CN109609019A - A kind of smart television meeting liquid crystal display UV cured resin coating - Google Patents
A kind of smart television meeting liquid crystal display UV cured resin coating Download PDFInfo
- Publication number
- CN109609019A CN109609019A CN201811369349.7A CN201811369349A CN109609019A CN 109609019 A CN109609019 A CN 109609019A CN 201811369349 A CN201811369349 A CN 201811369349A CN 109609019 A CN109609019 A CN 109609019A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- cured resin
- polyurethane acrylic
- acrylic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of smart television meeting liquid crystal display UV cured resin coating, the component including following weight proportion: 50-75 parts of UV-cured resin, 30-65 parts of solvent, 0.5-2 parts of photoinitiator, 1-3 parts of auxiliary agent;UV-cured resin includes high-functionality polyurethane acrylic resin, middle degree of functionality polyurethane acrylic resin and Silicone-Modified Acrylate Resin;The weight ratio of high-functionality polyurethane acrylic resin, middle degree of functionality polyurethane acrylic resin and Silicone-Modified Acrylate Resin is 2-3:3-4:1.Smart television meeting liquid crystal display transparent substrate surface is coated in using coating of the present invention, the coating scratch resistance capability formed after UV solidifies is strong, hardness is high, and wear-resisting property is good.
Description
Technical field
The present invention relates to a kind of UV cured resin coatings for protecting smart television meeting liquid crystal display.
Background technique
Liquid crystal display is the display equipment of planar ultra-thin, it is made of a certain number of colored or monochrome pixels, is placed
In front of light source or reflecting surface.Its cardinal principle is to generate point, line, surface cooperation back fluorescent tube with electric current stimulation liquid crystal molecule
Constitute picture.Smart television meeting is very low with liquid crystal display power consumption, therefore is favored by engineer, suitable for using battery
Electronic equipment.
In recent years, LCD technology and product are quickly grown, and smart television meeting liquid crystal display has become letter
The important component of breath industry.Smart television meeting mostly uses transparent synthesis high molecular material with liquid crystal display, such as: PC
(polycarbonate), PMMA(polymethyl methacrylate), PET(polyester) etc..It will cause drawing for surface in actual application
Wound, abrasion, conventional method are to coat one layer of colorless and transparent paint on surface, to improve the hardness, wear-resisting, anti-scratch etc. on surface
The performance of aspect has the function that protect surface.But the skin of paint on one side surface is easy to fall off, it cannot for a long time effectively
Protect basis material in ground;On the other hand, the coating and drying of skin of paint make the production of display screen become cumbersome, to increase life
Produce cost.
Ultraviolet light solidify (UV solidifies) coating be the 1960s exploitation a kind of environment-friendly and energy-efficient coating, the seventies I
State starts to set foot in the technical field, and tremendous development is just obtained after the nineties.Ultraviolet-curing paint is under ultraviolet light
Rapid curing, not only curing rate is fast, but also the energy can also be saved compared with heat curing coating.Currently, it is not only in timber, gold
Category, paper, is widely applied on leather plastics, but also on the materials such as optical fiber, printed wiring board, electronic component encapsulation at
Function application.But conventional ultraviolet curable coating hardness is poor, thus not rub resistance, easily scratch.
Summary of the invention
The purpose of the present invention is to solve defect existing in the prior art, provide that a kind of hardness is high, is suitable for intelligence
The UV of video conference liquid crystal display is coating material solidified.
In order to achieve the above object, the present invention provides a kind of smart television meeting liquid crystal display UV solidified resins
Coating, the component including following weight proportion: 50-75 parts of UV-cured resin, 30-65 parts of solvent, photoinitiator 0.5-2
Part, 1-3 parts of auxiliary agent;UV-cured resin includes high-functionality polyurethane acrylic resin, middle degree of functionality polyurethane acroleic acid
Resin and Silicone-Modified Acrylate Resin;High-functionality polyurethane acrylic resin, middle degree of functionality polyurethane acroleic acid tree
The weight ratio of rouge and Silicone-Modified Acrylate Resin is 2-3:3-4:1.
Auxiliary agent includes defoaming agent and levelling agent;Defoaming agent accounts for the 0.5%-1% of UV cured resin coating total weight;Levelling agent accounts for
The 1%-1.5% of UV cured resin coating total weight.
Wherein, defoaming agent preferred, polyethers modified silicon;Levelling agent preferred acrylate class levelling agent.Solvent is using organic molten
The mixed solvent that agent, preferably toluene and methyl proxitol are mixed with mass ratio 1:1.The preferred 1- hydroxy-cyclohexyl benzene of photoinitiator
Ketone.
The weight proportion of UV cured resin coating preferred ingredient of the present invention are as follows: 70 parts of UV-cured resin, 45 parts of solvent,
1 part of photoinitiator, 1 part of defoaming agent, 1 part of levelling agent;UV-cured resin include high-functionality polyurethane acrylic resin, in
Degree of functionality polyurethane acrylic resin and Silicone-Modified Acrylate Resin;High-functionality polyurethane acrylic resin, middle official
The weight ratio of energy degree polyurethane acrylic resin and Silicone-Modified Acrylate Resin is 2:4:1.
The present invention also provides the preparation methods of above-mentioned UV cured resin coating, it is characterised in that: is divided into the solvent
Three parts, a part of solvent addition UV-cured resin, which is uniformly mixed, obtains resin component slurries, and another part solvent adds
Enter photoinitiator and be uniformly mixed to obtain the solution containing photoinitiator, remainder solvent, which is uniformly mixed to obtain with auxiliary agent, contains auxiliary agent
Solution, by resin component slurries, the solution containing photoinitiator and the solution containing auxiliary agent be uniformly mixed up to the UV solidify
Cold coating.
The present invention is had the advantage that compared with prior art through the optimum ratio to ultraviolet-curing resin, is preferably mentioned
The high hardness of the formed coating of UV cured resin coating.The bubble in coating is reduced using defoaming agent, is improved using levelling agent
The flow leveling of film layer, increases the smoothness and feel of film layer after paint solidification.Simultaneously during the preparation process, in batches molten
Solution, more sufficiently.Smart television meeting liquid crystal display transparent substrate surface is coated in using coating of the present invention, is solidified through UV
The coating scratch resistance capability formed afterwards is strong, hardness is high, and wear-resisting property is good.
Specific embodiment
The present invention is described in detail combined with specific embodiments below.
1 coating of embodiment forms (parts by weight): high-functionality polyurethane acrylic resin be (SARTOMER company
CN9013) 40 parts of organosilicon-modified acrylics of degree of functionality polyurethane acrylic resin (CN983 of SARTOMER company) in 20 parts
Ester resin (EB1360 of Belgian UCB. S.A. (BE) Bruxelles Belgium) 10 parts of photoinitiators (1- hydroxycyclohexyl phenyl ketone), 1 part of toluene and propylene glycol first
45 parts of defoaming agents of base ether mixed solvent (mass ratio 1:1) (polyether-modified silicon), 1 part of levelling agent (esters of acrylic acid), 1 part of preparation side
Method: by high-functionality polyurethane acrylic resin, middle degree of functionality polyurethane acrylic resin and organosilicon-modified acrylate tree
The in the mixed solvent that rouge is added 1/3, which is uniformly mixed, obtains resin component slurries, and other 1/3 in the mixed solvent is added in photoinitiator
It is uniformly mixed and obtains the solution containing photoinitiator, the mixed solvent of remaining 1/3 part is uniformly mixed with defoaming agent and levelling agent
It obtains the solution containing auxiliary agent, resin component slurries, the solution containing photoinitiator and the solution containing auxiliary agent is uniformly mixed to obtain the final product
UV cured resin coating of the present invention.
2 coating of embodiment forms (parts by weight): high-functionality polyurethane acrylic resin be (SARTOMER company
CN9013) 26 parts of organosilicon-modified acrylics of degree of functionality polyurethane acrylic resin (CN983 of SARTOMER company) in 16 parts
Ester resin (EB1360 of Belgian UCB. S.A. (BE) Bruxelles Belgium) 8 parts of photoinitiators (1- hydroxycyclohexyl phenyl ketone), 0.5 part of toluene and propylene glycol first
30 parts of defoaming agents of base ether mixed solvent (mass ratio 1:1) (polyether-modified silicon), 0.4 part of levelling agent (esters of acrylic acid), 1 part of preparation side
Method: by high-functionality polyurethane acrylic resin, middle degree of functionality polyurethane acrylic resin and organosilicon-modified acrylate tree
The in the mixed solvent that rouge is added 1/3, which is uniformly mixed, obtains resin component slurries, and other 1/3 in the mixed solvent is added in photoinitiator
It is uniformly mixed and obtains the solution containing photoinitiator, the mixed solvent of remaining 1/3 part is uniformly mixed with defoaming agent and levelling agent
It obtains the solution containing auxiliary agent, resin component slurries, the solution containing photoinitiator and the solution containing auxiliary agent is uniformly mixed to obtain the final product
UV cured resin coating of the present invention.
3 coating of embodiment forms (parts by weight): high-functionality polyurethane acrylic resin be (SARTOMER company
CN9013) 35 parts of organosilicon-modified acrylics of degree of functionality polyurethane acrylic resin (CN983 of SARTOMER company) in 30 parts
Ester resin (EB1360 of Belgian UCB. S.A. (BE) Bruxelles Belgium) 10 parts of photoinitiators (1- hydroxycyclohexyl phenyl ketone), 2 parts of toluene and propylene glycol first
65 parts of defoaming agents of base ether mixed solvent (mass ratio 1:1) (polyether-modified silicon), 1 part of levelling agent (esters of acrylic acid), 1.5 parts of preparation sides
Method: by high-functionality polyurethane acrylic resin, middle degree of functionality polyurethane acrylic resin and organosilicon-modified acrylate tree
The in the mixed solvent that rouge is added 1/3, which is uniformly mixed, obtains resin component slurries, and other 1/3 in the mixed solvent is added in photoinitiator
It is uniformly mixed and obtains the solution containing photoinitiator, the mixed solvent of remaining 1/3 part is uniformly mixed with defoaming agent and levelling agent
It obtains the solution containing auxiliary agent, resin component slurries, the solution containing photoinitiator and the solution containing auxiliary agent is uniformly mixed to obtain the final product
UV cured resin coating of the present invention.
The coating being prepared in embodiment 1-3 is sprayed on plastic plate by performance test respectively, and (60mm × 60mm's is transparent
PCDMX2415 plate) on, 60 DEG C at a temperature of toast 5 minutes, then by ultraviolet light (energy be 1300 millijoules/square li
Rice) irradiation 25 seconds, the coating with a thickness of 12 microns is obtained on plastic plate.Obtained coating is performed the following performance tests,
The results are shown in Table 1.
1, test adhesive force draws 100 1 millimeter × 1 millimeter of square lattice with cross hatch device on the coating surface.Use the U.S.
The adhesive tape of the model 600 of 3M company production is smooth to be bonded on grid, a gap is not stayed, then with 60 ° of angle
Adhesive tape is uncovered rapidly, whether is had at observation coating scratching edge and is fallen off.
It such as falls off without any for 5B, the area that falls off is 4B between 0-5%, and falling off area between 5%-15% is 3B, is taken off
It is 2B that area, which is fallen, between 15%-35%, and falling off area between 35%-65% is 1B, and the above are 0B 65% for the area that falls off.
2, hardness test carries out hardness test according to method specified in chapter 4 in GB/6739T.
It is successively the pencil of 2H, 3H, 4H, 5H and 6H with Mitsubishi's (UNI) hardness, on sample, with 90 ° of angle application
The pencil of 1000 gram forces, 10 millimeters of strokes, each hardness draws 3 in different location, and whether observation appearance of coat has obvious scratch,
There is the minimum pencil hardness of scratch in record.
3, adhesion strength test matches PH-5813 gauge head using BYKPH-5811/PH-5811, and measuring head diameter is 0.75 milli
Rice, test angle are 90 °, apply certain load (N) and are streaked with the speed of 1 cm/s in coating surface, and observation coating surface is
No to have scratch, there is the minimum load power (N) of scratch in record.
The performance test of each embodiment prepares coating of table 1-
Claims (1)
1. a kind of smart television meeting liquid crystal display UV cured resin coating, it is characterised in that: match including following weight
The component of ratio: 50-75 parts of UV-cured resin, 30-65 parts of solvent, 0.5-2 parts of photoinitiator, 1-3 parts of auxiliary agent;It is described ultraviolet
Light-cured resin includes high-functionality polyurethane acrylic resin, middle degree of functionality polyurethane acrylic resin and organic-silicon-modified third
Alkene acid ester resin;The high-functionality polyurethane acrylic resin, middle degree of functionality polyurethane acrylic resin and organic-silicon-modified
The weight ratio of acrylate is 2-3:3-4:1;The auxiliary agent includes defoaming agent and levelling agent;The defoaming agent accounts for UV solidification
The 0.5%-1% of cold coating total weight;The levelling agent accounts for the 1%-1.5% of UV cured resin coating total weight;The defoaming agent
Using polyether-modified silicon;The levelling agent uses esters of acrylic acid levelling agent;The UV cured resin coating includes following weight
The component of proportion: 70 parts of UV-cured resin, 45 parts of solvent, 1 part of photoinitiator, 1 part of defoaming agent, 1 part of levelling agent;The purple
Outer light-cured resin includes high-functionality polyurethane acrylic resin, middle degree of functionality polyurethane acrylic resin and organic-silicon-modified
Acrylate;The high-functionality polyurethane acrylic resin, middle degree of functionality polyurethane acrylic resin and organosilicon change
Property acrylate weight ratio be 2:4:1;The solvent uses toluene and methyl proxitol mixed solution;The toluene
It is 1:1 with methyl proxitol mass ratio;The photoinitiator uses 1- hydroxycyclohexyl phenyl ketone;
The solvent is divided into three parts by UV cured resin coating preparation method, and ultraviolet light solidification tree is added in a part of solvent
Rouge, which is uniformly mixed, obtains resin component slurries, and another part solvent addition photoinitiator, which is uniformly mixed, to be obtained containing photoinitiator
Solution, remainder solvent are uniformly mixed to obtain the solution containing auxiliary agent with auxiliary agent, by resin component slurries, contain photoinitiator
Solution and solution containing auxiliary agent are uniformly mixed up to the UV cured resin coating.