention
Below in conjunction with accompanying drawing, the specific embodiment of the present invention is elaborated.
Embodiment 1:
As shown in Figure 1, the present invention includes interior cup 5 and outer cup 2, between interior cup outer wall 7 and outer cup inwall 8, be provided with interior PVB adhesive film 4, ornament 6 and outer PVB adhesive film 3a successively.The surface of described ornament 6 applies one deck heat-resistant fireproof high transparency glue, outer cup outer wall 9 sprays one deck sensitization discoloration ink, described interior cup outer wall 7 is parallel to each other with outer cup inwall 8 and all becomes reverse frustoconic structure, described ornament 6 can be petal and/or the plant base of leaf of drying process, but being not limited to this, can also be animal feather, artifacts, paint etc.
Accordingly, the step of its preparation method is as follows:
1) identical, two glasses varying in size of selected shape are as interior cup idiosome and outer cup idiosome, and inside and outside cup idiosome 2 ~ 5cm higher than finished glass cup;
2) on interior cup outer wall 7, be close to PVB adhesive film 4 in one deck, be pasted onto on interior PVB adhesive film 4 after ornament 6 outer surface one deck heat-resistant fireproof high transparency glue, and then be close to the outer PVB adhesive film 3a of one deck;
3) be inserted in outer cup idiosome by outer wall being provided with cup idiosome in PVB glued membrane, heat and keep temperature to be 60 ~ 80 DEG C, internal cup idiosome inner bottom part applies and keeps pressure to be 0.3 ~ 0.5MPa, described pressure is held time as 15-20min, makes described interior cup idiosome and outer cup idiosome be bonded together and discharge air therebetween;
4) glass autoclave is utilized to remove air remaining between inside and outside wall of cup and PVB glued membrane;
5) glass sealing machine is utilized to carry out sealing process;
6) anneal, lower the temperature;
7) reduce to after room temperature until temperature, outer cup outer wall 9 sprays one deck sensitization discoloration ink 1, this layer of sensitization discoloration ink 1 is 2 ~ 3cm apart from rim of a cup distance.
Embodiment 2:
As shown in Figure 2, with the difference of a kind of safe art glass cup of embodiment 1, embodiment 2 is only that described ornament 6 is set directly on interior cup outer wall 7, described PVB adhesive film is individual layer PVB adhesive film 3b.Described ornament 6 is at least the one in thermally transferred pattern, paint and glass spray carving works.
Embodiment 2 is only with the difference of a kind of safe art glass cup preparation method of embodiment 1: the step 2 in embodiment 2) carve for directly carrying out thermally transferred pattern, drawing and/or spray on interior cup outer wall 7, and then be close to individual layer PVB adhesive film 3b.
Described sensitization discoloration ink includes photochromic micro-encapsulation or other photosensitive colour-changing material, this sensitization discoloration ink is without being colourless under light conditions, become coloured under wavelength is the irradiation of 320 ~ 380nm light, as purple, skyblue, blueness, yellow, orange, redness, grey etc., can carry out that selection is monochromatic or polychrome is used in combination as required.
Described PVB glued membrane is by polyvinyl butyral resin, through plasticizer 3GO(triethylene glycol two tricaprylate) plasticizing extruding and shaping a kind of macromolecular material.
Described interior cup outer wall 7 and outer cup inwall 8 comprise bottom glass, and described interior PVB adhesive film 4, outer PVB adhesive film 3a and individual layer PVB adhesive film 3b also comprise bottom glass.
By reference to the accompanying drawings embodiments of the present invention are explained in detail above, but the present invention is not limited to above-mentioned embodiment, in the ken that described technical field those of ordinary skill possesses, various change can also be made under the prerequisite not departing from present inventive concept.
Claims (9)
1. a safe art glass cup, comprises interior cup (5) and outer cup (2), it is characterized in that being provided with PVB adhesive film and ornament (6) between described interior cup (5) and outer cup (2).
2. the safe art glass cup of one according to claim 1, it is characterized in that being provided with interior PVB adhesive film (4), ornament (6) and outer PVB adhesive film (3a) successively between described interior cup (5) and outer cup (2), described ornament (6) outer surface one deck heat-resistant fireproof high transparency glue.
3. the safe art glass cup of one according to claim 1, it is characterized in that described ornament (6) is set directly on interior cup outer wall (7), described PVB adhesive film is individual layer PVB adhesive film (3b).
4. the safe art glass cup of one according to claim 1, is characterized in that the outer wall (9) upper spraying one deck sensitization discoloration ink (1) of described outer cup (2).
5. the safe art glass cup of one according to claim 1, is characterized in that the outer wall (7) of described interior cup (5) is parallel to each other with the inwall (8) of outer cup (2) and all becomes reverse frustoconic structure.
6. the safe art glass cup of one according to claim 2, is characterized in that petal that described ornament (6) is drying process and/or plant base of leaf.
7. the safe art glass cup of one according to claim 3, is characterized in that described ornament (6) is at least the one in thermally transferred pattern, paint and glass spray carving works.
8. the preparation method of a kind of safe art glass cup according to claim 1 or 2 or 4 or 5 or 6, is characterized in that comprising the following steps:
Two glasses that selected shape is identical, vary in size are as interior cup idiosome and outer cup idiosome, and inside and outside cup idiosome 2 ~ 5cm higher than finished glass cup;
Interior cup outer wall (7) is close to PVB adhesive film (4) in one deck, is pasted onto on interior PVB adhesive film (4) after ornament (6) outer surface one deck heat-resistant fireproof high transparency glue, and then be close to the outer PVB adhesive film (3a) of one deck;
Be inserted in outer cup idiosome by outer wall being provided with cup idiosome in PVB glued membrane, heat and keep temperature to be 60 ~ 80 DEG C, internal cup idiosome inner bottom part applies and keeps pressure to be 0.3 ~ 0.5MPa, described pressure is held time as 15-20min, makes described interior cup idiosome and outer cup idiosome be bonded together and discharge air therebetween;
Glass autoclave is utilized to remove air remaining between inside and outside wall of cup and PVB glued membrane;
Glass sealing machine is utilized to carry out sealing process;
Annealing, cooling;
Reduce to after room temperature until temperature, at outer cup outer wall (9) upper spraying one deck sensitization discoloration ink (1), this layer of sensitization discoloration ink (1) is 2 ~ 3cm apart from rim of a cup distance.
9. the preparation method of a kind of safe art glass cup according to claim 1 or 3 or 4 or 5 or 7, is characterized in that comprising the following steps:
Two glasses that selected shape is identical, vary in size are as interior cup idiosome and outer cup idiosome, and inside and outside cup idiosome 2 ~ 5cm higher than finished glass cup;
Interior cup outer wall (7) is directly carried out thermally transferred pattern, drawing and/or spray carving, and then is close to individual layer PVB adhesive film (3b);
Be inserted in outer cup idiosome by outer wall being provided with cup idiosome in PVB glued membrane, heat and keep temperature to be 60 ~ 80 DEG C, internal cup idiosome inner bottom part applies and keeps pressure to be 0.3 ~ 0.5MPa, the time that described pressure maintains is 15-20min, makes described interior cup idiosome and outer cup idiosome be bonded together and discharge air therebetween;
Glass autoclave is utilized to remove air remaining between glass wall of cup and PVB glued membrane;
Glass sealing machine is utilized to carry out sealing process;
Annealing, cooling;
Reduce to after room temperature until temperature, at outer cup outer wall (9) upper spraying one deck sensitization discoloration ink (1), this layer of sensitization discoloration ink (1) is 2 ~ 3cm apart from rim of a cup distance.