CN105482751B - A kind of high performance polyurethane pressure sensitive adhesive - Google Patents
A kind of high performance polyurethane pressure sensitive adhesive Download PDFInfo
- Publication number
- CN105482751B CN105482751B CN201511010785.1A CN201511010785A CN105482751B CN 105482751 B CN105482751 B CN 105482751B CN 201511010785 A CN201511010785 A CN 201511010785A CN 105482751 B CN105482751 B CN 105482751B
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- pressure sensitive
- sensitive adhesive
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of high performance polyurethane pressure sensitive adhesive, include the raw material of following parts by weight：70 90 parts of neoprene, 60 80 parts of methyl methacrylate, 60 80 parts of hydroxyl polysiloxane, 30 50 parts of xylene resin, 30 50 parts of polyisocyanates, 20 40 parts of carbon fiber, 20 40 parts of olefine resin, 10 18 parts of azo-compound foaming agent, 10 18 parts of rosin resin, 5 10 parts of triethylamine, 5 10 parts of methylparafynol, 5 10 parts of polybutadiene, 48 parts of triethylamine, 12 parts of dibutyl tin laurate, 0.5 1 parts of N hydroxymethyl acrylamide；Its preparation method comprises the following steps：S1,70 90 parts of neoprene, 60 80 parts of methyl methacrylate, 60 80 parts of hydroxyl polysiloxane, 30 50 parts of xylene resin, 30 50 parts of polyisocyanates are weighed according to deal proportioning, reaction kettle is added in, the temperature of reaction kettle is increased to 60 80 DEG C, and is sufficiently stirred.The present invention prepares simple, the polyurethane contact adhesive performance height of preparation, environmentally friendly, is suitble to large-scale production.
Description
Technical field
The present invention relates to polyurethane contact adhesive technical field more particularly to a kind of high performance polyurethane pressure sensitive adhesives.
Background technology
The materials necks such as pressure sensitive adhesive and its product are widely used in handling official business, pack, electrician, electric appliance, etching, coating and house ornamentation
Domain, it is closely bound up with people’s lives.The pressure sensitive adhesive consumer goods, largely use in all trades and professions.Common pressure sensitive adhesive tape and mark
Label technology is very ripe, and drug on the market for yield, but the pressure sensitive adhesive in fields such as automobile, electronics industry require it is good
Cohesive force and bonding force, cohesive force ensure to be subject to after bonding that glue-line destruction, bonding will not occur when peeling force or shearing force
Card pressure sensitive adhesive of trying hard to keep has a higher peel strength, and the balance of cohesive force and bonding force can easily carry out adherend effectively to bond
Reparation or secondary bonding.
Pressure sensitive adhesive is mainly using solvent-type acrylic ester as mainstream at present, and the pollution and injury that are brought to environment and user are very
Greatly.With increasingly sound and people's environmental consciousness the enhancing of Environmental Protection in China regulation, quality is good, pollution-free, environment-friendly type gluing
Agent will substitute solvent-borne type.Polyurethane contact adhesive is nontoxic, free from environmental pollution, the saving energy, but current polyurethane contact adhesive performance
Not high, bonding force is not high and the degree of balance is not good enough, and we have proposed a kind of high performance polyurethane pressure sensitive adhesives therefore.
The content of the invention
Technical problems based on background technology, the present invention propose a kind of high performance polyurethane pressure sensitive adhesive.
A kind of high performance polyurethane pressure sensitive adhesive includes the raw material of following parts by weight：70-90 parts of neoprene, methyl methacrylate
60-80 parts of ester, 60-80 parts of hydroxyl polysiloxane, 30-50 parts of xylene resin, 30-50 parts of polyisocyanates, carbon fiber 20-40
Part, 20-40 parts of olefine resin, 10-18 parts of azo-compound foaming agent, 10-18 parts of rosin resin, 9-18 parts of triethylamine, methylpent
5-10 parts of alkynol, 5-10 parts of polybutadiene, 1-2 parts of dibutyl tin laurate, 0.5-1 parts of N hydroxymethyl acrylamide；
Its preparation method comprises the following steps：
S1 weighs 70-90 parts of neoprene, 60-80 parts of methyl methacrylate, hydroxyl polysiloxane 60- according to deal proportioning
80 parts, 30-50 parts of xylene resin, 30-50 parts of polyisocyanates, add in reaction kettle, the temperature of reaction kettle is increased to 60-80
DEG C, and be sufficiently stirred, continue 1-2h, obtain component A；
S2 weighs 20-40 parts of carbon fiber, 20-40 parts of olefine resin, azo-compound foaming agent 10-18 according to dosage proportioning
Part, 10-18 parts of rosin resin, 5-10 parts of triethylamine, 5-10 parts of methylparafynol, are put into agitating device, are sufficiently stirred 0.5-
1h obtains component B；
Component B is added in component A by S3, and adds in the triethylamine of 4-8 parts by weight, and 1-2 weights are added after being sufficiently stirred
The dibutyl tin laurate, the N hydroxymethyl acrylamide of 0.5-1 parts by weight of part are measured, obtains component C；
Component C is stood 2-3h by S4 at a temperature of 50-60 DEG C, and a kind of high property is can obtain after the time terminates cooling
It can polyurethane contact adhesive.
Preferably, the one kind of the polyisocyanates in IPDI, TDI.
Preferably, the neoprene, methyl methacrylate, the weight ratio of hydroxyl polysiloxane are 75-85：65-75：65-
75。
Preferably, the xylene resin, polyisocyanates, the weight ratio of carbon fiber are 35-45：35-45：25-35.
Preferably, the high performance polyurethane pressure sensitive adhesive includes the raw material of following parts by weight：80 parts of neoprene, methacrylic acid
70 parts of methyl esters, 70 parts of hydroxyl polysiloxane, 40 parts of xylene resin, 40 parts of polyisocyanates, 30 parts of carbon fiber, olefine resin 30
Part, 14 parts of azo-compound foaming agent, 14 parts of rosin resin, 13.5 parts of triethylamine, 7.5 parts of methylparafynol, polybutadiene 7.5
Part, 1.5 parts of dibutyl tin laurate, 0.75 part of N hydroxymethyl acrylamide.
In the present invention, neoprene is widely used in weatherproof product, and the anti-of pressure sensitive adhesive can be effectively improved for the pressure sensitive adhesive
Weathering capacity, methyl methacrylate are a kind of Organic Chemicals, are applied directly to the pressure sensitive adhesive and can improve its density and ask
Topic can obtain the pressure sensitive adhesive of superior performance, hydroxyl polysiloxane and diformazan by the raw material reaction of the present invention and preparation method
Benzene resin is used cooperatively, and can not only preferably adjust the cohesive force of pressure sensitive adhesive, moreover it is possible to adjust the bonding force of pressure sensitive adhesive, raw material
Between cooperation heightened crosslink density inside pressure sensitive adhesive, solve the problems, such as polyurethane contact adhesive poor performance, present invention system
Standby simple, the polyurethane contact adhesive performance of preparation is high, environmentally friendly, is suitble to large-scale production.
Specific embodiment
The present invention is made with reference to specific embodiment further to explain.
Embodiment one
A kind of high performance polyurethane pressure sensitive adhesive includes the raw material of following parts by weight：70 parts of neoprene, methyl methacrylate 60
Part, 60 parts of hydroxyl polysiloxane, 30 parts of xylene resin, 30 parts of polyisocyanates, 20 parts of carbon fiber, 20 parts of olefine resin, azo
10 parts of compound blowing agents, 10 parts of rosin resin, 9 parts of triethylamine, 5 parts of methylparafynol, 5 parts of polybutadiene, tin dilaurate two
1 part of butyl tin, 0.5 part of N hydroxymethyl acrylamide；
Its preparation method comprises the following steps：
S1 weighs 70 parts of neoprene, 60 parts of methyl methacrylate, 60 parts of hydroxyl polysiloxane, diformazan according to deal proportioning
30 parts of benzene resin, 30 parts of polyisocyanates add in reaction kettle, the temperature of reaction kettle are increased to 60 DEG C, and be sufficiently stirred, and continue
1h obtains component A；
S2 weighs 20 parts of carbon fiber, 20 parts of olefine resin, 10 parts of azo-compound foaming agent, rosin tree according to dosage proportioning
10 parts of fat, 5 parts of triethylamine, 5 parts of methylparafynol, are put into agitating device, are sufficiently stirred 0.5h, obtain component B；
Component B is added in component A by S3, and adds in the triethylamine of 4-8 parts by weight, and 1 weight is added after being sufficiently stirred
The dibutyl tin laurate, the N hydroxymethyl acrylamide of 0.5 parts by weight of part, obtain component C；
Component C is stood 2h by S4 at a temperature of 50 DEG C, and a kind of poly- ammonia of high-performance is can obtain after the time terminates cooling
Ester pressure-sensitive.
Embodiment two
A kind of high performance polyurethane pressure sensitive adhesive includes the raw material of following parts by weight：75 parts of neoprene, methyl methacrylate 65
Part, 65 parts of hydroxyl polysiloxane, 35 parts of xylene resin, 35 parts of polyisocyanates, 25 parts of carbon fiber, 25 parts of olefine resin, azo
12 parts of compound blowing agents, 12 parts of rosin resin, 11 parts of triethylamine, 6 parts of methylparafynol, 6 parts of polybutadiene, tin dilaurate two
1.25 parts of butyl tin, 0.6 part of N hydroxymethyl acrylamide；
Its preparation method comprises the following steps：
S1 weighs 75 parts of neoprene, 65 parts of methyl methacrylate, 65 parts of hydroxyl polysiloxane, diformazan according to deal proportioning
35 parts of benzene resin, 35 parts of polyisocyanates add in reaction kettle, the temperature of reaction kettle are increased to 65 DEG C, and be sufficiently stirred, and continue
1.25h obtains component A；
S2 weighs 25 parts of carbon fiber, 25 parts of olefine resin, 12 parts of azo-compound foaming agent, rosin tree according to dosage proportioning
12 parts of fat, 6 parts of triethylamine, 6 parts of methylparafynol, are put into agitating device, are sufficiently stirred 0.6h, obtain component B；
Component B is added in component A by S3, and adds in the triethylamine of 6 parts by weight, and 1.25 weights are added after being sufficiently stirred
The dibutyl tin laurate, the N hydroxymethyl acrylamide of 0.6 parts by weight of part are measured, obtains component C；
Component C is stood 2.25h by S4 at a temperature of 52.5 DEG C, and a kind of high property is can obtain after the time terminates cooling
It can polyurethane contact adhesive.
Embodiment three
A kind of high performance polyurethane pressure sensitive adhesive includes the raw material of following parts by weight：80 parts of neoprene, methyl methacrylate 70
Part, 70 parts of hydroxyl polysiloxane, 40 parts of xylene resin, 40 parts of polyisocyanates, 30 parts of carbon fiber, 30 parts of olefine resin, azo
14 parts of compound blowing agents, 14 parts of rosin resin, 13.5 parts of triethylamine, 7.5 parts of methylparafynol, 7.5 parts of polybutadiene, February
1.5 parts of dilaurylate, 0.75 part of N hydroxymethyl acrylamide；
Its preparation method comprises the following steps：
S1 weighs 80 parts of neoprene, 70 parts of methyl methacrylate, 70 parts of hydroxyl polysiloxane, diformazan according to deal proportioning
40 parts of benzene resin, 40 parts of polyisocyanates add in reaction kettle, the temperature of reaction kettle are increased to 70 DEG C, and be sufficiently stirred, and continue
1.5h obtains component A；
S2 weighs 30 parts of carbon fiber, 30 parts of olefine resin, 14 parts of azo-compound foaming agent, rosin tree according to dosage proportioning
14 parts of fat, 7.5 parts of triethylamine, 7.5 parts of methylparafynol, are put into agitating device, are sufficiently stirred 0.75h, obtain component B；
Component B is added in component A by S3, and adds in the triethylamine of 4-8 parts by weight, and 1.5 weights are added after being sufficiently stirred
The dibutyl tin laurate, the N hydroxymethyl acrylamide of 0.75 parts by weight of part are measured, obtains component C；
Component C is stood 2.5h by S4 at a temperature of 55 DEG C, and can obtain a kind of high-performance after the time terminates cooling gathers
Urethane pressure sensitive adhesive.
Example IV
A kind of high performance polyurethane pressure sensitive adhesive includes the raw material of following parts by weight：85 parts of neoprene, methyl methacrylate 75
Part, 75 parts of hydroxyl polysiloxane, 45 parts of xylene resin, 45 parts of polyisocyanates, 35 parts of carbon fiber, 35 parts of olefine resin, azo
16 parts of compound blowing agents, 16 parts of rosin resin, 16 parts of triethylamine, 9 parts of methylparafynol, 9 parts of polybutadiene, tin dilaurate two
1.75 parts of butyl tin, 0.9 part of N hydroxymethyl acrylamide；
Its preparation method comprises the following steps：
S1 weighs 85 parts of neoprene, 75 parts of methyl methacrylate, 75 parts of hydroxyl polysiloxane, diformazan according to deal proportioning
45 parts of benzene resin, 45 parts of polyisocyanates add in reaction kettle, the temperature of reaction kettle are increased to 75 DEG C, and be sufficiently stirred, and continue
1.75h obtains component A；
S2 weighs 35 parts of carbon fiber, 35 parts of olefine resin, 16 parts of azo-compound foaming agent, rosin tree according to dosage proportioning
16 parts of fat, 9 parts of triethylamine, 9 parts of methylparafynol, are put into agitating device, are sufficiently stirred 0.9h, obtain component B；
Component B is added in component A by S3, and adds in the triethylamine of 4-8 parts by weight, and 1.75 are added after being sufficiently stirred
The N hydroxymethyl acrylamide of the dibutyl tin laurate of parts by weight, 0.9 parts by weight obtains component C；
Component C is stood 2.75h by S4 at a temperature of 57.5 DEG C, and a kind of high property is can obtain after the time terminates cooling
It can polyurethane contact adhesive.
Embodiment five
A kind of high performance polyurethane pressure sensitive adhesive includes the raw material of following parts by weight：90 parts of neoprene, methyl methacrylate 80
Part, 80 parts of hydroxyl polysiloxane, 50 parts of xylene resin, 50 parts of polyisocyanates, 40 parts of carbon fiber, 40 parts of olefine resin, azo
18 parts of compound blowing agents, 18 parts of rosin resin, 18 parts of triethylamine, 10 parts of methylparafynol, 10 parts of polybutadiene, tin dilaurate
2 parts of dibutyl tin, 1 part of N hydroxymethyl acrylamide；
Its preparation method comprises the following steps：
S1 weighs 90 parts of neoprene, 80 parts of methyl methacrylate, 80 parts of hydroxyl polysiloxane, diformazan according to deal proportioning
50 parts of benzene resin, 50 parts of polyisocyanates add in reaction kettle, the temperature of reaction kettle are increased to 80 DEG C, and be sufficiently stirred, and continue
2h obtains component A；
S2 weighs 40 parts of carbon fiber, 40 parts of olefine resin, 18 parts of azo-compound foaming agent, rosin tree according to dosage proportioning
18 parts of fat, 10 parts of triethylamine, 10 parts of methylparafynol, are put into agitating device, are sufficiently stirred 1h, obtain component B；
Component B is added in component A by S3, and adds in the triethylamine of 8 parts by weight, and 2 parts by weight are added after being sufficiently stirred
Dibutyl tin laurate, the N hydroxymethyl acrylamide of 1 parts by weight, obtain component C；
Component C is stood 3h by S4 at a temperature of 60 DEG C, and a kind of poly- ammonia of high-performance is can obtain after the time terminates cooling
Ester pressure-sensitive.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (5)
1. a kind of high performance polyurethane pressure sensitive adhesive, which is characterized in that include the raw material of following parts by weight：70-90 parts of neoprene, methyl
60-80 parts of methyl acrylate, 60-80 parts of hydroxyl polysiloxane, 30-50 parts of xylene resin, 30-50 parts of polyisocyanates, carbon
20-40 parts of fiber, 20-40 parts of olefine resin, 10-18 parts of azo-compound foaming agent, 10-18 parts of rosin resin, triethylamine 9-18
Part, 5-10 parts of methylparafynol, 5-10 parts of polybutadiene, 1-2 parts of dibutyl tin laurate, N hydroxymethyl acrylamide 0.5-
1 part；
Its preparation method comprises the following steps：
S1, according to deal proportioning weigh 70-90 parts of neoprene, 60-80 parts of methyl methacrylate, 60-80 parts of hydroxyl polysiloxane,
30-50 parts of xylene resin, 30-50 parts of polyisocyanates add in reaction kettle, and the temperature of reaction kettle is increased to 60-80 DEG C, and
It is sufficiently stirred, continues 1-2h, obtain component A；
S2 weighs 20-40 parts of carbon fiber, 20-40 parts of olefine resin, 10-18 parts of azo-compound foaming agent, pine according to dosage proportioning
10-18 parts of botany bar gum, 5-10 parts of triethylamine, 5-10 parts of methylparafynol, are put into agitating device, are sufficiently stirred 0.5-1h, obtain
To component B；
Component B is added in component A by S3, and adds in the triethylamine of 4-8 parts by weight, and 1-2 parts by weight are added after being sufficiently stirred
Dibutyl tin laurate, the N hydroxymethyl acrylamide of 0.5-1 parts by weight, obtain component C；
Component C is stood 2-3h by S4 at a temperature of 50-60 DEG C, and can obtain a kind of high-performance after the time terminates cooling gathers
Urethane pressure sensitive adhesive.
2. a kind of high performance polyurethane pressure sensitive adhesive according to claim 1, which is characterized in that the polyisocyanates is selected from
One kind in IPDI, TDI.
3. a kind of high performance polyurethane pressure sensitive adhesive according to claim 1, which is characterized in that the neoprene, metering system
Sour methyl esters, the weight ratio of hydroxyl polysiloxane are 75-85：65-75：65-75.
4. a kind of high performance polyurethane pressure sensitive adhesive according to claim 1, which is characterized in that the xylene resin, more
Isocyanates, the weight ratio of carbon fiber are 35-45：35-45：25-35.
A kind of 5. high performance polyurethane pressure sensitive adhesive according to claim 1, which is characterized in that the high performance polyurethane pressure
Quick glue includes the raw material of following parts by weight：80 parts of neoprene, 70 parts of methyl methacrylate, 70 parts of hydroxyl polysiloxane, dimethylbenzene
40 parts of resin, 40 parts of polyisocyanates, 30 parts of carbon fiber, 30 parts of olefine resin, 14 parts of azo-compound foaming agent, rosin resin 14
Part, 13.5 parts of triethylamine, 7.5 parts of methylparafynol, 7.5 parts of polybutadiene, 1.5 parts of dibutyl tin laurate, N- methylols
0.75 part of acrylamide.