CN105505199B - A kind of anti-dazzle UV cured resin coatings of LCD display - Google Patents
A kind of anti-dazzle UV cured resin coatings of LCD display Download PDFInfo
- Publication number
- CN105505199B CN105505199B CN201610053122.6A CN201610053122A CN105505199B CN 105505199 B CN105505199 B CN 105505199B CN 201610053122 A CN201610053122 A CN 201610053122A CN 105505199 B CN105505199 B CN 105505199B
- Authority
- CN
- China
- Prior art keywords
- resin
- parts
- polyurethane acrylic
- acrylic resin
- functionality polyurethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of LCD display with anti-dazzle UV cured resin coatings, includes the component of following weight proportion:50 75 parts of UV-cured resin, 30 65 parts of solvent, 0.5 2 parts of light trigger, 0.2 0.5 parts of anti-dazzle particle, 13 parts of auxiliary agent;UV-cured resin includes high-functionality polyurethane acrylic resin, middle degree of functionality polyurethane acrylic resin and Silicone-Modified Acrylate Resin;The weight ratio of high-functionality polyurethane acrylic resin, middle degree of functionality polyurethane acrylic resin and Silicone-Modified Acrylate Resin is 23:3‑4:1.LCD display transparent substrate surface is coated in using coating of the present invention, the coating scratch resistance capability formed after UV solidifies is strong, hardness is high, and anti-wear performance is good, and has preferable anti-glare properties energy.
Description
Technical field
The present invention relates to a kind of anti-dazzle UV cured resin coatings for protecting LCD display.
Background technology
LCD (Liquid Crystal Display) LCDs, it is the display device of planar ultra-thin, it is by certain
Colour or the monochrome pixels composition of quantity, are positioned in front of light source or reflecting surface.Its cardinal principle is to stimulate liquid with electric current
Brilliant molecule produces point, line, surface and coordinates back fluorescent tube to form picture.LCD display power consumption is very low, therefore is favored by engineer,
It is suitable for use with the electronic equipment of battery.
In recent years, LCD Display Techniques and production development are rapid, and LCD display has become the important composition of information industry
Part.LCD display uses transparent synthesis high polymer material more, such as:PC(Makrolon)、PMMA(Poly-methyl methacrylate
Ester)、PET(Polyester)Deng.Scuffing, the abrasion on surface can be caused in actual application, conventional method is to coat one on surface
The paint of layer water white transparency, to improve the performance of the hardness on surface, wear-resisting, anti-scratch etc., have the function that to protect surface.
But the skin of paint on one side surface easily comes off, it is impossible to effectively protects matrix material for a long time;On the other hand, skin of paint
Coating and drying the making of display screen is become cumbersome, so as to add production cost.
Ultraviolet light solidifies(UV solidifies)Coating be the 1960s exploitation a kind of environment-friendly and energy-efficient coating, the seventies I
State starts to set foot in the technical field, and tremendous development is just obtained after the nineties.Ultraviolet-curing paint is under ultraviolet light
Rapid curing, not only curing rate is fast, and the energy can also be saved compared with heat curing coating.At present, it is not only in timber, gold
Category, plastics, paper, widely apply on leather, but also on the materials such as optical fiber, printed substrate, electronic component encapsulation into
Work(application.But conventional ultraviolet curable coating hardness is poor, thus not rub resistance, easily scratch.
Strong light caused by the strong light of the surrounding of LCD display outer surface reflection simultaneously or inside injects human eye, easily causes thorn
Eye is fuzzy, clearly display screen content, this phenomenon can not be referred to as dazzle.Therefore it provides a kind of have anti-dazzle and resist simultaneously
The UV cured resin coatings of scratch performance, turn into the emphasis of existing research.
The content of the invention
The invention aims to solve defect present in prior art, there is provided a kind of hardness is high, anti-dazzle, is applicable
It is coating material solidified in the UV of LCD display.
In order to achieve the above object, the invention provides a kind of LCD display with anti-dazzle UV cured resin coatings, including with
The component of lower weight proportion:UV-cured resin 50-75 parts, solvent 30-65 parts, light trigger 0.5-2 parts, anti-dazzle particle
0.2-0.5 parts, auxiliary agent 1-3 parts;UV-cured resin includes high-functionality polyurethane acrylic resin, middle degree of functionality polyurethane
Acrylic resin and Silicone-Modified Acrylate Resin;High-functionality polyurethane acrylic resin, middle degree of functionality polyurethane third
The weight of olefin(e) acid resin and Silicone-Modified Acrylate Resin ratio is 2-3:3-4:1.
Wherein, anti-dazzle particle includes nano silicon and organic fine particles;The quality of nano silicon and organic fine particles
Than for 1:1.
The preferred polystyrene resin particulate of organic fine particles, particle size are 1-6 μm.
Auxiliary agent includes defoamer, dispersant and levelling agent;Defoamer accounts for the 0.5%-1% of cold coating gross weight;Dispersant
Account for the 0.5%-1% of cold coating gross weight;Levelling agent accounts for the 1%-1.5% of cold coating gross weight.
The BYK088 of the preferably German BYK companies of defoamer;The ATU of the preferably German BYK companies of dispersant;The preferred moral of levelling agent
The BYK373 of BYK companies of state.
The weight proportion of the anti-dazzle UV cured resin coatings preferred ingredient of the present invention:70 parts of UV-cured resin, solvent 45
Part, 1 part of light trigger, 0.15 part of nano silicon, 0.15 part of polystyrene resin particulate, 0.5 part of dispersant, defoamer 1
Part, 1 part of levelling agent;UV-cured resin includes high-functionality polyurethane acrylic resin, middle degree of functionality polyurethane acroleic acid
Resin and Silicone-Modified Acrylate Resin;High-functionality polyurethane acrylic resin, middle degree of functionality polyurethane acroleic acid tree
The weight of fat and Silicone-Modified Acrylate Resin ratio is 2:4:1;Solvent uses toluene and methyl proxitol mixed solution;
Toluene and methyl proxitol mass ratio are 1:1;Light trigger uses 1- hydroxycyclohexyl phenyl ketones.
Present invention also offers the preparation method of above-mentioned anti-dazzle UV cured resin coatings, comprise the following steps:Will be above-mentioned molten
Agent is divided into three parts, and a part of solvent addition UV-cured resin is well mixed to obtain resin component slurries, another part
Solvent addition light trigger is well mixed to obtain the solution containing light trigger, and remainder solvent mixes with anti-dazzle particle auxiliary agent
The suspension containing auxiliary agent uniformly is obtained, resin component slurries, the solution containing light trigger and the suspension containing auxiliary agent are mixed
Uniformly produce the anti-dazzle UV cured resin coatings of the present invention.
The present invention has advantages below compared with prior art:By the optimum ratio to ultraviolet-curing resin, preferably carry
High UV cured resin coatings form the hardness of coating.By the selection to anti-dazzle particle, reach preferable anti-dazzle light action.
The bubble in coating is reduced using defoamer, the flow leveling of film layer after paint solidification is improved using levelling agent, increase applies
The smoothness and feel of film layer, the stability of coating is improved using reflection agent.Simultaneously in preparation process, dissolve in batches, more
Add fully.LCD display transparent substrate surface is coated in using coating of the present invention, the coating scratch resistance energy formed after UV solidifies
Power is strong, hardness is high, and anti-wear performance is good, and has preferable anti-glare properties energy.
Embodiment
With reference to specific embodiment, the present invention is described in detail.
Embodiment 1
Coating forms(Parts by weight):
High-functionality polyurethane acrylic resin(The CN9013 of SARTOMER companies)20 parts
Middle degree of functionality polyurethane acrylic resin(The CN983 of SARTOMER companies)40 parts
Silicone-Modified Acrylate Resin(The EB1360 of Belgian UCB. S.A. (BE) Bruxelles Belgium)10 parts
Light trigger(1- hydroxycyclohexyl phenyl ketones)1 part
Toluene and methyl proxitol mixed solvent(Mass ratio 1:1)45 parts
0.15 part of nano silicon
0.15 part of polystyrene resin particulate
Dispersant(The ATU of German BYK companies)0.5 part
Defoamer(The BYK088 of German BYK companies)1 part
Levelling agent(The BYK373 of German BYK companies)1 part
Preparation method:By high-functionality polyurethane acrylic resin, middle degree of functionality polyurethane acrylic resin and organosilicon
The in the mixed solvent of modified acrylic ester resin addition 1/3 is well mixed to obtain resin component slurries, and light trigger adds in addition
1/3 in the mixed solvent is well mixed to obtain the solution containing light trigger, the mixed solvent and nano-silica of remaining 1/3 part
SiClx, polystyrene resin particulate, dispersant, defoamer and levelling agent are well mixed to obtain the suspension containing auxiliary agent, by resin
Composition slurries, the solution containing light trigger and the suspension containing auxiliary agent are well mixed to produce anti-dazzle UV solidified resins of the present invention
Coating.
Embodiment 2
Coating forms(Parts by weight):
High-functionality polyurethane acrylic resin(The CN9013 of SARTOMER companies)16 parts
Middle degree of functionality polyurethane acrylic resin(The CN983 of SARTOMER companies)26 parts
Silicone-Modified Acrylate Resin(The EB1360 of Belgian UCB. S.A. (BE) Bruxelles Belgium)8 parts
Light trigger(1- hydroxycyclohexyl phenyl ketones)0.5 part
Toluene and methyl proxitol mixed solvent(Mass ratio 1:1)30 parts
0.1 part of nano silicon
0.1 part of polystyrene resin particulate
Dispersant(The ATU of German BYK companies)0.5 part
Defoamer(The BYK088 of German BYK companies)0.4 part
Levelling agent(The BYK373 of German BYK companies)1 part
Preparation method:By high-functionality polyurethane acrylic resin, middle degree of functionality polyurethane acrylic resin and organosilicon
The in the mixed solvent of modified acrylic ester resin addition 1/3 is well mixed to obtain resin component slurries, and light trigger adds in addition
1/3 in the mixed solvent is well mixed to obtain the solution containing light trigger, the mixed solvent and nano-silica of remaining 1/3 part
SiClx, polystyrene resin particulate, dispersant, defoamer and levelling agent are well mixed to obtain the suspension containing auxiliary agent, by resin
Composition slurries, the solution containing light trigger and the suspension containing auxiliary agent are well mixed to produce anti-dazzle UV solidified resins of the present invention
Coating.
Embodiment 3
Coating forms(Parts by weight):
High-functionality polyurethane acrylic resin(The CN9013 of SARTOMER companies)30 parts
Middle degree of functionality polyurethane acrylic resin(The CN983 of SARTOMER companies)35 parts
Silicone-Modified Acrylate Resin(The EB1360 of Belgian UCB. S.A. (BE) Bruxelles Belgium)10 parts
Light trigger(1- hydroxycyclohexyl phenyl ketones)2 parts
Toluene and methyl proxitol mixed solvent(Mass ratio 1:1)65 parts
0.2 part of nano silicon
0.2 part of polystyrene resin particulate
Dispersant(The ATU of German BYK companies)1 part
Defoamer(The BYK088 of German BYK companies)1 part
Levelling agent(The BYK373 of German BYK companies)1.5 part
Preparation method:By high-functionality polyurethane acrylic resin, middle degree of functionality polyurethane acrylic resin and organosilicon
The in the mixed solvent of modified acrylic ester resin addition 1/3 is well mixed to obtain resin component slurries, and light trigger adds in addition
1/3 in the mixed solvent is well mixed to obtain the solution containing light trigger, the mixed solvent and nano-silica of remaining 1/3 part
SiClx, polystyrene resin particulate, dispersant, defoamer and levelling agent are well mixed to obtain the suspension containing auxiliary agent, by resin
Composition slurries, the solution containing light trigger and the suspension containing auxiliary agent are well mixed to produce anti-dazzle UV solidified resins of the present invention
Coating.
Performance test
The coating being prepared in embodiment 1-3 is sprayed on plastic plate respectively(60mm × 60mm transparent PC
DMX2415 plates)On, toasted 5 minutes at a temperature of 60 DEG C, then by ultraviolet light(Energy is 1300 MJs/square centimeter)
Irradiation 25 seconds, the coating that thickness is 12 microns is obtained on plastic plate.Following performance test is carried out to resulting coating, as a result
As shown in table 1.
1st, adhesive force is tested
Draw 100 1 millimeter × 1 millimeter of square lattice on the coating surface with stroke lattice device.Produced with Minnesota Mining and Manufacturing Company
The adhesive tape of model 600 is smooth to be bonded on grid, is not stayed a space, is then uncovered adhesive tape rapidly with 60 ° of angle,
Whether have at observation coating scratching edge and come off.
Such as come off any for 5B, the area that comes off be 4B between 0-5%, and the area that comes off is 3B between 5%-15%, de-
It is 2B to fall area between 15%-35%, and the area that comes off is 1B between 35%-65%, and the area that comes off is 0B more than 65%.
2nd, hardness test
Hardness test is carried out according to method specified in chapter 4 in GB/6739T.
Mitsubishi is used successively(UNI)Hardness is 2H, 3H, 4H, 5H and 6H pencil, on sample, is applied with 90 ° of angle
1000 gram forces, 10 millimeters of strokes, the pencil of each hardness draw 3 in diverse location, and whether observation appearance of coat has obvious cut,
There is the minimum pencil hardness of cut in record.
3rd, adhesion strength is tested
PH-5813 gauge heads are matched somebody with somebody using BYK PH-5811/PH-5811, measuring head diameter is 0.75 millimeter, and test angle is
90 °, apply certain load(N)Streaked with the speed of 1 cel in coating surface, whether observation coating surface has cut, records
There is the minimum load power of cut(N).
4th, in anti-dazzle performance test
Black acrylic plate is bonded at the back side of plastic plate, the experiment slice of no backside reflection is made.Coating faces up, water
Placing flat under normal office environment, from the angle direction straight at 30 ° visually from, judge anti-dazzle performance.Specific standards
It is as follows:
(1)White blur:A- is visual good substantially without white blur;B- slightly has white blur, does not influence clarity;C-
White blur, slightly influence clarity;D- white blurs, influence clarity.
(2)Image reflects:A- reflects without image substantially, visual good;B- slightly has image reflection, does not influence observing effect;
C- images reflect, and slightly influence observing effect;D- images reflect, and influence observing effect.
The performance test of each embodiment prepares coating of table 1
Embodiment | Adhesive force | Hardness | Resistance to marring | Anti-dazzle performance |
1 | 5B | 6H | 9N | A+A |
2 | 5B | 5H | 8N | A+B |
3 | 5B | 5H | 8N | B+A |
Claims (6)
- A kind of 1. anti-dazzle UV cured resin coatings of LCD display, it is characterised in that:Include the component of following weight proportion:It is purple Outer light-cured resin 50-75 parts, solvent 30-65 parts, light trigger 0.5-2 parts, anti-dazzle particle 0.2-0.5 parts, auxiliary agent 1-3 parts; The UV-cured resin includes high-functionality polyurethane acrylic resin, middle degree of functionality polyurethane acrylic resin and organic Fluorine-silicon modified acrylic ester resin;The high-functionality polyurethane acrylic resin, middle degree of functionality polyurethane acrylic resin and have The weight ratio of machine fluorine-silicon modified acrylic ester resin is 2-3:3-4:1;The anti-dazzle particle includes nano silicon and organic micro- Grain;The mass ratio of the nano silicon and organic fine particles is 1:1.
- 2. cold coating according to claim 1, it is characterised in that:The organic fine particles are micro- using polystyrene resin Grain, particle size are 1-6 μm.
- 3. cold coating according to claim 2, it is characterised in that:The auxiliary agent includes defoamer, dispersant and levelling Agent;The defoamer accounts for the 0.5%-1% of cold coating gross weight;The dispersant accounts for the 0.5%-1% of cold coating gross weight;It is described Levelling agent accounts for the 1%-1.5% of cold coating gross weight.
- 4. cold coating according to claim 3, it is characterised in that:The defoamer is using German BYK companies BYK088;The dispersant uses the ATU of German BYK companies;The levelling agent uses the BYK373 of German BYK companies.
- 5. cold coating according to claim 4, it is characterised in that:The UV cured resin coatings are matched somebody with somebody including following weight The component of ratio:70 parts of UV-cured resin, 45 parts of solvent, 1 part of light trigger, 0.15 part of nano silicon, polystyrene 0.15 part of resin particle, 0.5 part of dispersant, 1 part of defoamer, 1 part of levelling agent;The UV-cured resin includes high functionality Polyurethane acrylic resin, middle degree of functionality polyurethane acrylic resin and Silicone-Modified Acrylate Resin;The high function Degree polyurethane acrylic resin, the weight ratio of middle degree of functionality polyurethane acrylic resin and Silicone-Modified Acrylate Resin are 2:4:1;The solvent uses toluene and methyl proxitol mixed solution;Toluene and the methyl proxitol mass ratio is 1: 1;The light trigger uses 1- hydroxycyclohexyl phenyl ketones.
- 6. the preparation method of any cold coating of claim 1 to 5, it is characterised in that:The solvent is divided into three portions Point, a part of solvent addition UV-cured resin is well mixed to obtain resin component slurries, and another part solvent adds light and drawn Hair agent is well mixed to obtain the solution containing light trigger, and remainder solvent is well mixed to obtain to contain with anti-dazzle particle auxiliary agent and helped The suspension of agent, resin component slurries, the solution containing light trigger and the suspension containing auxiliary agent are well mixed described in producing Cold coating.