CN105461356A - Red glaze and preparation method thereof - Google Patents
Red glaze and preparation method thereof Download PDFInfo
- Publication number
- CN105461356A CN105461356A CN201510970324.2A CN201510970324A CN105461356A CN 105461356 A CN105461356 A CN 105461356A CN 201510970324 A CN201510970324 A CN 201510970324A CN 105461356 A CN105461356 A CN 105461356A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- red
- preparation
- red glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a red glaze and a preparation method thereof, and relates to the technical field of glaze production. The red glaze is characterized by being prepared from the following raw material components in parts by weight: 30 to 34 parts of glaze stone, 22 to 24 parts of kiln slag, 11 to 12 parts of lead crystal material, 10 to 12 parts of white glass, 1 to 2 parts of pink salt, 1 to 2 parts of realgar, 1 to 2 parts of wine ferrous fluoborate, 10 to 12 parts of green glass, 2 to 3 parts of lime-ash soil and 3 to 4 parts of cement. The preparation method comprises the following steps: weighing all the component raw materials according to the proportions, and then respectively performing wet grinding; mixing the ground materials, and then screening through a 200 to 400-mesh screen; during glazing, soaking or pouring is required to be performed on an unglazed porcelain body for once, and after drying, spraying by using glaze slip containing 50 percent of water for three times, wherein a glaze layer is thick in the upper part and thin in the lower part, the glaze thickness is 1.5 to 2.0mm. The red glaze is pure in color, and easy to fire, and spots and knots are not liable to occur.
Description
Technical field:
The present invention relates to glaze production technical field, specifically a kind of red glaze and preparation method thereof.
Background technology:
Pottery is then the general name of pottery, stoneware and porcelain.Every potter's clay and these two kinds of clays of different nature of china clay are raw material, and the implements made through technical process such as batching, shaping, dry, roastings can be pottery.In prior art, red glaze is mainly by increasing the content of pigment, and then the intensity, hardness etc. of the symmetrical porcelain of pigment have certain disadvantageous effect, and color is impure, uneven, easily forms spot or node after firing.
Summary of the invention:
Technical problem to be solved by this invention is to provide a kind of pure color, easily fires, and is not easy red glaze causing spot and node and preparation method thereof.
Solve technical problem adopt following technical scheme:
A kind of red glaze, it is characterized in that: be made up of following feed composition by weight, glaze fruit 30 ~ 34 parts, kiln slag 22 ~ 24 parts, plumbous brilliant 11 ~ 12 parts, material, white glass 10 ~ 12 parts, red salt 1 ~ 2 part, realgar 1 ~ 2 part, wine ferrous fluoroborate 1 ~ 2 part, green glass 10 ~ 12 parts, two-ash soil 2 ~ 3 parts, trinity mixture fill 3 ~ 4 parts.
A kind of red glaze, it is characterized in that: be made up of following feed composition by weight, glaze fruit 32 parts, kiln slag 23 parts, plumbous brilliant 11.5 parts, material, white glass 11 parts, red salt 1 ~ 2 part, realgar 1.5 parts, wine ferrous fluoroborate 1.5 parts, green glass 11 parts, two-ash soil 2.5 parts, trinity mixture fill 3.5 parts.
A preparation method for red glaze, is characterized in that: comprise the following steps,
1) take each component raw material by proportioning, then carry out wet grinding respectively;
2) by the mixing of materials after grinding, 200 ~ 400 eye mesh screen screenings are then crossed;
3) during glazing, require on the porcelain body of biscuiting, soak or water once, after dry, spray three times again with the glaze slip of moisture 50%, glaze layer is upper thick and lower thin, the thick 1.5 ~ 2.0mm of glaze.
Temperature of burning paper as sacrificial offerings after described red glaze glazing is 1300 DEG C.
Play pure color in red glaze in porcelain in the present invention, intensity is high.Sintering temperature in the present invention, time controling more reasonable.
The invention has the beneficial effects as follows: pure color of the present invention, easily fire, be not easy to cause spot and node.
Embodiment:
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Embodiment one
A kind of red glaze, is made up of following feed composition by weight, glaze fruit 30 parts, kiln slag 22 parts, plumbous brilliant 11 parts, material, white glass 10 parts, red salt 1 part, realgar 1 part, wine ferrous fluoroborate 1 part, green glass 10 parts, two-ash soil 2 parts, trinity mixture fill 3 parts.
A preparation method for red glaze, comprises the following steps,
4) take each component raw material by proportioning, then carry out wet grinding respectively;
5) by the mixing of materials after grinding, 200 ~ 400 eye mesh screen screenings are then crossed;
6) during glazing, require on the porcelain body of biscuiting, soak or water once, after dry, spray three times again with the glaze slip of moisture 50%, glaze layer is upper thick and lower thin, the thick 1.5 ~ 2.0mm of glaze.
Temperature of burning paper as sacrificial offerings after red glaze glazing is 1300 DEG C.
Embodiment two
A kind of red glaze,: be made up of following feed composition by weight, glaze fruit 32 parts, kiln slag 23 parts, plumbous brilliant 11.5 parts, material, white glass 11 parts, red salt 1 ~ 2 part, realgar 1.5 parts, wine ferrous fluoroborate 1.5 parts, green glass 11 parts, two-ash soil 2.5 parts, trinity mixture fill 3.5 parts.
A preparation method for red glaze, comprises the following steps,
7) take each component raw material by proportioning, then carry out wet grinding respectively;
8) by the mixing of materials after grinding, 200 ~ 400 eye mesh screen screenings are then crossed;
9) during glazing, require on the porcelain body of biscuiting, soak or water once, after dry, spray three times again with the glaze slip of moisture 50%, glaze layer is upper thick and lower thin, the thick 1.5 ~ 2.0mm of glaze.
Temperature of burning paper as sacrificial offerings after described red glaze glazing is 1300 DEG C.
Embodiment three
A kind of red glaze, is made up of following feed composition by weight, glaze fruit 34 parts, kiln slag 24 parts, plumbous brilliant 12 parts, material, white glass 12 parts, red salt 2 parts, realgar 2 parts, wine ferrous fluoroborate 2 parts, green glass 12 parts, two-ash soil 3 parts, trinity mixture fill 4 parts.
A preparation method for red glaze, comprises the following steps,
1) take each component raw material by proportioning, then carry out wet grinding respectively;
2) by the mixing of materials after grinding, 200 ~ 400 eye mesh screen screenings are then crossed;
3) during glazing, require on the porcelain body of biscuiting, soak or water once, after dry, spray three times again with the glaze slip of moisture 50%, glaze layer is upper thick and lower thin, the thick 1.5 ~ 2.0mm of glaze.
Temperature of burning paper as sacrificial offerings after red glaze glazing is 1300 DEG C.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (4)
1. a red glaze, it is characterized in that: be made up of following feed composition by weight, glaze fruit 30 ~ 34 parts, kiln slag 22 ~ 24 parts, plumbous brilliant 11 ~ 12 parts, material, white glass 10 ~ 12 parts, red salt 1 ~ 2 part, realgar 1 ~ 2 part, wine ferrous fluoroborate 1 ~ 2 part, green glass 10 ~ 12 parts, two-ash soil 2 ~ 3 parts, trinity mixture fill 3 ~ 4 parts.
2. the red glaze of one according to claim 1, it is characterized in that: be made up of following feed composition by weight, glaze fruit 32 parts, kiln slag 23 parts, plumbous brilliant 11.5 parts, material, white glass 11 parts, red salt 1 ~ 2 part, realgar 1.5 parts, wine ferrous fluoroborate 1.5 parts, green glass 11 parts, two-ash soil 2.5 parts, trinity mixture fill 3.5 parts.
3. the preparation method of a kind of red glaze according to claim 1 and 2, is characterized in that: comprise the following steps,
1) take each component raw material by proportioning, then carry out wet grinding respectively;
2) by the mixing of materials after grinding, 200 ~ 400 eye mesh screen screenings are then crossed;
3) during glazing, require on the porcelain body of biscuiting, soak or water once, after dry, spray three times again with the glaze slip of moisture 50%, glaze layer is upper thick and lower thin, the thick 1.5 ~ 2.0mm of glaze.
4. the red glaze of one according to claim 1, is characterized in that: the temperature of burning paper as sacrificial offerings after described red glaze glazing is 1300 DEG C.