CN105462386A - Wallpaper mirror surface sizing agent - Google Patents
Wallpaper mirror surface sizing agent Download PDFInfo
- Publication number
- CN105462386A CN105462386A CN201610005969.7A CN201610005969A CN105462386A CN 105462386 A CN105462386 A CN 105462386A CN 201610005969 A CN201610005969 A CN 201610005969A CN 105462386 A CN105462386 A CN 105462386A
- Authority
- CN
- China
- Prior art keywords
- parts
- wallpaper
- minute surface
- viscosity
- surface slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a wallpaper mirror surface sizing agent. The wallpaper mirror surface sizing agent is prepared from, by mass, 100 parts of PVC450 resin powder, 55-65 parts of a plasticizer, 8-10 parts of soybean oil, 3-4 parts of a stabilizing agent, 5-8 parts of pearl powder and 20-25 parts of a viscosity reducer. By means of a specific proportion and a specific preparing method, the pearl powder can be applied to wallpaper as printing paint and smeared on the outmost layer of the wallpaper, the mirror surface effect is achieved, and scratches can be resisted.
Description
Technical field
The present invention relates to a kind of wallpaper printing material.
Background technology
Dioctyl phthalate (DOP) (DioctylPhthalate), be called for short dioctyl ester (DOP), being a kind of organic esters, is a kind of conventional fluidizer.
Can increase solution, colloid, solid, mixture stability chemicals be all stablizer.It can slow down reaction, keeps chemical equilibrium, reduces surface tension, prevents the effects such as light, thermolysis or oxygenolysis.
Pearly pigment transverse section has the physical structure being similar to pearl; Kernel is the mica of low optical specific refractory power, and being wrapped in outer field is the metal oxide of high refractive index, as titanium dioxide or ferric oxide etc.Ideally applying, pearly pigment is scattered in coating equably, and is parallel to material surface formation Multi-layers distributing, and the same in the pearl that coexists, incident beam can pass through multipath reflection, interferes embodiment place pearl effect.
Summary of the invention
The invention provides a kind of wallpaper minute surface slurry, by specific proportioning and preparation method, pearlescence can be applied to as printing coatings in wallpaper, be coated on wallpaper outermost layer, reach mirror effect, and can be anti-scratch.
Technical scheme of the present invention is: a kind of wallpaper minute surface slurry, and according to the mass fraction, its raw material is composed of the following components:
PVC450 resin-oatmeal: 100 parts; Fluidizer: 55 ~ 65 parts; Soybean oil: 8 ~ 10 parts; Stablizer: 3 ~ 4 parts; Pearlescence: 5 ~ 8 parts; Viscosity-depression agent: 20 ~ 25 parts.
Further, according to the mass fraction, its raw material is composed of the following components:
PVC450 resin-oatmeal: 100 parts; Fluidizer: 60 parts; Soybean oil: 9 parts; Stablizer: 3.5 parts; Pearlescence: 6 parts; Viscosity-depression agent: 22 parts.
Further, described fluidizer is dioctyl phthalate (DOP) (DOP).
Further, the maximum diameter of described pearlescence is 200-500nm.
Further, described stablizer is the combination of one or two or more kinds in lead stearate, 2-ethyl acetic acid lead, lead salicylate, tribasic lead stearate, Dythal, tribasic Malaysia lead plumbate or aluminium hydroxide.
The present invention also provides a kind of preparation method of wallpaper minute surface slurry, comprises the following steps:
(1) first stablizer and pearlescence are joined in stirring tank, mix;
(2) soybean oil is joined in stirring tank, mix;
(3) fluidizer and PVC450 resin-oatmeal are joined in stirring tank, mix under 130 ~ 150 degrees Celsius;
(4) add viscosity-depression agent by viscosity drop to 2300 ~ 2400 viscosity, obtain wallpaper minute surface slurry.
The invention has the beneficial effects as follows: by specific proportioning and preparation method, pearlescence (maximum diameter is 200-500nm) can be applied in wallpaper as printing coatings (never using in prior art), be coated on wallpaper outermost layer, reach mirror effect, and can be anti-scratch.
Embodiment
Embodiment 1
A kind of wallpaper minute surface slurry, according to the mass fraction, its raw material is composed of the following components:
PVC450 resin-oatmeal: 100 parts; Fluidizer: 55 parts; Soybean oil: 8 parts; Stablizer: 3 parts; Pearlescence: 5 parts; Viscosity-depression agent: 20 parts.
Embodiment 2
A kind of wallpaper minute surface slurry, according to the mass fraction, its raw material is composed of the following components:
PVC450 resin-oatmeal: 100 parts; Fluidizer: 60 parts; Soybean oil: 9 parts; Stablizer: 3.5 parts; Pearlescence: 6 parts; Viscosity-depression agent: 22 parts.
Embodiment 3
A kind of wallpaper minute surface slurry, according to the mass fraction, its raw material is composed of the following components:
PVC450 resin-oatmeal: 100 parts; Fluidizer: 65 parts; Soybean oil: 10 parts; Stablizer: 4 parts; Pearlescence: 8 parts; Viscosity-depression agent: 25 parts.
The present invention also provides a kind of preparation method of wallpaper minute surface slurry, comprises the following steps:
(1) first stablizer and pearlescence are joined in stirring tank, mix;
(2) soybean oil is joined in stirring tank, mix;
(3) fluidizer and PVC450 resin-oatmeal are joined in stirring tank, mix under 130 ~ 150 degrees Celsius;
(4) add viscosity-depression agent by viscosity drop to 2300 ~ 2400 viscosity, obtain wallpaper minute surface slurry.
The present invention, by specific proportioning and preparation method, makes pearlescence (maximum diameter is 200-500nm) can be applied to as printing coatings in wallpaper, is coated on wallpaper outermost layer, reaches mirror effect, and can be anti-scratch.
Although give detailed description and explanation to the specific embodiment of the present invention above; but what should indicate is; we can carry out various equivalence according to conception of the present invention to above-mentioned embodiment and change and amendment; its function produced do not exceed that specification sheets contains yet spiritual time, all should within protection scope of the present invention.
Claims (6)
1. a wallpaper minute surface slurry, is characterized in that, according to the mass fraction, its raw material is composed of the following components:
PVC450 resin-oatmeal: 100 parts; Fluidizer: 55 ~ 65 parts; Soybean oil: 8 ~ 10 parts; Stablizer: 3 ~ 4 parts; Pearlescence: 5 ~ 8 parts; Viscosity-depression agent: 20 ~ 25 parts.
2. a kind of wallpaper minute surface slurry according to claim 1, it is characterized in that, according to the mass fraction, its raw material is composed of the following components:
PVC450 resin-oatmeal: 100 parts; Fluidizer: 60 parts; Soybean oil: 9 parts; Stablizer: 3.5 parts; Pearlescence: 6 parts; Viscosity-depression agent: 22 parts.
3. a kind of wallpaper minute surface slurry according to claim 1, is characterized in that, described fluidizer is dioctyl phthalate (DOP) (DOP).
4. a kind of wallpaper minute surface slurry according to claim 1, is characterized in that, the maximum diameter of described pearlescence is 200-500nm.
5. a kind of wallpaper minute surface slurry according to claim 1, it is characterized in that, described stablizer is the combination of one or two or more kinds in lead stearate, 2-ethyl acetic acid lead, lead salicylate, tribasic lead stearate, Dythal, tribasic Malaysia lead plumbate or aluminium hydroxide.
6. a preparation method for claim 1-5 arbitrary wallpaper minute surface slurry, is characterized in that: comprise the following steps:
(1) first stablizer and pearlescence are joined in stirring tank, mix;
(2) soybean oil is joined in stirring tank, mix;
(3) fluidizer and PVC450 resin-oatmeal are joined in stirring tank, mix under 130 ~ 150 degrees Celsius;
(4) add viscosity-depression agent by viscosity drop to 2300 ~ 2400 viscosity, obtain wallpaper minute surface slurry.