CN105420543A - 一种黄铜合金及其制备方法 - Google Patents
一种黄铜合金及其制备方法 Download PDFInfo
- Publication number
- CN105420543A CN105420543A CN201510896064.9A CN201510896064A CN105420543A CN 105420543 A CN105420543 A CN 105420543A CN 201510896064 A CN201510896064 A CN 201510896064A CN 105420543 A CN105420543 A CN 105420543A
- Authority
- CN
- China
- Prior art keywords
- brass
- brass alloys
- antimony
- phosphorus
- brass alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种黄铜合金及其制备方法,其中,黄铜合金按重量份数比,其组成为:铜:57-60份,铋:0.5-1.0份,铅:0-0.25份,磷:0.005-0.05份,锑:0.1-1.0份,其余为锌及不可避免的杂质组成。
Description
技术领域
本发明涉及黄铜合金及其制备方法。
背景技术
铅作为一种对人体及环境危害极大的元素,比如铅对人体血液及神经系统,特别是对儿童的肾和脑神经可造成不可逆转的损伤。近年来,世界各国对铅给人体及环境带来的危害的认识越来越深入,并达成了广泛的共识,政府、各种组织针对铅的危害控制也形成了各种限令。比如:欧盟ROHS指令(电气电子设备有害物质之禁用令)2003年1月正式颁布,2006年7月1日正式实施,中国亦随后颁布了《电子信息产品污染控制管理办法》并于2007年3月1日起实施,近来又新颁布了水龙头国家环保标准《环境标志产品技术要求水嘴》,并从2008年4月1日开始正式实行。这一系列环保举措,都对金属中重金属元素铅的含量或析出量予以了严格限制。鉴于以上原因,开发加工用无铅铜合金材料,既符合环保发展趋势,又具有良好的市场前景。
发明内容
本发明的目的在于克服现有技术的不足,提供了环保的黄铜合金及其制备方法。
为解决上述技术问题,本发明采用的技术方案是:一种黄铜合金,按重量份数比,其组成为:铜:57-60份,铋:0.5-1.0份,铅:0-0.25份,磷:0.005-0.05份,锑:0.1-1.0份,其余为锌及不可避免的杂质组成。
其中,磷、锑均以中间合金形式加入或来自本身含有的再生废料中。
同时,本发明提供了一种所述的黄铜合金的制备方法:
采用工频有芯感应电炉在1200℃~1300℃熔化权利要求1的合金,并在1100℃~1200℃水平连续铸造为黄铜锭,在700℃~800℃采用挤压机进行挤压;中间退火采用500℃~60℃,1~4小时,去应力退火采用300~400℃,3~6小时。
与现有技术相比,本发明的有益效果是:
本发明低铅黄铜合金具有优良的可锻性和较好的切削加工性能及优良的耐腐蚀性能,并且用于供水系统管路装置、卫浴五金时具有一定的杀菌功能。
具体实施方式
下面结合具体实施方式对本发明作进一步的说明。
本发明提供一种黄铜合金,按重量份数比,其组成为:铜:57-60份,铋:0.5-1.0份,铅:0-0.25份,磷:0.005-0.05份,锑:0.1-1.0份,其余为锌及不可避免的杂质组成。
其中,磷、锑均以中间合金形式加入或来自本身含有的再生废料中。
同时,本发明提供了一种所述的黄铜合金的制备方法:
采用工频有芯感应电炉在1200℃~1300℃熔化权利要求1的合金,并在1100℃~1200℃水平连续铸造为黄铜锭,在700℃~800℃采用挤压机进行挤压;中间退火采用500℃~60℃,1~4小时,去应力退火采用300~400℃,3~6小时。
显然,本发明的上述实施例仅仅是为清楚地说明本发明所作的举例,而并非是对本发明的实施方式的限定。对于所属领域的普通技术人员来说,在上述说明的基础上还可以做出其它不同形式的变化或变动。这里无需也无法对所有的实施方式予以穷举。凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等,均应包含在本发明权利要求的保护范围之内。
Claims (3)
1.一种黄铜合金,其特征在于:按重量份数比,其组成为:铜:57-60份,铋:0.5-1.0份,铅:0-0.25份,磷:0.005-0.05份,锑:0.1-1.0份,其余为锌及不可避免的杂质组成。
2.根据权利要求1所述的黄铜合金,其特征在于:磷、锑均以中间合金形式加入或来自本身含有的再生废料中。
3.一种根据权利要求1所述的黄铜合金的制备方法:
采用工频有芯感应电炉在1200℃~1300℃熔化权利要求1的合金,并在1100℃~1200℃水平连续铸造为黄铜锭,在700℃~800℃采用挤压机进行挤压;中间退火采用500℃~60℃,1~4小时,去应力退火采用300~400℃,3~6小时。