CN105504991A - 一种用于陶瓷产品数码立体打印墨水及其工艺 - Google Patents
一种用于陶瓷产品数码立体打印墨水及其工艺 Download PDFInfo
- Publication number
- CN105504991A CN105504991A CN201610056039.4A CN201610056039A CN105504991A CN 105504991 A CN105504991 A CN 105504991A CN 201610056039 A CN201610056039 A CN 201610056039A CN 105504991 A CN105504991 A CN 105504991A
- Authority
- CN
- China
- Prior art keywords
- agent
- ink
- ceramic product
- starting material
- marking ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用于陶瓷产品数码立体打印墨水及其工艺,原材料按重量百分比分别为:醇酯十二7%-14%、二乙二醇甲醚30%-40%、五氧化二钒35%-55%、分散剂3%-8%、流平剂0.5%-1.5%和PH调解剂1%-2%,所述的分散剂为Solsperse-17000,流平剂为EFKA-3236,PH调解剂为氨水、三甲胺或硫酸盐,将所述原材料搅拌混合均匀;投入研磨机研磨5-7h;调试细度最大粒径d100<1um,平均粒径为250-350nm;通过离心机离心,转齿≥7000rad,流量控制在8kg/min;离心后通过1um滤芯过滤,包装;其质量稳定,打印出的图案颜色清晰准确、均匀鲜艳,成品美观。
Description
技术领域
本发明涉及打印耗材数码喷墨技术领域,具体涉及一种用于陶瓷产品数码立体打印墨水及其工艺。
背景技术
陶瓷产品喷墨技术是通过软件对产品图片设计,随意性强,可塑性,变化广,经过电脑传输到打印机输出到瓷砖表面。
传统的陶瓷产品喷墨技术通常采用丝网印花技术和滚筒印花技术,其缺陷在于:需要制片、晒网、刻版等工序,生产周期长,效率低,原材料浪费大,产品稳定性差,图案清晰度、精度低,产品档次低,可设计性低。
发明内容
本发明的目的是提供一种用于陶瓷产品数码立体打印墨水及其工艺,其质量稳定,不但打印出的图案颜色清晰准确、均匀鲜艳,成品美观,而且具有良好的耐候性和耐化学稳定性。
本发明解决其技术问题所采用的技术方案是:一种用于陶瓷产品数码立体打印墨水,其特征在于,原材料按重量百分比分别为:醇酯十二7%-14%、二乙二醇甲醚30%-40%、五氧化二钒35%-55%、分散剂3%-8%、流平剂0.5%-1.5%和PH调解剂1%-2%,所述的分散剂为Solsperse-17000,流平剂为EFKA-3236,PH调解剂为氨水、三甲胺或硫酸盐。
作为优选的,原材料按重量百分比分别为:醇酯十二11%、二乙二醇甲醚35%、五氧化二钒46%、分散剂Solsperse-17000为6%、流平剂EFKA-3236为0.8%和PH调解剂氨水1.2%。
本发明一种用于陶瓷产品数码立体打印墨水的工艺,其特征在于包括以下步骤:
a.将所述原材料搅拌混合均匀;
b.投入研磨机研磨5-7h;
c.调试细度最大粒径d100<1um,平均粒径为250-350nm;
d.通过离心机离心,转齿≥7000rad,流量控制在8kg/min;
e.离心后通过1um滤芯过滤,包装。
本发明的有益效果是:体现出无可比拟的技术优势和经济效益;简化了墨水的制作工艺流程,使墨水的稳定性得到了极大的改善,从而减少喷头的堵塞,提高了打印速度和打印质量;充分体现出个性化和艺术化;打印瓷砖经烧制后形成设计所需的立体图案;打印出来的产品图案精度高,可印制出复杂、高精度装饰图案,使产品档次提高;提高印制出图案的耐候性和耐化学稳定性,而且生产周期短,原材料浪费低,生产效率高,可达到节能减排、绿色环保、回归自然的效果。
具体实施方式
为了使本发明所解决的技术问题、技术方案及有益效果更加清楚明白,以下结合实施例,对本发明作进一步的说明。应当理解,此处所描述的实施例仅仅用于解释本发明,并不用于限定本发明。
实施例1
一种用于陶瓷产品数码立体打印墨水,其原材料按重量百分比分别为:醇酯十二8%、二乙二醇甲醚34%、五氧化二钒52%、分散剂Solsperse-17000为4%、流平剂EFKA-3236为0.6%和PH调解剂硫酸盐1.4%。
制作本实施例一种用于陶瓷产品数码立体打印墨水的具体步骤为:
a.将所述原材料搅拌混合均匀;
b.投入研磨机研磨7h;
c.调试细度最大粒径d100<1um,平均粒径为350nm;
d.通过离心机离心,转齿为8000rad,流量控制在8kg/min;
e.离心后通过1um滤芯过滤,包装。
实施例2
一种用于陶瓷产品数码立体打印墨水,其原材料按重量百分比分别为:醇酯十二12%、二乙二醇甲醚36%、五氧化二钒42%、分散剂Solsperse-17000为7%、流平剂EFKA-3236为1.2%和PH调解剂氨水1.8%。制作本实施例一种用于陶瓷产品数码立体打印墨水的具体步骤为:
a.将所述原材料搅拌混合均匀;
b.投入研磨机研磨5h;
c.调试细度最大粒径d100<1um,平均粒径为250nm;
d.通过离心机离心,转齿为7500rad,流量控制在8kg/min;
e.离心后通过1um滤芯过滤,包装。
实施例3
一种用于陶瓷产品数码立体打印墨水,其原材料按重量百分比分别为:醇酯十二11%、二乙二醇甲醚35%、五氧化二钒46%、分散剂Solsperse-17000为6%、流平剂EFKA-3236为0.8%和PH调解剂氨水1.2%。制作本实施例一种用于陶瓷产品数码立体打印墨水的具体步骤为:
a.将所述原材料搅拌混合均匀;
b.投入研磨机研磨6h;
c.调试细度最大粒径d100<1um,平均粒径为300nm;
d.通过离心机离心,转齿为7000rad,流量控制在8kg/min;
e.离心后通过1um滤芯过滤,包装。
实施例4
一种用于陶瓷产品数码立体打印墨水,其原材料按重量百分比分别为:醇酯十二14%、二乙二醇甲醚40%、五氧化二钒38%、分散剂Solsperse-17000为5%、流平剂EFKA-3236为1%和PH调解剂氨水2%。制作本实施例一种用于陶瓷产品数码立体打印墨水的具体步骤为:
a.将所述原材料搅拌混合均匀;
b.投入研磨机研磨7h;
c.调试细度最大粒径d100<1um,平均粒径为320nm;
d.通过离心机离心,转齿为7200rad,流量控制在8kg/min;
e.离心后通过1um滤芯过滤,包装。
实施例5
一种用于陶瓷产品数码立体打印墨水,其原材料按重量百分比分别为:醇酯十二10%、二乙二醇甲醚30%、五氧化二钒50%、分散剂Solsperse-17000为8%、流平剂EFKA-3236为0.5%和PH调解剂三甲胺1.5%。制作本实施例一种用于陶瓷产品数码立体打印墨水的具体步骤为:
a.将所述原材料搅拌混合均匀;
b.投入研磨机研磨5h;
c.调试细度最大粒径d100<1um,平均粒径为280nm;
d.通过离心机离心,转齿为7800rad,流量控制在8kg/min;
e.离心后通过1um滤芯过滤,包装。
以上所述仅为本发明的较佳实施例,并不用以限制本发明,凡在本发明的精神和原则之内所作的任何修改、同等替换和改进等,均应落在本发明的保护范围之内。
Claims (3)
1.一种用于陶瓷产品数码立体打印墨水,其特征在于,原材料按重量百分比分别为:醇酯十二7%-14%、二乙二醇甲醚30%-40%、五氧化二钒35%-55%、分散剂3%-8%、流平剂0.5%-1.5%和PH调解剂1%-2%,所述的分散剂为Solsperse-17000,流平剂为EFKA-3236,PH调解剂为氨水、三甲胺或硫酸盐。
2.根据权利要求1所述的一种用于陶瓷产品数码立体打印墨水,其特征在于,原材料按重量百分比分别为:醇酯十二11%、二乙二醇甲醚35%、五氧化二钒46%、分散剂Solsperse-17000为6%、流平剂EFKA-3236为0.8%和PH调解剂氨水1.2%。
3.一种用于陶瓷产品数码立体打印墨水的工艺,其特征在于包括以下步骤:
a.将所述原材料搅拌混合均匀;
b.投入研磨机研磨5-7h;
c.调试细度最大粒径d100<1um,平均粒径为250-350nm;
d.通过离心机离心,转齿≥7000rad,流量控制在8kg/min;
e.离心后通过1um滤芯过滤,包装。